Abstract
Understanding inorganic nanocrystal (NC) growth dynamic pathways under their native fabrication environment remains a central goal of science, as it is crucial for rationalizing novel nanoformulations with desired architectures and functionalities. We here present an in-situ method for quantifying, in real time, NCs’ size evolution at sub-nm resolution, their concentration, and reactants consumption rate for studying NC growth mechanisms. Analyzing sequential high-resolution liquid-state 19F-NMR spectra obtained in-situ and validating by ex-situ cryoTEM, we explore the growth evolution of fluoride-based NCs (CaF2 and SrF2) in water, without disturbing the synthesis conditions. We find that the same nanomaterial (CaF2) can grow by either a particle-coalescence or classical-growth mechanism, as regulated by the capping ligand, resulting in different crystallographic properties and functional features of the fabricated NC. The ability to reveal, in real time, mechanistic pathways at which NCs grow open unique opportunities for tunning the properties of functional materials.
Similar content being viewed by others
Introduction
Colloidal inorganic nanocrystals (NCs) have revolutionized science thanks to their provision of a controllable synthetic platform for tackling fundamental challenges in materials science and their utility in a variety of applications, from catalysis and renewable energy to nanomedicine1,2,3,4,5,6. Their exceptional features (e.g., optical, magnetic, chemical, catalytic, and electrical) often stem from their composition, size, and morphology, emphasizing the essentialness of mechanistic knowledge on NC formation from solution for strategizing novel fabrications. The relationships between NC growth pathways and resultant architectures and functions were revealed thanks to the development of a variety of ex situ and in situ methodologies7. Both spectroscopy- and microscopy-based techniques allow us to monitor NCs’ size evolution, alternations in chemical composition, crystallography properties, and change in shape throughout the course of their formation8,9,10,11,12,13,14,15,16,17,18,19. However, they often require temporal reaction sampling, destructive-energy radiation applications, the use of out-of-equilibrium conditions (e.g., drying, freezing, heating, vacuum) and custom-made apparatuses. Thus, there is a need to implement accessible, alternative in situ approaches that can be performed under authentic nanofabrication settings.
Fluoride-based NCs (i.e., nanofluorides) have garnered much attention recently due to their potential use in optics, catalysis, optoelectronics, bioimaging, superconductor devices, batteries, and lubricants20. Amongst their advantages over other inorganic NCs, their low phonon energies and high chemical stability stand out, making nanofluorides one of the preferable host-materials for upconversion fluorescence21,22,23,24,25,26. These unique characteristics are governed by their crystallinity, size, shape, and introduced impurities, which are strictly regulated by their formation pathways27,28,29. Interestingly, the rich fluoride content and relatively small-size of colloidal nanofluorides result in a characteristically high-resolution 19F-NMR spectrum while in solution30. This property has been exploited to design water-dispersed CaF2 NCs as nanotracers for in vivo 19F-MRI applications, but also provides unprecedented opportunity to use nanofluorides as a platform for tracking NC formation in real time with a high-resolution (HR) NMR setup.
The unique capabilities of NMR-based approaches, which allow the monitoring of changes in the chemical environment of a variety of NMR active nuclei, offer a versatile tool for studying growth pathways and kinetics, surface chemistry, and the physical properties of both organic and inorganic materials31,32,33,34,35,36. In particular, the spectral resolution of NMR shows promise for the characterization of nanomaterials by way of detecting both the organic ligands37 and inorganic core elements38 as a means to explore their formation in solution. Moreover, the ability to spectrally resolve surface from bulk atoms via NMR39,40,41,42,43 makes this method an attractive way to characterize inorganic NC architecture.
Inspired by these studies, we herein present a high-resolution liquid-state NMR-based approach for studying the dynamics of NCs’ size evolution in a quantitative manner without disturbing the reaction conditions (e.g., avoiding sampling, destructive radiation, unwanted heating, undesired freezing, drying, vacuum, etc.). By synthesizing nanofluorides under in situ NMR conditions, and based on the ability to detect the 19F-NMR signals of MF2 (M = Ca2+ or Sr2+) in water, we are able to probe their sub-nm growth over the entire course of their formation, highlighting their controllable growth mechanisms (coalescence vs. classical simple grow), which result in different morphological and functional features.
Results
HR-NMR accurately determines the diameter of NCs in solution
Prior to conducting HR-NMR studies on water-dispersed, small-sized CaF2 NCs capped with 2-aminoethyl phosphate (AEP, at pH7, molecular structure, Fig. 1a), they were synthesized and fully characterized with complementary techniques. Cryo-TEM images revealed monodispersed NCs with an average size of 3.7 ± 0.6 nm (Fig. 1b and Supplementary Fig. 1a) with the confirmed composition of calcium, fluoride, and phosphate (from the ligand), as evaluated by high-angle annular dark-field (HAADF) STEM imaging and energy dispersive X-ray spectroscopy (EDS) (Fig. 1c). The fluorite, faced cubic centered (fcc), crystal structure of the obtained AEP-CaF2 NCs was confirmed by powder X-ray diffraction (XRD, Supplementary Fig. 1b) and their relatively small size as well as their monodispersity were preserved in water, as revealed by dynamic light scattering (DLS, Supplementary Fig. 1c).
The high-resolution 19F-NMR studies of the synthesized AEP-CaF2 NCs in water resulted in a 19F-NMR spectrum, from which two populations of fluorides could be detected, at −105 and −109 ppm, assigned to fluorides at the surface and core of the NCs, respectively44,45 (Fig. 1d). This assignment was further supported by the significant paramagnetic effect on the 19F-NMR peak attributed to the fluorides on the surface of the formulation (Supplementary Fig. 2) emphasizing one of the key features of NMR to provide detailed information that reflects the chemical environment of constituent nuclei. Indeed, NMR studies of nuclei within the NCs (rather than nuclei of the coating ligands) can distinguish between the nuclei at the NC’s solid core and those located at the outer surface, due to differences in chemical environments, relaxation properties, and crystallinity characteristics39,40,41,42,43.
We next deconvolved the obtained 19F-NMR spectrum for AEP-CaF2 NCs, using computational line fitting to quantify the ratio between the 19F-atoms at the surface of CaF2 NCs (Fig. 1d, pink) and the 19F-atoms at the core of CaF2 NCs (Fig. 1d, light-blue). From this ratio and by using Eq. (1) (Fig. 1e, Supplementary Note 1), we could calculate the average diameter of the AEP-CaF2 NCs in water, which was found to be 4.1 nm (Fig. 1d). This ability to quantify the average diameter of water-dispersed nanofluorides from their HR-19F-NMR spectrum by classification and quantification of surface and core atoms provides a unique approach for evaluating the average size of NCs while in solution.
To demonstrate the robustness and reproducibility of this approach, we applied it to evaluate the sizes of various nanofluoride (CaF2 or SrF2) fabrications (Fig. 1f and Supplementary Fig. 3) from their HR 19F-NMR spectra and found them to be in good correlation (r2 = 0.989) with the sizes obtained from HR-TEM images. This ability to accurately determine the average size of a variety of small-sized NCs demonstrates not only the uniqueness but also the potential variability of the proposed HR-NMR-based method. Importantly, magic-angle spinning (MAS) solid-state 19F-NMR of the same synthetic AEP-CaF2 colloids’ powder showed a similar 19F-NMR spectrum (Supplementary Fig. 4a) to that obtained using high-resolution 19F-NMR (Supplementary Fig. 4b), from which similar NC diameters were calculated. This observation confirms that water-dispersed AEP-CaF2 NCs tumble fast enough in solution so as to average out the intrinsic homonuclear dipolar interactions, allowing to directly detect their fluoride content with HR liquid-state 19F-NMR setups.
Observing NC growth in real time with HR-NMR
The ability to evaluate NC sizes at nanometer scale directly from solution without disturbing the system, using the HR 1D-NMR spectrum, offers a platform to monitor, in real time, NC growth dynamics. We validated this possibility by synthesizing nanofluorides in an NMR tube under ambient conditions while acquiring consecutive 19F-NMR spectra from reaction initiation to final formation, monitoring simultaneously the size of the NCs, their concentration at each timepoint of the reaction and the consumption of the F- anions. Controlling the reaction conditions allowed to shed light on the dynamics of NC formation, highlighting their growth mechanism.
To synthesize the NCs, we started by adding a solution of Ca2+ cations to an aqueous reaction solution containing both F- anions and AEP capping ligands.
The NMR tube was then placed in a 9.4T NMR spectrometer and sequential 19F-NMR spectra were acquired to follow the temporal formation of CaF2 colloids, resulting in a 19F-NMR stack plot (Fig. 2a). Our results showed that each 19F-NMR spectrum consisted of two main distinct peaks that could be, simultaneously, identified and assigned. One peak resonated at −120 ppm, assigned to the free F- anion, indicating its consumption with time (Supplementary Fig. 5). The second downfield 19F-NMR peak was attributed to the fluoride content of the CaF2 NC, from which the NC’s diameter could be determined using the approach outlined in Fig. 1. Representative line fittings of the experimental 19F-NMR spectra obtained at three different time points after reaction initiation (i.e., 6, 200, and 1000 min) are presented in Fig. 2b, depicting the varying ratio between the two 19F-spin populations of NCs, which reflects their size evolution. Representative cryo-TEM images of the reaction solution at the same reaction time points (i.e., 6, 200, and 1000 min) are shown above each spectrum in Fig. 2b. The amounts of 19F-atoms on the NC surface (pink) and in its core (light blue) were quantified and plotted as a function of the reaction time (Fig. 2c, 3 min temporal resolution). The diameter of the CaF2 NCs at each timepoint was then derived from each individual 19F-NMR spectrum (using Eq. (1) and Supplementary Note 1) and plotted as a function of reaction time (Fig. 2d). From that plot, a notably rapid formation (3 min after reaction initiation) of ultrasmall CaF2 NCs (2.3 nm) is observed, followed by a period of relatively fast growth (up to 3.2 nm within the first 20 min), which then gives way to much slower growth dynamics. In the regime of rapid NCs growth, the 19F-NMR resonance of the surface atoms was significantly affected, as expected for smaller NCs that display a larger curvature (Supplementary Fig. 6).
Intriguingly, a mild but pronounced decrease in NC diameter was observed between 20 and 30 min (Fig. 2d inset) that is followed by a continuous growth, a phenomenon that could indicate coalescence events during NC growth10,46,47. In parallel to the fast growth rate of the NCs (first 20 min, Fig. 2d), a significant reduction in their concentration was noted (first 20 min, Fig. 2e and Supplementary Equation 2), which was followed by a milder decrease in their total concentration. This observation that numerous small NCs transform into larger (but fewer) NCs, together with the detected intermediate stage (Fig. 2d inset), supports the notion that AEP-CaF2 NCs predominantly grow through coalescence7,48, a conclusion that is in good agreement with the “coalescence point” that can clearly be seen in the inset of Fig. 2d and found to be reproducible (N = 4, Supplementary Fig. 7). Such coalescence events were also captured by both cryo-TEM (Supplementary Fig. 8) and high-resolution TEM (Supplementary Fig. 9) images sampled 25 min from the reaction initiation. Such a mechanistic pathway is promoted by the unfavorable thermodynamic state of initially formed ultrasmall NCs10, together with a relatively high number of NCs in solution, which may increase their collision probabilities and, essentially, lead to their coalescence to form larger, more stable NCs. Note here that Ostwald ripening mechanistic pathway may also occur but it is probably much less prominent than coalescence for AEP-CaF2 NCs growth, as reflected in both in situ NMR spectroscopy (Fig. 2 and Supplementary Fig. 7) and TEM imaging (Supplementary Fig. 8 and Supplementary Fig. 9). Importantly, we further validated the temporal change in the size of the NCs over time with ex situ cryo-TEM. To that end, the reaction mixture was sampled at three different stages (6 min, 200 min, and 1000 min; Fig. 2b and Supplementary Fig. 10). The NC diameters obtained from cryo-TEM images (Supplementary Fig. 10e) were in a very good correlation (Supplementary Fig. 10f, R2 = 0.98) with those calculated from in situ 19F-NMR at the same reaction stages.
The generality of the proposed in-situ 19F-NMR for studying NC formation and growth was demonstrated also for SrF2 NCs (Fig. 3 and Supplementary Fig. 11). Compared to CaF2 NCs, the SrF2 NCs were larger, as determined by cryo-TEM (Fig. 3a, b) and DLS (Fig. 3c). The difference in size in the sub-nm range could be clearly depicted by the HR-19F-NMR approach (Fig. 3d, e), and the method was applied to monitor, in situ and in real time, the formation of AEP-SrF2 NCs. Notably, at three minutes after reaction initiation, the SrF2 NCs were much larger than the CaF2 NCs (2.9 nm vs. 2.3 nm, respectively), a size difference that was preserved throughout the reaction. Similar to the case of CaF2, the temporal evolution of SrF2 NCs is characterized by an initial fast growth followed by a moderate leveling-off of the size with time. Importantly, for both investigated nanofluorides, the concentration of the NCs in the solution decreased in parallel to their growth (Figs. 2d, e, 3e, and Supplementary Fig. 11b). To further elucidate this formation mechanism, we monitored the ligands during NC synthesis by way of in situ liquid-state 31P-NMR (Supplementary Fig. 12). The 31P-NMR peak of free AEP in solution is a clear narrow triplet. Upon the initial formation of NCs, this triplet broadens probably due to the restricted mobility of the bound ligands to the numerous very small NCs that had formed. As the reaction progresses, when the number of NCs in the solution drops (Fig. 2e and Supplementary Fig. 11b), free AEP-ligands are re-released to the solution and their 31P-NMR peak narrows again due to their faster tumbling rates.
The role of ligands in the NC growth pathways
It is well known that ligands regulate NC formation mechanisms and dynamics, as they were found to be key elements in stabilizing both the reaction intermediates8,49 and formed colloids50,51. Specifically, differences in NC growth mechanisms have been attributed to the different affinities of the ligands to the cations52,53 and to their role in stabilizing the formed colloids54. Therefore, we decided to study the growth dynamics of CaF2 NCs in water using a different capping ligand. In contrast to AEP (Fig. 1a), negatively charged ligands may hinder NC interactions at the NC’s initial growth stage, due to electrostatic repulsion, which could lead to a different growth mechanism55. Interestingly, applying in situ 19F-NMR to the synthesis of CaF2 NCs in the presence of the negatively charged citric acid (citrate at pH = 7, Fig. 4a) as the capping ligand revealed a different growth mechanism than that observed for AEP-CaF2 (compare Fig. 2 and Fig. 4). We detected in the representative 19F-NMR spectra obtained at different reaction time points (i.e., 6 min, 200 min, and 1000 min, Fig. 4b) a notable consumption of free fluoride (peak at −120 ppm). This observation implies a growth mechanism that differs from particle-coalescence found for AEP-CaF2. Assigning the 19F-NMR peaks at −105 and −109 ppm to the fluorides of the surface and of the core of Cit-CaF2NCs, respectively, allows to determine their size evolution (using Eq. (1) and Supplementary Note 1), revealing their continuous growth (Fig. 4c), while their final size was further verified by TEM (Supplementary Fig. 13).
Importantly, contrary to that observed for AEP-CaF2 NCs (Fig. 2e), the concentration of the growing Cit-CaF2 NCs was near-constant throughout the synthesis (Fig. 4d, black). This observation, in addition to the significant depletion of the F- anion throughout Cit-CaF2’s growth (which is negligible for AEP-CaF2, Supplementary Fig. 5), suggests a different growth mechanism. While AEP-CaF2 NCs grow mostly by coalescence, as reflected by the pronounced reduction in their concentration (Fig. 2), Cit-CaF2 NCs primarily grow by the classical simple-growth mechanism10. This result emphasizes another advantage of our proposed approach. Besides its capability to determine NCs’ size evolution, it can also differentiate between two different growth mechanisms as schematically depicted in Fig. 5 (coalescence vs. simple classical growth, Fig. 5a, b). Nevertheless, it is important to mention here that although the proposed in situ NMR approach allowed to investigate NC growth pathways, it failed to pick-up early and rapid nucleation phases.
Finally, we studied the crystallographic features and spin-lattice relaxation properties of AEP-CaF2 and Cit-CaF2 NCs, as it was shown that the growth mechanism as well as the properties of the capping ligands impact the obtained architectures and characteristics of as-synthesized NCs56,57. Interestingly, HR TEM images of the coalesced AEP-CaF2 NCs showed crystallographic twinning defects for majority of the NCs (Fig. 5a and Supplementary Fig. 14), which were not observed in the crystalline Cit-CaF2 NCs (Fig. 5b and Supplementary Fig. 14). In addition, the longitudinal relaxation time T1 of the NCs’ fluoride content was shorter in AEP-CaF2 NCs as compared to that of Cit-CaF2 NCs (Supplementary Fig. 15). Such shorter T1 values of the defected NCs correlate with previous reports where mechanical stress-mediated lattice distortions of CaF2 powders resulted in significant reduced T1 values58, and should play a critical role in their future design as MRI tracers59. Our presented method for elucidating the contribution of the capping ligands to the nanofluoride’s characteristics could be used for tuning them as functional nanomaterials for a variety of uses, as both their crystallinity60 and relaxation times59 were found to be key features in their performances.
In summary, we show here an approach for the real-time monitoring of NC evolution in solution based on the ability to detect in situ NMR signals of the elements of as-synthesized nanoformulations. The demonstrated ability to accurately determine the average NC diameter at each timepoint during the synthesis has provided us with valuable insight into NC growth mechanisms in solution. We found that in the presence of a phosphate-based ligand, NCs grow predominantly via particle coalescence, while a carboxylate-based ligand leads to a simple-growth mechanism of the same material. Each pathway yields different crystallographic features, and, consequently, distinct relaxation properties, highlighting the link between crystal growth dynamics, structure, and function. These findings should have numerous implications in the growing field of nanofluorides23,24,25,27,59,61 but also for other types of nanomaterials62,63,64,65,66 where the crystal properties determine the NC functionality. The generality of our NMR-based approach for revealing in-depth mechanistic insights of fluoride-NCs, is highlighted by the similar pattern of the NC evolution profiles found for other types of NCs studied by other in situ methods10,46,47. Therefore, we envision that the fundamental principles in NCs growth underlined here have the potential to serve as a foundation for future studies of other types of materials. Finally, the accessibility of high-resolution NMR spectrometers, in addition to the versatility of NMR acquisition schemes and the ability to study a variety of nuclei (beyond 1H and 19F), could be implemented to elucidate the growth mechanism from a perspective different from those provided by existing in situ techniques.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Park, J. et al. Ultra-large-scale syntheses of monodisperse nanocrystals. Nat. Mater. 3, 891–895 (2004).
Alivisatos, P. The use of nanocrystals in biological detection. Nat. Biotechnol. 22, 47–52 (2004).
Yu, J. H. et al. High-resolution three-photon biomedical imaging using doped ZnS nanocrystals. Nat. Mater. 12, 359–366 (2013).
Lee, J.-H. et al. Artificially engineered magnetic nanoparticles for ultra-sensitive molecular imaging. Nat. Med. 13, 95 (2006).
Wang, D. & Li, Y. Bimetallic nanocrystals: liquid‐phase synthesis and catalytic applications. Adv. Mater. 23, 1044–1060 (2011).
Schaller, R. D. & Klimov, V. I. High efficiency carrier multiplication in PbSe nanocrystals: implications for solar energy conversion. Phys. Rev. Lett. 92, 186601 (2004).
Thanh, N. T., Maclean, N. & Mahiddine, S. Mechanisms of nucleation and growth of nanoparticles in solution. Chem. Rev. 114, 7610–7630 (2014).
Chang, H. et al. Molecular-level understanding of continuous growth from iron-oxo clusters to iron oxide nanoparticles. J. Am. Chem. Soc. 141, 7037–7045 (2019).
Li, J., Wang, H., Lin, L., Fang, Q. & Peng, X. Quantitative identification of basic growth channels for formation of monodisperse nanocrystals. J. Am. Chem. Soc. 140, 5474–5484 (2018).
Zheng, H. et al. Observation of single colloidal platinum nanocrystal growth trajectories. Science 324, 1309–1312 (2009).
Cheong, S., Watt, J., Ingham, B., Toney, M. F. & Tilley, R. D. In situ and ex situ studies of platinum nanocrystals: growth and evolution in solution. J. Am. Chem. Soc. 131, 14590–14595 (2009).
Williamson, M. J., Tromp, R. M., Vereecken, P. M., Hull, R. & Ross, F. M. Dynamic microscopy of nanoscale cluster growth at the solid–liquid interface. Nat. Mater. 2, 532–536 (2003).
Peng, Z. A. & Peng, X. Mechanisms of the shape evolution of CdSe nanocrystals. J. Am. Chem. Soc. 123, 1389–1395 (2001).
Polte, J. et al. Mechanism of gold nanoparticle formation in the classical citrate synthesis method derived from coupled in situ XANES and SAXS evaluation. J. Am. Chem. Soc. 132, 1296–1301 (2010).
Kwon, S. G. et al. Kinetics of monodisperse iron oxide nanocrystal formation by “heating-up” process. J. Am. Chem. Soc. 129, 12571–12584 (2007).
Yuk, J. M. et al. High-resolution EM of colloidal nanocrystal growth using graphene liquid cells. Science 336, 61–64 (2012).
Kwon, O. et al. Exsolution trends and co-segregation aspects of self-grown catalyst nanoparticles in perovskites. Nat. Commun. 8, 15967 (2017).
Shen, X. et al. Deconvolution of octahedral Pt3Ni nanoparticle growth pathway from in situ characterizations. Nat. Commun. 9, 4485 (2018).
Mikhlin, Y. et al. Submicrometer intermediates in the citrate synthesis of gold nanoparticles: new insights into the nucleation and crystal growth mechanisms. J. Colloid Interface Sci. 362, 330–336 (2011).
Fedorov, P., Luginina, A., Kuznetsov, S. & Osiko, V. Nanofluorides. J. Fluor. Chem. 132, 1012–1039 (2011).
Stouwdam, J. & Veggel, F. Near-infrared emission of redispersible Er3+, Nd3+, and Ho3+ doped LaF3 Nanoparticles. Nano Lett. 2, 733–737 (2002).
Heer, S., Kömpe, K., Güdel, H. U. & Haase, M. Highly efficient multicolor upconversion emission in transparent colloids of lanthanide-doped NaYF4 nanocrystals. Adv. Mat. 16, 2102–2105 (2004).
Wang, F. & Liu, X. Upconversion multicolor fine-tuning: visible to near-infrared emission from lanthanide-doped NaYF4 nanoparticles. J. Am. Chem. Soc. 130, 5642–5643 (2008).
Zhao, J. et al. Single-nanocrystal sensitivity achieved by enhanced upconversion luminescence. Nat. Nanotechnol. 8, 729–734 (2013).
Liu, Y. et al. Amplified stimulated emission in upconversion nanoparticles for super-resolution nanoscopy. Nature 543, 229–233 (2017).
Deng, R. et al. Temporal full-colour tuning through non-steady-state upconversion. Nat. Nanotechnol. 10, 237–242 (2015).
Wang, F. et al. Simultaneous phase and size control of upconversion nanocrystals through lanthanide doping. Nature 463, 1061–1065 (2010).
Mai, H. X. et al. High-quality sodium rare-earth fluoride nanocrystals: controlled synthesis and optical properties. J. Am. Chem. Soc. 128, 6426–6436 (2006).
Chen, D. et al. Modifying the size and shape of monodisperse bifunctional alkaline-earth fluoride nanocrystals through lanthanide doping. J. Am. Chem. Soc. 132, 9976–9978 (2010).
Ashur, I., Allouche‐Arnon, H. & Bar‐Shir, A. Calcium fluoride nanocrystals: tracers for in vivo 19F magnetic resonance imaging. Angew. Chem. Int. Ed. Engl. 57, 7478–7482 (2018).
Hughes, C. E., Williams, P. A. & Harris, K. D. “CLASSIC NMR”: an in-situ NMR strategy for mapping the time-evolution of crystallization processes by combined liquid-state and solid-state measurements. Angew. Chem. Int. Ed. Engl. 53, 8939–8943 (2014).
Goulet, P. J. & Lennox, R. B. New insights into Brust−Schiffrin metal nanoparticle synthesis. J. Am. Chem. Soc. 132, 9582–9584 (2010).
Li, Y. et al. Mechanistic insights into the Brust-Schiffrin two-phase synthesis of organo-chalcogenate-protected metal nanoparticles. J. Am. Chem. Soc. 133, 2092–2095 (2011).
Doyen, M., Bartik, K. & Bruylants, G. UV–Vis and NMR study of the formation of gold nanoparticles by citrate reduction: Observation of gold–citrate aggregates. J. Colloid Interface Sci. 399, 1–5 (2013).
Marbella, L. E. & Millstone, J. E. NMR techniques for noble metal nanoparticles. Chem. Mater. 27, 2721–2739 (2015).
Vioglio, P. C. et al. A Strategy for probing the evolution of crystallization processes by low-temperature solid-state NMR and dynamic nuclear polarization. J. Phys. Chem. Lett. 10, 1505–1510 (2019).
Liu, X., Yu, M., Kim, H., Mameli, M. & Stellacci, F. Determination of monolayer-protected gold nanoparticle ligand-shell morphology using NMR. Nat. Commun. 3, 1182 (2012).
Straney, P. J., Marbella, L. E., Andolina, C. M., Nuhfer, N. T. & Millstone, J. E. Decoupling mechanisms of platinum deposition on colloidal gold nanoparticle substrates. J. Am. Chem. Soc. 136, 7873–7876 (2014).
Ladizhansky, V., Hodes, G. & Vega, S. Surface properties of precipitated CdS nanoparticles studied by NMR. J. Phys. Chem. B 102, 8505–8509 (1998).
Rees, G. J. et al. Characterisation of platinum-based fuel cell catalyst materials using 195Pt wideline solid state NMR. Phys. Chem. Chem. Phys. 15, 17195–17207 (2013).
Thayer, A. M., Steigerwald, M. L., Duncan, T. M. & Douglass, D. C. NMR study of semiconductor molecular clusters. Phys. Rev. Lett. 60, 2673–2676 (1988).
de Queiroz, T. B. et al. Probing surface effects on α-NaYF4 nanoparticles by nuclear magnetic resonance. J. Phys. Chem. C. 124, 9523–9535 (2020).
Lovingood, D. D., Achey, R., Paravastu, A. K. & Strouse, G. F. Size- and site-dependent reconstruction in CdSe QDs evidenced by 77Se{1H} CP-MAS NMR spectroscopy. J. Am. Chem. Soc. 132, 3344–3354 (2010).
Sadoc, A. et al. NMR parameters in alkali, alkaline earth and rare earth fluorides from first principle calculations. Phys. Chem. Chem. Phys. 13, 18539–18550 (2011).
Witter, R., Roming, M., Feldmann, C. & Ulrich, A. S. Multilayered core–shell structure of polyol-stabilized calcium fluoride nanoparticles characterized by NMR. J. Colloid Interface Sci. 390, 250–257 (2013).
Niu, K.-Y., Liao, H.-G. & Zheng, H. Visualization of the coalescence of bismuth nanoparticles. Microsc. Microanal. 20, 416–424 (2014).
Polte, J. et al. Nucleation and growth of gold nanoparticles studied via in situ small angle X-ray scattering at millisecond time resolution. ACS Nano 4, 1076–1082 (2010).
Polte, J. Fundamental growth principles of colloidal metal nanoparticles—a new perspective. CrystEngComm 17, 6809–6830 (2015).
Boles, M. A., Ling, D., Hyeon, T. & Talapin, D. V. The surface science of nanocrystals. Nat. Mater. 15, 141 (2016).
Nenon, D. P. et al. Design principles for trap-free CsPbX3 nanocrystals: enumerating and eliminating surface halide vacancies with softer Lewis bases. J. Am. Chem. Soc. 140, 17760–17772 (2018).
Lazzari, S. et al. Ligand-mediated nanocrystal growth. Langmuir 34, 3307–3315 (2018).
van Embden, J. & Mulvaney, P. Nucleation and growth of CdSe nanocrystals in a binary ligand system. Langmuir 21, 10226–10233 (2005).
Owen, J. S., Chan, E. M., Liu, H. & Alivisatos, A. P. Precursor conversion kinetics and the nucleation of cadmium selenide nanocrystals. J. Am. Chem. Soc. 132, 18206–18213 (2010).
Kovalenko, M. V., Scheele, M. & Talapin, D. V. Colloidal nanocrystals with molecular metal chalcogenide surface ligands. Science 324, 1417–1420 (2009).
Heuer-Jungemann, A. et al. The role of ligands in the chemical synthesis and applications of inorganic nanoparticles. Chem. Rev. 119, 4819–4880 (2019).
Leite, E. et al. Crystal growth in colloidal tin oxide nanocrystals induced by coalescence at room temperature. Appl. Phys. Lett. 83, 1566–1568 (2003).
Penn, R. L. & Banfield, J. F. J. S. Imperfect oriented attachment: dislocation generation in defect-free nanocrystals. Science 281, 969–971 (1998).
Abdellatief, M., Abele, M., Leoni, M. & Scardi, P. Combined X-ray diffraction and solid-state 19F magic angle spinning NMR analysis of lattice defects in nanocrystalline CaF2. J. Appl. Crystalogr. 46, 1049–1057 (2013).
Mashiach, R. et al. Inducing defects in 19F-nanocrystals provides paramagnetic-free relaxation enhancement for improved in vivo hotspot MRI. Nano Lett. 20, 7207–7212 (2020).
Dyck, N. C., van Veggel, F. C. & Demopoulos, G. P. Size-dependent maximization of upconversion efficiency of citrate-stabilized beta-phase NaYF4:Yb3+,Er3+ crystals via annealing. ACS Appl. Mater. Interfaces 5, 11661–11667 (2013).
Fan, X. et al. Defect-enriched iron fluoride-oxide nanoporous thin films bifunctional catalyst for water splitting. Nat. Commun. 9, 1809 (2018).
Bekenstein, Y. et al. The making and breaking of lead-free double perovskite nanocrystals of cesium silver-bismuth halide compositions. Nano Lett. 18, 3502–3508 (2018).
Kong, M. et al. Tuning the relative concentration ratio of bulk defects to surface defects in TiO2 nanocrystals leads to high photocatalytic efficiency. J. Am. Chem. Soc. 133, 16414–16417 (2011).
Hardy, D. A., Tigaa, R. A., McBride, J. R., Ortega, R. E. & Strouse, G. F. Structure-fFunction correlation: engineering high quantum yields in down-shifting nNanophosphors. J. Am. Chem. Soc. 141, 20416–20423 (2019).
Zhao, Z. et al. Octapod iron oxide nanoparticles as high-performance T2 contrast agents for magnetic resonance imaging. Nat. Commun. 4, 2266 (2013).
Mann, A. K. P., Wu, Z., Calaza, F. C. & Overbury, S. H. Adsorption and reaction of acetaldehyde on shape-controlled CeO2 nanocrystals: elucidation of structure–function relationships. ACS Catal. 4, 2437–2448 (2014).
Acknowledgements
This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation program (grant agreement No 677715).
Author information
Authors and Affiliations
Contributions
R.M. and A.B.-S. designed the study. R.M. and A.L. designed the CaF2 synthesis and R.M. carried out the real-time synthesis of the nanofluorides. R.M. and L.A. designed and performed the high-resolution NMR experiments. R.M., V.A., and M.L. performed the computational line fitting of the NMR data. V.A. and M.L. performed the solid-state NMR experiments. H.W. and B.R. performed the cryo-TEM experiments. L.H. and O.B performed the EM-related studies (TEM and EDS). R.M. analyzed all the data shown and R.M. and A.B.-S. wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Jeffrey Reimer, Gilles Bruylants and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mashiach, R., Weissman, H., Avram, L. et al. In situ NMR reveals real-time nanocrystal growth evolution via monomer-attachment or particle-coalescence. Nat Commun 12, 229 (2021). https://doi.org/10.1038/s41467-020-20512-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-20512-6
- Springer Nature Limited
This article is cited by
-
Non-classical crystallization in soft and organic materials
Nature Reviews Materials (2024)
-
The rise and fall of adenine clusters in the gas phase: a glimpse into crystal growth and nucleation
Analytical and Bioanalytical Chemistry (2024)
-
Molecular dynamics study on structural and atomic evolution between Au and Ni nanoparticles through coalescence
Scientific Reports (2021)