Abstract
Graphene has been extensively utilized as an electrode material for nonaqueous electrochemical capacitors. However, a comprehensive understanding of the charging mechanism and ion arrangement at the graphene/electrolyte interface remain elusive. Herein, a gap-enhanced Raman spectroscopic strategy is designed to characterize the dynamic interfacial process of graphene with an adjustable number of layers, which is based on synergistic enhancement of localized surface plasmons from shell-isolated nanoparticles and a metal substrate. By employing such a strategy combined with complementary characterization techniques, we study the potential-dependent configuration of adsorbed ions and capacitance curves for graphene based on the number of layers. As the number of layers increases, the properties of graphene transform from a metalloid nature to graphite-like behavior. The charging mechanism shifts from co-ion desorption in single-layer graphene to ion exchange domination in few-layer graphene. The increase in area specific capacitance from 64 to 145 µF cm–2 is attributed to the influence on ion packing, thereby impacting the electrochemical performance. Furthermore, the potential-dependent coordination structure of lithium bis(fluorosulfonyl) imide in tetraglyme ([Li(G4)][FSI]) at graphene/electrolyte interface is revealed. This work adds to the understanding of graphene interfaces with distinct properties, offering insights for optimization of electrochemical capacitors.
Similar content being viewed by others
Introduction
The pursuit of energy storage and conversion systems with higher energy densities continues to be a focal point in contemporary energy research. electrochemical capacitors represent an emerging class of electrochemical energy devices that bridge the gap between conventional capacitors and batteries. They amalgamate the high-power attributes of conventional capacitors with the high-energy characteristics inherent to batteries1. The remarkable power-handling capabilities and extended cycling lifespan of electrochemical capacitors come at the cost of reduced energy density. Recently, material-focused research has been carried out to mitigate this trade-off by fine-tuning the performance of carbon electrodes2,3, and by incorporating ionic liquid electrolytes engineered to withstand higher voltages4. Both strategies have achieved notable improvements in energy density while preserving power density.
Graphene is a promising carbon material for use as an electrode in electrochemical energy storage devices due to its stable physical structure, large specific surface area (~ 2600 m2·g–1), and excellent electrical conductivity5. The first report on the use of graphene as an electrode material for electrochemical capacitors was published in 20086, showing the great potential of its application in electrochemical storage devices. In the realm of electrochemical capacitor applications, graphene materials present distinctive advantages. Their outstanding specific surface area enables the attainment of higher specific capacitance and energy storage density. In addition, their exceptional electrical and thermal conductivity work synergistically to diminish internal resistances within capacitors, thereby elevating charge-discharge rates and power densities. The layered structure facilitates electrolyte wetting and ion adsorption/desorption, while the stable stacking of layers effectively leverages double layer surface area to augment capacitance, thus facilitating ion diffusion7. Single-layer graphene serves as a typical zero-bandgap material, which exhibits a behavior mechanism similar to that of graphite as the number of layers increases8,9,10,11. This evolution from metalloid to graphitic-like attributes triggers consequential changes in the chemical nature of graphene, thereby exerting a pronounced influence on the ensuing electrochemical behavior at interfaces. On the other hand, the exploration of innovative electrolytes plays a pivotal role in enhancing electrochemical capacitor performance, encompassing the electrochemical window, safety, and adaptability in broad temperature ranges12. Solvate ionic liquids stand out by not only harnessing the advantages of ionic liquids but also leveraging the introduction of alkali metal ions to significantly boost system conductivity13,14. Lithium bis(fluorosulfonyl) imide (LiFSI) with a weakly associated anion can promote ion dissociation. Glyme molecules (CH3O(CH2-CH2O)nCH3), serving as multidentate ligands, create stable complexes with alkali metal cations in electrolytes. These complexes contribute to high conductivity, low viscosity, and low melting points in the system, thereby further reducing impedance and enhancing rate capability15. Accurately revealing the graphene/solvate ionic liquid interface can provide profound insights into interfacial behavior, which benefits understanding the energy storage mechanism and guiding the design of graphene-based nonaqueous electrochemical capacitors.
The mechanism of charge storage in electrochemical capacitors has traditionally been attributed to the electrosorption of ions on the surface of a charged electrode to form an electrical double layer16. Nevertheless, contemporary empirical observations have unveiled a more intricate mechanism, wherein factors such as relative pore/ion sizes17,18, along with desolvation effects19,20, play pivotal roles. Numerous inquiries concerning the charging mechanism in practical devices persist without clear answers. In particular, how the configuration of adsorbed ions influences the capacitance, or whether the exchange of ions with opposite charges, coupled with the ejection of co-ions from charged electrodes, contributes to the formation of the electrical double layer. Therefore, exploring the charging mechanism of the electrical double layer and understanding its relationship with the electrochemical performance remains a challenge so far. Although the charging mechanism has been intensively investigated by various advanced experimental techniques1,21 and theoretical simulations22,23, the charge/ion separation mechanism during the dynamic process of interfacial polarization at the graphene/electrolyte interface is still not well understood, hindering the large-scale application of graphene materials in electrochemical capacitor devices.
Raman spectroscopy stands as a powerful technique for in-situ characterization of electrochemical interfaces at the molecular level. Nevertheless, the plasmon resonance at graphene surfaces lies beyond the visible light range, thereby precluding electromagnetic field enhancement. Meanwhile, its chemical enhancement factor hovers around 102, thus rendering Raman signals insufficient24,25. Therefore, obtaining Raman signals at graphene surfaces remains a challenge. Shell-isolated nanoparticle-enhanced Raman spectroscopy (SHINERS) has emerged as one of the most effective methods for probing interfacial processes. For example, it has been extensively applied to investigate interfacial reactions in aqueous solutions26,27. The principle of SHINERS is to coat an ultra-thin (~ 2 nm thick) and inert shell on the surface of metal nanoparticles with surface-enhanced Raman spectroscopy (SERS) activity, whose enhancement is mainly from the enhanced near electric field generated by surface plasmon (SP), which is the collective oscillation of free electrons in plasmonic nanomaterials such as gold, silver, and copper under the excitation of electromagnetic radiation. The SHINERS avoid direct contact of the measured species with plasmonic nanomaterials and allow for tracking an interfacial process on any substrate surface28,29. Recently, we developed a depth-sensitive plasmon-enhanced Raman spectroscopy (DS-PERS) method based on SHINERS to monitor and elucidate the process of sequential formation of solid-electrolyte interphase (SEI) on the Cu current collector and then on the freshly deposited Li30. Unfortunately, the enhancement of the Raman signals on graphene is too weak to directly obtain high-quality Raman signals at the graphene/electrolyte interface, even using SHINERS.
Herein, we design a gap-enhanced Raman spectroscopy strategy for studying the behavior and mechanism of the graphene/electrolyte interface. A sandwich configuration is employed for achieving the enhancement using the localized surface plasmon (LSP) effect coupling between shell-isolated nanoparticles (SHINs) and metal substrate. The bottom layer of the configuration is Au substrate, the top layer is Au@SiO2 nanoparticles, and the middle layer is graphene with an adjustable number of layers. With the LSP effect, the Raman signal of the measured species at the graphene surface is enhanced. Solvate ionic liquid ([Li(G4)][FSI]) is used as the electrolyte to understand the adsorption behavior in the electrical double layer of graphene/[Li(G4)][FSI] interface and the potential dependence of different coordination structures of [Li(G4)][FSI] at the interface. By modulating the number of graphene layers, a transition from metalloid to graphite-like can be achieved. Through the combination of in-situ Raman spectroscopy with electrochemical techniques, the interface of graphene/electrolyte with diverse properties was explored. Our investigations unveil significant dependencies of ion adsorption configurations and mechanisms on the number of graphene layers. These findings deliver comprehensive insights into the adsorption and exchange processes of ions on graphene electrodes, thereby offering novel avenues for comprehending and manipulating the charging dynamics of electrochemical capacitors.
Results and discussion
Fundamental concept of gap-enhanced Raman spectroscopy
The sandwich configuration of the Au substrate coupled with shell-isolated nanoparticles to enhance the Raman signal is shown in Fig. 1a, which is abbreviated as Au@SiO2/graphene/Au. Graphene was transferred onto a flat Au substrate, and then Au@SiO2 nanoparticles were transferred on the surface of the graphene to construct an Au@SiO2/graphene/Au electrode. SEM image of SHINs on graphene is shown in Fig. S1. In addition, by manipulating the growth time of graphene on a copper substrate using the Chemical Vapor Deposition (CVD) method, accurate control over the number of graphene layers can be achieved. With the increase of the number of graphene layers, the property of graphene could gradually transform from metalloid to graphite-like. Within this specific configuration of coupling with the metal substrate, under appropriate laser irradiation, highly SERS-active Au nanoparticles coated with an ultra-thin (~ 2 nm thick) SiO2 shell can generate an exceptionally strong electromagnetic field, which amplifies the Raman signals of adsorbed species at the graphene interface. Consequently, the potential-dependent information of adsorbed species at the graphene interface can be obtained.
In order to verify the feasibility of the sandwich configuration of graphene with different layers, the COMSOL finite element method was used to simulate the electromagnetic field distribution of the configuration. The results are shown in Fig. 1b. It is evident that the most intense region of Raman scattering enhancement, commonly referred to as the hotspot, is localized precisely at the interface between the nanoparticles and the graphene. The enhancement factor for the single-layer graphene (SLG) configuration can reach the order of 109, while for the three-layer graphene (3LG) configuration, the enhancement factor can reach the order of 108. Even in the case of a six-layer graphene (6LG) configuration, the enhancement factor can still reach the order of 106 or higher, demonstrating the synergistic interplay of electromagnetic field enhancement and chemical enhancement. It should be pointed out that six-layer graphene exhibits a behavior similar to graphite10. Similar enhancement was observed on the Cu substrate (Figure S2). Building upon the aforementioned, the challenge of weak coupling between graphene and shell-isolated nanoparticles is effectively addressed by the sandwich configuration (Figs. S3–5), which can be used to investigate the graphene/electrolyte interface and track the displacement of all electrolyte species including solvent molecules, thus provide a comprehensive description of the structure of the electrical double layer.
The sandwich configuration was characterized by Raman spectroscopy, transmission electron microscopy (TEM), and atomic force microscopy (AFM). Figure 1c shows the Raman spectra of graphene under the laser irradiation of 532 nm. Compared with SLG, the increase in the number of layers results in a much broader and up-shift 2D band. The further increase in the number of layers leads to a significant decrease in the relative intensity of the 2D peak31. The results show that SLG, bilayer, and few-layer graphene have been successfully transferred to Au substrates. As shown in AFM images (Fig. 1d and Figure S6), graphene with different layers is observed on the smooth substrate. The measured height of single and six-layer graphene is about 0.4 and 2.5 nm, respectively. The sandwich configuration was further characterized by TEM (Fig. 1e), with Au@SiO2 nanoparticles positioned above the graphene and Au substrates situated below the graphene. The size of the gap between Au@SiO2 nanoparticles and Au substrate is about 2.5 nm (~ 0.4 nm for a single-layer)32, indicating that the six-layer graphene is successfully inserted into the nanogap.
Electrochemical techniques and in situ AFM
The chemical structure of lithium bis(fluorosulfonyl) imide in tetraglyme ([Li(G4)][FSI]) is shown in Fig. 2a. Cyclic voltammetry measurements of graphene in [Li(G4)][FSI] were conducted with a scan rate of 10 mV s–1 between 2.1 and 3.9 V (vs. Li+/Li) in a three-electrode cell, showing capacitive charge-discharge behavior (Fig. 2b). By comparing with the CV of Highly Oriented Pyrolytic Graphite (HOPG) in [Li(G4)][FSI], the metalloid to graphite-like properties of the graphene with tunable number of layers were confirmed (Figure S7). Metalloid SLG and 3LG can strongly adsorb anions and cations, resulting in hysteresis behavior in the CV curves, while the adsorption of anions and cations on graphite-like 6LG is weak, and thus the hysteresis behavior disappears, indicating that the number of graphene layers can affect the adsorption kinetics in electrical double layer. Ion adsorption on metal electrodes is much stronger than on carbon electrodes, leading to a quite different electrical double layer structure33.
As a two-dimensional nanomaterial, graphene presents quantum capacitance (QC)34. The differential capacitance curve of graphene electrodes with different layer numbers is shown in Fig. 2c, and the Nyquist and complex capacitance diagrams are shown in Figures S8–10. With the increase in the number of graphene layers, the differential capacitance curve changes from U-shape to V-shape. For single-layer graphene, the quantum capacitance plays a dominant role, thus the total capacitance behavior of the interface is similar to the quantum capacitance behavior. The potential of zero charges (PZC) corresponds to the potential with the minimum differential capacitance35. The total differential capacitance curve exhibits symmetry around the PZC, both in the positive and negative directions. For few-layer graphene (6LG), electrical double layer capacitance takes a dominant role, with a higher quantity of anions adsorbed at the interface in comparison to cations. As a result, the differential capacitance curve exhibits a characteristic left-low, right-high profile. The differential capacitance curve for HOPG is depicted in Figure S11, showing a distinctive V-shape. Our results are supported by the experiments for the graphene/ionic-liquid interface, which show that total capacitance is limited by quantum capacitance when the number of graphene layers (N) is less than 4 and by EDL capacitance when N > 436,37. At the same time, it can be found that the differential capacitance increases with the number of graphene layers. At the metalloid single-layer graphene interface, the robust charge-charge interactions prompt cations and anions to establish Coulombic ordering and densely ion arrangements. Disrupting this ordered structure requires substantial polarization (E < 2.5 V or E > 3.5 V), consequently leading to a reduction in capacitance. Conversely, at graphite-like few-layer graphene interface, the charge-charge interactions are less pronounced, leading to reduced Coulombic ordering and more loosely packed ion configurations. This facilitates the separation of cations and anions under low polarization, resulting in a higher capacitance. The electrochemical capacitors utilizing few-layer graphene with an ABA stacking structure can achieve higher double layer capacitance compared to single-layer graphene. This occurrence is attributed to the increased intensity of image forces in ABA stacking, which disrupts ionic ordering and facilitates the formation of effective free ions38.
We further investigated the nanostructures of anions and cations at the interface by atomic force microscopy (AFM), which is a powerful method to detect the ion arrangement and layered structure of electrical double layers in ionic liquids39,40,41. Figure 2d, e and Figure S12, 13 show potential-dependent force-distance curves. It can be seen that there exists a multilayer interfacial structure at the nanometer scale from the electrode surface, which gradually attenuates at the electrolyte side. In Fig. 2d, the EDL of this system consists of two layers of nanostructures, the measured thicknesses of the two layers are 0.52 and 0.32 nm, respectively. The corresponding layer thicknesses match the size of Li(G4)+ and FSI– ions42. Therefore, it is reasonable to infer that the negatively charged electrode leads to the enrichment of Li(G4)+ cations in the innermost layer, and the second layer is composed of FSI– anions. When the electrode is positively charged, the thickness of the first layer decreases from 0.52 to 0.32 nm, and the thickness of the second layer increases from 0.32 to 0.52 nm, which demonstrates that the innermost layer of the EDL is enriched with FSI– anions, and the second layer is enriched with Li(G4)+ cations. The above show that the thickness of the electrical double layer is within 1 nm, the ultra-thin (1 nm thick) electrical double layer benefits obtaining higher specific capacitance.
Distinguishing charge storage mechanisms
Although AFM reveals the potential-dependent rearrangement of cations and anions, and the number and thickness of the layered structure at the interface, it lacks chemical sensitivity. In order to further understand the energy storage mechanism of the electrical double layer at the molecular level, Raman spectra of the electrode/[Li(G4)][FSI] interface were obtained using the Au@SiO2/graphene/Au sandwich configuration. For single-layer graphene, in-situ Raman measurements were performed in a wide potential region from 2.1 to 3.7 V (Fig. 3a). We opted for a 785 nm laser wavelength to investigate the adsorption configuration of ions and avoid fluorescence interference. In the very low energy regime, the intensity of the G and 2D peaks is suppressed due to the conservation of angular momentum associated with continuous rotational symmetry in the low-energy regime43. Consequently, the G and 2D peaks were not observed. The spectral peaks at 260 and 293 cm–1, which are assigned respectively to the rocking of S-F and SO244, exhibit potential dependence and a notable inflection point at 3.0 V (vs. Li+/Li), indicating that the PZC is around 3.0 V, being close to the aforementioned potential with the minimum differential capacitance. At potentials positive of the PZC (Fig. 3a, blue), the intensity of the rocking of SO2 at the interface is stronger than that of SF, which is similar to the bulk spectrum. It is referred that FSI– anions are lying flat on the graphene. While FSI– ions adjacent to the graphene maintain a parallel arrangement with respect to the electrodes surface in N-down configuration (Fig. 3b), Li(G4)+ ions also maintain a parallel arrangement with respect to the electrodes to maximize the Coulombic interaction with the paralleled aligned FSI– ions. The band at 1400–1500 cm–1 represents the CH2 bending/scissoring mode of G445, the peak exhibits a blueshift corresponding to the positive shift of the potential, which suggests that Li(G4)+ cations are pushed away from the electrode surface, as shown in Figure S14. A portion of Li(G4)+ rearranges in the vertical direction and desorbs from the electrode.
However, at potentials negative of the PZC (Fig. 3a, purple), the peak intensity of the rocking of SO2 at the interface is weaker than that of the rocking of SF, indicating that FSI– anions are pushed away from the electrode surface. The peak at 868 cm–1 represents the breathing mode of crown ether-like Li(G4)+46, which appears at 3.3 V and then shifts to 874 cm–1 as the potential decreases to 2.7 V, as shown in Figure S15. Meanwhile, for the two peaks at 930 and 1138 cm–1 being the coupling mode of CH2 bending, CO stretching, and CC stretching vibration47, the peak of CH2 bending/scissoring mode of G4 undergoes a redshift in correlation with the negative shift of the potential. Moreover, Li(G4)+ is absorbed on the surface lying flat, which further shows that the FSI– ions are rearranged and desorbed from the electrode, and there is an increase in the intensity of Li(G4)+ ions in the first ionic layer. That is the rearrangement of the ionic layer due to the polarization of the electrode is accompanied by the transition of the ions near the electrode. Thus, at the metalloid interface, the charging mechanism is that within the electrical double layer adjacent to the electrode, the desorption of the co-ion with charge being the same as the electrode is more pronounced than the adsorption of counter-ion with charge opposite to the electrode. Regarding the strong vibration peak appearing at 2.9 V at ~ 1400 cm–1, it is ascribed to the asymmetry stretching of SO2. When the potential shifts from negative to positive relative to PZC, the interface undergoes a transition from FSI– co-ion desorption to Li(G4)+ co-ion desorption. The alteration in the configuration of FSI– leads to the observed SO2 asymmetry stretching. It should be noted that when using the Au@SiO2/graphite configuration, the adsorption behavior of the above electrolyte components at the electrochemical interface cannot be observed, as graphite could not provide electromagnetic field enhancement and chemical enhancement factor is only 102, as shown in Figures S16, 17.
By adjusting the thickness of graphene, the interface between graphene and [Li(G4)][FSI] is further explored to understand the behavior of graphene as a host material in electrochemical capacitors. As shown in Figure S18, when the number of graphene layers increases to three, the potential-dependent behavior of FSI– and Li(G4)+ can still be observed at the hot spot, which is similar to the interfacial behavior of single-layer graphene. However, when the number of graphene layers increases to six, the spectra present different characteristics as shown in Fig. 4a. At potential around the PZC, the peak intensity of SO2 is nearly equivalent to that of SF, indicating that the N atoms in the anions are not close to the electrode surface, which is an N-up configuration, and that both anions and cations adsorb on graphene surface (Fig. 4b). With positive shift of the potential, the SF peak intensity increases while the SO2 peak intensity decreases, which is ascribed to the orientation change of the absorbed FSI– anions from flat adsorption to oblique adsorption and the increase of the number of anions accommodated at the interface. The Raman signal of the CH2 bending/scissoring mode of G4 (1400–1500 cm–1) becomes weak until it disappears, indicating that Li(G4)+ cations move away from the interface and the number of cations decreases. At potentials negative of PZC, the peak intensity of SF decreases while the peak intensity of SO2 increases, i.e., the configuration of the anion undergoes inversion. The Raman signal reduces as the potential shifts negatively, and the FSI– ions transfer until they move away from the interface. The Raman signal of the CH2 bending/scissoring mode of G4 (1400–1500 cm–1) increases with the negative shift of potential, showing that the number of cations increases and Li(G4)+ cations adsorb on the surface lying flat.
The six-layer graphene exhibits distinct D-band and G-band observed at the interface and both of them present potential-dependent behavior. The D band is located at 1350 cm–1 which is a defect-activated double-resonance Raman process31, and the G band is located at 1580 cm–1 which is caused by the in-plane vibration of sp2 carbon atoms48. When E < PZC, the intensity of the D-band gradually increases because the cations adsorb on the electrode surface (Fig. 4c). However, the change of adsorbate on graphene causes the shift of the G band to present a potential dependence, and anions and cations adsorb on the surface as electron acceptor dopants49,50, as shown in Fig. 4d. At a negatively charged interface, the G-band undergoes a gradual blueshift from ca. 1598 to 1613 cm–1 as the potential decreases to 2.1 V, with Li(G4)+ cations migrating from the bulk to the interface. As the surface becomes neutral or positive, the G-band begins to significantly broaden, and the redshift is observed with a positive shift of potential since the Li(G4)+ cations orient away from the surface and towards the bulk while the FSI– anions arrange at the interface. This shows that charge storage at the graphite-like interface is actually driven by ion exchange, whereby counter-ions are adsorbed to the interface while co-ions are simultaneously ejected, which is significantly different from the behavior of single-layer graphene metalloid interfaces.
The above experiments show that the sandwich configuration of Au substrate coupled with shell-isolated nanoparticles to enhance Raman signals can indeed obtain information about graphene with different layers at the molecular level from the graphene/electrolyte interface, thus providing an effective method for in-depth research on the electrochemical energy storage mechanism of graphene-based electrochemical capacitors. Figure S19 shows the charge/discharge behavior of single-layer/single-layer, single-layer/six-layer, and six-layer/six-layer at 10 A g–1 in the potential range from – 0.8 to 0.8 V, respectively. The capacitance is estimated using the following formula (\({C}_{s}=\frac{i\cdot \varDelta t}{\varDelta V\cdot S}\)). The area-specific capacitance of single-layer/single-layer is 64 µF cm–2, which is mainly dominated by the charging mechanism of co-ion desorption. With the increase of the number of layers, the area-specific capacitance of six-layer/six-layer is 145 µF cm–2, which is turned into the charging mechanism dominated by ion exchange. The relationship between the charging mechanism and the electrochemical performance has been correlated. Charging via co-ion desorption is anticipated to alleviate the enthalpic penalty associated with interactions among charges, thereby simultaneously enhancing entropy. Consequently, co-ion desorption should optimize capacitance51. The ion exchange mechanism, in principle, mitigates the enthalpic penalty linked to denser ion packing by maintaining a relatively constant total density throughout charging. Simultaneously, the entropic penalty associated with charging is also reduced52. We conducted a further comparison of the energy density of electrochemical capacitors operating under two predominant mechanisms, as shown in Table S1. Ion exchange plays a significant role in maximizing ion packing, consequently influencing the charging rate and capacitance. The above results provide a direct insight into the charge storage process in graphene electrodes with different layer numbers at the molecular level, showing that the charging mechanism depends on the layer numbers of graphene.
Revealing coordination structures at the interface
In order to further increase the energy density of electrochemical capacitors, as a type of new capacitor-hybrid electrochemical capacitors, lithium-ion capacitor has been developed in recent years53,54, which is an electrochemical energy storage device with performance between lithium-ion batteries and electrochemical capacitors. An intercalated/deintercalated lithium-ion electrode material and an electrical double layer capacitor electrode material with a large specific surface area are used for the two poles, respectively. The energy storage mechanism includes both the intercalation/deintercalation of lithium ions in the electrode material and the absorption/desorption of electrolyte ions on the surface of the electrode material. Therefore, lithium-ion capacitors combine the advantages of lithium-ion batteries and electrochemical capacitors, which not only have higher power density and longer cycle life than lithium-ion batteries but also have higher energy density than electrochemical capacitors. Solvate ionic liquid is a promising class of electrolyte for lithium-ion capacitors. LiFSI exhibits weak ion-ion interactions, while G4 provides strong ion-solvent interactions, which collectively influence the desolvation process, thus affecting the Li+ deintercalation behavior on the electrode surface. When LiFSI is dissolved in a solvent, Li+ ions interact with the solvent molecules and FSI– anions, resulting in the following three types of coordination structures: Solvent-separated ion pairs (SSIP), in which only solvent molecules are present in the solvation shell around cation; Contact ion pairs (CIP), solvent molecules and one anion are present in the solvation shell around the cation to form a neutral complex; Aggregates (AGG), solvent molecules and multiple anions are present in the solvation shell around the cation55. The anions in the form of CIP and AGG are the main precursors of anion-derived SEI film56. Therefore, coordination structures in electrolytes play a vital role in dictating the components and structure of anion-derived SEI57,58, and thus affect the performance of lithium-ion capacitors. The sandwich configuration provides the opportunity to reveal the coordination structure of [Li(G4)][FSI] at the graphene/electrolyte interface by Raman spectroscopy.
Potential-dependent Raman spectra of coordination structures at single-layer graphene/[Li(G4)][FSI] interface are shown in Fig. 5. The peaks at 700–770 cm–1 are assigned to the S-N stretching vibrations of FSI- anions, which are highly sensitive to the coordination environment59,60. For the free and uncoordinated FSI- anion, SSIP (Fig. 5a, teal) has a peak at about 720 cm–1. The peaks of CIP (Fig. 5a, blue) and AGG (Fig. 5a, orange) are about 730 cm–1 and 745 cm–1, respectively, when the lithium salt and solvent are mixed in an equal molar ratio55. We analyzed the peaks measured at the interface to obtain information on coordination structures. As shown in Fig. 5b, c, at potentials negative of PZC, the content of SSIP decreases and the content of AGG increases with the negative shift of potential, while at potentials positive of PZC, SSIP content increases and AGG content decreases with the positive shift of potential, which is related to the change of anion and cation adsorption at the interface. The content and frequency of ion pairs present a turning point at 3.0 V. The content of SSIP has a local minimum point at 3.0 V, while the content of CIP + AGG has a local maximum point at 3.0 V. In the double layer region, the content of CIP + AGG is higher than SSIP, indicating that the coordination structure at the interface is potential-dependent, as shown in Fig. 5d. The peak of AGG at 743 cm–1 appears at 2.9 V and then shifts to 747 cm–1 as the potential decreases to 2.1 V, while the peak of AGG at 741 cm–1 appears at 3.1 V and then shifts to 749 cm–1 as the potential increases to 3.7 V, as shown in Fig. 5a. For few-layer graphene, the dependence of the coordination structure content on the potential can also be observed, as shown in Figure S20. However, due to the weak interaction between the electrode and the electrolyte, the ion packing is relatively loose, and the multilayer structure promotes electrolyte wetting and enhances ion adsorption/desorption, so the peak shift of the coordination structure with the potential is not obvious. These changes between single-layer graphene and few-layer graphene can be distinctly observed through Raman obtained from the Au@SiO2/graphene/Au sandwich configuration, thus revealing the coordination structure of the solvate ionic liquid at the electrode/electrolyte interface, which will greatly improve our understanding of the complicated interfacial behavior of graphene and solvate ionic liquid-based hybrid capacitors.
In summary, we have developed a gap-enhanced Raman spectroscopy strategy of utilizing the LSP effect from the coupling of SHINs with a metal substrate for graphene electrodes with adjustable layers. This method has been employed to investigate the interfacial behavior and mechanism on graphene electrodes and can be further extended to other non-metallic substrates or indirect SERS platforms. The combination of in-situ Raman spectroscopy with electrochemical techniques facilitates a deeper understanding of the charged storage mechanism of graphene with varying layers and properties in electrochemical capacitors. We monitor a change of the total capacitance curve from U-shape to V-shape, which is attributed to a decrease in quantum capacitance contribution and an increase in electrical double layer capacitance contribution, along with the variation of anions/cations configuration. The charged storage mechanisms are related to the number of graphene layers. For single-layer graphene, charging proceeds by the desorption of co-ion, whereas for few-layer graphene, co-ion/counter-ion exchange dominates. The relationship between the charging mechanism of the electrical double layer and the electrochemical performance has been correlated. The area specific capacitance of single-layer/single-layer graphene is 64 µF cm–2, while the area specific capacitance of six-layer/six-layer graphene is 145 µF cm–2. Furthermore, the coordination structure of [Li(G4)][FSI] at the graphene/electrolyte interface has been revealed, which indicates that the coordination structure at the interface is potential-dependent. The above finding offers new insights into the electrochemical interfaces between graphene and electrolyte. The gap-enhanced Raman spectroscopy strategy could expand the range of in-situ studies of various two-dimensional materials, including electrical double layer, electrolyte decomposition, SEI formation, and electrocatalysis.
Methods
Materials
Tetraglyme (G4, Santa Cruz, ≥ 99.8 %) and Lithium Bis(fluorosulfonyl)imide (LiFSI, Nippon Shokubai, ≥ 99.9 %) were mixed with a mole ratio of LiFSI: G4 = 1:1 in a glovebox filled with argon gas (VG1500, H2O < 0.1 ppm, O2 < 0.1 ppm), and the mixture was stirred for 24 h to obtain a homogeneous liquid at room temperature. The liquid was abbreviated as [Li(G4)][FSI], which was stored and used in a glovebox to prevent H2O contamination. Chloroauric acid (99.99 %), sodium citrate (99.0 %), and (3-aminopropyl) trimethoxysilane (APTMS, 97 %) were purchased from Alfa Aesar; sodium silicate solution (27 % SiO2) was purchased from Sigma-Aldrich. All chemicals were used as received without further purification.
Synthesis of Au@SiO2 shell-isolated nanoparticles
The synthesis of gold nanoparticles was carried out using the classic sodium citrate reduction method61. A 0.01% weight fraction HAuCl4 aqueous solution (200 mL) was heated to boiling, followed by the rapid addition of a 1 % weight fraction sodium citrate aqueous solution (1.4 mL). Maintaining a gentle boil for 40 min yielded 55 nm gold nanoparticles. Taking 30 mL of the 55 nm gold nanoparticle solution, 0.4 mL of a 1 mM solution of 3-aminopropyltrimethoxysilane was added, followed by stirring for 15 min. Subsequently, 3.2 mL of a 0.54 % sodium silicate aqueous solution was added and stirring was continued for 3 min. The reaction vessel was then heated in a water bath at 95 °C, and after 20 min, core-shell particles with a shell thickness of ~ 2 nm were obtained, as depicted in Figure S1.
Preparation of Au@SiO2/graphene/Au structure
25 µm-thick Cu foil was annealed in an H2 atmosphere at 1000 °C, followed by the growth of graphene in an H2/CH4 atmosphere while maintaining elevated temperatures at 1150 °C. After completion of the growth, the system was cooled to room temperature62. Similarly, controlling the growth time of graphene enabled the production of multilayer graphene. A uniform layer of PMMA film was spun onto the flat graphene/Cu foil surface, cured through heating (at about 100 °C), and then subjected to ammonium persulfate etchant, causing Cu to be etched away. This yielded PMMA/graphene floating on the surface, which was meticulously rinsed with deionized water and subsequently transferred onto a Si substrate coated with 100 nm thick Au via thermal evaporation. Following drying, PMMA was removed using acetone, resulting in the graphene/Au substrate at room temperature63. Dispersion of SHINs in ultra-pure water led to their deposition onto the graphene/Au substrate, followed by vacuum drying. The subsequent assembly of the electrochemical cell was conducted within an argon glovebox with 0.1 ppm H2O and O2 at room temperature.
COMSOL finite element method simulation
The electromagnetic field distribution in Au@SiO2/graphene/Au configuration was calculated by COMSOL finite element analysis software. In the simulation, the diameter of Au nanoparticles was set to 55 nm, the incident laser wavelength was 785 nm, and the fine structure was 1 × 1 × 1 nm3.
In situ Raman spectroscopy
Raman microscopy (Nanophoton Corporation Vis-NIR-XU) with a 785 nm laser wavelength was used to record Raman signals, and a 785 nm laser was used to avoid the fluorescent background of the electrolyte, as shown in Figure S21. A 10 mm × 10 mm graphene/Au substrate decorated with SHINs was used as the working electrode, with Li foils (purchased from China Energy Lithium Co., Ltd., ≥ 99.9 %) serving as both the reference and counter electrodes. The setup employed 500 μL of electrolyte and was assembled in an argon-filled glove box (H2O and O2 < 0.1 ppm) at room temperature. All Raman measurements were performed by using a 50 × microscope objective with a numerical aperture of 0.45. The laser power was controlled at about 0.7 mW and the accumulation time was set to 60 s. The peak-versus-potential plot can be fitted with a linear equation, with the fitted line representing the slope of the Stark shift in cm–1/V.
AFM force spectrum measurement
All AFM (Bruker Icon) characterizations were performed in an argon-filled glovebox (MIKROUNA, H2O < 0.1 ppm, O2 < 0.1 ppm) equipped with an electrochemical workstation (CHI660E, Chenhua Instruments). The CSG30 probe (TipsNano) with an elastic coefficient of 0.6 N m–1 was used to measure force curves. A freshly cleaved HOPG (20 mm 20 mm, ZYB) was used as the working electrode, and two Li wires (purchased from China Energy Lithium Co., Ltd., ≥ 99.9 %) were used as the counter electrode and the reference electrode, respectively. The setup utilized 600 µL of electrolyte. At least 20 force curves were recorded at each potential at room temperature.
Electrochemical measurements
Cyclic voltammetry was conducted using a three-electrode configuration on an electrochemical workstation (CHI760E, Chenhua Instruments) at room temperature. A 10 mm × 10 mm graphene/Au substrate served as the working electrode, while two lithium strips (purchased from China Energy Lithium Co., Ltd., ≥ 99.9 %) were employed as the counter electrode and the reference electrode, respectively. The volume of electrolyte used was 600 µL. All potentials stated in the study were with respect to Li+/Li reference. Electrochemical impedance spectroscopy (EIS) tests were carried out on an electrochemical workstation (PGSTAT128N, Metrohm). The frequency ranged from 100 kHz to 1 Hz with an amplitude of 10 mV, and the equivalent circuit employed was R-(R)(P)-(R)(P)35,64.
Data availability
The data that support the findings of this study have been included in the main text and Supplementary Information. All other relevant data supporting the findings of this study are available from the corresponding authors upon request.
References
Forse, Alexander C. et al. Direct observation of ion dynamics in supercapacitor electrodes using in situ diffusion NMR spectroscopy. Nat. Energy 2, 16216 (2017).
Xiao, J. et al. Electrolyte gating in graphene-based supercapacitors and its use for probing nanoconfined charging dynamics. Nat. Nanotechnol. 15, 683–689 (2020).
Shao, Y. et al. Graphene-based materials for flexible supercapacitors. Chem. Soc. Rev. 44, 3639–3665 (2015).
Wang, X. et al. Electrode material–ionic liquid coupling for electrochemical energy storage. Nat. Rev. Mater. 5, 787–808 (2020).
Novoselov, K. S. et al. A roadmap for graphene. Nature 490, 192–200 (2012).
Stoller, M. D., Park, S., Zhu, Y., An, J. & Ruoff, R. S. Graphene-based ultracapacitors. Nano Lett. 8, 3498–3502 (2008).
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Wallace, P. R. The band theory of graphite. Phys. Rev. 71, 622–634 (1947).
Hui, J., Burgess, M., Zhang, J. & Rodriguez-Lopez, J. Layer number dependence of Li(+) intercalation on few-layer graphene and electrochemical imaging of Its solid-electrolyte interphase evolution. ACS Nano 10, 4248–4257 (2016).
Pollak, E. et al. The interaction of Li+ with single-layer and few-layer graphene. Nano Lett. 10, 3386–3388 (2010).
Feng, J. et al. Ion regulation of ionic liquid electrolytes for supercapacitors. Energy Environ. Sci. 14, 2859–2882 (2021).
Yoshida, K. et al. Oxidative-stability enhancement and charge transport mechanism in glyme-lithium salt equimolar complexes. J. Am. Chem. Soc. 133, 13121–13129 (2011).
Ugata, Y. et al. Solvate electrolytes for Li and Na batteries: structures, transport properties, and electrochemistry. Phys. Chem. Chem. Phys. 23, 21419–21436 (2021).
Ueno, K. et al. Glyme-lithium salt equimolar molten mixtures: concentrated solutions or solvate ionic liquids? J. Phys. Chem. B 116, 11323–11331 (2012).
Griffin, J. M. et al. In situ NMR and electrochemical quartz crystal microbalance techniques reveal the structure of the electrical double layer in supercapacitors. Nat. Mater. 14, 812–819 (2015).
Chmiola, J. et al. Anomalous increase in carbon capacitance at pore sizes less than 1 nanometer. Science 313, 1760–1763 (2006).
Largeot, Celine et al. Relation between the ion size and pore size for an electric double-layer capacitor. J. Am. Chem. Soc. 130, 2730–2731 (2008).
Vix-Guterl, C. et al. Electrochemical energy storage in ordered porous carbon materials. Carbon 43, 1293–1302 (2005).
Chmiola, J., Largeot, C., Taberna, P. L., Simon, P. & Gogotsi, Y. Desolvation of ions in subnanometer pores and its effect on capacitance and double-layer theory. Angew. Chem. Int. Ed. 47, 3392–3395 (2008).
Richey, F. W., Dyatkin, B., Gogotsi, Y. & Elabd, Y. A. Ion dynamics in porous carbon electrodes in supercapacitors using in situ infrared spectroelectrochemistry. J. Am. Chem. Soc. 135, 12818–12826 (2013).
Merlet, C. et al. Highly confined ions store charge more efficiently in supercapacitors. Nat. Commun. 4, 2701 (2013).
Merlet, C. et al. On the molecular origin of supercapacitance in nanoporous carbon electrodes. Nat. Mater. 11, 306–310 (2012).
Ling, X. et al. Can graphene be used as a substrate for Raman enhancement? Nano Lett. 10, 553–561 (2010).
Zhang, N., Tong, L. & Zhang, J. Graphene-based enhanced Raman scattering toward analytical applications. Chem. Mater. 28, 6426–6435 (2016).
Wang, Y. H. et al. In situ Raman spectroscopy reveals the structure and dissociation of interfacial water. Nature 600, 81–85 (2021).
Li, J. F. et al. Shell-isolated nanoparticle-enhanced Raman spectroscopy. Nature 464, 392–395 (2010).
Wu, D. Y., Li, J. F., Ren, B. & Tian, Z. Q. Electrochemical surface-enhanced Raman spectroscopy of nanostructures. Chem. Soc. Rev. 37, 1025–1041, (2008).
Ding, S.-Y. et al. Nanostructure-based plasmon-enhanced Raman spectroscopy for surface analysis of materials. Nat. Rev. Mater. 1, 16021 (2016).
Gu, Y. et al. Resolving nanostructure and chemistry of solid-electrolyte interphase on lithium anodes by depth-sensitive plasmon-enhanced Raman spectroscopy. Nat. Commun. 14, 3536 (2023).
Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401 (2006).
Novoselov, K. S. et al. Two-dimensional atomic crystals. PNAS 102, 10451–10453 (2005).
Bi, S. et al. Minimizing the electrosorption of water from humid ionic liquids on electrodes. Nat. Commun. 9, 5222 (2018).
Xia, J., Chen, F., Li, J. & Tao, N. Measurement of the quantum capacitance of graphene. Nat. Nanotechnol. 4, 505–509 (2009).
Ye, J. L. et al. Charge storage mechanisms of single-layer graphene in ionic liquid. J. Am. Chem. Soc. 141, 16559–16563 (2019).
Uesugi, E., Goto, H., Eguchi, R., Fujiwara, A. & Kubozono, Y. Electric double-layer capacitance between an ionic liquid and few-layer graphene. Sci. Rep. 3, 1595 (2013).
Zhan, C., Neal, J., Wu, J. & Jiang, D.-E. Quantum effects on the capacitance of graphene-based electrodes. J. Phys. Chem. C 119, 22297–22303 (2015).
Mo, T. et al. Energy storage mechanism in supercapacitors with porous graphdiynes: Effects of pore topology and electrode metallicity. Adv. Mater. 35, e2301118 (2023).
Yan, J.-W., Tian, Z.-Q. & Mao, B.-W. Molecular-level understanding of electric double layer in ionic liquids. Curr. Opin. Electrochem. 4, 105–111 (2017).
Zhong, Y. X. et al. Resolving fine structures of the electric double layer of electrochemical interfaces in ionic liquids with an AFM tip modification strategy. J. Am. Chem. Soc. 136, 14682–14685 (2014).
Zhang, X. et al. Probing double layer structures of Au (111)-BMIPF6 ionic liquid interfaces from potential-dependent AFM force curves. Chem. Commun. 48, 582–584 (2012).
McLean, B. et al. Nanostructure of [Li(G4)] TFSI and [Li(G4)] NO3 solvate ionic liquids at HOPG and Au(111) electrode interfaces as a function of potential. Phys. Chem. Chem. Phys. 17, 325–333 (2015).
Reichardt, S. & Wirtz, L. Ab initio calculation of the G peak intensity of graphene: Laser-energy and Fermi-energy dependence and importance of quantum interference effects. Phys. Rev. B 95, 195422 (2017).
Li, L. et al. Transport and electrochemical properties and spectral features of non-aqueous electrolytes containing LiFSI in linear carbonate solvents. J. Electrochem. Soc. 158, A74–A82 (2011).
Fawdon, J., Ihli, J., Mantia, F. & Pasta, M. Characterising lithium-ion electrolytes via operando Raman microspectroscopy. Nat. Commun. 12, 4053 (2021).
Terada, S., Ikeda, K., Ueno, K., Dokko, K. & Watanabe, M. Liquid structures and transport properties of lithium Bis(fluorosulfonyl)amide/Glyme solvate ionic liquids for lithium batteries. Aust. J. Chem. 72, 70–80, (2019).
Ducasse, L. et al. Spectroscopic study of poly(ethylene oxide)6: LiX complexes (X = PF6, AsF6, SbF6, ClO4). Phys. Chem. Chem. Phys. 5, 567–574 (2003).
Ferrari, A. C. & Basko, D. M. Raman spectroscopy as a versatile tool for studying the properties of graphene. Nat. Nanotechnol. 8, 235–246 (2013).
Shi, H. et al. Sensing local pH and ion concentration at graphene electrode surfaces using in situ Raman spectroscopy. Nanoscale 10, 2398–2403 (2018).
Das, A. et al. Monitoring dopants by Raman scattering in an electrochemically top-gated graphene transistor. Nat. Nanotechnol. 3, 210–215 (2008).
Kondrat, S. & Kornyshev, A. A. Pressing a spring: what does it take to maximize the energy storage in nanoporous supercapacitors? Nanoscale Horiz. 1, 45–52 (2016).
Forse, A. C., Merlet, C., Griffin, J. M. & Grey, C. P. New perspectives on the charging mechanisms of supercapacitors. J. Am. Chem. Soc. 138, 5731–5744 (2016).
Xing, F., Bi, Z., Su, F., Liu, F. & Wu, Z. S. Unraveling the design principles of battery‐supercapacitor hybrid devices: From fundamental mechanisms to microstructure engineering and challenging perspectives. Adv. Energy Mater. 12, https://doi.org/10.1002/aenm.202200594 (2022).
Ma, Y., Chang, H., Zhang, M. & Chen, Y. Graphene-based materials for lithium-ion hybrid supercapacitors. Adv. Mater. 27, 5296–5308 (2015).
Geysens, P. et al. Solvation structure of sodium Bis(fluorosulfonyl)imide-glyme solvate ionic liquids and Its influence on cycling of Na-MNC cathodes. J. Phys. Chem. B 122, 275–289 (2018).
Yamada, Y. et al. Unusual stability of acetonitrile-based superconcentrated electrolytes for fast-charging lithium-ion batteries. J. Am. Chem. Soc. 136, 5039–5046 (2014).
Li, T. et al. Stable anion-derived solid electrolyte interphase in lithium metal batteries. Angew. Chem. Int Ed. 60, 22683–22687 (2021).
Piao, N. et al. Countersolvent electrolytes for lithium‐metal batteries. Adv. Energy Mater. 10, https://doi.org/10.1002/aenm.201903568 (2020).
Brouillette, D. et al. Stable solvates in solution of lithium bis(trifluoromethylsulfone imide in glymes and other aprotic solvents: Phase diagrams, crystallography and Raman spectroscopy.Phys. Chem. Chem. Phys.4, 6063–6071 (2002).
Yoon, H., Best, A. S., Forsyth, M., MacFarlane, D. R. & Howlett, P. C. Physical properties of high Li-ion content N-propyl-N-methylpyrrolidinium bis(fluorosulfonyl)imide based ionic liquid electrolytes. Phys. Chem. Chem. Phys. 17, 4656–4663 (2015).
Frens, G. Controlled nucleation for the regulation of the particle size in monodisperse gold suspensions. Nat. Phys. Sci. 241, 20–22 (1973).
Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324, 1312–1314 (2009).
Li, X. et al. Transfer of large-area graphene films for high performance transparent conductive electrodes. Nano Lett. 9, 4359–4363 (2009).
Li, M.-G. et al. The electrochemical interface of Ag(111) in 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide ionic liquid—A combined in-situ scanning probe microscopy and impedance study. Electrochim. Acta 197, 282–289 (2016).
Acknowledgements
This research was financially supported by the National Natural Science Foundation of China (22021001 (J.F.L.), 22072123 (J.W.Y.), T2293692 (J.F.L.), 22202162 (E.M.Y.), 21925404 (J.F.L.), 22372140 (J.W.Y.)) and China Postdoctoral Science Foundation (2022M722648 (E.M.Y)).
Author information
Authors and Affiliations
Contributions
J.W.Y., Y.G., and X.T.Y. conceived the idea. X.T.Y., J.W.Y., and Y.G. designed experiments and analyzed results. E.M.Y. conducted the COMSOL simulations. R.Y.Z. and L.H.Z. performed experiments. J.W.Y., J.F.L., Y.G., and X.T.Y. wrote the manuscript. W.W.W., K.X.L., D.Y.W., and B.W.M. helped with the discussion. All authors discussed and analyzed the data.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Yanwu Zhu, and the other, anonymous, reviewer for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yin, XT., You, EM., Zhou, RY. et al. Unraveling the energy storage mechanism in graphene-based nonaqueous electrochemical capacitors by gap-enhanced Raman spectroscopy. Nat Commun 15, 5624 (2024). https://doi.org/10.1038/s41467-024-49973-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-49973-9
- Springer Nature Limited