Abstract
On the >1 µm scale the morphology of semicrystalline plastics like polyethylene or Nylon features spherulites, “shish-kebabs”, cylinddrites and other crystalline aggregates which strongly affect mechanical and other material properties. Current imaging techniques give only a 2D picture of these objects. Here we show how they can be visualized in 3D using fluorescent labels and confocal microscopy. As a result, we see spherulites in 3D, both in neat polymers and their nanocomposites, and observe how unevenly nanoparticles and other additives are distributed in the material. Images of i-polypropylene and biodegradable poly(lactic acid) reveal previously unsuspected morphologies such as “vases” and “goblets”, nonspherical “spherulites” and, unexpectedly, “shish-kebabs” grown from quiescent melt. Also surprisingly, in nanocomposite sheets spherulite nucleation is seen to be copied from one surface to another, mediated by crystallization-induced pressure drop and local melt-flow. These first results reveal unfamiliar modes of self-assembly in familiar plastics and open fresh perspectives on polymer microstructure.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Spherulites, shish-kebabs, cylindrites, and other morphological features of bulk semicrystalline polymers (SCP) have so far been studied using methods such as polarized optical microscopy (POM)1, transmission electron (TEM)2, or atomic force microscopy (AFM)3. For these studies either thin films or thin sections were used, giving 2D but not 3D pictures. The organization in the 3rd dimension has been implied rather than observed, and confined to tedious and destructive microtome sectioning. True 3D imaging of SCP morphology has not yet been reported.
Electron tomography has been used for visualizing chemically heterogeneous structures of polymer blends4, block copolymers5,6,7,8 and nanoparticle assemblies in block copolymers9 and polypeptides10. The method is successful when absorption contrast exists between chemically different species and where the structures are on a ≤1 µm scale11. However it is not at its best for studying SCP morphology where (a) the objects (e.g. spherulites) are on a scale of tens and hundreds of µm and (b) where there is no chemical contrast. In addition, exposing a SCP to a very high irradiation dose required by electron tomography will completely destroy the crystallinity of an organic polymer, and with it, the only available contrast, that between the crystalline and amorphous phase.
Recently, more exotic 3D imaging techniques have been tried, such as using X-rays based on the minute difference in X-ray refractive index in polymer blends12 and foams13. Despite some success, these methods suffer from low contrast and require highly specialized and scarce coherent synchrotron X-ray beamlines.
Regarding SCP nanocomposites, the distribution of nanoparticles (NPs) in these systems is still relatively poorly understood. TEM of thin sections had some success in locating metal NPs but giving a very localized picture14. The location of silica NPs in polymers like polypropylene and poly(ethylene oxide) has been studied because of the commercial importance of such nanocomposites. However, due to difficulties visualizing submicron SiO2 NPs only diffraction techniques were used, such as small-angle X-ray or neutron scattering (SAXS, SANS), giving a spatially averaged picture of NP aggregation rather than an image of their location15. In fact even 2D imaging has been missing. For example, it had been assumed that as spherulite grows during polymer solidification, small NPs (<5 nm) could be excluded but larger ones would stay trapped within the spherulites, thus remaining as uniformly dispersed in the solid polymer as in the precursor melt. However, our preliminary 2D studies using labeled NPs have shown that, contrary to theoretical predictions, large NPs are to a considerable extent pushed ahead of growing spherulites and deposited at their boundaries16 with potentially serious consequences for material integrity.
Beside spherulites, cylindrites, “shish-kebabs,” and transcrystalline layers17,18,19, interest in morphology on the µm to mm scale in SCPs also includes cavities produced during solidification20 or cooling. Polymer spherulites are aggregates of thin (10–50 nm) crystalline lamellae grown mainly radially from the common nucleus21,22,23. The classic method of viewing them is POM. In Fig. 1(a1, a3) the birefringent spherulites of isotactic polypropylene (iPP) are seen to grow from the isotropic melt. However this method is inevitably restricted to thin films, normally significantly thinner than the spherulite diameter, thus imaging disks rather than spheres. The long-standing question is how to visualize spherulites and, generally, polymer morphology on this scale in 3D.
Results and discussion
An appropriate contrast method is required, as a start. We were inspired by the work of Calvert et al.24,25,26 who used fluorescence microscopy (FM) to view the distribution of a UV absorber in iPP and observed a lowered concentration of the additive within the spherulites. In Fig. 1(a2, a4) we show FM images recorded during the same crystallization run and from the same area as in the POM images in Fig. 1(a1, a3). The iPP had the hydrophobic dye Nile Red (NR) added, initially uniformly dispersed (Supplementary Fig. S1 in Supplementary Information). The low-fluorescence circles are seen to coincide with the birefringent “spherulites,” i.e., disks, in POM images. Moreover, the melt close to the growing spherulites is visibly brighter, as the dye is partially rejected and concentrated ahead of the spherulite growth front. A study by 2D FM of spherulite growth in NR-doped iPP and poly(lactic acid) (PLA) is reported in ref. 16.
Another advantage of FM is its ability to clearly image cracks and cavities that are mostly overlooked by POM27—see Fig. 1(a5). This fluorescence micrograph, taken from a fully crystallized film of NR-doped PLA, shows a cavity (black, top right) surrounded by a dye-rich polymer. It also shows Newton fringes outlining the areas where the polymer had detached from the glass due to its contraction upon crystallization. The effect of crystallization-induced negative pressure28 will help explain some of the observations described further on.
The technique
In order to use fluorescence to observe the morphology in 3D, we employ confocal laser microscopy. In materials science it has been utilized in studies of polymer blends and block copolymers29,30,31, relying on the difference in solubility or binding of the dye in the chemically different domains. We are aware of only one, indeed a very interesting recent use of this technique in a thin-film homopolymer, where a mechanically cleavable group was incorporated into the chains to give fluorescent radicals, thus marking stress points in the crystallizing material32. To observe true 3D morphology in bulk homopolymers here we create contrast in two different ways: (a) by first producing a uniform blend of polymer and fluorophore and then allowing partial exclusion of the fluorophore from the growing spherulites, which results in the dye being concentrated at spherulite boundaries; (b) by immersing the already crystallized polymer in a solution of a fluorescent dye and relying on the dye’s preferential diffusion and deposition along spherulite boundaries. The fluorophore for both methods (a and b) used in this work for imaging pure polymers was commercial Nile Red. For the study of nanocomposites it was the silica nanoparticles themselves that acted as the labels, 200 nm in diameter, highly monodisperse and chemically modified with a custom-synthesized NR derivative—see Supplementary Fig. S216.
To create a 3D image, the sample is xy-scanned by exciting laser layer by layer and subsequently the slices are combined in a z-stack and visualized in a variety of ways, as shown in Figs. 1–3. We used the 2-photon fluorescence method, whereby a near-IR laser is employed for scanning, causing upconversion and fluorescence emission of visible light33. The 2-photon method has several advantages over the more conventional 1-photon method34,35. First, the resolution in z-direction is higher, as illustrated in Fig. 1(b1). In simple terms, this can be understood by assuming that fluorescence intensity scales with the square of exciting light intensity, in the same way as the rate of a second-order chemical reaction A + A → A2 is proportional to [A]2. Accordingly, for a Gaussian z-profile of exciting light intensity, we have also a Gaussian of fluorescence but with a smaller halfwidth, \(\sqrt{2}/2\), of that of the exciting light. In principle, the same should apply to xy resolution but since this is higher than z-resolution anyway and determined by the diffraction limit, the above advantage of 2-photon excitation is canceled by its longer wavelength. Limiting the fluorescence to a smaller excitation volume also has the effect of increasing the signal-to-noise ratio. A further advantage is the deeper penetration of IR light compared to visible, due to its weaker scattering on the optically inhomogeneous spherulitic polymer—see Fig. 1(b2) where attenuation at increasing depth in polystyrene is compared for 1- and 2-photon fluorescence of NR. It is worth recalling that IR photography is used for a clearer view in misty conditions for the same reason. A yet further advantage is reduced photo-bleaching by the lower energy laser.
Pure dye-labeled polymers
In this work, an xy-scan was recorded in 1 µm z-increments. As an example, Fig. 1(c1-c9) shows nine slices, 12 µm apart, from an NR-doped iPP sample using false colors to represent fluorescence intensity (see the scale at the bottom right). The 3D image constructed from the full z-stack is shown as a solid slab in Fig. 1(c10) and an xz and a yz slice in Fig. 1(c11) and (c12), respectively—see also Supplementary Video 1. The boundaries between spherulites can be clearly seen as straight bright lines in either xy, xz, or yz planes. This is a result of the dye having been partially rejected from the growing spherulites and remaining concentrated at boundary planes after the spherulites had collided. We note, furthermore, that the dye concentration inside the spherulites is not uniform; it is the lowest in the center (black). This has already been noted previously in 2D fluorescence micrographs16,25 and was tentatively attributed to a higher crystallinity of spherulite centers. However, the higher fluorescence away from the center is also partially due to the back diffusion of the dye from the boundaries after crystallization16.
If the sole aim is to visualize the morphology rather than investigate the distribution of additives, the fluorescent label can be introduced after sample solidification. This is illustrated in Fig. 1d where NR had been infiltrated into solid iPP by sample immersion in a solution of the dye. A suitable immersion time has to be used; examples of under- and over-immersion are shown in Supplementary Fig. S3. The dye can be seen again to occupy spherulite boundaries, this time because they present preferred diffusion pathways and increased swelling sites. Figure 1(d1) also illustrates another method of 3D visualization, referred to here as “porous” rendering, whereby only fluorescence above a certain threshold is registered; this leaves spherulite interior transparent—see also Supplementary Video 2. Porous rendering can be applied irrespective of whether the dye-infiltration or dye-rejection method is applied, or whether pure polymers or their composites are imaged (see also Fig. 3(a2)).
The images show directly how after crystallization the polymer volume is divided into tessellating irregular Voronoi polyhedra that are conventionally referred to as spherulites, and that are the topological duals of the nucleation centers.
Beside showing the internal structure, 3D confocal imaging is useful for mapping surface irregularities, which can, moreover, be accurately related to the underlying internal morphology, such as spherulite boundaries. Figure 1(d1, d2) of NR-labeled iPP again provides a good example, where the vertical slice in (d2) is taken along the dotted line in (d1). The cracks (white in (d2)) are seen to run along spherulite boundaries, appearing as double walls between spherulites. Propagation of internal cracks can be clearly followed in their entirety by manipulating the 3D-rendered landscape, as seen in the video. Another example of visualization of surface irregularities and internal cavities is presented in Fig. 1e for PLA.
In order to observe 3D morphology during the growth of spherulites before they collide, and test if they are really spherical, their isothermal growth was interrupted by quenching. Selected 3D images of arrested spherulites of iPP are shown in Fig. 2a, c, and of PLA in Fig. 2b, d. False-color solids in Fig. 2(a1, b1) show the low-fluorescent (blue) spherulites surrounded by highly fluorescent (yellow) quenched melt. In iPP the brighter halo surrounding some spherulites can also be seen, coming from the rejected dye. The darker spherulite centers are even more evident than in Fig. 1, as the back-diffusing dye has not had a chance to reach them16.
A particularly useful rendering technique for part-crystallized polymers is to highlight interfaces with the maximum gradient in fluorescence intensity. This outlines the spherulite surface very clearly and is applied in Fig. 2(a2, b2–4) and Supplementary Videos 3 and 4. We are not aware of any previous in-situ images of spherical spherulites. But how spherical are they? That the discs commonly observed in xy plane by POM are circular is well established. What about the third dimension? Fig. 2(c, d) show vertical sections through selected spherulites from Fig. 2(a, b). Comparing their vertical section with the inscribed reference circles, we can say that the spherulites are closely spherical but elongate somewhat when approaching the polymer-glass interface—more on this in the next section.
Polymers with nanoparticles
We now turn to polymers containing nanoparticles. While the presence of the NPs did not have a significant effect on spherulite growth rate16, it increased their nucleation rate ∼fivefold in the PLA + NP blend—see Supplementary Figs. S4 (calorimetry), S6 (POM), and S7 (graph). Figure 3(a1–a4) show part of a fully crystallized sheet of PLA containing 200 nm dye-labeled silica NPs. Similar morphology is also seen in an equivalent nanocomposite of iPP in Fig. 3b. The observed contrast relies entirely on the redistribution during spherulite growth of the NPs originally homogeneously dispersed in the melt. Had they all been immobile and remained occluded within the spherulites, as theory based on Stokes–Einstein law had predicted36, images in Fig. 3 and in another subsequent figure that also shows the morphology of NP-containing polymer would have been featureless. In fact, the theory gives the diffusion rate of 200 nm NPs a thousand times lower than needed to escape a growing spherulite16. While NP aggregation on polymer matrix crystallization has been observed by SAXS36, the location of the aggregates was unknown. A possible explanation of the unsuspected ability of NPs of this size to be “pushed” and excluded from the growing spherulites is the existence of a depletion layer ahead of the growth front, its high negative pressure20,28 pulling-in the particles16. More unsuspected and profound consequences of such negative pressure are described below in subsequent figures.
The heightened presence of nanoparticles at the spherulite growth front is also illustrated by SEM of fractured part-crystallized PLA nanocomposite (Fig. 4a). The surface shown is that below a detached spherulite. Unlike the rather smooth surface of a similarly prepared pure PLA sample in Fig. 4b, the boundary surface of the nanocomposite is full of holes and interlamellar gaps left by the numerous accumulated NPs. In comparison, SEM of a fracture surface of amorphous PLA + NP blend of the same composition, quenched from the melt to below Tg and shown in Supplementary Fig. S5, shows only a few isolated single-particle holes.
An interesting feature of Fig. 3a is that in many cases the spherulites tend to appear roughly above each other, forming columns—see Fig. 3(a3, a4) and the Supplementary Video 5 of the “porous” 3d landscape in Fig. 3(a2). This is unexpected, as it is normally assumed that spherulites nucleate randomly and independently.
However, the biggest surprise of the current study is discovered in the part-crystallized PLA nanocomposite. Figure 5(a1, a2) are z-slices at the bottom and the top surface of a film of PLA with labeled 200 nm NPs. The top surface is almost an exact copy of the bottom one, with even the smallest spherulites nearly exactly above each other. Moreover, the mirrored spherulites have almost exactly the same diameter, meaning that they nucleated on opposite surfaces within seconds of each other. How did they communicate?
Observing the 3D morphology in Fig. 5b, revealed by surface rendering, brings us closer to the answer. The picture shows what appears like a treasure find of ancient bowls, vases, and goblets. The objects have C∞ symmetry and most have a widened circular base at the bottom and the top; these are believed to be half-spherulites nucleated on opposite surfaces. In panels c1–c4, we present our explanation of the formation of a “goblet,” by showing individual pieces of “crockery” each at a different stage of development. The corresponding schematics are shown in panel d. The formation of a half-spherulite at the top surface (c1, d1) creates negative pressure around it as well as at the surface opposite, where the supply of replacement polymer by diffusion is most limited. This is where nucleation of the second half-spherulite is stress induced (c2, d2). As both half-spherulites grow toward each other a connecting stress field and elongational flow develop37 and trigger nucleation and growth of what appears to be shish-kebabs38; these initiate the formation of the “stand” of the goblet (c3, d3). In fact, we were fortunate to have captured the beginning of fibrous shish-kebab formation—see inset in Fig. 5(c3). Thus a goblet is formed (Fig. 5(c4, d4)). Had crystallization continued isothermally, it would have ended as a polyhedral column, but its high-crystallinity inner core would have remained goblet shaped, as suggested by the white-line-delineated area in Fig. 3(a3) right.
Other objects in Fig. 5b, with bulging centers, are thought to have nucleated within the film interior but as the initial spherulite grew the negative pressure built up at both nearby surfaces; this had induced additional half-spherulite nucleation, their growth and eventual merger into a column-like object—see several examples in Figs. 3(a4) and 5b. It is likely that most of them include shish-kebab segments, which continued growing laterally to form a “cylindrite” 39.
Numerical simulations of stress distribution and fluid flow in a layer with a fluid sink close to one surface, and two sinks at opposing surfaces, are shown in Fig. 6(a, b), corroborating the above interpretation of the cause of the intriguing observed morphologies. The situation where a spherulite nucleates in the sheet interior is also modeled. The pressure distribution and flow lines shown in Fig. 6c confirm again the negative pressure peaks at both surfaces nearest to the growing spherulite. As the spherulite approaches the surface, the negative pressure increases greatly (Fig. 6d). This explains the appearance of additional surface half-spherulites and their merger with the initial spherulite and the formation of “vases” with a “neck” and columns in Figs. 2(c, d), 3(a3, a4) and 5b.
To our knowledge, this is the first observation of shish-kebab formation in the quiescent melt. Shish-kebabs, or “row-nucleated structures,” normally form in flowing melt or solution, or under externally applied stress, particularly if the polymer has cross-links38,40. The stress causing shish-kebab nucleation in the present case is self-generated by spherulite crystallization. The fact that these unusual morphologies are most pronounced in polymers with added NPs can be attributed to the restrictive effect of silica NPs on polymer chain mobility41,42,43. That same effect also causes increased cavitation in NP-containing polymers16. The nanoparticles can be regarded here as acting like physical cross-links. In the current experiments, NP concentration is low, while in most practical applications their concentration is higher, thus the effects revealed here are expected to be even more pronounced. However, even without NPs there is the acceleration of spherulite growth when approaching substrate surface, seen both in pure iPP (Fig. 2c) and in PLA (Fig. 2d). Figure 6e clearly shows that the asphericity of spherulites increases with proximity to the substrate even in neat PLA and, to a lesser extent, also in iPP (Supplementary Fig. S8). A PLA spherulite may have a diameter measured vertically up to 25% larger than horizontally. This suggests that the negative pressure28 affecting morphology and spherulite growth kinetics is a universal phenomenon in semicrystalline polymers, and in their nanocomposites in particular.
The higher asphericity of PLA spherulites compared to that of iPP can be attributed to lower mobility of PLA in the 120–130 °C temperature range—cf. glass transition temperatures of ∼60 °C for PLA and −10−0 °C for iPP. The slower chain diffusion in PLA will cause the buildup of higher negative pressure. Additional restriction to diffusion in PLA nanocomposite will arise from the interaction of polar PLA with the polar silica, a stronger attraction than that between the silica and the nonpolar iPP. This would explain why the unusual morphologies in Fig. 5 are seen in PLA nanocomposite, and why nonspherical spherulites are mostly observed in PLA and less so in iPP. Effects on 3D morphology of other factors, such as molecular weight and the nature of the polymer, as well as the type, concentration, size, and coating of the NPS, are all subjects of current and future investigations.
Conclusions and outlook
We have shown how morphology of semicrystalline polymers and their nanocomposites can be visualized in 3D on the critical 10–1000 µm scale. The first 3D images of growing and fully grown spherulites have revealed that they are not always spherical, that in nanocomposites their nucleation can be copied across from one surface to another through growth-induced negative pressure, and that this can induce shish-kebabs formation in the static melt. All this results in morphologies that escaped previous notice due to a lack of 3D imaging. The technique is expected to be applied to other systems, revealing further unknown morphological features of polymers and nanocomposites.
Methods
Materials
iPP (Mw = 2.5 × 105 g/mol and Mn = 6.7 × 104 g/mol), Nile Red (C20H18N2O2), anhydrous p-xylene 99%, and dioxane were purchased from Sigma-Aldrich. PLLA 4032D containing around 2% D-lactide (Mw = 2.23 × 105 g/mol and Mn = 1.06 × 105 g/mol) was obtained from NatureWorks (USA). The syntheses of the Nile Red derivative 9-diethylamino-2-(triethoxysilyl-3-propyloxy)-5H-benzo[α]phenoxazin-5-one and SiO2 NPs of 200 nm were carried out according to refs. 44,45, respectively. Their hybridization is described in ref. 16.
Sample preparation
Dye- and NP-doped polymers were prepared by freeze-drying mixed solutions in order to obtain a uniform mixture of NR and the polymers. For iPP + NR sample, iPP pellets and NR powder (2000:1 wt ratio) were first dissolved in p-xylene (130 °C, mild stirring). The solution was frozen by quenching in liquid nitrogen, after which the solvent was sublimed off under vacuum at 0 °C. For PLA + NR sample, the solvent was dioxane and the solution mixing temperature was 50 °C. The final concentration of NR in both the iPP and PLA was 0.05 wt%. Supplementary figure S1 illustrates the uniformity of the polymer-dye blends.
For polymer-nanoparticle blends NPs were first dispersed in methanol (sonication, 60 min), then the NP suspension was mixed with polymer solution followed by freeze-drying. The solvents and dissolution temperatures were the same as above. The concentration of 200 nm NPs in both the iPP and PLA was 1.3 wt%.
For crystallization of dye- and NP-doped polymers the samples were placed between a glass slide and a coverslip, annealed at 210 °C for 10 min to erase thermal history. They were then cooled to Tc at the highest cooling rate allowed by the hot stage (ca 30 °C/min) and maintained at Tc for a set period. Afterwards, the samples were quenched in ice water.
Dye-labeling by immersion of neat iPP sheets crystallized at 130 °C for 12 min was carried out by placing the sheet in a flask with NR/p-xylene solution (6 mg/L). The temperature was set at 25 °C for the penetration of NR into iPP film, as this temperature left the crystalline regions unaffected46,47.
Microscopy
Two-photon confocal fluorescence microscopy was done on an Upright Zeiss LSM 510 META confocal microscope equipped with a Chameleon Ti-Sapphire femtosecond pulsed laser with a wavelength of 1000 nm, an oil-immersion 40 × /1.30 objective, and a HFT KP650 dichroic mirror accepting laser wavelength >650 nm and allowing through fluorescent emission <650 nm. xy plane slices were captured by line-by-line scanning and moved along z-axis direction 1 μm steps. The 3D rendering methods are described in figure captions.
Scanning electron microscopy was performed on a field-emission instrument (Inspect F, FEI, USA), operating at 5 kV. Small pieces of ~200 μm thick neat PLA and PLA + NP 200 nm samples were melt crystallized at 130 °C for 10 min and immersed in liquid nitrogen for 1 h, then cryogenically fractured. The smooth fracture surface was sputter-coated with gold.
Finite element analysis
FEA of negative pressure and melt flow caused by spherulite growth is carried out using Mathematica, by solving the Navier-Stokes equations in a 2D box of size 6 × 1. The growing spherulites are represented by circular boundaries at coordinates (0,z), with z = 0.1 (close to the bottom surface), 0.5 (middle of the box), 0.6 (slightly above the middle) or 0.9 (close to the top surface) respectively, with a radius of 0.05 or 0.2 and a constant outflow rate at the boundary. Two counterbalancing inflowing boundaries are placed close to the two side edges of the box, at coordinates (±2.5, 0.5). The flow rates are set to zero at the four straight boundaries of the box. The equations are solved numerically in iterations until the estimated normalized error is smaller than 10−5 for the dataset.
Data availability
The raw images (.lsm files) generated in this study are available for download at the figshare database, https://doi.org/10.6084/m9.figshare.14910291
References
Keller, A. Morphology of crystalline synthetic polymers. Nature. 171, 170–171 (1953).
Sawyer, L., Grubb, D. T. & Meyers, G. F. Polymer Microscopy (Springer, 2008).
Mullin, N. & Hobbs, J. K. Direct imaging of polyethylene films at single-chain resolution with torsional tapping atomic force microscopy. Phys. Rev. Lett. 107, 197801 (2011).
Sengupta, P. & Noordermeer, J. W. M. Three-dimensional structure of olefinic thermoplastic elastomer blends using electron tomography. Macromol. Rapid Commun. 26, 542–547 (2005).
Sugimori, H., Nishi, T. & Jinnai, H. Dual-axis electron tomography for three-dimensional observations of polymeric nanostructures. Macromolecules. 38, 10226–10233 (2005).
Jinnai, H., Spontak, R. J. & Nishi, T. Transmission electron microtomography and polymer nanostructures. Macromolecules. 43, 1675–1688 (2010).
Segal-Peretz, T. et al. Characterizing the three-dimensional structure of block copolymers via sequential infiltration synthesis and scanning transmission electron tomography. ACS Nano. 9, 5333–5347 (2015).
Ren, J., Segal-Peretz, T., Zhou, C., Craig, G. S. W. & Nealey, P. F. Three-dimensional superlattice engineering with block copolymer epitaxy. Sci. Adv. 6, eaaz0002 (2020).
Zhao, Y. et al. Small-molecule-directed nanoparticle assembly towards stimuli-responsive nanocomposites. Nat. Mater. 8, 979–985 (2009).
Manai, G. et al. Bidimensional lamellar assembly by coordination of peptidic homopolymers to platinum nanoparticles. Nat. Comms. 11, 2051 (2020).
Ikehara, T., Jinnai, H., Kaneko, T., Nishioka, H. & Nishi, T. Local lamellar structures in banded spherulites analyzed by three-dimensional electron tomography. J. Polym. Sci. 45, 1122–1125 (2007).
Momose, A., Fujii, A., Kadowaki, H. & Jinnai, H. Three-dimensional observation of polymer blend by X-ray phase tomography. Macromolecules. 38, 7197–7200 (2005).
Perez-Tamarit, S., Solorzano, E., Mokso, R. & Rodriguez-Perez, M. A. In-situ understanding of pore nucleation and growth in polyurethane foams by using real-time synchrotron X-ray tomography. Polymer. 166, 50–54 (2019).
Masirek, R. et al. Nucleation of isotactic polypropylene crystallization by gold nanoparticles. J. Polym. Sci. 48, 469–478 (2010).
Zhao, D. et al. Tunable multiscale nanoparticle ordering by polymer crystallization. ACS Cent. Sci. 3, 751–758 (2017).
Yang, S. G., Xie, H. J., Saba, H., Cseh, L. & Ungar, G. Fluorescence microscopy tracking of dyes, nanoparticles and quantum dots during growth of polymer spherulites. Polymer. 191, 122246 (2020).
Bassett, D. C. Principles of polymer morphology (Cambridge University Press, 1981).
Gedde, U. W. & Hedenqvist, M. S. Fundamental polymer science. (Springer, 2019).
Yue, K. et al. A few rediscovered and challenging topics in polymer crystals and crystallization. Polym. Cryst. 1, e10053 (2018).
Galeski, A., Koenczoel, L., Piorkowska, E. & Baer, E. Acoustic-emission during polymer crystallization. Nature. 325, 40–41 (1987).
Norton, D. R. & Keller, A. The spherulitic and lamellar morphology of melt-crystallized i-polypropylene. Polymer. 26, 704–716 (1985).
Crist, B. & Schultz, J. M. Polymer spherulites: A critical review. Prog. Polym. Sci. 56, 1–63 (2016).
Lovinger, A. J. Twisted crystals and the origin of banding in spherulites of semicrystalline polymers. Macromolecules. 53, 741–745 (2020).
Ryan, T. G. & Calvert, P. D. Diffusion and annealing in crystallizing polymers. Polymer. 23, 877–883 (1982).
Calvert, P. D. & Ryan, T. G. Reversible secondary crystallization during cooling of polypropylene. Polymer. 25, 921–926 (1984).
Billingham, N. C., Calvert, P. D. & Uzuner, A. Studies of diffusion in polymers by ultraviolet microscopy .2. Diffusion of atactic fractions in isotactic polypropylene. Polymer. 31, 258–264 (1990).
Hobbs, J. K., McMaster, T. J., Miles, M. J. & Barham, P. J. Cracking in spherulites of poly(hydroxybutyrate). Polymer. 37, 3241–3246 (1996).
Pawlak, A. & Galeski, A. Stability of spherulite growth-rate. J. Polym. Sci. 28, 1813–1821 (1990).
Yoshida, S. & Trifkovic, M. Unraveling the effect of 3d particle localization on coarsening dynamics and rheological properties in cocontinuous polymer blend nanocomposites. Macromolecules. 52, 7678–7687 (2019).
Jinnai, H. et al. Observation of fine structure in bicontinuous phase-separated domains of a polymer blend by laser scanning confocal microscopy. Macromolecules. 34, 5186–5191 (2001).
Lee, W. M., Yoon, J. S., Lee, H. J. & Thomas, E. L. Direct 3-d imaging of the evolution of block copolymer microstructures using laser scanning confocal microscopy. Macromolecules. 40, 6021–6024 (2007).
Kato, S. et al. Crystallization-induced mechanofluorescence for visualization of polymer crystallization. Nat. Commun. 12, 126 (2021).
Denk, W., Strickler, J. H. & Webb, W. W. 2-photon laser scanning fluorescence microscopy. Science. 248, 73–76 (1990).
Bush, P. G., Wokosin, D. L. & Hall, A. C. Two- versus one photon excitation laser scanning microscopy: critical importance of excitation wavelength. Front. Biosci. 12, 2646–2657 (2007).
Benninger, R. K. P. & Piston, D. W. Two-photon excitation microscopy for the study of living cells and tissues. Curr. Protoc. Cell Biol. 59, 4.11.11–14.11.24 (2013).
Ning, X. et al. Nanoparticle organization by growing polyethylene crystal fronts. ACS Macro Lett. 8, 1341–1346 (2019).
Carrington, S. P., Tatham, J. P., Odell, J. A. & Saez, A. E. Macromolecular dynamics in extensional flows .2. The evolution of molecular strain. Polymer. 38, 4595–4607 (1997).
Kimata, S. et al. Molecular basis of the shish-kebab morphology in polymer crystallization. Science. 316, 1014–1017 (2007).
Xu, H., Xie, L. & Hakkarainen, M. Beyond a model of polymer processing-triggered shear: reconciling shish-kebab formation and control of chain degradation in sheared poly(l-lactic acid). ACS Sustain. Chem. Eng. 3, 1443–1452 (2015).
Clough, S. B. High temperature x-ray diffraction from drawn and stress-crystallized polyethylene. J. Polym. Sci. B. Polym. Lett. 8, 519–523 (1970).
Kennedy, M., Turturro, G., Brown, G. R. & Stpierre, L. E. Silica retards radial growth of spherulites in isotactic polystyrene. Nature. 287, 316–317 (1980).
Metzner, A. B. Rheology of suspensions in polymeric liquids. J. Rheol. 29, 739–775 (1985).
Krishnamoorti, R., Ren, J. X. & Silva, A. S. Shear response of layered silicate nanocomposites. J. Chem. Phys. 114, 4968–4973 (2001).
Martin-Brown, S. A., Fu, Y., Saroja, G., Collinson, M. M. & Higgins, D. A. Single-molecule studies of diffusion by oligomer-bound dyes in organically modified sol-gel-derived silicate films. Anal. Chem. 77, 486–494 (2005).
Yokoi, T. et al. Mechanism of formation of uniform-sized silica nanospheres catalyzed by basic amino acids. Chem. Mater. 21, 3719–3729 (2009).
Blackadder, D. A. & Lepoidevin, G. J. Dissolution of polypropylene in organic-solvents: 1. Partial dissolution. Polym. 17, 387–394 (1976).
Blackadder, D. A. & Lepoidevin, G. J. Dissolution of polypropylene in organic-solvents: 2. Steady-state dissolution process. Polymer. 17, 768–776 (1976).
Acknowledgements
For support with confocal microscopy we thank Dr. Nicola Green. Financial support is acknowledged from the 111 Project 2.0 of China (BP2018008), from EPSRC (EP-P002250, EP-T003294), from NSFC (21674099, 52003215), and China Postdoctoral Science Foundation (2021M692515). S.G.Y. thanks C.S.C. for stipend.
Author information
Authors and Affiliations
Contributions
G.U. initiated and supervised the study. P.K. and Z.Z.W. introduced and developed the polymer sample preparation and imaging technique, H.S. and H.Y.X. synthesized and labeled the nanoparticles and prepared the nanocomposites under supervision from L.C., S.G.Y. obtained most of the included figures, developed most of the visualization techniques, prepared the figures and the videos. X.B.Z. performed the flow- and stress-field calculations in Fig. 6. G.U. wrote the paper with significant contribution from S.G.Y. All authors participated in discussions.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Milana Trifkovic and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yang, SG., Wei, ZZ., Cseh, L. et al. Bowls, vases and goblets—the microcrockery of polymer and nanocomposite morphology revealed by two-photon optical tomography. Nat Commun 12, 5054 (2021). https://doi.org/10.1038/s41467-021-25297-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-25297-w
- Springer Nature Limited
This article is cited by
-
Crystallization, morphology, optical properties, tear properties and antibacterial properties of nano zinc oxide composites
Journal of Polymer Research (2023)