Abstract
Since thermoelectric materials have different physical and chemical properties, the design of contact layers requires dedicated efforts, and the welding temperatures are distinctly different. Therefore, a general interface design and connection technology can greatly facilitate the development of thermoelectric devices. Herein, we proposed a screening strategy for the contact materials based on the calculation of phase diagram method, and Mg2Ni has been identified as a matched contact layer for n-type Mg3Sb2-based materials. And this screening strategy can be effectively applied to other thermoelectric materials. By adopting the low-temperature sintering silver nanoparticles technology, the Zintl phase thermoelectric device can be fabricated at low temperature but operate at medium temperature. The single-leg n-type Mg3.15Co0.05SbBi0.99Se0.01 device achieves an efficiency of ~13.3%, and a high efficiency of ~11% at the temperature difference of 430 K has been realized for the Zintl phase thermoelectric device comprised together with p-type Yb0.9Mg0.9Zn1.198Ag0.002Sb2. Additionally, the thermal aging and thermal cycle experiments proved the long-term reliability of the Mg2Ni/Mg3.15Co0.05SbBi0.99Se0.01 interface and the nano-silver sintering joints. Our work paves an effective avenue for the development of advanced devices for thermoelectric power generation.
Similar content being viewed by others
Introduction
Thermoelectric (TE) devices are capable of converting dispersed waste heat into electricity to achieve the full utilization of energy and support the global sustainable development1,2,3. A prospective TE device should possess high efficiency, low cost, and long-term stability. Among the state-of-the-art TE materials, Zintl phase materials are one of the most promising TE materials with excellent TE performance, together with abundant and environmentally friendly constituent elements4,5.
To facilitate the fabrication of high-performance devices, the design of two critical layers (i.e., contact and bonding layers) is of great importance. The contact layers are usually introduced to connect TE materials and the metallization layers, and the bonding layers are needed to connect the metallization layer and electrodes. They are of great significance in reducing the additional electrical and thermal resistance as well as the potential thermal stress, thereby greatly improving the performance and reliability of TE devices. Presently, due to the lack of reliable design for these interfaces, the efficiency of the Zintl phase device is low and cannot meet the requirements of the application6,7. Furthermore, the activity of constituent elements and the high coefficient of thermal expansion (CTE) further complicate the fabrication, hence delaying the development of highly efficient and stable Zintl phase devices8,9.
Traditionally, the selection of contact materials has been based on an empirical method, including the selection of high-melting-point metals to reduce reaction rates, matched CTE to improve mechanical reliability, and suitable work function to reduce contact resistance10. However, this trial-and-error method of screening is time- and cost-consuming and difficult to guide other materials systems. Phase diagram engineering has long been applied to develop various functional materials, and has recently been adopted to design the compositions and microstructures of TE materials11,12,13,14. The CALPHAD (CALculation of PHAse Diagram) method describes the thermodynamic properties of materials quantitatively using the Gibbs energy of each phase with corresponding parameters and simulates the kinetic process by solving diffusion equations numerically15,16, which is critical for designing heterogeneous interfaces. In addition, to reduce the performance loss of electronic devices caused by the welding process, a variety of new connection technologies have been studied17,18,19,20. With the advantages of low-temperature connection and high-temperature service, low-temperature silver nanoparticles (Ag NPs) sintering has been applied to various functional material devices19,21, and has now been adopted to fabricate TE devices22,23,24.
In this work, the CALPHAD method was employed to screen the contact materials, and Ag NPs were used to realize the bonding connection. By using the CALPHAD method, the thermal stability between the TE material and other phases at a specific temperature can be evaluated, and it can guide an efficient screening of the possible interface materials. As an example, Mg2Ni has been identified as the contact layer for the n-type Mg3.15Co0.05SbBi0.99Se0.01. Combining the low-temperature Ag NPs sintering technology, a full Zintl phase device is fabricated. Advanced high conversion efficiency of ~11% in the single-stage Zintl phase device is achieved, and satisfactory long-term stability is realized. This study proves the feasibility of the CALPHAD method in screening the contact materials, and the reliability of low-temperature Ag NPs sintering for TE devices, which can be applied to the design and fabrication of other TE devices.
Results and discussion
A multiple-layer structure, including TE legs, barrier layers (screened by CALPHAD, Fig. 1a), solder layers (Ag NPs, Fig. 1c), electrode layers, and pre-circuited AlN ceramic plates were constructed for the device fabrication, as demonstrated in Fig. 1b. To design the contact layers with low contact resistance and good thermal stability, an efficient screening strategy was proposed by considering the diffusion doping effect together with thermodynamic stability. In view of previous in-depth studies on element doping effect25,26,27,28,29,30, we can quickly identify potential congener doping or inert doping of single elements. Then, using CALPHAD to calculate the target phase diagram, candidate interface materials could be screened out according to the thermodynamic phase equilibrium between the TE material and other phases. Figure 1a shows the isothermal section at 773 K of the Mg-Ni-Sb ternary phase diagram that was obtained by the CALPHAD method based on the involved binary phase diagram and its thermodynamic data. Apparently, Mg2Ni is predicted as one of the promising candidates for a barrier layer for n-type Mg3Sb2 alloy, which consists of n-type doping elements and is thermodynamically stable to this alloy.
Herein, Mg3.15Co0.05SbBi0.99Se0.01 (n-Zintl) and Yb0.9Mg0.9Zn1.198Ag0.002Sb2 (p-Zintl)31 are chosen as the n-type and p-type leg, respectively. Detailed TE properties are presented in Figs. S1, S2. A high average dimensionless TE figure-of-merit (zT) value of ~1.34 between 300 K and 700 K was achieved by the regulation of Mg vacancies and Bi alloying in n-Zintl. Since the welding temperature is normally 100–300 K higher than the designed hot-side temperature, we annealed these two samples at 973 K for 20 min to simulate the welding effect and found that the TE properties degraded dramatically, especially in n-type samples (Inset in Fig. 1c). Compared with traditional brazing, Ag NPs sintering could be accomplished at 573 K for 10 min24. A similar simulation was performed and the results are presented in the inset of Fig. 1c, showing the unchanged properties at this temperature. Therefore, in order to ensure the thermoelectric properties of the material, it is necessary to avoid excessive welding temperature during the preparation of the Zintl device.
Finally, combined with the topologic structure design, a full Zintl phase device was fabricated. A record high conversion efficiency of ~11% in the single-stage Zintl phase device was achieved (Fig. 1d), which is ~33% higher than the state-of-the-art full Zintl phase device32 (at Th = 673 K) and close to the other single-stage devices9,32,33,34,35,36,37,38. The thermodynamic stability between TE materials and barrier materials ensures the excellent long-term stability of the devices, which is verified by stable power output and conversion efficiency after 50 thermal cycles between hot-side temperatures of 473 K and 673 K (Fig. 1e). In addition, the Zintl phase device possesses low-cost price advantages9,32,33,34,35,36,37,38,39,40 (Fig. 1f).
Herein, we propose an efficient screening strategy guided by diffusion doping effects and the CALPHAD method. A single pure metal cannot meet the requirements of the Mg3Sb2 material for the contact layer, which has been confirmed by experiments41,42,43. Since the diffusion of elements is inevitable, we need to follow the doping matching principle to select inert doping elements (such as Ni, Nb, Co, and Fe, etc. Supplementary Fig. 3). Mg is a necessary element to ensure the n-type conduction of Mg3Sb2-based materials, and can improve the CTE of the alloys to match with TE materials44. Querying the existing binary phase diagrams of Mg alloys, we choose Mg-Ni as a candidate. Based on the thermodynamic data of Mg-Ni45,46,47, Mg-Sb48, and Ni-Sb49 binary phase diagram, we calculated the ternary phase diagram of Mg-Ni-Sb with the help of Pandat software (Supplementary Fig. 4). The establishment of the multi-component phase diagram is able to predict the diffusion-reaction transformations between the two interfaces50,51,52, and quickly screen out thermodynamically stable components among many multi-component phases. Taking the Ni-Mg3Sb2 connection interface as an example, we can make a vertical section along the connection line between Ni and Mg3Sb2 in the ternary phase diagram to check out the transformation at the interface. As shown in Fig. 2a, we obtained the equilibrium phase diagram of Ni-Mg3Sb2 at different ratios and temperatures. When the temperature is set as 773 K (the red dotted line in Fig. 2a), with the increase of Mg3Sb2 ratio, the predictable interfacial reaction structure may appear as Ni, Ni+MgNi2, MgNi2 + MgSbNi, MgSbNi+Mg2Ni, and Mg3Sb2 + Mg2Ni. Obviously, if the metal Ni is selected as the contact material, then the contact layer will undergo complex reactions. Besides, it should be noted that the mass balance line (the red dotted line in Figs. 1a, 2a) is not the diffusion path, but it can predict the interface structure to a certain extent. And the calculated Gibbs energy of the Mg3Sb2 + Mg2Ni system is the lowest among all the composition systems, which means that this system is thermodynamically stable (Fig. 2b). The longitudinal profile of Mg2Ni-Mg3Sb2 also proves that no chemical reaction occurs in the two-phase region regardless of the composition ratio from room temperature to 873 K, except for the solid solution and precipitation of Mg (Fig. 2c and Supplementary Fig. 5). These works are also carried out in Mg-Ni-Bi system53,54, and we got the same conclusion (Supplementary Fig. 6). With the powerful thermodynamic calculation capability of CALPHAD, we can quickly screen out Mg2Ni materials that are in thermodynamic equilibrium with Mg3(Sb, Bi)2, thus ensuring the thermal stability of the connection interface.
The Mg2Ni/n-Zintl joints were then fabricated, and the interfacial structure evolution under accelerated aging time was systematically investigated. According to elemental mapping results and compositional profiles (Fig. 2d and Supplementary Fig. 7), a thinner interlayer composed of Mg-Sb(Bi)-Ni exists at the interface of the prepared junction. Excess Ni observed in the Mg2Ni layer (Supplementary Fig. 8), considering the Mg volatilization during sintering, which caused the interface composition to partially deviate from the Mg2Ni-Mg3Sb2 two-phase region, leading to the formation of the Mg-Sb(Bi)-Ni phase (corresponding phase diagram shown in Supplementary Fig. 9, and chemical compositions of interlayer list in Table S1). After 100 h of aging, the excess Ni near the interlayer interface was consumed. The interface entered a local thermodynamic equilibrium state, and no obvious change occurred in the subsequent 700-hour aging (Supplementary Fig. 10). Based on the experimental thickness of the intermediate layer during the aging process and the kinetic equation, the kinetic parameters and growth curves of the Mg2Ni joint at the aging temperature of 673 K were obtained (Supplementary Fig. 11). Since the degree of reaction is much weaker than that in direct contact with Ni, the initial contact resistivity of the Mg2Ni joint is only 2.5 μΩ cm2 (lower penal in Fig. 2d), which is also better than other reported joints so far38,41,42,55. Without considering other factors, the contact resistivity (ρc) is composed of interface electrical loss and intermediate layer loss, where the former is approximately constant and the latter is linear with the thickness of the intermediate layer33. If the thickness is calculated by diffusion theory, the change of contact resistance over time can be predicted (Fig. 2e), which shows that the contact resistivity is lower than 10 μΩ cm2 after 1000 days of aging. In contrast, the thickness of the intermediate layer in the Ni/n-Zintl joint rapidly increased to ~25 μm after aging for 400 h (Supplementary Figs. 12, 13). Moreover, due to the difference in the thermal expansion coefficient between Ni and n-Zintl, holes and cracks appear in TE materials near the interface. And the contact resistance of the Ni joint is greater than that of the Mg2Ni joint and increases to >200 μΩ cm2 in 400 h (upper penal in Fig. 2e). Benefiting from the CTE matching of Mg2Ni with n-Zintl (Supplementary Fig. 14) and the defect-free dense interface, the Mg2Ni joint has satisfactory shear strength (σs) of ~25 MPa (Fig. 2f). And due to the thermodynamic stability of the designed interface structure, the decay of σs is very slow in aging process, while the σs of Ni/n-Zintl joint decays to less than 10 MPa. More importantly, the matching contact materials were developed in p-type Mg3Sb2 and PbTe materials through the CALPHAD method in this work (Supplementary Figs. 15, 16)56,57,58,59,60, which proved the applicability of this screening strategy.
Since higher zTs tend to be achieved at elevated temperatures, a larger temperature difference for the same average zT represents a higher efficiency. The pursuit of higher zT and efficiency has brought the service temperature of TE materials close to the temperature limit of their thermal stability, which leads to an extremely narrow soldering temperature range for device fabrication61,62,63. The use of a conventional filler inevitably results in a low working temperature (unfavorable for the output power of the TE device) or a high welding temperature (unfavorable for the thermal stability of the TE material). In recent reports, the conductive filling paste was frequently used due to its simple application process and short-term high-temperature tolerance6,64. However, the decline of conductivity at high temperatures and the complete sacrifice of strength limits the application prospects of the prepared TE devices. Low-temperature connection technology can realize the connection at a temperature lower than the service temperature to avoid performance loss. Our previous work proved that Ag NPs as welding fillers could realize the preparation and service of low-, medium- and even high-temperature thermoelectric devices24. The thermal stability and reliability of low-temperature sintered nano-silver at high temperatures are concerns in the field of thermoelectricity, which has not been fully studied yet.
Due to the increase in specific surface energy caused by the nanonization of particles, nano-silver can be sintered at a lower temperature and pressure65. Figure 3a presents the schematic diagram of the nano-silver sintering process using the sintering temperature of 573 K and pressure of 10 MPa in this work. The morphology of Ag NPs before and after sintering has been characterized, and the results are shown in Fig. 3b. The Ag NPs have an approximately spherical shape with a diameter of about 50 nm and are covered with an organic layer to prevent oxidation and self-adhesive connections. After sintering, the protection layer evaporates, and the particles are connected to each other to form a network structure, and the re-melting temperature returns to the melting point of silver due to the increase in size24. Considering the higher service temperature of the TE device than other normal electronic devices, the mechanical reliability of solder joints during aging has been studied. The nano-silver network structure of as-sintered joints is uniformly distributed and well connected at the interface, as shown in Fig. 3c. The average σs of the as-sintered joint is up to 117 MPa (Fig. 3d), which is higher than that of many traditional welded joints66. However, during the long-aging process at 773 K, the sintered network structure grows, so the uniformly distributed micropores accumulate into larger pores67,68, which causes the σs of the joint to drop rapidly to 45 MPa within 25 h and maintain at 40–65 MPa within the subsequent 800-hour aging process. Thus we imposed different pressures during the aging process. The samples undergo the process of secondary sintering with the σs of the joint maintaining above 90 MPa during the 100-hour aging process under the pressure of 0.5–1 MPa. Due to the densification of the nano-silver structure accompanied by lateral shrinkage, there are residual pores in part of the joint structure (Fig. 3c and Supplementary Fig. 17), the σs of the joint cannot exceed the strength before aging, but it is completely sufficient to meet the service requirements of TE devices. In addition, the average contact resistivity of the Ag NP bonding interface is about 1 μΩ cm2 (Insets in Fig. 3e, f), which is negligible compared to the internal resistance of the thermoelectric legs.
A highly efficient and reliable device requires n- and p-type materials with high TE performance and matched physical properties to reduce device residual thermal stress. Through a series of material optimization, our previous work has achieved high TE properties in both n- and p-type Zintls, i.e., Mg3.15Co0.05SbBi0.99Se0.01 (n-Zintl) and Yb0.9Mg0.9Zn1.198Ag0.002Sb2 (p-Zintl)5,31. Temperature-dependent electrical and thermal transport properties of the materials are measured parallel and perpendicular to the hot-pressing direction, both of which are almost similar (Fig. 4a and Supplementary Figs. 1, 2).
A sandwich structure of Ag/Mg2Ni/n-Zintl enables low total interfacial resistivity (ρtotal) of 7.1 μΩ cm2 (Fig. 3e and Supplementary Figs. 18). Combined with Ag NPs sintering, we successfully prepared an n-Zintl single-leg device that can safely serve at high temperatures, and the results are shown in Supplementary Fig. 19 (As for comparison, the simulation results are provided in Supplementary Fig. 20). The single-leg device achieves a record efficiency of 13.3% and an output power density of 1.2 W cm−2 at a temperature difference of 430 K. Under a high current density of 16 A cm-2, the efficiency is basically unchanged after aging for 100 h at Th = 723 K and a ΔT = 430 K (attenuation rate is less than 5%) (Supplementary Fig. 21), indicating the high thermal stability of Mg2Ni and sintered Ag NPs joints. The zT value and theoretical efficiency of Yb0.9Mg0.9Zn1.198Ag0.002Sb2 outperform the previously reported 1-2-2-type Zintl materials and are comparable to other p-type materials in the tested temperature range (Supplementary Fig. 22)69,70,71,72,73,74,75,76,77,78,79,80,81,82,83,84,85. The sandwich structure of Ag/Ni/Fe-Sb86 is used to prepare the p-Zintl single-leg device, resulting in low ρtotal values of 5.5 μΩ cm2 (Fig. 3f and Supplementary Figs. 23). An efficiency of ~9.17% (theoretical efficiency is 11%) for this p-Zintl single-leg device at Th = 723 K and a ΔT = 430 K has been realized (Supplementary Fig. 24, 25). As a comparison, 11 types of state-of-the-art p-type Zintl-phase materials and 6 types of other materials69,70,71,72,73,74,75,76,77,78,79,80,81,82,83,84,85 were selected, and the theoretical efficiency of devices constructed using them along with n-Zintl was calculated (Fig. 4b). Due to the difference in electrical and thermal properties, TE pairs composed of different n- and p-type TE materials will achieve the optimal conversion efficiency at different cross-sectional area ratios. Ap/An = 1 is desirable since the heat transfer and thermal stress are more uniform under this condition, and the filling fraction of TE legs can be increased. Finite element simulations were employed to obtain the optimal cross-sectional area ratio (Ap/An) of the p- and n-type legs for maximum conversion efficiency (ηmax). According to the simulation results, p-type Zintl phase materials achieve the highest efficiency near Ap/An = 1 due to similar thermal and electrical properties, but the device efficiency is relatively low. The Ap/An of other advanced TE materials is different from unity due to the difference in physical properties, but high zTs increase the overall efficiency of the device. Among them, p-Zintl is one of the few materials that simultaneously achieves Ap/An close to 1 and has a high device efficiency, reaching ~13%. Figure 4c shows the thermal expansion properties of the n-Zintl and other p-type materials, where the thermal expansion performance of p-Zintl well matches that of n-Zintl.
In the geometry design of the thermoelectric device, we include the interfacial resistance and consider the effect of height. For a fixed total cross-sectional area (Apn), the output performance and conversion efficiency of the device drop rapidly as H decreases (Fig. 4d and Supplementary Fig. 26). Since the thermocouple is placed at the interface between the device and the heater or heat sink (the temperature at both ends of device is fixed during simulation), as H decreases, the influence of the interface thermal resistance increases, and the actual temperature difference between the two ends of the TE legs decreases. In order to verify the performance and reliability of the device, a two-couple Zintl phase device with Ap/An = 1 was prepared and characterized. At the cold-side temperature of 293 K, the current (I), output voltage (U), P, and ηmax of this device were measured under different ΔT (Figs. 4e, f). A record ηmax of ~11% was realized when Th reached 723 K, close to the predicted value of ~12% (Supplementary Figs. 27, 28). The maximum power density (ωmax) of the device was 0.51 W cm−2, close to the calculated value of 0.54 W cm−2. After 50 thermal cycles between hot-side temperatures of 473 K and 673 K, the internal resistance and output performance of the Zintl device remain stable, i.e., the attenuation rate is less than 8% (Fig. 1e and Supplementary Fig. 29). The high thermal stability of the device can be partly attributed to the matching physical properties of p- and n-type Zintl phase materials.
To sum up, the computational phase diagram method was successfully applied to efficiently screen thermodynamically stable contact materials. It has been demonstrated that Mg2Ni/Mg3.15Co0.05SbBi0.99Se0.01 joints have excellent contact electrical properties and thermal stability. The low-temperature Ag NPs sintering substantially reduces the welding temperature to ensure the integrity of the interface and the high thermoelectric performance of the materials, and the proven high-temperature service reliability ensures the stability of the thermoelectric devices. The single-leg and two-couple devices with Mg2Ni/Mg3.15Co0.05SbBi0.99Se0.01 junctions achieve high η of ~13.3% and ~11%, respectively, with good stability and thermal cycling performance. Our work not only proves the potential of Zintl thermoelectric materials and devices, but also provides a feasible path from contact design to device connection, thus greatly promoting the development of advanced thermoelectric power generation devices with high efficiency and remarkable reliability.
Methods
Preparation and measurement of joints and devices. High-purity raw materials were directly weighed according to the nominal composition Mg3.15Co0.05SbBi0.99Se0.01 (n-Zintl), loaded into a ball-milling jaw in a glovebox, and finally subjected to the milling process for 10 h (SPEX SamplePrep 8000 Mixer Mill). The p-type Yb0.9Mg0.9Zn1.198Ag0.002Sb2 (p-Zintl) sample was synthesized by ball-milling for 5 h31. The p-type Mg2.475Zn0.5Na0.0125Sb2 materials were obtained by ball-milling the raw materials for 10 h71. The p-type Na0.02Pb0.98Te materials were obtained by melting at 1273 K for 6 h24,70. The contact materials Mg2Ni, Fe-Sb and Fe-Te alloys were also obtained by ball-milling the raw materials for 10 h. The raw powders of Mg2Ni were sintered using the SPS method under 40 MPa at 773 K for 10 min. Then, the sintered bulk was ball milled for 6 min to get the final powders.
After sintering the n-Zintl powders at 1023 K under 50 MPa for 2 min, the bulk sample was polished and sintered with Mg2Ni powders and Ag powders at 773 K under 40 MPa for 10 min to obtain the n-Zintl junctions. The p-Zintl powders were sintered with Fe-Sb powders, Ni powders, and Ag powders at 923 K under 40 MPa for 5 min. The p-type Mg3Sb2/Fe-Sb junctions were prepared in a similar way. The p-type PbTe/Fe-Te junctions were obtained by hot-pressing at 773 K for 5 min under a pressure of 50 MPa. For the aging test, there are at least three parallel specimens for each aging time.
The sintered junctions were cut into about 3.6 × 3.6 × 7 mm3. After grinding and polishing, a protective coating of boron nitride from a commercial source was sprayed on the four sides of the n-Zintl thermoelectric legs, while the hot and cold ends were shielded. Then the hot and cold sides of the TE legs were sintered onto Ag electrode foil or Ag-plated copper metalized ceramic substrate using Ag NP paste at 573 K for 10 min under 10 MPa. The same sintering process was used to prepare welding joints on Ag-plated copper sheets for the shear strength test. The overall size of the 2-pair device was about 10 × 10 × 9 mm3. Copper wires were soldered onto the cold side of Cu electrodes to measure the current and voltage. Aerogel slurry was filled within the thermoelectric legs to reduce heat loss due to convection and radiation. The measurements of the device were conducted in a homemade testing system41.
Characterization methods. A commercial system (ULVAC ZEM-3) was used to characterize the electrical conductivity (σ) and Seebeck coefficient (S). Thermal conductivity (к) was calculated by к = d × Cp × D, where d is the density measured by the Archimedean method, Cp is the specific heat capacity measured by differential scanning calorimetry (Netzsch DSC 404 C), and D is the thermal diffusivity measured by laser flash method (Netzsch LFA457). The coefficient of thermal expansion was determined by the thermal mechanical analyzer (TMA 402, Netzsch). Scanning electron microscopy (SEM, Phenom Pro) and an attached energy dispersive spectrometer were used to analyze the microstructure and phase composition. A bonding testing instrument (TRY, MFM-1200) was used to characterize the shear strength with a shear height of 100 μm and shear speed of 200 μm s−1. A homemade four-probe measurement system41 was used to measure the interfacial resistivity of the junctions with an alternating current of 0.1 A. The geometric optimization of thermoelectric devices was simulated and analyzed by finite element analysis software COMSOL Multi-physics24,87. The simulation boundary conditions were determined according to Supplementary Table 2.
CALPHAD modeling. We take the Mg-Ni-Sb as an example to explain the CALPHAD process in detail. Thermodynamic modeling of the Mg-Ni-Sb system was based on data from Mg-Ni45,46,47, Mg-Sb48, and Ni-Sb49 binary subsystems, and the corresponding binary phase diagrams are presented in Supplementary Fig. 2. All phases involved in Mg-Ni-Sb can be divided into the solution phases and the intermetallic phases. The Gibbs energy of pure elements at stable element reference (SER, 298.15 K and 105 Pa) were taken from the SGTE (Scientific Group Thermodata Europe) database88.
The solution phases based on the elements of Mg, Ni, Sb, and the liquid are described with a substitutional solution model and associate solution model, whose (phase φ) molar Gibbs energy could be defined as:
where xi and 0Gi respectively denotes the mole fraction and the ideal molar Gibbs energy of a phase for the element i, R the gas constant, T the absolute temperature, EGm the excess molar Gibbs energy that is expressed as Redlich-Kister formula:
where Li,j is the binary interaction parameters of the species i and j, and vLi,j,k is the ternary interaction parameters of the species i, j, and k (v = 0, 1, 2 and i, j, k = Mg, Ni, Sb, Mg3Sb2). The binary and the ternary interaction parameters take the following form:
where a, b, c, d, e, f, g and h are the coefficients to be optimized. In most cases, only the first one or two terms of the above equation are used.
There are 10 intermetallic phases existing in the Mg-Ni-Sb system, in which the Mg2Ni, ζ-NiSb2, and MgNiSb were modeled as the stoichiometric compounds. And the solubility of the other element in α-Mg3Sb2, β-Mg3Sb2, MgNi2, δ-Ni3Sb, β-Ni3Sb, θ-Ni5Sb2, and γ-NiSb was considered. All the intermetallic phases are treated as a sublattice model and the Gibbs energy is described based on the Compound Energy Formalism (CEF) proposed by Mats Hillert89.
The crystallographic data of all the phases in the Mg-Ni-Sb system are listed in Table S3 and the optimized parameters are listed in Table S4. Similar CALPHAD work has also been carried out for the Mg-Ni-Bi system, Mg-Sb-Fe system, and Pb-Te-Fe system, and the corresponding information is listed in Table S5 to Table S8. All calculations in this work were performed by Pandat software.
Uncertainty analysis. The uncertainty of the temperature difference (ΔTCu), heat flow (Q), output power (P), and efficiency (η) was calculated by standard error analysis and propagation method as following formulas:
The uncertainty of κCu, ACu, LCu (8 mm ± 0.1 mm), I, U, and T are 7%, 0.5%, 1.25%, 1%, 1%, and ±0.01 K, respectively. Table R9 lists the estimated uncertainty of ΔTCu, Q, and η measurements for the Zintl-based devices.
Data availability
All data are available in the main text or the supplementary materials. The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Snyder, G. J. & Toberer, E. S. Complex thermoelectric materials. Nat. Mater. 7, 105–114 (2008).
Bell, L. E. Cooling, heating, generating power, and recovering waste heat with thermoelectric systems. Science 321, 1457–1461 (2008).
Yan, Q. & Kanatzidis, M. G. High-performance thermoelectrics and challenges for practical devices. Nat. Mater. 21, 503–513 (2022).
Tamaki, H., Sato, H. K. & Kanno, T. Isotropic conduction network and defect chemistry in Mg3+δSb2-based layered Zintl compounds with high thermoelectric performance. Adv. Mater. 28, 10182–10187 (2016).
Zhang, F. et al. High-performance n-type Mg3Sb2 towards thermoelectric application near room temperature. Adv. Funct. Mater. 30, 1906143 (2019).
Liu, Z. et al. Demonstration of ultrahigh thermoelectric efficiency of ∼7.3% in Mg3Sb2/MgAgSb module for low-temperature energy harvesting. Joule 5, 1196–1208 (2021).
Liang, Z. et al. High thermoelectric energy conversion efficiency of a unicouple of n-type Mg3Bi2 and p-type Bi2Te3. Mater. Today Phys. 19, 100413 (2021).
He, W. et al. High thermoelectric performance in low-cost SnS0.91Se0.09 crystals. Science 365, 1418–1424 (2019).
Jiang, B. et al. High figure-of-merit and power generation in high-entropy GeTe-based thermoelectrics. Science 377, 208–213 (2022).
Liu, W. & Bai, S. Thermoelectric interface materials: a perspective to the challenge of thermoelectric power generation module. J. Mater. 5, 321–336 (2019).
Deng, P.-Y. et al. Eliciting high-performance thermoelectric materials via phase diagram engineering: a review. Adv. Energy Sustainability Res. 2, 2100054 (2021).
Kim, S. I. et al. Dense dislocation arrays embedded in grain boundaries for high-performance bulk thermoelectrics. Science 348, 109–114 (2015).
Androulakis, J. et al. Spinodal decomposition and nucleation and growth as a means to bulk nanostructured thermoelectrics: enhanced performance in Pb1-xSnxTe-PbS. J. Am. Chem. Soc. 129, 9780–9788 (2007).
Heinz, N. A., Ikeda, T., Pei, Y. & Snyder, G. J. Applying quantitative microstructure control in advanced functional composites. Adv. Funct. Mater. 24, 2135–2153 (2014).
Sundman, B. Computational thermodynamics: the Calphad method. (Cambridge University Press, 2007).
Saunders, N. & Miodownik, A. P. CALPHAD (calculation of phase diagrams): A comprehensive guide. (Elsevier, 1998).
Liu, H., Wang, K., Aasmundtveit, K. & Hoivik, N. Intermetallic compound formation mechanisms for Cu-Sn solid-liquid interdiffusion bonding. J. Electron. Mater. 41, 2453–2462 (2012).
MacDonald, W. & Eagar, T. Transient liquid phase bonding. Annu. Rev. Mater. Sci. 22, 23–46 (1992).
Wang, T., Chen, X., Lu, G.-Q. & Lei, G.-Y. Low-temperature sintering with nano-silver paste in die-attached interconnection. J. Electron. Mater. 36, 1333–1340 (2007).
Kahler, J. et al. Sintering of copper particles for die attach. IEEE Trans. Compon. Packag. Manuf. Technol. 2, 1587–1591 (2012).
Panaccione, P. et al. Improved heat dissipation and optical performance of high-power LED packaging with sintered nanosilver die-attach material. J. Microelectron. Electron. Packag. 7, 164–168 (2010).
Kähler, J., Stranz, A., Waag, A. & Peiner, E. Thermoelectric coolers with sintered silver interconnects. J. Electron. Mater 43, 2397–2404 (2014).
Wu, W., Bentaleb, A., Waag, A. & Peiner, E. Fabrication and characterization of single-pair thermoelectric generators of bismuth telluride using silver-sintering technology. Mater. Today: Proc. 5, 10401–10407 (2018).
Yin, L. et al. Low-temperature sintering of Ag nanoparticles for high-performance thermoelectric module design. Nat. Energy 8, 665–674 (2023).
Shuai, J. et al. Tuning the carrier scattering mechanism to effectively improve the thermoelectric properties. Energy Environ. Sci. 10, 799–807 (2017).
Zhu, W. et al. Enhanced average thermoelectric properties of n‑type Mg3Sb2 based materials by mixed-valence Ni doping. J. Alloy. Compd. 924, 166598 (2022).
Mao, J. et al. Manipulation of ionized impurity scattering for achieving high thermoelectric performance in n-type Mg3Sb2-based materials. Proc. Natl Acad. Sci. 114, 10548–10553 (2017).
Huang, L. et al. Thermoelectric performance improvement of p-type Mg3Sb2-based materials by Zn and Ag co-doping. Mater. Today Phys. 21, 100564 (2021).
Wang, Y. et al. Optimizing the thermoelectric performance of p-type Mg3Sb2 by Sn doping. Vacuum 177, 109388 (2020).
Bhardwaj, A. & Misra, D. K. Enhancing thermoelectric properties of a p-type Mg3Sb2- based Zintl phase compound by Pb substitution in the anionic framework. RSC Adv. 4, 34552–34560 (2014).
Zhang, Z. et al. A dual role by incorporation of magnesium in YbZn2Sb2 Zintl phase for enhanced thermoelectric performance. Adv. Energy Mater. 10, 2001229 (2020).
Jiang, M. et al. High-efficiency and reliable same-parent thermoelectric modules using Mg3Sb2-based compounds. Natl Sci. Rev. 10, nwad095 (2023).
Chu, J. et al. Electrode interface optimization advances conversion efficiency and stability of thermoelectric devices. Nat. Commun. 11, 2723 (2020).
Jia, B. et al. Realizing high thermoelectric performance in non-nanostructured n-type PbTe. Energy Environ. Sci. 15, 1920–1929 (2022).
Ying, P. et al. A robust thermoelectric module based on MgAgSb/Mg3(Sb,Bi)2 with a conversion efficiency of 8.5% and a maximum cooling of 72 K. Energy Environ. Sci. 15, 2557–2566 (2022).
Liu, R. et al. Thermal-inert and ohmic-contact interface for high performance half-Heusler based thermoelectric generator. Nat. Commun. 13, 7738 (2022).
Bu, Z. et al. An over 10% module efficiency obtained using non-Bi2Te3 thermoelectric materials for recovering heat of <600 K. Energy Environ. Sci. 14, 6506–6513 (2021).
Fu, Y. et al. Mg3(Bi,Sb)2-based thermoelectric modules for efficient and reliable waste-heat utilization up to 750 K. Energy Environ. Sci. 15, 3265–3274 (2022).
Zhu, B. et al. Realizing record high performance in n-type Bi2Te3-based thermoelectric materials. Energy Environ. Sci. 13, 2106–2114 (2020).
Yu, J. et al. Half-Heusler thermoelectric module with high conversion efficiency and high power density. Adv. Energy Mater. 10, 2000888 (2020).
Yin, L. et al. Reliable n-type Mg3.2Sb1.5Bi0.49Te0.01/304 stainless steel junction for thermoelectric applications. Acta Mater. 198, 25–34 (2020).
Wu, X. et al. A general design strategy for thermoelectric interface materials in n-type Mg3Sb1.5Bi0.5 single leg used in TEGs. Acta Mater. 226, 117616 (2022).
Wang, Y. et al. Suppression of interfacial diffusion in Mg3Sb2 thermoelectric materials through an Mg4.3Sb3Ni/Mg3.2Sb2Y0.05 /Mg4.3Sb3Ni-graded structure. ACS Appl. Mater. Interfaces 14, 33419–33428 (2022).
Ohno, S. et al. Phase boundary mapping to obtain n-type Mg3Sb2-based thermoelectrics. Joule 2, 141–154 (2018).
Jacobs, M. & Spencer, P. A critical thermodynamic evaluation of the system Mg-Ni. Calphad 22, 513–525 (1998).
Li, Q. et al. Experimental investigation and thermodynamic modeling of the phase equilibria at the Mg-Ni side in the La-Mg-Ni ternary system. J. Alloy. Compd. 509, 2478–2486 (2011).
Miettinen, J. Thermodynamic description of Cu-Mg-Ni and Cu-Mg-Zn systems. Calphad 32, 389–398 (2008).
Zhang, J., Wang, J. & Yuan, Y. A thermodynamic assessment of the Mg-Sn-Sb ternary system. Calphad 75, 102361 (2021).
Zhang, Y., Li, C., Du, Z. & Guo, C. A thermodynamic assessment of Ni-Sb system. Calphad 32, 378–388 (2008).
Kirkaldy, J. S. & Brown, L. Diffusion behaviour in ternary, multiphase systems. Can. Metall. Q. 2, 89–115 (1963).
Engstro, A. & Morral, J. Computer simulations of Ni-Cr-Al multiphase diffusion couples. Acta Mater. 45, 1189–1199 (1997).
Wu, K., Morral, J. & Wang, Y. Horns on diffusion paths in multiphase diffusion couples. Acta Mater. 54, 5501–5507 (2006).
Niu, C. et al. A thermodynamic assessment of the Bi–Mg–Sn ternary system. Calphad 39, 37–46 (2012).
Vassilev, G., Gandova, V. & Docheva, P. Comments and reconciliation of the Ni-Bi-system thermodynamic reassessments. Cryst. Res. Technol. 44, 25–30 (2008).
Wu, X. et al. Interface and surface engineering realized high efficiency of 13% and improved thermal stability in Mg3Sb1.5Bi0.5-based thermoelectric generation devices. Adv. Energy Mater. 12, 2203039 (2022).
Dilner, D., Kjellqvist, L. & Selleby, M. Thermodynamic assessment of the Fe-Ca-S, Fe-Mg-O and Fe-Mg-S. Syst. J. Phase Equilib. Diffus. 37, 277–292 (2016).
Pei, B., Björkman, B., Sundman, B. & Jansson, B. A thermodynamic assessment of the iron-antimony system. Calphad 19, 1–15 (1995).
Gierlotka, W., Łapsa, J. & Jendrzejczyk-Handzlik, D. Thermodynamic description of the Pb-Te system using ionic liquid model. J. Alloy. Compd. 479, 152–156 (2009).
Vaajamo, I. & Taskinen, P. A thermodynamic assessment of the iron-lead binary system. Thermochim. Acta 524, 56–61 (2011).
Arvhult, C. M., Guéneau, C., Gossé, S. & Selleby, M. Thermodynamic assessment of the Fe-Te system. Part II: Thermodynamic modeling. J. Alloy. Compd. 767, 883–893 (2018).
Rowe, D. M. CRC handbook of thermoelectrics. (CRC Press, 2018).
Shang, H. et al. N-type Mg3Sb2-xBix with improved thermal stability for thermoelectric power generation. Acta Mater. 201, 572–579 (2020).
Zhang, F. & Saxena, S. Phase stability and thermal expansion property of FeSi2. Scr. Mater. 54, 1375–1377 (2006).
Jiang, B. et al. Realizing high-efficiency power generation in low-cost PbS-based thermoelectric materials. Energy Environ. Sci. 13, 579–591 (2020).
Lu, G.-Q., Calata, J. N., Lei, G. & Chen, X. Low-temperature and pressureless sintering technology for high-performance and high-temperature interconnection of semiconductor devices. in 2007 International Conference on Thermal, Mechanical and Multi-Physics Simulation Experiments in Microelectronics and Micro-Systems. EuroSime 2007. 1–5 (IEEE, 2007).
Pan, J., Toleno, B. J., Chou, T. C. & Dee, W. J. The effect of reflow profile on SnPb and SnAgCu solder joint shear strength. Soldering Surf. Mt. Technol. 18, 48–56 (2006).
Zhao, Z. et al. The mechanism of pore segregation in the sintered nano Ag for high temperature power electronics applications. Mater. Lett. 228, 168–171 (2018).
Zhang, H. et al. Failure analysis and reliability evaluation of silver-sintered die attachment for high-temperature applications. Microelectron. Reliab. 94, 46–55 (2019).
Niu, Y. et al. Enhanced average thermoelectric figure of merit of p-type Zintl phase Mg2ZnSb2 via Zn vacancy tuning and hole doping. ACS Appl. Mater. Interfaces 12, 37330–37337 (2020).
Ren, Z. et al. Significantly enhanced thermoelectric properties of p-type Mg3Sb2 via co-doping of Na and Zn. Acta Mater. 143, 265–271 (2018).
Shuai, J. et al. Higher thermoelectric performance of Zintl phases (Eu0.5Yb0.5)1−xCaxMg2Bi2 by band engineering and strain fluctuation. Proc. Natl Acad. Sci. 113, E4125–E4132 (2016).
Shuai, J. et al. Thermoelectric properties of Bi-based Zintl compounds Ca1-xYbxMg2Bi2. J. Mater. Chem. A 4, 4312–4320 (2016).
Shuai, J. et al. Thermoelectric properties of Zintl compound Ca1-xNaxMg2Bi1.98. Appl. Phys. Lett. 108, 183901 (2016).
Shuai, J. et al. Thermoelectric properties of Na-doped Zintl compound: Mg3-xNaxSb2. Acta Mater. 93, 187–193 (2015).
Toberer, E. S. et al. Traversing the metal-insulator transition in a Zintl phase: rational enhancement of thermoelectric efficiency in Yb14Mn1-xAlxSb11. Adv. Funct. Mater. 18, 2795–2800 (2008).
Chen, C. et al. Enhanced thermoelectric performance of Zintl phase Ca9Zn4+xSb9 by beneficial disorder on the selective cationic site. ACS Appl. Mater. Interfaces 11, 37741–37747 (2019).
Zevalkink, A. et al. Thermoelectric properties of Sr3GaSb3-a chain-forming Zintl compound. Energy Environ. Sci. 5, 9121–9128, (2012).
Toberer, E. S., Zevalkink, A., Crisosto, N. & Snyder, G. J. The Zintl compound Ca5Al2Sb6 for low-cost thermoelectric power generation. Adv. Funct. Mater. 20, 4375–4380 (2010).
Kazem, N. et al. High temperature thermoelectric properties of the solid-solution Zintl phase Eu11Cd6-xZnxSb12. Chem. Mater. 27, 4413–4421 (2015).
Zhu, H. et al. Discovery of ZrCoBi based half Heuslers with high thermoelectric conversion efficiency. Nat. Commun. 9, 2497 (2018).
He, R. et al. Achieving high power factor and output power density in p-type half-Heuslers Nb1-xTixFeSb. Proc. Natl Acad. Sci. 113, 13576–13581 (2016).
Sui, J. et al. Texturation boosts the thermoelectric performance of BiCuSeO oxyselenides. Energy Environ. Sci. 6, 2916–2920, (2013).
Peng, S. et al. Enhanced thermoelectric and mechanical properties of p-type skutterudites with in situ formed Fe3Si nanoprecipitate. Inorg. Chem. Front. 4, 1697–1703 (2017).
Zhao, L.-D. et al. Ultralow thermal conductivity and high thermoelectric figure of merit in SnSe crystals. Nature 508, 373–377 (2014).
Qiu, P. et al. High-efficiency and stable thermoelectric module based on liquid-like materials. Joule 3, 1538–1548 (2019).
Sun, Y. et al. Low contact resistivity and excellent thermal stability of p-type YbMg0.8Zn1.2Sb2/Fe-Sb junction for thermoelectric applications. Acta Mater. 235, 118066 (2022).
Zhang, Q. et al. Realizing a thermoelectric conversion efficiency of 12% in bismuth telluride/skutterudite segmented modules through full-parameter optimization and energy-loss minimized integration. Energy Environ. Sci. 10, 956–963 (2017).
Dinsdale, A. T. SGTE data for pure elements. Calphad 15, 317–425 (1991).
Hillert, M. The compound energy formalism. J. Alloy. Compd. 320, 161–176 (2001).
Namsani, S., Gahtori, B., Auluck, S. & Singh, J. K. An interaction potential to study the thermal structure evolution of a thermoelectric material: β-Cu2Se. J. Comput. Chem. 38, 2161–2170 (2017).
Acknowledgements
This work was supported by the National Key Research and Development Program of China (2023YFB3809400), the Shenzhen Science and Technology Program (KQTD20200820113045081). Q.Z. acknowledges financial support from the National Natural Science Foundation of China (52172194, 51971081), the Natural Science Foundation for Distinguished Young Scholars of Guangdong Province of China (2020B1515020023), and the Shenzhen Science and Technology Program (RCJC20210609103733073). X.F.L. acknowledges financial support from the National Natural Science Foundation of China (52302232), the China Postdoctoral Science Foundation (2022M720941). J.M. acknowledges financial support from the National Natural Science Foundation of China (52101248), Shenzhen fundamental research projects (JCYJ20210324132808020).
Author information
Authors and Affiliations
Contributions
Q.Z. and L.Y. designed this work. L.Y., X.F.L., C.C., and Z.W.Z. synthesized the samples and conducted the transport property measurements. X.F.L. conducted the calculation of the phase diagram. L.Y., X.B., and J.X.C. conducted the experimental study on device fabrication and characterization. Q.Z., L.Y., X.F.L., J.M., F.C., and X.J.L. discussed the results. L.Y., X.F.L., Q.Z., J.M., and F.C. wrote this manuscript and all authors edited it.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Lei Miao and the other anonymous reviewer for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yin, L., Li, X., Bao, X. et al. CALPHAD accelerated design of advanced full-Zintl thermoelectric device. Nat Commun 15, 1468 (2024). https://doi.org/10.1038/s41467-024-45869-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-45869-w
- Springer Nature Limited