Abstract
The cornerstones of emerging high-performance organic photovoltaic devices are bulk heterojunctions, which usually contain both structure disorders and bicontinuous interpenetrating grain boundaries with interfacial defects. This feature complicates fundamental understanding of their working mechanism. Highly-ordered crystalline organic p–n heterojunctions with well-defined interface and tailored layer thickness, are highly desirable to understand the nature of organic heterojunctions. However, direct growth of such a crystalline organic p–n heterojunction remains a huge challenge. In this work, we report a design rationale to fabricate monolayer molecular crystals based p–n heterojunctions. In an organic field-effect transistor configuration, we achieved a well-balanced ambipolar charge transport, comparable to single component monolayer molecular crystals devices, demonstrating the high-quality interface in the heterojunctions. In an organic solar cell device based on the p–n junction, we show the device exhibits gate-tunable open-circuit voltage up to 1.04 V, a record-high value in organic single crystalline photovoltaics.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Semiconductor p–n heterojunctions are essential building blocks for various optoelectronic devices and important platforms for investigation of device physics1,2,3, though most of the p–n heterojunctions by far are based on inorganic semiconductors4,5,6,7,8,9,10,11,12,13,14,15. Taking organic photovoltaic (OPV) devices as an example, critical physical processes such as exciton dissociation, which essentially dominate the efficiency of OPVs, occurs at the p–n heterojunction interfaces. However, the fundamental physical mechanisms regarding these processes are still under debate. This is because the exciton diffusion length is typically about 5–20 nm in OPVs16,17, while the thickness of p–n junction is typically higher than this length. Therefore, semiconductor layers outside the exciton diffusion range bring challenges for probing the exciton-related processes underneath. On the other hand, when thickness of the p–n junction is downscaled to the molecular level, excitons generated by photon absorption would be present directly at the p–n junction interface with low loss, and then probably completely dissociate into free holes and electrons. It has been experimentally validated higher device performance could be obtained when size of micro-phase domain decreased18,19, and the optimized micro-phase domain size might vary from case to case depending on the materials used. However, the bulk heterojunctions inevitably comprise both structure disorders and complex interpenetrating grain boundaries with interfacial defects, which poses difficulties for elucidating the exciton physics in OPV studies. Hence, achieving highly ordered crystalline p–n heterojunctions with atomically well-defined interface at monolayer thickness limit, is a powerful strategy for studying exciton physics without the limitations imposed by exciton diffusion lengths, as well as an efficient way to reveal the fundamental mechanisms in organic optoelectronic devices. Organic p–n junctions consisting of monolayer molecule crystals (MMCs) combine the advantages of MMCs and crystalline heterojunctions20,21,22,23,24,25,26,27,28,29,30,31,32,33,34,35,36, which not only have the inherently efficient charge carrier transport in molecular crystals, but also have bilayer thickness with atomically sharp junction interface15, providing a perfect solution to the above-mentioned challenges. However, the direct growth of such thin single-crystalline p–n heterojunctions remains a huge challenge, which significantly limits their applications in organic optoelectronic devices.
Results
Growth and characterization of MMCs based p–n heterojunctions
The low yield of MMCs and lack of a general growth strategy significantly hinders the mass production of MMCs and limits their further application in p–n heterojunctions. Thus, to overcome this challenge is urgent. In our current study, we proposed a controllable two-dimensional space phase separation method, and MMCs are obtained from a solution mixture of poly(methyl methacrylate) (PMMA) and 2,6-bis(4-hexylphenyl)anthracene (C6DPA, Fig. 1a)29. By optimizing the parameters, such as the concentration of PMMA and C6DPA weight concentration in the solution system (Supplementary Note 1 and Supplementary Figs. 1–7), large scale MMCs could be obtained when the thickness of the blended films is tuned under 10 nm by adopting 4 mg mL−1 PMMA and 20 wt.% of C6DPA, and the control of the concentrations is vital for the successful fabrication of MMCs. The films exhibit uniform color and brightness under cross-polarized microscopic observation (Fig. 1b and Supplementary Fig. 1d, e), typical characteristic of single-crystalline films. Further atomic force microscopy (AFM) measurement evidences a thickness of 2.7 ± 0.1 nm (Fig. 1c), smaller than the DFT calculated molecular length of C6DPA (3.2 nm), indicating a tilted angle of around 57.6° (Supplementary Note 2), which is observed in other monolayer37,38. Moreover, optical and fluorescent microscopic images indicate the uniformity of crystals with uniform color distribution, and the maximal lateral size of the MMCs reaches up to 0.47 mm (Fig. 1e, f). High-resolution AFM (HR-AFM, Fig. 1d) and grazing incidence wide-angle X-ray scattering (GIWAXS, Supplementary Fig. 8) results demonstrate the MMCs have highly ordered structure, where the lattice constants along the b and c axes are 0.45 nm and 0.47 nm, respectively, with a θ ~ 99.5°, while the coherence length is about 13 nm. It indicates that C6DPA MMCs are exclusively distributed on the top of PMMA layer rather than on the surface of SiO2 substrates or inside the PMMA, according to photo-induced force microscopy (PiFM) and time of flight secondary ion mass spectrometry (TOF-SIMS, Fig. 2, Supplementary Note 3 and Supplementary Figs. 9 and 10).
Successful preparation of a series of MMCs, such as 2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene (C8BTBT)33, 1,4-bis((5′-hexyl-2,2′-bithiophen-5-yl)ethynyl)benzene (HTEB)39 and 2,2′-(2,8-bis(3-hexylundecyl)-1,3,7,9-tetraoxo-1,2,3,7,8,9-hexahydro-[1,3]dithiolo[4′,5′:5,6]benzo[1,2,3,4-lmn][1,3]dithiolo[4,5-f][3,8]phenanthroline-5,11-diylidene)dimalononitrile (NDI40) (Supplementary Fig. 11), opens a way to fabricate bimolecular layer p–n junctions by the two-dimensional space phase separation method. One possible strategy to achieve ultra-thin p–n heterojunctions is to use a blend of p-, n-type semiconductors and PMMA in the processes. A p–n heterojunction is indeed obtained by the one-step spin-coating method when a NDI (n-type, 0.2 mg mL−1)/C6DPA (p-type, 1 mg mL−1) blend was employed. However, this strategy has not yet been successful in other p-/n-type semiconductor blends. We suspect that the p–n heterojunctions can be formed by our method only when the two crystals share similar lattice parameters (Fig. 1m, n, Supplementary Fig. 12 and Supplementary Table 1). Different from the p–n heterojunctions fabricated by mechanically transferring, the thickness of the heterojunction prepared by our method can be precisely controlled at a bimolecular level (Fig. 1g, h). Optical images, fluorescent images, and AFM images confirm that the heterojunctions have a distinct boundary (Fig. 1h–k), with the monolayer NDI crystal (1.7 nm) located on the top of the heterojunction. The absorption and fluorescent spectra of the MMCs and bilayer p–n junctions are also recorded and illustrated in Supplementary Note 4 and Supplementary Fig. 13. Transmission electron microscope (TEM) and TOF-SIMS characterizations (Fig. 1l and Supplementary Fig. 14) also indicate the bilayer structure of the heterojunction and the bottom C6DPA MMC structure with a thickness of 2.8 nm. The embedded bottom C6DPA MMC has been verified by thickness effect on intensity of Raman spectrum (Supplementary Fig. 15).
The two-dimensional space phase separation process would be dominated by multiple factors, including surface energies, evaporation rate of the solvent, and spin speed41,42,43. To validate the versatility of our fabrication strategy, a variety of substrates were used, including SiO2, Si, quartz, Hf2O5, and plastics (polyethylene terephthalate (PET)). Oxygen plasma treatment was used to improve the wetting property of substrates (Supplementary Methods), and similar MMCs of C6DPA could be obtained from these substrates (Supplementary Figs. 1h and 7). We also investigate the effect of polymer composition on the formation of MMCs by preparing the samples from mixture of C6DPA and other polymers, such as poly(3-hexylthiophene) (P3HT, regiorandom) and poly[2,5-bis(3-tetradecylthiophen-2-yl)thieno[3,2-b]thiophene] (PBTTT-C14). We observe that MMCs could be obtained from the C6DPA/P3HT, but not from C6DPA/PBTTT-C14 (Supplementary Fig. 16). Given the remarkable difference in crystallinity between P3HT and PBTTT-C14, it suggests that crystallinity of the polymer may play a critical role in the phase separation processes. To validate our hypothesis, we used the P3HT possessing different regioregularity, with crystallinity following P3HT (regular, regioregularity ≥ 95%) > P3HT (regioregular, regioregularity ≥ 90%) > P3HT (regiorandom) for solution mixtures (Supplementary Fig. 17). After spin-coating the mixture, C6DPA MMCs were obtained on both regiorandom P3HT and regioregular P3HT, with the former one having better morphology uniformity. In comparison, no MMCs could be observed for the regular P3HT/C6DPA mixture (Supplementary Fig. 16). Such results imply that amorphous polymers are in favor of forming MMCs.
During the spin-coating process, phase separation between PMMA and C6DPA occurred with C6DPA located on top of the PMMA films. With the effect of centrifugal force, the formation of thick and multilayer crystals has been suppressed effectively. In order to understand the self-assembly processes of C6DPA crystalline films on C6DPA/PMMA interface, the dynamics of C6DPA molecules with chlorobenzene were imitated by non-equilibrium molecular dynamics simulations, as shown in Fig. 2e44. The results show that the C6DPA molecules can form a relatively ordered and obliquely oriented monolayer on amorphous PMMA upon solvent evaporation. The formation of C6DPA crystalline films began because of the stronger intermolecular interaction between C6DPA molecules (π–π) compared with that between C6DPA and PMMA (C–H ∙ ∙ ∙ π).
Device fabrication and performance
The high quality of MMCs promises many potential applications such as organic field-effect transistors (OFETs) and organic circuits. The OFETs based on C6DPA MMCs with bottom-gate top-contact device configuration were fabricated. Au stripes were transferred onto MMCs as source and drain electrodes to obtain abrupt metal-semiconductor contacts29,31,32,34, and SiO2 (300 nm)/PMMA was used as gate dielectric. All electrical characterizations of the C6DPA MMC devices were carried out under ambient conditions and all the devices exhibit well-defined transfer characteristics (Fig. 3a and Supplementary Fig. 18). The average mobility of C6DPA MMC devices was estimated to be 1.10 cm2 V−1 s−1 with the highest mobility up to 1.61 cm2 V−1 s−1. We have also evaluated the performance of OFETs based on other MMCs (Fig. 3b, Supplementary Fig. 19). For instance, OFETs based on C8BTBT MMCs exhibit a maximum mobility of 3.16 cm2 V−1 s−1 (Supplementary Fig. 19b), which is higher than the device with ultrathin active layers obtained from other solution process45. The devices with different thickness of C6DPA were compared (Fig. 3c, Supplementary Note 5 and Supplementary Fig. 20) by solvent vapor annealing (SVA) of MMCs/PMMA in saturated chlorobenzene atmosphere. Interestingly, the MMC devices possess a higher mobility compared with the thick crystals. The sharp increase in mobilities for C6DPA MMCs-based OFETs could be interpreted by the reduced contact resistance29,30,31,32,35. In addition, OFETs with ultralow operation voltage have also been fabricated on Si substrates by employing the PMMA layer as dielectric, and the mobility was extracted to be about 0.84 cm2 V−1 s−1 at the 2 V operation voltage (Supplementary Fig. 21). Moreover, the ultra-thin structure of MMCs enables the fabrication of ultra-thin, transparent, flexible, and wearable devices (Supplementary Note 6 and Supplementary Figs. 22–24). For the bilayer p–n junction, we also performed electrical measurements on the corresponding OFETs (see Fig. 3d) and successfully observed ambipolar transport behaviors, indicating the good contact between the p-type C6DPA and n-type NDI MMCs (see Fig. 3e). The hole and electron mobilities are 0.54 and 0.50 cm2 V−1 s−1 at VDS = ± 60 V, respectively, which shows well-balanced ambipolar charge transport performance. With the ambipolar p–n junction transistor device as the basic unit, inverters were also prepared, which exhibit gain of ~14 (see Fig. 3f).
The bimolecular layer single-crystalline p–n heterojunctions provide ideal platforms for the understanding and development of OPVs. In order to explore the photovoltaic properties of the NDI/C6DPA p–n heterojunction, lateral p–n heterojunction photovoltaic devices were fabricated by transferring Au and Ag films onto the surface of the C6DPA and NDI crystals, respectively, to form asymmetric contacts (Fig. 4a). In such a device, when excitons are generated by photon absorption, they would dissociate at the p–n junction interface immediately, following which hole carriers can easily transport along the p-conducting channel to the anode, and simultaneously electrons will move to the upper n-type layer and get collected by the cathode. Figure 4a shows the current–voltage (I–V) characteristics with different gate bias under the white light illumination (26.9 mW cm−2) in ambient conditions. From these data, we extracted the short circuit current (Isc) and open-circuit voltage (Voc) versus the gate voltage (VG) as shown in Fig. 4b. Isc increases linearly with the VG, whereas Voc is also tuned by VG and it first increases with VG and then decreases. Besides, it was seen that Isc and Voc keep increasing as the light intensity increases from 5.1 to 26.9 mW cm−2 (white light, see Fig. 4c and Supplementary Fig. 25), which is consistent with previous studies for normal organic solar cells46,47,48.
The maximum value of Voc is 1.04 ± 0.2 V at VG = −40 V, which is the highest value achieved in organic single-crystalline p–n heterojunctions so far, to the best of our knowledge. For a reference, the energy level difference between LUMO of n-type and HOMO of p-type is about 1.3 eV (see Supplementary Fig. 26). As VG increases, Isc increases linearly with the |VG| and this is attributed to the increased gate-induced hole concentrations and thus the current. The relation between |Voc| and VG is rather complicated. In regular inorganic p–n junctions, the Voc increases if the majority carriers in either side of the p–n junction are increased, due to the enlarged difference between the quasi-Fermi levels for electrons and holes. This trend was exactly observed in our device when VG was varied from 0 V to −40 V (Supplementary Fig. 27), where the hole concentration gradually increased in the p-channel side. However, at higher gate bias, |Voc| decreased and this may be explained as follows: the quasi-Fermi level of the p-type C6DPA moves closer to HOMO as gate bias increases. However, the gate electric field could also downshift the energy levels of the n-type NDI (including the quasi-Fermi level) and induce carrier tunneling across the junction interface. As a result, the open-circuit voltage Voc = (kT/q)*ln(Iph/Idark) decreases. Nevertheless, these results represent interesting physics regarding to the physical processes in OPVs and can be essential to understanding the device physics in OPVs.
Discussion
In summary, we report a simple and universal method, namely two-dimensional phase separation method, to controllably prepare uniform, high-quality, and large-area MMCs by blending the small molecule semiconductors with amorphous polymers. With this method, C6DPA MMCs with a lateral size of more than 400 μm were successfully obtained. More importantly, the method is found to be generally applicable to other small molecular semiconductors such as C8BTBT, HTEB, and NDI, and can be performed on various substrates. Furthermore, we report the one-step growth strategy for constructing ultra-thin vertical organic crystalline p–n junctions with atomically clean and sharp interfaces, and demonstrate their application in a prototype photovoltaic device. This study not only provides a simple yet effective solution for the facile fabrication of MMC-based p–n heterojunctions, but also offers a promising strategy to achieve next-generation optoelectronic devices at monolayer limit.
Methods
Materials
The C6DPA MMCs were prepared by spin-coating the PMMA/C6DPA (weight ratio = 4:1) solution on the SiO2/Si++ substrates at 1500 rpm for 10 s, in which the dielectric layer is composed of SiO2 and PMMA (capacitance, 9.5 nFcm−2). Other MMCs could also be obtained by this way but from different small molecule/polymer blends, that is 1 mg mL−1 HTEB and 4 mg mL−1 PMMA for HTEB MMCs, 2 mg mL−1 C8BTBT and 4 mg mL−1 PMMA for C8BTBT MMCs and 0.5 mg mL−1 NDI and 4 mg mL−1 PMMA for NDI MMCs, respectively. The growth processes of the MMCs are described in the Supplementary Methods.
Measurements
Raman and fluorescent spectra were carried out by WITec alpha300R Confocal Raman Microscope. The microscope images and AFM images of MMCs were carried out by DM4M fluorescent microscope and Nanoscope IIIa instrument (Digital Instruments), respectively. HR-AFM were carried out by Cypher ES Environmental AFM (Oxford Instruments AR). The detailed information of structure characterization of MMCs are provided in the Supplementary Methods.
The electrical characteristics of the devices were measured by Keithley 4200-SCS and Agilent B1500A semiconductor parameter analyzer. The mobility was extracted from the saturated region characteristics by the equation below: \(\mu =\frac{2L}{W{{\rm{C}}}_{{\rm{i}}}}\times {\left(\frac{{\rm{d}}\sqrt{{I}_{{\rm{DS}}}}}{{\rm{d}}{V}_{{\rm{G}}}}\right)}^{2}\). As for the bimolecular layer p–n heterojunction devices, the influence of gate bias and light intensity was explored in ambient conditions. The current–voltage (I–V) characteristics of different gate bias were carried out under the white light illumination (26.9 mW cm−2). The influence of light intensity was explored as the light intensity increased from 5.1 to 26.9 mW cm−2.
Simulations
Molecular dynamics (MD) simulations were performed by the Gromacs-4.6.7 software package with the general AMBER force field, which are described in the Supplementary Methods.
Statistics and reproducibility
MMCs can be obtained with similar results for more than 60 times independent experiment. More than 20 OFETs and 5 inverters and 5 OPVs were prepared, and similar results were obtained.
Data availability
The data that support the finding of this study are included within the Article and its Supplementary Information files, or available from the corresponding authors upon reasonable request.
References
Sze, S. M. Physics of Semiconductor Devices, 2nd edn. (Wiley, 1981).
Yang, T. et al. Van der Waals epitaxial growth and optoelectronics of large-scale WSe2/SnS2 vertical bilayer p–n junctions. Nat. Commun. 8, 1906 (2017).
Li, J. et al. General synthesis of two-dimensional van der Waals heterostructure arrays. Nature 579, 368–374 (2020).
Jiang, S., Li, L., Wang, Z., Shan, J. & Mak, K. F. Spin tunnel field-effect transistors based on two-dimensional van der Waals heterostructures. Nat. Electron. 2, 159–163 (2019).
Frisenda, R., Molina-Mendoza, A. J., Mueller, T., Castellanos-Gomez, A. & van der Zant, H. S. J. Atomically thin p–n junctions based on two-dimensional materials. Chem. Soc. Rev. 47, 3339–3358 (2018).
Liu, Y. et al. Approaching the Schottky-Mott limit in van der Waals metal-semiconductor junctions. Nature 557, 696–700 (2018).
Liu, Y. et al. Van der Waals heterostructures and devices. Nat. Rev. Mater. 1, 16042 (2016).
Zhu, C. R. et al. In situ grown epitaxial heterojunction exhibits high performance electrocatalytic water splitting. Adv. Mater. 30, 1705516 (2018).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Chang, J. F., Gwinner, M. C., Caironi, M., Sakanoue, T. & Sirringhaus, H. Conjugated-polymer-based lateral heterostructures defined by high-resolution photolithography. Adv. Funct. Mater. 20, 2825–2832 (2010).
Duan, X. et al. Lateral epitaxial growth of two-dimensional layered semiconductor heterojunctions. Nat. Nanotechnol. 9, 1024–1030 (2014).
Cheng, H. C. et al. Van der Waals heterojunction devices based on organohalide perovskites and two dimensional materials. Nano Lett. 16, 367–373 (2016).
Chuang, S. et al. Near-ideal electrical properties of InAs/WSe2 van der Waals heterojunction diodes. Appl. Phys. Lett. 102, 242101 (2013).
Cheng, R. et al. Electroluminescence and photocurrent generation from atomically sharp WSe2/MoS2 heterojunction p–n diodes. Nano Lett. 14, 5590–5597 (2014).
Shi, E. et al. Two-dimensional halide perovskite lateral epitaxial heterostructures. Nature 580, 614–620 (2020).
Lin, Y., Li, Y. & Zhan, X. Small molecule semiconductors for high-efficiency organic photovoltaics. Chem. Soc. Rev. 41, 4245–4272 (2012).
Lunt, R. R., Giebink, N. C., Belak, A. A., Benziger, J. B. & Forrest, S. R. Exciton diffusion lengths of organic semiconductor thin films measured by spectrally resolved photoluminescence quenching. J. Appl. Phys. 105, 053711 (2009).
Li, W. et al. Universal correlation between fibril width and quantum efficiency in diketopyrrolopyrrole-based polymer solar cells. J. Am. Chem. Soc. 135, 18942–18948 (2013).
Li, W. et al. Effect of the fibrillar microstructure on the efficiency of high molecular weight diketopyrrolopyrrole-based polymer solar cells. Adv. Mater. 26, 1565–1570 (2014).
Lezama, I. G. et al. Single-crystal organic charge-transfer interfaces probed using Schottky-gated heterostructures. Nat. Mater. 11, 788–794 (2012).
Alves, H., Pinto, R. M. & Macoas, E. S. Photoconductive response in organic charge transfer interfaces with high quantum efficiency. Nat. Commun. 4, 1842 (2013).
Takahashi, Y. et al. Charge conduction properties at the contact interface between (phthalocyaninato)nickel(II) and electron acceptor single crystals. Chem. Mater. 26, 993–998 (2014).
Huang, S., Peng, B. & Chan, P. K. L. Ambipolar organic field-effect transistors based on a dual-function, ultrathin and highly crystalline 2,9-didecyldinaphtho[2,3-b:2′,3′-f]thieno[3,2-b]thiophene (C10-DNTT) layer. Adv. Energy Mater. 3, 1700268 (2017).
Novak, M. et al. Low-voltage p- and n-type organic self-assembled monolayer field effect transistors. Nano Lett. 11, 156–159 (2011).
Cui, Q. H. et al. Coaxial organic p–n heterojunction nanowire arrays: one-step synthesis and photoelectric properties. Adv. Mater. 24, 2332–2336 (2012).
Zhang, Y. et al. Organic single-crystalline p–n junction nanoribbons. J. Am. Chem. Soc. 132, 11580–11584 (2010).
He, D. W. et al. Two-dimensional quasi-freestanding molecular crystals for high-performance organic field-effect transistors. Nat. Commun. 5, 5162 (2014).
Li, H., Fan, C., Fu, W., Xin, H. L. & Chen, H. Solution-grown organic single-crystalline donor-acceptor heterojunctions for photovoltaics. Angew. Chem. Int. Ed. 54, 956–960 (2015).
Xu, C. et al. A general method for growing two-dimensional crystals of organic semiconductors by “solution epitaxy”. Angew. Chem. Int. Ed. 55, 9519–9523 (2016).
Wang, C. et al. N-type 2D organic single crystals for high-performance organic field-effect transistors and near-infrared phototransistors. Adv. Mater. 30, 1706260 (2018).
Shi, Y. et al. Bottom-up growth of n-type monolayer molecular crystals on polymeric substrate for optoelectronic device applications. Nat. Commun. 9, 2933 (2018).
Jiang, L. et al. Millimeter-sized molecular monolayer two-dimensional crystals. Adv. Mater. 23, 2059–2063 (2011).
He, D. et al. Ultrahigh mobility and efficient charge injection in monolayer organic thin-film transistors on boron nitride. Sci. Adv. 3, 1701186 (2017).
Jiang, L. et al. Realizing low-voltage operating crystalline monolayer organic field-effect transistors with a low contact resistance. J. Mater. Chem. C. 7, 3436–3442 (2019).
Liu, J., Jiang, L., Hu, W., Liu, Y. & Zhu, D. Monolayer organic field-effect transistors. Sci. China Chem. 62, 313–330 (2019).
Zhao, H. et al. Strong optical response and light emission from a monolayer molecular crystal. Nat. Commun. 10, 5589 (2019).
Flesch, H.-G. et al. Microstructure and phase behavior of a quinquethiophene-based self-assembled monolayer as a function of temperature. J. Phys. Chem. C. 115, 22925–22930 (2011).
Sizov, A. S. et al. Easily processable highly ordered Langmuir-Blodgett films of quaterthiophene disiloxane dimer for monolayer organic field-effect transistors. Langmuir 30, 15327–15334 (2014).
Meng, Q. et al. New type of organic semiconductors for field-effect transistors with carbon-carbon triple bonds. J. Mater. Chem. 19, 1477–1482 (2009).
Zhang, F. et al. Critical role of alkyl chain branching of organic semiconductors in enabling solution-processed n-channel organic thin-film transistors with mobility of up to 3.50 cm2 V−1 s−1. J. Am. Chem. Soc. 135, 2338–2349 (2013).
Liu, C. et al. Solution-processable organic single crystals with bandlike transport in field-effect transistors. Adv. Mater. 23, 523–526 (2011).
Chua, L. L., Ho, P. K. H., Sirringhaus, H. & Friend, R. H. Observation of field-effect transistor behavior at self-organized interfaces. Adv. Mater. 16, 1609–1615 (2004).
Genzer, J. & Kramer, E. J. Wetting of substrates with phase-separated binary polymer mixtures. Phys. Rev. Lett. 78, 4946–4949 (1997).
Han, G., Shen, X., Duan, R., Geng, H. & Yi, Y. Revealing the influence of the solvent evaporation rate and thermal annealing on the molecular packing and charge transport of DPP(TBFu)2. J. Mater. Chem. C. 4, 4654–4661 (2016).
Wang, Q. et al. 2D single-crystalline molecular semiconductors with precise layer definition achieved by floating-coffee-ring-driven assembly. Adv. Funct. Mater. 26, 3191–3198 (2016).
Cui, Y. et al. Wide-gap non-fullerene acceptor enabling high-performance organic photovoltaic cells for indoor applications. Nat. Energy 4, 768–775 (2019).
Cowan, S. R., Roy, A. & Heeger, A. J. Recombination in polymer–fullerene bulk heterojunction solar cells. Phys. Rev. B 82, 245207 (2010).
Koster, L. J. A., Mihailetchi, V. D., Ramaker, R. & Blom, P. W. M. Light intensity dependence of open-circuit voltage of polymer: fullerene solar cells. Appl. Phys. Lett. 86, 123509 (2005).
Acknowledgements
This work was supported by the Ministry of Science and Technology of China (2017YFA0204704, 2016YFB0401100), the National Natural Science Foundation of China (21873108, 21805284, 22075295), the Chinese Academy of Sciences (Hundred Talents Plan, the Strategic Priority Research Program (Grant No. XDB30000000)). The authors thank Prof. J.G. Mei, Prof. J.P. Wang, Prof. F. Gao, Prof. H.L. Dong, and Prof. X.F. Liu for insightful suggestion.
Author information
Authors and Affiliations
Contributions
L.J. designed and supervised the project with S.W., W.H., Y.L., and H.S.; J.L. and X.G. synthesized the compounds; M.X. prepared the samples, performed the measurements, and carried out the analysis with help from J.L., X.Z. C.L., and Y.H.; G.H. and Y.Y. carried out the simulations. Y.S. and C.L.L. performed measurement and analysis of HR-AFM with help from D.W.; Z.C. and Z.L. performed the GIWAXS experiment and carried out the analysis. Ji. L. provided insightful advice. M.X, J.L., and L.J. wrote the manuscript. All authors contributed to discussions.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Xinran Wang and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xiao, M., Liu, J., Liu, C. et al. Sub-5 nm single crystalline organic p–n heterojunctions. Nat Commun 12, 2774 (2021). https://doi.org/10.1038/s41467-021-23066-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-23066-3
- Springer Nature Limited
This article is cited by
-
Organic donor-acceptor heterojunctions for high performance circularly polarized light detection
Nature Communications (2022)
-
Monolayer molecular crystals for low-energy consumption optical synaptic transistors
Nano Research (2022)