Abstract
Established techniques for ion implantation rely on technically advanced and costly machines like particle accelerators that only few research groups possess. We report here about a new and surprisingly simple ion implantation method that is based upon a widespread laboratory instrument: The scanning electron microscope. We show that it can be utilized to ionize atoms and molecules from the restgas by collisions with electrons of the beam and subsequently accelerate and implant them into an insulating sample by the effect of a potential building up at the sample surface. Our method is demonstrated by the implantation of nitrogen ions into diamond and their subsequent conversion to nitrogen vacancy centres which can be easily measured by fluorescence confocal microscopy. To provide evidence that the observed centres are truly generated in the way we describe, we supplied a 98% isotopically enriched 15N gas to the chamber, whose natural abundance is very low. By employing the method of optically detected magnetic resonance, we were thus able to verify that the investigated centres are actually created from the 15N isotopes. We also show that this method is compatible with lithography techniques using e-beam resist, as demonstrated by the implantation of lines using PMMA.
Similar content being viewed by others
Introduction
The development of the electron microscope in the 1930s was a milestone in many fields of natural sciences1. Its high resolution enabled scientists to investigate very small objects like cells or large molecules. The wide area of application and the gradually dropping costs of electron microscopes led to the fact that today most natural science institutes have such a device. In this research paper we report about another application of the electron microscope apart from its imaging technique, that was to our best knowledge not published up to now. We demonstrate here that the implantation of ions is feasible by the simple means of a scanning electron microscope (SEM) only. Usually an ion accelerator is needed for a precise implantation of atoms, which is not available in many research facilities because of the technical complexity and correspondingly high costs.
The proof of principle of our concept is done with nitrogen atoms/molecules and their conversion and detection as nitrogen vacancy (NV) centres2. If not explicitly stated otherwise by writing NV centre we refer to the negatively charged type (NV−). The NV centre consists of a substitutional nitrogen atom next to a vacancy in the diamond lattice. The centre has a zero phonon optical transition at a wavelength of 638 nm3 between its triplet ground state 3A2 and its first excited state 3E, which is also a spin triplet. In addition, there is an other decay path comprising a metastable singlet state. The ground state triplet has a splitting at zero magnetic field of 2.87 GHz4 between the m S = 0 and m S = ±1 electron spin sublevels. This energy level constitution opens the possibility for the initialization, manipulation and read out of the centres quantum state and therefore its employment as a qubit5,6,7. The method described here is highly relevant for the research work on NV centres because nitrogen implantation into ultrapure diamond8 is a often used technique for the generation of NV centres.
Results
Identification of NV centres
To demonstrate our method a rectangular area on the front side of an electronic grade diamond (\({{\rm{N}}}_{{\rm{s}}}^{0}\le 5\) ppb) was irradiated with a low energy electron beam in a SEM. The SEM was equipped with an additional gas inlet, so that isotopically enriched nitrogen (98% 15N) can be directed into the chamber. After the diamond was annealed in vacuum to form NV centres, fluorescence images and spectra of the sample were recorded. Fig. 1a) shows a fluorescence spectrum of the central region of the electron beam irradiated area of the sample. The zero phonon line (ZPL) of NV− is clearly visible at 638 nm. Additionally, the ZPL of the neutrally charged NV centre (NV0) can be seen at 575 nm. Both are accompanied by their characteristic phonon side bands. These spectra could be recorded everywhere in the irradiated area, proving that the generated defects are really NV centres. No NV centres could be found in the other sectors of the sample. But a lower fluorescence signal could be measured around the irradiated area, quickly dropping down to the point where individual centres were resolvable. A possible explanation for this effect is discussed below. Figure 1b) shows a fluorescence image of these single centres near the irradiated area. Conducted photon antibunching measurements9 and taken spectra verified that the fluorescing spots were indeed single NV centres.
Identification of nitrogen-15
The generated NV centres were also investigated with optically detected magnetic resonance (ODMR) measurements to identify whether their constituting nitrogen atoms are of the isotope type 14N or 15N. Their distinction is possible because of the different nuclear spin of 14N (I = 1) and 15N (I = 1/2) that leads to a differing hyperfine coupling to the electron spin (S = 1) of the NV centre. To make a statistically sound statement, the ODMR spectra of 49 centres were recorded in a batch measurement. Figure 2 depicts two ODMR spectra for one of these centres, where the detected fluorescence is plotted over the irradiated microwave frequency. Figure 2a shows the continuous wave (cw) spectrum of this centre over a range from 2.77 GHz to 2.97 GHz. The cw spectrum exhibits the expected behavior for a NV centre at zero magnetic field with the single dip in fluorescence at 2.87 GHz. This resonance corresponds to the microwave excited transition between the m S = 0 and m S = ±1 electron spin sublevels. In Fig. 2b a pulsed spectrum of the same NV centre is depicted. Here the 2.87 GHz resonance is further investigated in a range of 20 MHz. The spectrum shows the typical dual separation of the dip that is expected for the hyperfine interaction between a nuclear spin of I = 1/2 and the electron spin of S = 1 of the NV centre at zero magnetic field. This hyperfine interaction leads to a twofold splitting of the electron spin sublevels and hence the dual separation of the dip in the fluorescence. The magnitude of this hyperfine splitting is determined by a fit of a Lorentzian function to the data that yields a separation of 3 MHz.
This value is in good agreement with data from the literature10 for the hyperfine splitting in the ground state of a NV centre that comprises a 15N atom. In the case of the constituting nitrogen atom of the NV centre is a 14N isotope, a threefold splitting of the electron spin sublevels and hence in the dip in the fluorescence would be expected. The magnitude of this splitting is stated in the literature as −2.16 MHz11. Additional splittings due to the hyperfine interaction of the NV electron spin with other nuclear spins are possible and were indeed observed in some of the recorded spectra. Because only a nuclear spin of I ≠ 0 gives rise to hyperfine interactions, the most common nuclei for this interaction are 13C isotopes. For a profound treatment of this matter we refer to the corresponding literature12. Figure 3 shows a histogram of all measured centres that could be identified as 15NV centre grouped by the magnitude of their splitting. All these centres have a twofold splitting of the 2.87 GHz resonance that ranges from 2.85 MHz to 3.95 MHz.
Investigation of generated structures
Following the analysis of the electron irradiation process on the front side of the sample, an electrically insulating PMMA mask comprising a set of lines and circles was created on the surface of the back side by electron beam lithography. The sector of the diamond containing the openings was subsequently irradiated with the electron beam of a SEM with no gas inlet. After the annealing process, confocal investigations of this sector showed an increased signal at the spots were the openings of the mask have been. Again recorded spectra confirmed that the detected fluorescence originated from NV centres. Figure 4a shows a fluorescence image of one of the created lines, where the line itself is sharply delimited from the background. The white spot at the left side of the line’s lower edge is a contamination. In Fig. 4b a graph depicts the averaged fluorescence along the cross section of this line and the surrounding background (without the contamination). From this the width of the line is determined as 10.67 μm, which is fairly close to the intended value of 10 μm. While the lines exhibited a moderate density of NV centres, the circles only featured a very low density of NV centres. In fact only the signal of one set of circles that consisted of a 10 μm, a 5 μm and a 3 μm circle could be located with the confocal microscope. The signal was so weak that it was hardly distinguishable from the background.
Discussion
The mechanism for ion implantation via a scanning electron microscope is depicted in Fig. 5 and can be described as follows: The electron beam of the SEM is focused onto the sample. Due to the electrically insulating character of the diamond, the electrons can not run off and start to accumulate in it. As a result, a negative electrical potential builds up that causes an electric field. Because this field also repels the electrons of the beam, the potential however only builds up to the point when it is equal to the acceleration voltage of the electron gun of the SEM. Furthermore, the 15N molecules which are led into the chamber and therefore to the sample by the gas inlet (or in the case of the back side irradiation simply the 14N residual gas molecules) interact with the electrons of the SEM beam by impact ionization yielding nitrogen ions. The positively charged ions then get attracted by the negative potential in the sample. On the acceleration track they obtain a kinetic energy corresponding to the accelerating voltage. With the obtained energy, the ions are now able to penetrate into the sample and interact with the atoms of the sample material e.g. generating vacancies like in conventional ion implantation. While some of the molecular ions are already dissociated by the impact ionization process, the rest of them breaks apart during the collision with the sample surface. In a subsequent annealing process the vacancies become mobile and thereby enabling NV centre formation13.
Even so the method was demonstrated by the implantation of nitrogen ions into diamond, it is expected that because of the underlying physical processes (impact ionization, coulomb interaction) it will work for any other ion species in the gaseous state and also for other insulating substrates. Since the kinetic energy of the ions is limited by the accelerating voltage of the electron gun of the SEM, energies from less than 1 keV up to 30 keV should be feasible. In 27 of our 49 recorded ODMR spectra the observed hyperfine splitting could be clearly assigned to NV centres which are constituted of a 15N isotope. No spectra could be assigned to NV centres comprising a 14N isotope. That corresponds to a ratio of at least 55.1% of 15N containing centres. Considering the natural abundance of the 15N isotope of 0.364%14, nitrogen atoms that got into the sample during the manufacturing process or their incorporation during other steps of the experiment by accident can be ruled out as the source of the 15NV centres. The conducted experiments prove that the generated NV centres are truly formed from the implanted 15N ions and therefore that our concept is correct.
We attribute the deviation of the magnitude of the splitting of some centres from the literature value to the particular surface proximity of the NV centres, that arises from the low implantation energy of the nitrogen ions (≤700 eV). Because near the surface the centres are exposed to strain which influences the magnitude of the splitting15. Furthermore, a spectral broadening was observed for some centres that is probably induced by paramagnetic impurities which are located at the surface as well16. The remaining 22 centres that could not be assigned probably either had such a disturbing environment that their spectra were too much deformed to reliably assign them to 15NV or 14NV centres or the tracker simply failed to keep track of them. Nevertheless, the majority of the centres exhibit fluorescence and ODMR spectra that are comparable to those of NV centres created by classical ion implantation8,10,17.
The observation that a lower density of NV centres was also generated around the area which was irradiated with electrons can be explained by the presented implantation mechanism as well. Because the delivered nitrogen molecules distribute equally in the chamber of the SEM and will have different directions of movement, the vector of motion of some of the nitrogen particles will confine a smaller angle with the sample surface then others. If the angle is small enough the deflection of the particle, that is induced by the electron generated potential in the sample, will not suffice to direct it on a trajectory where it hits the sample in the irradiated area. The ion will instead collide with the surface only when it has already passed the irradiated area, so that it is implanted a bit away from it.
Conclusion
In conclusion, we have introduced a new method for the implantation of ions into electrically insulating material. This method is based on the impact ionization of gaseous particles, which are brought into interaction with an electron beam and subsequently attracted by a potential induced by the same electron beam, which eventually leads to the implantation of the ions into the insulating sample. It stands out from other established implantation techniques because of its technical simplicity and the associated low costs. The proof of principle was done with nitrogen atoms/molecules that could be verified through generated nitrogen vacancy centres. While fluorescence spectra show that the created colour centres are indeed NV centres, the recorded ODMR spectra prove by identification of the 15N isotopes in the centres, that the way the N atoms got into the sample material is as we described it. We also showed that the location of the implanted ions can be restricted to small areas by using an electrically insulating PMMA mask.
Methods
An electronic grade, single crystal diamond, grown by chemical vapor deposition, was used as a sample in this experiment. The manufacturer, Element 6, stated the initial nitrogen content as below 5 ppb. In a first step the diamond was cleaned in an ultrasonic bath of acetone followed by isopropyl alcohol. Then a 661 μm × 516.4 μm large area on the front side of the sample was irradiated with a low energy electron beam (E kin = 700 eV) with a beam current of 35 pA for about 100 hous in a SEM (DSM 982 GEMINI Zeiss), which was modified with an additional gas inlet. The gas inflow, which comes from a metallic cylinder filled with isotopically enriched nitrogen (98% 15N, euriso-top) is precisely controlled with a needle valve. The gas is then guided via a silicone tube to a copper ring that is placed between the beam exit and the sample. Six small holes were drilled on the lower part of the inner face of the ring to direct the gas onto the sample. The pressure in the chamber was regulated to 6⋅10−6 mbar. After the implantation process the sample was annealed in vacuum at 800 °C for 2 hours to trigger the NV centre formation and subsequently cleaned by etching in a mixture of nitric acid, sulfuric acid and perchloric acid at boiling point for 4 hours. Fluorescence images and spectra of single NV centres and NV ensembles were recorded with a home build confocal microscope equipped with single-photon counting modules and a CCD supported grating spectrometer using a 0.95 NA air objective and a laser light wavelength of 532 nm. Additionally, spectra of ODMR measurements of the ground state of single centres were recorded with another setup that uses the same laser light wavelength and a 1.35 NA oil objective. ODMR is based on a decrease in the emitted fluorescence intensity of the centre caused by the depopulation of the m S = 0 state that is achieved by scanning microwaves in an appropriate frequency range. The ODMR data were recorded without applying a magnetic field (B = 0) and includes continuous wave spectra (simultaneous microwave and optical excitation) as well as pulsed spectra (applying a π pulse followed by optical illumination).
After the evaluation of the first electron irradiation process with the optical setup, the sample was once again cleaned in an ultrasonic bath of acetone followed by isopropyl alcohol. Then the back side of the sample was spin coated with a PMMA electron beam resist at 3500 rpm for 30 s and another 30 s at 3500 rpm down to 0 rpm. Following this a set of lines (width of 10 μm) and circles (diameter of 10 μm to 0.5 μm) was drawn by exposing the sample to a beam of focused electrons at the dual beam microscope Nova NanoLab 200 from FEI and subsequent developing. This procedure formed an electrically insulating mask consisting of PMMA on the sample surface. Afterwards, in the sector of the diamond comprising the set of structures, a 400 μm × 300 μm large area was irradiated with the electron beam (E kin = 800 eV, 1 nA) of a SEM (CS44 CamScan) with no gas inlet for 96 hours. The chamber pressure was 5•10−6 mbar. After the irradiation process the mask was removed in an ultrasonic bath of acetone. The following annealing and etching processes were under the same conditions as before and the subsequently recorded fluorescence images and spectra were taken with the aforementioned confocal microscope.
References
Freundlich, M. Origin of the electron microscope. Science, New Series 142, 185–188 (1963).
Doherty, M. W. et al. The nitrogen-vacancy colour centre in diamond. Physics Reports 528, 1–45 (2013).
Du Preez, L. Electron paramagnetic resonance and optical investigations of defect centres in diamond, University of Witwaters (1965).
Gruber, A. et al. Scanning confocal optical microscopy and magnetic resonance on single defect centers. Science 276, 2012–2014 (1997).
Jelezko, F., Gaebel, T., Popa, I., Gruber, A. & Wrachtrup, J. Observation of coherent oscillations in a single electron spin. Phys. Rev. Lett. 92, 076401 (2004).
Neumann, P. et al. Quantum register based on coupled electron spins in a room-temperature solid. Nat. Phys. 6, 249–253 (2010).
Childress, L. et al. Coherent dynamics of coupled electron and nuclear spin qubits in diamond. Science 314, 281–285 (2006).
Meijer, J. et al. Generation of single color centers by focused nitrogen implantation. Applied Physics Letters 87, 261909 (2005).
Kurtsiefer, C., Mayer, S., Zarda, P. & Weinfurter, H. Stable solid-state source of single photons. Phys. Rev. Lett. 85, 290–293 (2000).
Rabeau, J. R. et al. Implantation of labelled single nitrogen vacancy centers in diamond using 15n. Applied Physics Letters 88, 023113 (2006).
Smeltzer, B., McIntyre, J. & Childress, L. Robust control of individual nuclear spins in diamond. Phys. Rev. A 80, 050302 (2009).
Dréau, A., Maze, J., Lesik, M., Roch, J. & Jacques, V. High-resolution spectroscopy of single nv defects coupled with nearby 13c nuclear spins in diamond. Phys. Rev. B 85, 134107 (2012).
Pezzagna, S., Naydenov, B., Jelezko, F., Wrachtrup, J. & Meijer, J. Creation efficiency of nitrogen-vacancy centres in diamond. New Journal of Physics 12, 065017 (2010).
Lide, D. CRC Handbook of Chemistry and Physics: A Ready-reference Book of Chemical and Physical Data, 86 edn (CRC-Press, 2005).
Doherty, M. et al. Theory of the ground-state spin of the nv− center in diamond. Phys. Rev. B 85, 205203 (2012).
Ofori-Okai, B. et al. Spin properties of very shallow nitrogen vacancy defects in diamond. Phys. Rev. B 86, 081406 (2012).
Loretz, M., Pezzagna, S., Meijer, J. & Degen, C. Nanoscale nuclear magnetic resonance with a 1.9-nm-deep nitrogen-vacancy sensor. Applied Physics Letters 104, 033102 (2014).
Acknowledgements
The authors acknowledge financial support from the Free State of Saxony under the program SAW-2015-IOM-1 and Volkswagen Foundation. We also acknowledge support from the German Research Foundation (DFG) and Universität Leipzig within the program of Open Access Publishing. The authors acknowledge further the technical support from J. Starke and C. Pahnke.
Author information
Authors and Affiliations
Contributions
J.M. conceived the experiments. S.B., N.R., St.J. and R.J. conducted the experiments. S.B. analyzed the results and wrote the paper. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Becker, S., Raatz, N., Jankuhn, S. et al. Nitrogen implantation with a scanning electron microscope. Sci Rep 8, 32 (2018). https://doi.org/10.1038/s41598-017-18373-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-18373-z
- Springer Nature Limited
This article is cited by
-
Coulomb-driven single defect engineering for scalable qubits and spin sensors in diamond
Nature Communications (2019)
-
Assessment of residents’ total environmental exposure to heavy metals in China
Scientific Reports (2019)