Abstract
Cesium lead halide perovskites exhibit outstanding optical and electronic properties for a wide range of applications in optoelectronics and for light-emitting devices. Yet, the physics of the band-edge exciton, whose recombination is at the origin of the photoluminescence, is not elucidated. Here, we unveil the exciton fine structure of individual cesium lead iodide perovskite nanocrystals and demonstrate that it is governed by the electron-hole exchange interaction and nanocrystal shape anisotropy. The lowest-energy exciton state is a long-lived dark singlet state, which promotes the creation of biexcitons at low temperatures and thus correlated photon pairs. These bright quantum emitters in the near-infrared have a photon statistics that can readily be tuned from bunching to antibunching, using magnetic or thermal coupling between dark and bright exciton sublevels.
Similar content being viewed by others
Introduction
Recent advances in the colloidal synthesis of strongly emitting perovskite nanocrystals (NCs) open up new opportunities for the fabrication of tunable light sources based on the composition and quantum size effect tuning1, such as light-emitting diodes and lasers2, and for the exploration of their potential use as quantum light sources3,4,5,6. The knowledge of the band-edge exciton fine structure in perovskites and the ability to tailor it with NC composition, morphology, or external fields are of prime importance for the development of efficient single-photon sources or sources of entangled photons for quantum information processes7,8,9, and for applications in optoelectronics and spin-based technologies10,11,12. Yet, the bright or dark character of the ground exciton in perovskites is the subject of continuing debate. The band-edge exciton of perovskites is formed with a hole (h) in an S-like state with angular momentum Jh = 1/2 and an electron (e) in a spin-orbit split-off state with angular momentum Je = 1/213,14. The resulting four-fold degenerate exciton level is split by the electron–hole exchange interaction into a dark ground singlet state (J = 0) and a bright triplet (J = 1). At liquid helium temperatures, single cesium lead halide (CsPbX3) perovskite NCs display a bright photoluminescence (PL) with a spectral fingerprint assigned to the bright triplet structure15,16,17,18,19,20. It has been speculated that this brightness takes its origin in a polar lattice symmetry breaking that would reverse the exciton sub-levels ordering by a Rashba effect and thus place the bright triplet exciton below the dark singlet20,21. While the spectral signature of a dark exciton lying below the bright triplet has been found in hybrid organic–inorganic formamidinium lead bromide (FAPbBr3) NCs22, theoretical calculations still predict order inversion in CsPbX3 NCs23 and thus far, no signature of a low-lying dark exciton state has been found in such NCs.
Here, we demonstrate that the band-edge exciton fine structure of inorganic CsPbI3 NCs presents a dark ground singlet state. We fully explain the fine structure splittings with a theoretical model solely based on the electron–hole exchange interaction and NC shape anisotropy. In the view of applications to quantum technologies, we introduce resonant PL excitation of the excitonic sublevels to investigate the indistinguishability character of the photons emitted by these NCs. Importantly, we demonstrate that the presence of a long-lived ground exciton state favors the formation of biexcitons and thus the emission of pairs of correlated photons. We show that this is a general behavior that can be observed for perovskite NCs as well as for conventional CdSe quantum dots. This property makes single CsPbI3 NCs versatile bright, quantum light sources in the near infrared with photon statistics that can be tuned from bunching to antibunching, using magnetic coupling or thermal mixing between dark and bright exciton states.
Results
Spectral signatures of the NCs’ luminescence
The CsPbI3 NCs of this study are synthesized with an orthorhombic γ-phase crystal structure24,25 (Fig. 1a). They display cuboid shapes with an average side of 11.2 ± 1.2 nm and an apparent aspect ratio of 1.13 on average from electron microscopy imaging (see Fig. 1b, c). When dissolved in hexane, NCs exhibit a bright red PL centered at 1.81 eV, with a high color purity and a PL quantum yield exceeding 65% at room temperature. The PL peak energy is slightly blue-shifted as compared with the bulk material (~1.73 eV)26, indicating a regime of weak quantum confinement in these NCs with a mean size slightly larger than twice the exciton Bohr radius aB = 4.6 nm in CsPbI327. Using a home-built scanning confocal microscope operating at cryogenic temperatures, we have investigated the PL spectra of single NCs dispersed in a polystyrene matrix and weakly excited at a laser wavelength of 561 nm (see “Methods” section for details). Their emission energy centered on 1.77 eV (Fig. 1a) is red-shifted with respect to the room temperature value, due to a displacement of the valence band energy with lattice contraction28. At low temperature (~4 K), thermal dephasing is reduced and the PL spectra of single NCs present sharp peaks attributed to the zero-phonon emission lines (ZPLs) resulting from the recombination of the charge complexes formed in the NC, as exemplified in the typical spectral trail displayed in Fig. 1d. This trail shows an emission switch of a NC from its neutral state, displaying ZPLs labeled X for the exciton and XX for the biexciton16, to its charged state characterized by a single ZPL labeled X*. As shown in Fig. 1e, integrating the spectra gives greater details of the fine structure of these charge complexes, as well as the longitudinal optical (LO) phonon replicas of the ZPLs. The exciton fine structure is revealed both through the biexciton-to-exciton transitions and through the bright exciton recombination. Mapping the biexcitonic transition multiplet XX onto the excitonic one X (see inset of Fig.1e) shows evidence for a perfect match in their spectral structures and allows a straightforward correspondence of the transition lines (see also Supplementary Fig. 1). As exemplified in Fig. 2 and Supplementary Fig. 2, this spectroscopic study reveals one-line, two-line, or three-line PL spectra in proportions of ~5%, 30%, and ~65%, respectively. Within a resolution of ~120 µeV, these spectral structures result from a subtle interplay of crystal structure and shape anisotropy effects15,29,30. For instance, assuming a cubic symmetry of the NC crystal structure (resp. shape), shape (resp. crystal structure) anisotropy governs the number of bright levels: Single-line, two-line, and three-line spectra will be, respectively, assigned to cubic, tetragonal, and orthorhombic anisotropy of the NC shape (resp. crystal structure).
Exciton fine structure and signature of the dark singlet
The spectral signature of the dark singlet exciton is evidenced under the application of an external magnetic field, as demonstrated in Fig. 2 (see other examples in Supplementary Fig. 2). Regardless of the triplet structure, a new emission line indeed emerges from the LO-phonon sidebands, a few meV below the bright triplet, as a signature of magnetic brightening of a low-lying dark exciton state in these inorganic lead halide perovskites. Despite this level ordering, perovskite NCs display an intense luminescence at low temperature because of an extremely reduced bright-to-dark phonon-assisted relaxation22,31, a remarkable property of these materials as compared to more conventional III–V or II–VI semiconductors. Indeed, spin relaxation processes involving polar acoustic phonons related to piezoelectricity are absent32, and carrier–phonon interactions via deformation potentials are reduced in these structurally soft semiconductors with strong lattice anharmonicity affecting the optical modes33. The structure of the optical phonon modes of the CsPbI3 NCs is detailed in Supplementary Fig. 3 and compared with that of CsPbBr3 NCs. It shows evidence that the bright-to-dark relaxation remains inhibited even when the bright-dark splitting coincides with the phonon modes. The fact that phonons do not carry angular momentum likely explains why the bright-to-dark relaxation is inhibited in perovskites34. Indeed, it requires Raman-like phonon processes involving two-phonon modes whose energy difference matches the bright-dark splitting22,31 (see Fig. 2d and Supplementary Fig. 4). Interestingly, a direct signature of extremely slow phonon relaxation within the bright sublevels is the equality in relative weights between the corresponding XX and X triplet components (see Fig. 1e and Supplementary Fig. 1). It proves that the relaxation is slower than the exciton recombination, whose lifetime is on the nanosecond time scale. This points to a negligible Rashba-like spin–orbit coupling35,36,37 that would allow one-phonon bright-to-dark relaxation in these materials.
We have studied the exciton fine structure of tens of individual NCs and find a clear increase of the bright triplet splittings (up to ~1 meV) and the bright-dark splittings (up to ~5 meV) with the exciton recombination energy, as shown in Fig. 3a, b and Supplementary Fig. 5. The trend of such a correlation also shows up for the bright triplet splittings of CsPbBr3 NCs (see Supplementary Fig. 6) and CsPbBr2Cl NCs20. These results demonstrate that fine structure splittings are dominated by the exchange interaction under the combined effects of quantum confinement and screening of the electron–hole interaction. Indeed, the contribution of the Rashba effect to the bright state splittings has been predicted to decrease with increasing NC sizes38, which points to a reduced contribution of this effect in cesium lead halide perovskite NCs. In order to reproduce these results, we have calculated the exchange interaction for cuboid shaped NCs with a cubic crystal phase in the weak quantum confinement regime, using a variational approach based on an effective mass model for the monoelectronic states (Supplementary Note 1). Figure 3c shows the results obtained in the case of a tetragonal NC shape, where the bright sublevels form a doublet comprising a non-degenerate sublevel (Z state) defined by the NC elongation axis and a two-fold degenerate sublevel (X and Y states). Their splitting increases with the NC aspect ratio (see also Supplementary Fig. 7), and their ordering becomes reversed when the NC shape switches from flattened to elongated. This is illustrated in Fig. 3d, where the PL spectra of two nearly tetragonal NCs with different aspect ratios are presented (NCs with sides \(L_{\mathrm{x}} \approx L_{\mathrm{y}} \, > \, L_{\mathrm{z}}\) for the left spectrum, and \(L_{\mathrm{x}} \approx L_{\mathrm{y}} \, < \, L_{\mathrm{z}}\) for the right spectrum). Importantly, our observations are in contradiction with the assumption of a Rashba effect that would always place the bright Z level below the twofold degenerate X–Y level23. This is also the case in CsPbBr3 NCs, as shown in Supplementary Fig. 6. Finally, we find that the evolution of the calculated bright-dark splitting as a function of the exciton recombination energy (Fig. 3e) is in quantitative agreement with the experimental results when taking into account the effect of dielectric confinement on the exchange interaction. More quantitative comparison between theory and experiment, in particular the assignment of non-degenerate bright triplet ZPLs to the levels X, Y, and Z, would require refined models that take into account crystal phase and shape anisotropies39 together with the knowledge of the low-temperature crystal structure, 3D shape, orientation, and dielectric environment of each NC.
In order to predict the offset of the dark ground state in the fine structure of lead halide perovskites, we have calculated the exchange interaction in bulk perovskites with various compositions and plotted them as a function of their exciton Bohr radius in Fig. 3f. The weakest value is obtained for FAPbI3 perovskites. It is consistent with spectroscopic studies of weakly confined single FAPbI3 NCs, which present a narrow exciton fine structure within a few hundred µeV that could not be resolved under a magnetic field of 7 T31. CsPbBr3 perovskites display the largest bulk exchange interaction, explaining why the distributions of bright triplet splittings measured in CsPbBr3 NCs15,18,20 are larger than those of FAPbBr3 and CsPbI3 NCs. Despite spectroscopic investigations on different CsPbBr3 NCs with different sizes, shapes, and surface ligands, we could not observe magnetic brightening of the dark state with magnetic fields up to 7 T15 for different exciton confinement regimes (NCs with sizes ~4 to ~20 nm) and different surface ligands. Since magnetic brightening is inversely proportional to the square of the bright-dark splitting, it is likely negligible at such fields due to a large offset between the dark ground singlet state and the bright triplet in these NCs. This picture is supported by the onset of a long-time component in the PL decay of ensembles of CsPbBr3 NCs at fields higher than 10 T40, as an indirect signature of a low-lying long-lived sublevel41.
Exciton optical coherence lifetime
Due to their bright PL in the near-infrared and sharp ZPLs at low temperature, single CsPbI3 NCs are attractive solid-state emitters for a potential use as quantum light sources. In particular, sources that deliver single indistinguishable photons on demand are required for a number of quantum information processing schemes7. Such photons stem from the ZPL when its spectral linewidth \(1/\pi T_2\) reaches its fundamental lower bound \(1/\left( {2\pi T_1} \right)\), where T2 is the optical coherence lifetime of the emission and T1 the emitting state lifetime. Time-resolved photon-correlation Fourier spectroscopy has provided a coherence lifetime T2 ~ 80 ps for individual CsPbBr3 NCs6. However, time-resolved approaches without spectral filtering fail at identifying the charge complexes at the origin of the emission. For CsPbI3 NCs, a similar coherence lifetime has been extracted from first-order PL correlation measurements42. In these early investigations, the excess energy between absorption and emitted photons may induce spectral diffusion of the transition energy31. We thus measure the ultimate limit of the optical coherence lifetime of perovskite NCs through resonant excitation on their excitonic ZPLs. Resonant excitation spectra are recorded by scanning a single-mode laser across one of the fine structure ZPLs, while collecting the fraction of PL emitted on the LO phonon replicas, as shown in Fig. 4a. A narrow Lorentzian ZPL is presented in Fig. 4b with a homogeneous linewidth as narrow as ~5 GHz FWHM, corresponding to an optical coherence time T2 ~ 64 ps. This value is still short in comparison with the exciton lifetime T1 ~ 1 ns measured on the same NC (see Fig. 4c). A possible origin of ZPL broadening is fast-spectral diffusion induced by fluctuations of the local electric field and dielectric screening, as a result of charge noise produced by charge displacements at the surface of the NCs or in its local environment. These processes are likely the same as those responsible for slow spectral diffusion accompanied by variations of the exciton fine-structure splittings. As shown in Supplementary Fig. 8, the fine-structure splittings increase with the exciton recombination energy, which suggests that the spectral jumps take their origin in fluctuations of the dielectric confinement that affects both the transition energy and the electron–hole exchange interaction. Despite these homogeneous broadening mechanisms, our high-resolution PL excitation method provides a precious tool to investigate subtle lifts of degeneracy in the exciton fine structure, that would be buried within the spectral resolution of the PL spectra. In further investigations, such variations of the exciton fine structure should be correlated with the 3D characterization of the NCs morphology.
Tuning the photon statistics of single NCs
We now study the statistics of the photons emitted by individual CsPbI3 NCs, using a Hanbury Brown and Twiss coincidence setup to measure the histograms of time delays between consecutive photon pairs. A striking feature is the strong bunching observed at low temperatures with the PL signal formed by all emission lines, as exemplified in Fig. 5a. We attribute this behavior to the exciton-shelving role played by the long-lived ground exciton state, which favors the generation of biexcitons in the NCs, followed by biexciton to bright-exciton-correlated photon pairs. The photon bunching character weakens when the temperature is raised. This results from thermal mixing between bright and dark states, which shortens the effective lifetime of the dark state. As this lifetime approaches its limit given by twice the bright exciton lifetime, photon bunching turns to antibunching (see Fig. 5a and Supplementary Figs. 4, 9) with a zero-delay autocorrelation function set by the biexciton radiative yield. This behavior is well reproduced with simulated autocorrelation functions (Fig. 5b) deduced from the solutions of rate equations in a simple four-level model including the zero-exciton ground level, thermally mixed bright and dark exciton sublevels and a biexciton level (see Supplementary Note 2). To further support the role of the dark state on the photon statistics, we have studied the evolution of the autocorrelation function with magnetic fields. Clearly, magnetic coupling of dark and bright states leads to shortening of the long component of the PL decay and to weakening of the photon bunching, as shown in Fig. 5c (see other examples in Supplementary Figs. 9–11). It is worth noting the systematic evolution of the photon statistics from bunching to antibunching when the excitation intensity is increased (Supplementary Fig. 12). We attribute this dependence to the growing depopulation of the dark exciton state through the formation of a biexciton, whose radiative recombination solely populates the bright exciton states.
In order to generalize the picture of a long-lived ground state promoting photon pairs in quantum dots, we have performed similar experiments on CdSe core–shell NCs (see Supplementary Fig. 13), which present a ground “dark” exciton sublevel located a few meV below the lowest bright state43. Strong photon bunching is observed for single CdSe NCs at liquid helium temperatures and weak intensities. However, the transition from bunching to antibunching occurs at much lower temperatures than for perovskites, as soon as the thermal energy approaches the dark-bright splitting. Indeed, thermalization between fine structure sublevels is mediated in these NCs by one acoustic phonon whose energy matches the bright-dark splitting44,45, while in perovskite NCs it occurs through a second-order process with high-energy phonons.
Finally, cross-correlation measurements complement the identification of the biexciton emission in perovskite NCs and show their suitability as sources of correlated photon pairs. As shown in Fig. 5d, energy-resolved photon cross-correlation histograms display an asymmetric bunching for positive delay times, owing to the cascaded emission of photon pairs with a biexciton recombination photon preceding an exciton recombination photon. Strong photon antibunching at low temperature is retrieved in single CsPbI3 NCs when filtering the emission from the exciton recombination lines.
Discussion
This study addresses the debate concerning the physical interactions at the origin of the band-edge exciton fine structure in lead halide perovskites. In particular, the singlet–triplet sublevel ordering and the triplet splittings are set by the electron–hole exchange interaction, which is exalted by quantum confinement and affected by the NC shape anisotropy. The remarkable brightness of these nanoemitters at low temperature takes its origin in the efficient inhibition of the phonon-assisted relaxation between the band-edge exciton sublevels. Moreover, the low-lying long-lived ground exciton state can be exploited to tune the quantum properties of the light emitted by perovskite NCs. Compared to CdSe NCs that have benefited from decades of developments and now achieve near-unity PL quantum yields46, leading to the realization of CW lasing with these materials47, synthesis of perovskite NCs is still in its infancy. One can foresee important developments motivated by the promising prospects of these materials as classical or quantum light sources. The next investigations will aim at reducing the dephasing rate and spectral diffusion in these materials and improve the indistinguishability character of the emitted photons, with the application of strong local electric fields that stabilize the charge distributions in the NC, or further surface passivation with suitable ligands or the growth of inorganic shells. In general, photon pairs emitted by conventional quantum dots undergo various entanglement degrading effects such as band mixing, exciton spin-flip processes and fine structure splitting, which drastically reduce their degree of entanglement. With a view to achieving ideal sources of entangled photons, perovskite NCs exhibit pure electron and hole bands, extremely slow spin-flip relaxation and, for a fraction of them, degenerate bright triplet emission.
Methods
Preparation of cesium-oleate precursor
In a 100 mL three-necked round bottom flask a mixture of 0.5 g Cs2CO3, 2 mL OA, and 50 mL ODE is dried at 120 °C for 2 h under vacuum, followed by purging with nitrogen for 30 min. The reaction is finished when the Cs2CO3 powder dissolves completely to give a clear solution. The prepared solution of cesium oleate in ODE (0.06 M) is used as cesium precursor and stored under nitrogen atmosphere.
Synthesis of colloidal CsPbI3 NCs
In a 100 mL three-necked round bottom flask, 200 mg PbI2 (0.43 mmol) are suspended in ODE (10 mL). The reaction mixture is degassed at 100 °C under vacuum for 3 h. Subsequently, 1 mL OA, 1 mL OAm, and 1 mL TOP are added under nitrogen atmosphere. The reaction temperature is increased to 175 °C and preheated (~70 °C) Cs-oleate solution (1.6 mL, 0.06 M) is swiftly injected to the reaction flask. In 10 s the reaction mixture is cooled by a water-ice bath.
Purification of CsPbI3 NCs
Purification of the synthesized NCs is conducted in a glovebox under inert atmosphere. In order to remove the excess of ligands, 35 mL anhydrous MeOAc are added to the crude solution, then centrifuged at 12,100 rpm for 1 min (20,130 × g, centrifuge: Eppendorf 5810R). The supernatant is discarded and the precipitate is dissolved in ~5 mL anhydrous hexane. The resulting solution is centrifuged at 4000 rpm for 10 min and the precipitate is discarded. The obtained solution of CsPbI3 NCs (supernatant) is used for further studies.
Single NC spectroscopy
The NCs in hexane are kept under Ar atmosphere for further analysis. For measurements on single NCs at cryogenic temperatures, a dilute solution of CsPbI3 NCs is mixed with a 2 wt% polystyrene solution and spin-coated onto a clean sapphire coverslip with a rotation speed of 2000 rpm. A home-built scanning confocal microscope based on a 0.95 numerical aperture objective is placed in a cryostat and used to image single NCs by raster scanning the sample. For the acquisition of PL spectra, the NCs are excited at 561 nm with a cw laser passed through a clean-up filter. The emitted photons are filtered from the scattered laser light with a band-pass filter (centered at 700 nm with a band width of 70 nm) and sent to a single-photon counting avalanche photodiode and a spectrograph (with a resolution of ~120 µeV using a grating of 1800 lines/mm). For resonant PL excitation spectra, a single-mode tunable Ti:Sa laser is used, together with a long-pass filter (with a nominal edge wavelength of 715 nm) whose transmission curve is tunable under a tilt of the incidence angle. PL decays are recorded with a conventional time-correlated single-photon-counting setup using a pulsed laser source (optical parametric oscillator at 561 nm, 200 fs pulse width, with a repetition rate reduced to 8 MHz with a pulse-picker). A Hanbury Brown and Twiss setup is used to build the start–stop coincidence histograms. Filtering of the exciton or biexciton ZPLs is performed with tunable long-pass (with a nominal edge wavelength of 715 nm) and short-pass (with a nominal edge wavelength of 720 nm) filters.
Data availability
All relevant data that support our experimental findings are available from the corresponding author upon reasonable request.
References
Kovalenko, M. V., Protesescu, L. & Bodnarchuk, M. I. Properties and potential optoelectronic applications of lead halide perovskite nanocrystals. Science 358, 745–750 (2017).
Yan, F., Tan, S. T., Li, X. & Demir, H. V. Light generation in lead halide perovskite nanocrystals: LEDs, color converters, lasers, and other applications. Small 15, 1902079 (2019).
Park, Y.-S., Guo, S., Makarov, N. S. & Klimov, V. I. Room temperature single-photon emission from individual perovskite quantum dots. ACS Nano 9, 10386–10393 (2015).
Hu, F. et al. Superior optical properties of perovskite nanocrystals as single photon emitters. ACS Nano 9, 12410–12416 (2015).
Rainò, G. et al. Superfluorescence from lead halide perovskite quantum dot superlattices. Nature 563, 671–675 (2018).
Utzat, H. et al. Coherent single-photon emission from colloidal lead halide perovskite quantum dots. Science 363, 1068–1072 (2019).
Lounis, B. & Orrit, M. Single-photon sources. Rep. Prog. Phys. 68, 1129–1179 (2005).
Benson, O., Santori, C., Pelton, M. & Yamamoto, Y. Regulated and entangled photons from a single quantum dot. Phys. Rev. Lett. 84, 2513–2516 (2000).
Stevenson, R. M. et al. A semiconductor source of triggered entangled photon pairs. Nature 439, 179–182 (2006).
Kim, M., Im, J., Freeman, A. J., Ihm, J. & Jin, H. Switchable S = 1/2 and J = 1/2 Rashba bands in ferroelectric halide perovskites. PNAS 111, 6900–6904 (2014).
Zheng, F., Tan, L. Z., Liu, S. & Rappe, A. M. Rashba spin–orbit coupling enhanced carrier lifetime in CH3NH3PbI3. Nano Lett. 15, 7794–7800 (2015).
Kepenekian, M. et al. Rashba and dresselhaus effects in hybrid organic–inorganic perovskites: from basics to devices. ACS Nano 9, 11557–11567 (2015).
Tanaka, K. et al. Comparative study on the excitons in lead-halide-based perovskite-type crystals CH3NH3PbBr3 CH3NH3PbI3. Solid State Commun. 127, 619–623 (2003).
Even, J. Pedestrian guide to symmetry properties of the reference cubic structure of 3D all-inorganic and hybrid perovskites. J. Phys. Chem. Lett. 6, 2238–2242 (2015).
Fu, M. et al. Neutral and charged exciton fine structure in single lead halide perovskite nanocrystals revealed by magneto-optical spectroscopy. Nano Lett. 17, 2895–2901 (2017).
Yin, C. et al. Bright-exciton fine-structure splittings in single perovskite nanocrystals. Phys. Rev. Lett. 119, 026401 (2017).
Ramade, J. et al. Exciton–phonon coupling in a CsPbBr3 single nanocrystal. Appl. Phys. Lett. 112, 072104 (2018).
Ramade, J. et al. Fine structure of excitons and electron–hole exchange energy in polymorphic CsPbBr3 single nanocrystals. Nanoscale 10, 6393–6401 (2018).
Isarov, M. et al. Rashba effect in a single colloidal CsPbBr3 perovskite nanocrystal detected by magneto-optical measurements. Nano Lett. 17, 5020–5026 (2017).
Becker, M. A. et al. Bright triplet excitons in caesium lead halide perovskites. Nature 553, 189–193 (2018).
Sercel, P. C. & Efros, A. L. Band-edge exciton in CdSe and other II−VI and III−V compound semiconductor nanocrystals—revisited. Nano Lett. 18, 4061–4068 (2018).
Tamarat, P. et al. The ground exciton state of formamidinium lead bromide perovskite nanocrystals is a singlet dark state. Nat. Mater. 18, 717–724 (2019).
Sercel, P. C. et al. Exciton fine structure in perovskite nanocrystals. Nano Lett. 19, 4068–4077 (2019).
Bertolotti, F. et al. Coherent nanotwins and dynamic disorder in cesium lead halide perovskite nanocrystals. ACS Nano 11, 3819–3831 (2017).
Thomas, C. J. et al. Thermal stability of the black perovskite phase in cesium lead iodide nanocrystals under humid conditions. Chem. Mater. 31, 9750–9758 (2019).
Eperon, G. E. et al. Materials chemistry A. J. Mater. Chem. A 3, 19688–19695 (2015).
Yang, Z. et al. Impact of the halide cage on the electronic properties of fully inorganic cesium lead halide perovskites. ACS Energy Lett. 2, 1621–1627 (2017).
Dar, M. I. et al. Origin of unusual bandgap shift and dual emission in organic–inorganic lead halide perovskites. Sci. Adv. 2, e1601156 (2016).
Nestoklon, M. O. et al. Optical orientation and alignment of excitons in ensembles of inorganic perovskite nanocrystals. Phys. Rev. B 97, 235304 (2018).
Ben Aich, R. et al. Bright-exciton splittings in inorganic cesium lead halide perovskite nanocrystals. Phys. Rev. Appl. 11, 034042 (2019).
Fu, M. et al. Unraveling exciton–phonon coupling in individual FAPbI3 nanocrystals emitting near-infrared single photons. Nat. Commun. 9, 3318 (2018).
Neukirch, A. J. et al. Polaron stabilization by cooperative lattice distortion and cation rotations in hybrid perovskite materials. Nano Lett. 16, 3809–3816 (2016).
Miyata, K., Atallah, T. L. & Zhu, X.-Y. Lead halide perovskites: crystal–liquid duality, phonon glass electron crystals, and large polaron formation. Sci. Adv. 3, e1701469 (2017).
Wei, H., Guo, G.-C. & He, L. Slow exciton spin relaxation in single self-assembled In1−xGaxAs/GaAs quantum dots. Phys. Rev. B 89, 576 (2014).
Khaetskii, A. V. & Nazarov, Y. V. Spin relaxation in semiconductor quantum dots. Phys. Rev. B 61, 12639–12642 (2000).
Khaetskii, A. V. & Nazarov, Y. V. Spin-flip transitions between Zeeman sublevels in semiconductor quantum dots. Phys. Rev. B 64, 413 (2001).
Golovach, V. N., Khaetskii, A. & Loss, D. Phonon-induced decay of the electron spin in quantum dots. Phys. Rev. Lett. 93, 110 (2004).
Sercel, P. C., Lyons, J. L., Bernstein, N. & Efros, A. L. Quasicubic model for metal halide perovskite nanocrystals. J. Chem. Phys. 151, 234106 (2019).
Ben Aich, R., Ben Radhia, S., Boujdaria, K., Chamarro, M. & Testelin, C. Multiband k·p model for tetragonal crystals: application to hybrid halide perovskite nanocrystals. J. Phys. Chem. Lett. 11, 808–817 (2020).
Canneson, D. et al. Negatively charged and dark excitons in CsPbBr3 perovskite nanocrystals revealed by high magnetic fields. Nano Lett. 17, 6177–6183 (2017).
Labeau, O., Tamarat, P. & Lounis, B. Temperature dependence of the luminescence lifetime of single CdSe/ZnS quantum dots. Phys. Rev. Lett. 90, 257404 (2003).
Lv, Y. et al. Quantum interference in a single perovskite nanocrystal. Nano Lett. 19, 4442–4447 (2019).
Fernée, M. J., Tamarat, P. & Lounis, B. Cryogenic single-nanocrystal spectroscopy: reading the spectral fingerprint of individual CdSe quantum dots. J. Phys. Chem. Lett. 4, 609–618 (2013).
Biadala, L., Louyer, Y., Tamarat, P. & Lounis, B. Direct observation of the two lowest exciton zero-phonon lines in single CdSe/ZnS nanocrystals. Phys. Rev. Lett. 103, 037404 (2009).
Louyer, Y., Biadala, L., Tamarat, P. & Lounis, B. Spectroscopy of neutral and charged exciton states in single CdSe/ZnS nanocrystals. Appl. Phys. Lett. 96, 203111 (2010).
Jeong, B. G. et al. Colloidal spherical quantum wells with near-unity photoluminescence quantum yield and suppressed blinking. ACS Nano 10, 9297–9305 (2016).
Roh, J., Park, Y.-S., Lim, J. & Klimov, V. I. Optically pumped colloidal-quantum-dot lasing in LED-like devices with an integrated optical cavity. Nat. Commun. 11, 271 (2020).
Acknowledgements
We acknowledge the financial support from the French National Agency for Research, Région Aquitaine, Idex Bordeaux (LAPHIA Program), and the EUR Light S&T. J.E. and B.L. acknowledge the Institut universitaire de France. M.V.K. and A.S. acknowledge financial support from EU via Horizon 2020 [EMPAPOSTDOCS-II program, which received funding under Marie Skłodowska-Curie grant agreement number 754364 and ERC Consolidator Grant SCALE-HALO, grant agreement 819740]. We thank Ihor Cherniukh for electron microscopy imaging.
Author information
Authors and Affiliations
Contributions
A.S., M.I.B., and M.V.K. prepared the samples and performed the ensemble characterization. P.T. and L.H. performed the optical experiments. P.T., L.H., J.-B.T., and B.L. analyzed and interpreted the data. L.B. and Y.L. performed the experiments on CdSe NCs. J.E. developed the model of exchange interaction for the exciton fine structure. P.T., L.H., J.E. and B.L. wrote the manuscript with inputs from all authors. B.L. supervised the project.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Tamarat, P., Hou, L., Trebbia, JB. et al. The dark exciton ground state promotes photon-pair emission in individual perovskite nanocrystals. Nat Commun 11, 6001 (2020). https://doi.org/10.1038/s41467-020-19740-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-19740-7
- Springer Nature Limited
This article is cited by
-
Single-photon superradiance in individual caesium lead halide quantum dots
Nature (2024)
-
Coherent phenomena and dynamics of lead halide perovskite nanocrystals for quantum information technologies
Nature Materials (2024)
-
Luminescent metal-halide perovskites: fundamentals, synthesis, and light-emitting devices
Science China Chemistry (2024)
-
Ultrafast relaxation of lattice distortion in two-dimensional perovskites
Nature Physics (2023)
-
Universal scaling laws for charge-carrier interactions with quantum confinement in lead-halide perovskites
Nature Communications (2023)