Abstract
Efficient electrocatalysts for hydrogen evolution reaction are key to realize clean hydrogen production through water splitting. As an important family of functional materials, transition metal oxides are generally believed inactive towards hydrogen evolution reaction, although many of them show high activity for oxygen evolution reaction. Here we report the remarkable electrocatalytic activity for hydrogen evolution reaction of a layered metal oxide, Ruddlesden−Popper-type Sr2RuO4 with alternative perovskite layer and rock-salt SrO layer, in an alkaline solution, which is comparable to those of the best electrocatalysts ever reported. By theoretical calculations, such excellent activity is attributed mainly to an unusual synergistic effect in the layered structure, whereby the (001) SrO-terminated surface cleaved in rock-salt layer facilitates a barrier-free water dissociation while the active apical oxygen site in perovskite layer promotes favorable hydrogen adsorption and evolution. Moreover, the activity of such layered oxide can be further improved by electrochemistry-induced activation.
Similar content being viewed by others
Introduction
With the accelerating depletion of fossil fuels and associated negative environmental impact from their excessive use, clean and renewable energy alternatives have been receiving great demand during the past years1. Hydrogen (H2), which possesses the highest gravimetric energy density and zero-carbon nature, is regarded as a promising energy carrier or fuel to replace fossil fuels2. Globally, hydrogen production mainly comes from the industrial steam reforming with converting natural gas and water into carbon dioxide and hydrogen, whereas the energy inefficiency of the conversion process and the existence of carbon-containing residues can lead to high costs and low purity of the hydrogen products3. To address this, an alternative technique to produce hydrogen is via electrochemical water splitting, which benefits from unlimited water resources, stable output, high product purity, feasibility of large-scale production, and the capability of integrating renewable energy as power source4. However, the rate of the hydrogen evolution reaction (HER) in water splitting is relatively sluggish and requires an efficient electrocatalyst to promote the HER process5. Notably, the HER kinetics for most catalysts in alkaline solutions is at least two orders of magnitude slower than in acidic ones due to the extra water dissociation step6. Although platinum (Pt) metal demonstrates favorable activity for HER in both acidic and alkaline media, the scarcity, high cost and poor stability severely limit the viability for commercial applications5. Extensive efforts have been devoted to the development of highly active and durable Pt-free HER catalysts in alkaline solutions to achieve economical hydrogen production.
As a large and important class of inorganic compounds, transition metal oxides (TMOs) have attracted great interest in many fields (e.g., efficient oxygen evolution reaction (OER) catalysts in alkaline solutions) by virtue of the merits of their stability, abundance, accessibility, and environmental friendliness7,8. However, bulk TMOs are generally deemed as inactive materials for alkaline HER because of poor electrical conductivity and inappropriate hydrogen adsorption energy9,10. For example, ruthenium dioxide (RuO2), a state-of-the-art OER electrocatalyst, was found to be only moderately active for HER11,12.
To date, several important trials have been conducted to develop oxides that can serve as efficient HER electrocatalysts. Since the mass activity of a catalyst is determined by both the intrinsic activity and the amount of active sites, increasing the amount of active sites is a direct way to increase the mass activity. Luo et al. synthesized a nonstoichiometric and mesoporous MoO3−x with high surface area of 52 m2 g−1 via an inverse micelle-template method13, which shows favorable electrocatalytic activity for HER in an alkaline condition, achieving an overpotential of 138 mV at 10 mA cm−2. Wang et al. fabricated some TMO nanoparticles with diameters of 2–5 nm using lithium-induced electrochemical conversion reactions, demonstrating excellent activity for OER and favorable activity for HER14. To further increase the activity, Qiao et al. applied surface strain engineering strategy to alter the surface atom and electronic structure of nanostructured CoO, thus enhancing the alkaline HER activity8. Despite these efforts, the HER activity of oxides in alkaline media, especially in bulk counterpart, remains much inferior to that of the benchmark Pt catalyst; also, the synthetic processes are complex, of low yield, and difficult for cost-effective and wide-scale fabrication. Therefore, simple and effective strategies are still needed for the development of metal oxide-based electrocatalysts with high intrinsic HER activity.
In addition to the simple TMOs, complex oxides containing more than one metal (e.g., perovskite oxides) have been the focus of numerous studies for various applications by virtue of their structural and compositional flexibility15,16,17,18. The multiple elements and variable structures of complex oxides can give rise to some unique bulk material properties (e.g., crystal, electronic and conductive properties), which then affect the surface properties of the oxides directly or indirectly, and consequently their electrocatalytic activities19,20. Thus, engineering the bulk structure can provide new opportunities to screen for superior catalysts.
Here we report our findings in rational design of a layered Ruddlesden−Popper (RP)-type oxide Sr2RuO4, derived from RuO2, demonstrating dramatically enhanced electrocatalytic activity for HER. Although the specific surface area of bulk Sr2RuO4 is relatively low (~1.4 m2 g−1), the turnover frequency (TOF) for HER is ~10 times higher that of RuO2. When evaluated in 1 M KOH solution, the outstanding HER activity is reflected by an overpotential of only 61 mV at 10 mA cm−2 and a low Tafel slope of 51 mV dec−1, comparable to those of the commercial Pt/C catalyst and surpassing all metal oxides and other well-known Pt-free catalysts reported to date. Theoretical and experimental analyses reveal that an unusual synergistic effect in the layered RP structure possibly contributes to the HER activity of Sr2RuO4: SrO-terminated surface cleaved in rock-salt layer promotes water dissociation without a barrier while the active apical oxygen site in the perovskite layer enables favorable hydrogen adsorption and evolution. Besides, the HER activity of Sr2RuO4 can be further improved by the interface synergy between in situ formation of Ru nanoparticle and oxide substrate over the surface as well as incremental electrochemical surface area (ECSA) during electrochemistry-induced activation process. The design strategy of the layered RP Sr2RuO4 oxide and the derived synergistic effect for HER catalysis may be applicable to knowledge-based design of more efficient nonprecious electrocatalysts.
Results
Bulk structure characterization
Since RuO2 has only modest activity for HER in the alkaline solution, the electrocatalytic activity of several Ru-based oxides with different crystal structures was characterized to determine the effect of crystal structure on activity. Figure 1a–c shows the X-ray diffraction (XRD) patterns of RuO2, SrRuO3, and Sr2RuO4 powders synthesized using a solid-state reaction process. All diffraction peaks of the three oxide samples match well with those of the corresponding standard patterns (JCPDS No. 71-2273, 89-5713, and 81-1978, respectively), indicating their phase purity without observable impurities. This is also confirmed by the Rietveld refinement of the XRD patterns (Supplementary Fig. 1); the space group is P42/mnm for RuO2, Pnma for SrRuO3, and I4/mmm for Sr2RuO4. The local crystal structure and overall network of the [RuO6] octahedra in the three structures are schematically shown in inserted Fig. 1a–c based on the Rietveld analysis along with the detailed structure parameters (Supplementary Table 1). Particularly, Sr2RuO4 oxide crystallizes in the K2NiF4-type structure with layers of corner-linked [RuO6] octahedra separated by [SrO] rock-salt layers along the c-direction, which is schematically illustrated in Fig. 1d. Actually, Sr2RuO4 belongs to the so-called RP series with the formula Srn+1RunO3n+121. These strontium ruthenates consist of alternative perovskite SrRuO3 layer and SrO rock-salt layer. The layered RP crystal structure of Sr2RuO4 is further confirmed by the selected-area electron-diffraction (SAED) pattern along the [010] zone axes and the corresponding high-resolution transmission electron microscopy (HRTEM) image. The SAED pattern in Fig. 1e and fast Fourier transform (FFT) images insert in Fig. 1f clearly reflect the tetragonally arranged diffraction spots of [010] zone axes. In addition, a lattice fringe with lattice spacing of 0.64 nm was observed in the HRTEM image (Fig. 1f), corresponding to the (002) plane of Sr2RuO4 oxide. X-ray absorption spectroscopy (XAS) technique was further performed to analyze the oxidation state of Ru in the Sr2RuO4. Supplementary Fig. 2 shows the Ru-L2,3 XAS spectra of the as-synthesized Sr2RuO4 sample and the reference samples with different valence states of Ru. The Ru-L2,3 spectra of the as-synthesized Sr2RuO4 sample is completely the same as the reference Sr2RuO4 (including spectra shape and peak position), suggesting the character of stoichiometry and only Ru4+ in the as-synthesized Sr2RuO4 sample.
The morphologies of RuO2, SrRuO3, and Sr2RuO4 powders were examined by scanning electron microscopy (SEM) as displayed in Supplementary Fig. 3. Micrometer-sized particles were observed, suggesting the bulk nature of the as-synthesized SrRuO3 and Sr2RuO4 oxides by solid-state reaction method. The RuO2 appears to have smaller particle size than SrRuO3 and Sr2RuO4, and accordingly have larger surface areas as calculated from the Brunauer−Emmett−Teller (BET) measurements (Supplementary Fig. 4).
We also use density functional theory (DFT) calculations to unveil the electronic structures of RuO2, SrRuO3, and Sr2RuO4 by calculating the density of states (DOS) (Fig. 1g and Supplementary Fig. 5). It can be found clearly that the DOS profiles of Ru and O change significantly among the three oxides, accordingly having different electronic structures. Nevertheless, the three oxides all present a typical metallic behavior with predominantly Ru 4d and O 2p orbital crossing the Fermi level, which is highly beneficial to electrocatalysis due to high electronic conductivity10. Based on the above combined analysis, the Sr2RuO4 exhibits distinctive structural features (e.g., alternative layers, [RuO6] coordination geometry, Ru−O bond length, states near Fermi level) relative to RuO2 and SrRuO3, although they have the same oxidation state of Ru4+ and similar morphology. These structural features in Sr2RuO4 are the key factors for enhancing the HER activity, as to be discussed below.
Comprehensive evaluation of HER activity
To evaluate the electrocatalytic HER activity of RuO2, SrRuO3, and Sr2RuO4 oxides with different crystal structures in alkaline media, an electrochemical cell with a three-electrode configuration in an Ar-saturated 1 M KOH solution was used. Unless indicated otherwise, all potentials in this study were referenced to a reversible hydrogen electrode (RHE, see Supplementary Fig. 6 for RHE calibration) and iR-corrected to eliminate the ohmic potential drop across the electrolyte. Figure 2a shows the polarization curves gained from linear sweep voltammetry at a scan rate of 5 mV s−1. Sr2RuO4 can effectively catalyze alkaline HER with an extremely low onset overpotential (defined here as the overpotential at 1 mA cm−2) of ~3 mV; as a comparison, RuO2 and SrRuO3 show much larger onset potential of ~46 and ~28 mV, respectively. It is also seen that the added conductive carbon, which is always identified as a conductive additive and support in oxide electrodes22,23,24, displays negligible HER activity (Supplementary Fig. 7). Besides, the Sr2RuO4 requires a small overpotential of 61 mV to obtain a current density of −10 mA cm−2, much lower than that of the RuO2 (95 mV) and SrRuO3 (101 mV) catalysts. The result suggests that the [RuO6] octahedra layer in the Sr2RuO4 structure has much higher electrocatalytic activity for HER than those in the other two crystal structures.
To gain more insight into the electrochemical behavior of the electrocatalysts, polarizations in a broader range of overpotential were acquired and presented in Fig. 2b. In general, HER in an alkaline electrolyte includes two steps, i.e., electron-coupled water dissociation (the formation of Had by the Volmer step) and the concomitant transformation of Had into molecular H2 (the Heyrovsky or Tafel step)5,25. A Tafel slope for the Volmer, Heyrovsky, and Tafel step, as the rate-determining step for HER, is expected to be ~120, ~40, and ~30 mV dec−1 respectively5,25. Sr2RuO4 yields a Tafel slope of 51 mV dec−1, which is close to the RuO2 (49 mV dec−1) and SrRuO3 (67 mV dec−1), suggesting hydrogen evolution via Volmer−Heyrovsky mechanism in the alkaline electrolyte for all three oxides, and that the Heyrovsky step is the rate-limiting step. Also, small Tafel slope of Sr2RuO4 implies fast HER kinetics. Furthermore, the exchange current density (j0) was obtained from extrapolating the Tafel plots to zero overpotential. The j0 is dependent sensitively on the nature of the catalyst material and determines the rate of the intrinsic electron transfer between the catalyst and the electrolyte solution26. The j0 value of Sr2RuO4 is 0.898 mA cm−2, which is ~8-fold and ~2-fold higher than that of RuO2 (0.115 mA cm−2) and SrRuO3 (0.409 mA cm−2), respectively. As a whole, the high HER kinetic metrics (including the small overpotential, low Tafel slope, and high exchange current density) highlight the outstanding catalytic activity of Sr2RuO4 for HER in alkaline media, in particular by considering its small specific surface area (1.4 m2 g−1). Such excellent HER activity of Sr2RuO4 is superior to those of other metal oxides and Ru-based catalysts (Fig. 2c) as well as various well-known active Pt-free catalysts reported to date. A detailed HER activity comparison with previously reported representative HER catalysts, including metal/alloy, metal phosphides, metal sulfides, metal selenides, metal carbides, functional carbon and composites etc., demonstrates that Sr2RuO4 is among the most active HER catalyst in alkaline media (Supplementary Table 2).
It is well known that the overall catalytic activity of an electrocatalyst system is generally determined by two key factors: the intrinsic activity of each active site and the number of active sites27. To assess the intrinsic activity of RuO2, SrRuO3, and Sr2RuO4 oxides, it is necessary to eliminate the contribution derived from the surface areas and thereby calculate the specific activity (SA) normalized to the real oxide surface area or ECSA. The real oxide surface area and ECSA are estimated from the BET measurements (Supplementary Fig. 4) and double-layer capacitance (Cdl) measurements (Supplementary Fig. 8), respectively. The Cdl obtained from a cyclic voltammetry (CV) method is expected to be linearly proportional to the ECSA5,25. As shown in Fig. 2d and Supplementary Fig. 9, the SA of Sr2RuO4 is much higher than that of RuO2 and SrRuO3, regardless of the current densities normalized by the BET surface area or ECSA. For example, at η = 0.1 V, the Sr2RuO4 delivers an SA of 7.93 mA cm−2BET, which is ~15 and ~4 times higher than that for RuO2 and SrRuO3. The TOF, which is associated with the number of H2 molecules evolved per second per active site, is another important parameter that characterizes the intrinsic activity of an electrocatalyst28,29,30. In this work, TOF values were calculated according to a well-known method reported by the Jaramillo group (see the Supplementary Information for detailed calculations, Supplementary Fig. 10 and Supplementary Note 1)29,30. Figure 2e shows the TOF (per surface active O atom) versus potential plots of RuO2, SrRuO3, and Sr2RuO4 catalysts, and it reveals that the TOF values follows the order in the sequence of Sr2RuO4 > SrRuO3 > RuO2. Particularly, the Sr2RuO4 electrocatalyst delivers an extremely high TOF value of 0.90 s−1 at overpotential (η) of 0.1 V, which is evidently larger than that of some well-known HER catalysts in 1 M KOH solution, e.g., Ru/NG (0.35 s−1), Ni5P4 (0.79 s−1), NiCo2Px (0.056 s−1), Ni-Mo alloy (0.05 s−1), Ni-MoS2 (0.08 s−1), S-CoO NRs (0.41 s−1), NiP2-CeO2 (0.593 s−1) (Supplementary Table 3). According to the HER activities of RuO2, SrRuO3, and Sr2RuO4 summarized in Supplementary Table 4, the intrinsic HER activity of the layered RP Sr2RuO4 oxide is almost one order of magnitude higher than that of the RuO2, yet the ruthenium content is much less, only ~61 wt% of that in RuO2, producing the dual beneficial effects of activity enhancement and cost reduction simultaneously. The HER activity was further confirmed by the Faradaic efficiency, which is assessed by comparing the theoretical and detected volumes of generated gases during potentiostatic electrolysis experiments. As shown in Supplementary Fig. 11, the detected volume of gases matches the theoretical one, implying a high Faraday efficiency close to 100%. Moreover, the Sr2RuO4 oxide catalyst prepared by a simple solid-state reaction method enables HER activity comparable to that of the commercial Pt/C catalyst (Supplementary Fig. 12 and Supplementary Fig. 13). Although Sr2RuO4 still exhibits somewhat lower mass activity than the commercial Pt/C, it is more advantageous in price activity (Fig. 2f) and SA (Supplementary Fig. 14) considering the difference in their price (Supplementary Table 5) and specific surface area. It is also worthwhile to note that Sr2RuO4 shows much better durability than the benchmark Pt/C catalyst, demonstrating its value for practical application (Supplementary Fig. 15). The poor durability of Pt/C catalyst may be related to the dissolution of Pt surface atoms, the agglomeration of Pt particles, and the corrosion of the carbon support31,32.
Theoretical study
Clearly, the layered RP Sr2RuO4 oxide exhibits significantly higher HER activity than the simple oxide RuO2 and perovskite oxide SrRuO3 in alkaline media. To explore the origin of the high electrocatalytic activity, we resorted to DFT calculations. HER in an alkaline solution that is considered to proceed via two steps5,8,9,25,28, i.e., either Volmer−Heyrovsky or Volmer−Tafel pathways (Volmer: * + H2O + e− → H* + OH−; Heyrovsky: H* + H2O + e− → H2 + OH−; Tafel: H* + H* → H2, where * is the active site). Based on the above analysis of Tafel slope, the three oxides including Sr2RuO4 underwent a Volmer−Heyrovsky pathway in alkaline media. TMOs are generally regarded as unfavorable catalysts for converting H* to H2 (either too strong H* adsorption on oxygen ion or too weak H* adsorption on metal ion)8,9,29,33; thus we first studied hydrogen adsorption on the catalysts surface. The adsorption-free energy of H* (ΔGH*) is a key descriptor of the HER activity in both alkaline and acidic conditions, and generally a ΔGH* value close to zero results in superior HER activity due to the optimal balance between absorption and desorption of hydrogen atoms on the active sites9,10,28,34,35. Hence, the ΔGH* at the metal site or oxygen (O) site for RuO2, SrRuO3, and Sr2RuO4 was calculated using DFT according to the as-built catalyst structural models (Supplementary Fig. 16-18), along with Ru and Pt metals as references. Notably, the (001) SrO-terminated surface of Sr2RuO4, the (010) RuO2-terminated surface of SrRuO3, (110) surface of RuO2, and (0001) surface of Ru and (111) surface of Pt were used in our theoretical investigation considering that they are among the most usually observed and most stable ones in both experimental and theoretical studies21,28,36,37,38,39. Besides, based on previous findings that octahedral rotation happens on the surface of Sr2RuO421,40, the RuO6 octahedral unit rotated alternatingly by ~8.4° is also considered (Fig. 3a). Figure 3b shows the ΔGH* values on all the possible sites for the studied samples. The ΔGH* value on Ru and O site for RuO2 is 0.48 and −0.8 eV, respectively, indicating that the H* adsorption is either too weak or too strong. Consequently, the HER kinetics are sluggish on the RuO2 surface. For SrRuO3, the H binding strength is relatively too strong regardless of whether H adsorbs on Ru or O site, resulting in suppressed H desorption and H2 production is thus hindered. Impressively, the ΔGH* value on the O site of Sr2RuO4 is only −0.08 eV, which is most close to ideal zero and very similar to Pt (−0.10 eV), suggesting an optimum hydrogen adsorption strength on the surface of Sr2RuO4. The H* adsorption ability of transition metal compounds at the nonmetal site has been recently reported to relate to the electronic structure of metal elements (e.g., d-band center)41,42 and geometry factors (e.g., bond length)41,43,44. Thus, the d-band center of Ru (Supplementary Fig. 19) and Ru−O bond length were calculated for RuO2, SrRuO3, and Sr2RuO4 oxides. As seen from Fig. 3c, the ΔGH*@O value increases as the d-band center downshifts and Ru−O bond length increases, which is consistent with previous resports41. Especially, Sr2RuO4 delivers weaker H adsorption ability resulting from the downshift of the d-band center and the increase of bond length compared to SrRuO3 and RuO2, generating optimal level (close to 0) contributing to the highest HER activity. It is worth noting that there are only small variations in the adsorption energies calculated in vacuum and with solvation effects considered (Supplementary Table 6). In addition, the coverage effect of H on ΔGH* for Sr2RuO4 and SrRuO3 was also considered. The results as shown in Supplementary Fig. 20 support the conclusion that Sr2RuO4 can achieve higher coverages with lower potentials while the same is not necessarily the case for SrRuO3 as going from low coverage to high coverage involves high potentials (θH = 0.25–0.5 ML).
Notably, apart from the ΔGH* value, the water dissociation kinetics is also very crucial to the overall reaction rate for the alkaline HER4,8,9,28,35, which can be reflected by the activity difference between acidic and alkaline media of Pt/C and Sr2RuO4 catalysts. For benchmark Pt/C catalyst, the HER activity in an alkaline solution is lower than that in an acidic solution (Supplementary Fig. 21), indicating sluggish water dissociation in the catalytic process. Nevertheless, judged from the overpotential and TOF, Sr2RuO4 exhibits higher HER activity in an alkaline solution than in an acidic solution (Supplementary Fig. 22), due likely to faster kinetics for water dissociation, as demonstrated by Diebold et al. using low-temperature scanning tunneling microscopy (STM)21. They found that this layered RP structure easily cleaves apart in the rock-salt layer, and water dissociation is facile on the SrO-terminated surface21. We further performed DFT calculation of the energies for the water dissociation to demonstrate this phenomenon. To gain a more comprehensive picture about the H2 evolution reaction mechanism, we modeled the complete Volmer−Heyrovsky mechanism occurring at the most stable surfaces of Sr2RuO4 and SrRuO3. As displayed in Fig. 3d, e, Sr2RuO4 shows much lower energy barrier for water dissociation as compared with SrRuO3. Strikingly, on the SrO-terminated surface of Sr2RuO4, the kinetics to split water molecules is very favorable with the first water molecule splitting via a barrierless pathway. For the second water molecule splitting via the Heyrovsky step (H* + H2O + e− → H2 + * + OH−), the energy barrier is 1.66 eV at U = 0 V and can drop to 0.84 eV at USHE = 0.83 V. In contrast, SrRuO3 presents large barriers for water dissociation on the most stable RuO2-termination surface, in particular for the second water molecule in the Heyrovsky step where the barrier is about 2.6 eV at U = 0 V. The facile water dissociation results in strong hydroxylation on the surface of Sr2RuO4, which was characterized by X-ray photoelectron spectroscopy (XPS). XPS spectra of O 1s species (Supplementary Fig. 23) and the corresponding deconvolution results (Supplementary Table 7) demonstrate much larger number of −OH on the surface for Sr2RuO4. Abundant −OH on the surface was further confirmed by considering the Sr 3d spectra of Sr2RuO4 (Supplementary Fig. 24), and the result shows the formation of hydroxide surface species. Previous studies have proven that (hydro-)oxides can effectively promote the dissociation of water9,33,45,46, and thereby it is believed that abundant −OH specie on the surface of Sr2RuO4 is beneficial additionally to the water dissociation. Therefore, by theoretical calculations, we reasonably identified the origin of perfect HER performance of the layered RP Sr2RuO4 catalyst. Briefly, the outstanding HER catalytic activity in alkaline media of Sr2RuO4 oxide may be ascribed to an unusual synergistic effect in the RP layered structure, whereby the SrO-terminated surface cleaved in the rock-salt layer promotes water dissociation and the apical oxygen site in the perovskite layer enables favorable hydrogen adsorption for recombination into H2.
Further activity improvement induced by electrochemical activation
It is interesting to note that the HER activity is further improved after long-term stability test (Supplementary Fig. 15). During the chronopotentiometry test at −10 mA cm−2, the overpotential gradually decreases in the first ~5 h and then becomes stable during the next 25 h, indicating an activation process with self-improved activity for Sr2RuO447,48,49,50. The activation process was further verified by accelerated durability test (ADT) with continuous cycling in the HER potential window (Fig. 4a), showing that the overpotential decreases distinctly. To obtain a deeper understanding and to seek the origin of the activation phenomenon during the electrocatalytic process, the Sr2RuO4 catalyst after ADT of 1000 cycles (denoted as ADT-Sr2RuO4) was carefully characterized. Firstly, we checked the change in ECSA of Sr2RuO4 and ADT-Sr2RuO4, which is estimated from the double-layer capacitances by CV method (Supplementary Fig. 8e and Fig. 25). Figure 4b displays the current density differences as a function of scan rate of Sr2RuO4 and ADT-Sr2RuO4, and the result displays that the ECSA of ADT-Sr2RuO4 is nearly two times larger than that of pristine Sr2RuO4. The evident increase of ECSA after ADT may be associated with the change in the microstructure and composition of the catalysts47,48,49,50. The XRD patterns (Fig. 4c) shows that there is no apparent variation in the peak pattern and position between Sr2RuO4 and ADT-Sr2RuO4, revealing the unchanged bulk crystal structure of Sr2RuO4 during ADT. XAS technique was adopted to investigate the surface electronic structure of the transition metal. As displayed in Fig. 4d, a 0.2-eV shift of Ru-L2,3 edge toward low photo energy was observed for ADT-Sr2RuO4 relative to Sr2RuO4, which implies partial reduction of surface Ru4+. Moreover, the surface morphology was also examined and Supplementary Fig. 26 shows TEM images of the surface regions of ADT-Sr2RuO4. It is clearly seen that some nanoparticles with a radius of 10–15 nm are dispersed on the ADT-Sr2RuO4 surface. The lattice fringe with lattice space of 0.23 nm corresponds to the (001) plane of hexagonal Ru, suggesting that these nanoparticles are composed of metallic Ru in accordance with the XAS result. The high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) image (Fig. 4e) together with the energy-dispersive X-ray spectroscopy (EDX) elemental mapping and point spectra (Fig. 4f) further collectively confirm the formation of metallic Ru nanoparticles and oxide on the surface of ADT-Sr2RuO4. In conjunction with the above XRD, XAS, TEM, STEM, EDX and electrochemical results, we can conclude that the further-improved activity for Sr2RuO4 through electrochemical activation mainly originates from the interface synergy between in situ formation of Ru nanoparticle and oxide substrate over the surface51,52,53 as well as increased ECSA. The complete picture of interface synergy between these two components requires a future in-depth work.
Discussion
In summary, we have demonstrated that that layered RP Sr2RuO4 oxide has very high electrocatalytic activity for HER in alkaline media. Remarkably, when evaluated in 1 M KOH solution, the catalyst exhibits an onset overpotential of only 3 mV, low overpotential of 61 mV at 10 mA cm−2, low Tafel slope of 51 mV dec−1, large exchange current density of 0.898 mA cm−2, and high TOF values (e.g., 0.90 s−1 at overpotential of 100 mV), which is comparable to a commercial Pt/C catalyst and competitive with the best Pt-free electrocatalysts ever reported. Such excellent HER activity of Sr2RuO4 is attributed mainly to a synergistic effect associated with the layered RP structure, in which the SrO-terminated surface cleaved the in rock-salt layer promotes water dissociation, and the apical oxygen site in the perovskite layer facilitates favorable hydrogen adsorption, as confirmed by experiments and theoretical calculations. The favorable hydrogen adsorption for Sr2RuO4 on oxygen site is closely associated with the d-band center of Ru and Ru−O bond length. Moreover, the HER activity of Sr2RuO4 can be further enhanced by interface synergy between in situ formation of Ru nanoparticle and oxide substrate over the surface as well as increased active sites during the long-term stability test, which are substantiated by XRD, XAS, TEM, STEM, EDX and electrochemical analysis. This work not only demonstrates a new family of layered RP Sr2RuO4 oxide as an efficient HER catalysts, but also opens a new avenue for the development of next-generation high-performance electrocatalysts through unusual synergistic effects in the crystal structure.
Methods
Catalyst synthesis
The Sr2RuO4 was synthesized by traditional solid-state reaction route. Taking the synthesis of Sr2RuO4 as an example, stoichiometric amounts of SrCO3 and RuO2 were weighed and mixed using a high-energy ball mill (Planetary Mono Mill, Pulverisette 6, Fritsch) in ethanol media under 400 rpm for 1 h. The homogeneously dispersed mixture was then dried and calcined at 1200 °C in air for 20 h to form the Sr2RuO4 powders. SrRuO3 was also prepared by the identical procedure as Sr2RuO4 with the exception of the distinction of raw materials and their contents. The RuO2 powder used in this study was purchased from Alfer Aesar and the commercial Pt/C catalyst was purchased from Johnson Matthey Company.
Basic characterizations
The crystal structure of the as-prepared powders was studied by room temperature XRD (Rigaku Smartlab) using filtered Cu-Kα radiation (λ = 1.5418 Å) at a tube voltage of 40 kV and current of 40 mA. XRD patterns were collected by step scanning with an interval of 0.02° in the 2θ range of 10–90°. More detailed structural information (e.g., the space group and lattice parameters) was attained by Rietveld refinements using the GSAS-EXPGUI package. HRTEM images and the corresponding SAED patterns were obtained on a transmission election microscope (TEM, FEI Tecnai G2T20) at an accelerating voltage of 300 kV. HAADF-STEM images along with the corresponding EDX compositional line profiles were attained on a field-emission transmission electron microscope (FEI Tecnai G2 F30 STWIN) equipped with an EDX analyzer at 200 kV. SEM images were obtained using a Hitachi S-4800 scanning electron micro-analyzer. Nitrogen adsorption isotherms were tested under 77 K (BELSORP II) and the specific surface areas were calculated by the BET methods. An Agilent (7820 A) gas chromatography system equipped with an HP-plot molecular sieve (5 Å) column and a thermal conductivity detector was employed to obtain gas chromatography data. Hydrogen was detected using a long (24 m length) column with a nitrogen carrier gas. The surface element states were probed using an XPS (PHI5000 VersaProbe equipped with an Al Kα X-ray source) and public XPSPEAK software package was used to fit the obtained data. The synchrotron-based measurements were carried out using the soft X-ray spectroscopy beamline at the Taiwan Synchrotron. The Ru-L3 XAS spectra were measured in the total-electron-yield mode. Ru-L3 XAS spectra of Ru-based standard references (RuCl3, Sr2RuO4, and Sr2GdRuO6) were collected under the same conditions.
Electrode preparation
Working electrodes for HER measurements were prepared by a controlled drop-casting method including an RDE comprising a glassy carbon (GC) electrode with 0.196 cm2 (Pine Research Instrumentation), which was prepolished with aqueous alumina suspension. To eliminate the electrode conductivity restriction within thin film working electrodes, the catalysts in this study were mixed with as-obtained conductive carbon (Super P Li) at a 1:1 mass ratio. Briefly, a 5 μL aliquot of the catalyst ink, which was prepared by sonication of a mixture of 10 mg of oxide powder and 10 mg of conductive carbon dispersed in 1 mL ethanol and 100 μL of 5 wt% Nafion solution for at least 1 h, was dropped on the GC surface, generating an approximate catalyst loading of 0.464 mgtotal cm−2 (0.232 mgoxide cm−2) and was left to dry before the electrochemical tests. Working electrode containing commercial 20 wt% Pt/C catalyst was prepared according to the following procedures. Ten milligrams Pt/C and 100 μL of 5 wt% Nafion solution were ultrasonically dispersed in 1 mL of ethanol to form a homogeneous ink. Five microliters of the homogeneous ink was transferred onto the surface of the GC substrate, generating an approximate catalyst loading of 0.232 mgtotal cm−2 (0.0464 mgPt cm−2).
Electrochemical measurements
HER performance of catalysts in alkaline or acidic solutions was assessed on a CHI 760D electrochemistry workstation at room temperature in a standard three-electrode electrochemical cell (Pine Research Instrumentation) in an RDE configuration. Catalysts cast on RDE, graphite rod and Ag|AgCl (3.5 M KCl) were used as the working electrode, counter electrode, and reference electrode, respectively. Throughout the measurement, the RDE electrode was rotated at 1600 rpm to remove the bubbles formed at the electrode surface. The electrolyte solution was bubbled with Ar for ~30 min before HER tests and maintained under Ar atmosphere during the test period. HER polarization curves were recorded from −0.8 to −1.6 V vs. Ag|AgCl in 1 M KOH solutions and from 0 to −0.6 V vs. Ag|AgCl in 0.5 H2SO4 solutions. IR compensation for all polarization curves in this study was performed unless noted otherwise. Tafel plots were obtained by replotting the polarization curves as overpotential (η) versus the logarithm of current density (log |J|). Extrapolating the Tafel plots to the overpotential of 0 V to attain the exchange current density (j0). Accelerated durability tests of catalysts were conducted through continuous potential cycling ranged from −0.8 to −1.4 V vs. Ag|AgCl for 1000 cycles at a scan rate of 100 mV s−1. The chronopotentiometry tests were performed at a constant cathodic current density of 10 mA cm−2. CV tests were conducted in the potential range between −0.8 and −0.9 V vs. Ag|AgCl (where no faradic current was observed) with different sweeping rates of 20, 40, 60, 80, and 100 mV s−1 to measure the electrochemical double-layer capacitance (Cdl). The slopes obtained from the plots as the halves of the positive and negative current density differences at the center of the scanning potential range (i.e., −0.85 V) versus scan rates are the Cdl values.
Computational methods
Electronic structure calculations were performed using the Vienna ab initio Simulation Package (VASP)54,55. Exchange and correlation were described using the generalized gradient approximation with the Perdew−Burke−Ernzerhof functional56. The projector augmented wavefunction method57 was used to describe pseudopotentials. Van der Waals correction was employed in all calculations58. A kinetic energy cut-off of 500 eV was used. Unit cells of Ru, Pt, RuO2, SrRuO3, and Sr2RuO4 were fully relaxed, and the resulting structures were cleaved to construct symmetric slabs which were sandwiched in about 20 Å of vacuum. Hydrogen adsorption was investigated by placing H on various sites on the metal and oxides surfaces, and the binding energy was calculated as:
where \(E_{{\mathrm H} \ast }\), \(E_{{\mathrm {bare}}}\), and \(E_{{\mathrm H}_2}\) are the total energies of an adsorbed hydrogen, the bare surface and the energy of a hydrogen molecule, respectively. Free energies \({\mathrm{\Delta }}G_{{\mathrm H}^ \ast }\), were obtained by adding the zero-point energy (ZPE) and entropic correction to the binding energy such as \({\mathrm{\Delta }}G_{{\mathrm H}^ \ast } = {\mathrm{\Delta }}E_{\mathrm H} + {\mathrm{\Delta }}E_{{\mathrm {ZPE}}} - T{\mathrm{\Delta }}S\). The total correction \({\mathrm{\Delta }}E_{\mathrm{ZPE}} - T{\mathrm{\Delta }}S\) was estimated to be 0.24 eV for metals and oxides and this value is used consistently throughout59. Metal d-band centers were determined by evaluating the centroid of the projected DOS including valence and conduction states relative to the Fermi level. Water dissociation barriers were calculated using the climbing image nudged elastic band60 (CI-NEB) using five images and a force tolerance of 0.02 eV/Å. The Volmer−Heyrovsky pathway of HER in alkaline media (2H2O + 2e− → H2 + 2OH−) proceeds through two electrochemical elementary steps and two electrons involved (H2O + * + e− → H* + OH−; H* + H2O + e− → H2 + * + OH−; where the * denotes the catalyst surface). The effect of pH can be accounted for within the computational hydrogen electrode formalism by including the changes due to kBTln10*pH (kB is Boltzmann’s constant) for which the chemical potential for H+ + e− = 1/2H2 − kBTln10*pH. A pH = 14 corresponding to fully alkaline conditions results in an equilibrium potential of 0.83 V. The energy of G(OH−) can be obtained from G(H2O) and G(H+) via G(OH−) = G(H2O) − G(H+) = G(H2O) − G(1/2H2) + kBTln10*pH41.
Data availability
The data that support the findings of this study are available from the corresponding authors upon request.
References
Chu, S. & Majumdar, A. Opportunities and challenges for a sustainable energy future. Nature 488, 294–303 (2012).
Turner, J. A. Sustainable hydrogen production. Science 305, 972–974 (2004).
Zou, X. & Zhang, Y. Noble metal-free hydrogen evolution catalysts for water splitting. Chem. Soc. Rev. 44, 5148–5180 (2015).
Zeng, K. & Zhang, D. Recent progress in alkaline water electrolysis for hydrogen production and applications. Prog. Energy Combust. Sci. 36, 307–326 (2010).
Zhu, Y. et al. A perovskite nanorod as bifunctional electrocatalyst for overall water splitting. Adv. Energy Mater. 7, 1602122 (2017).
Durst, J. et al. New insights into the electrochemical hydrogen oxidation and evolution reaction mechanism. Energy Environ. Sci. 7, 2250–2260 (2014).
Wu, R., Zhang, J., Shi, Y., Liu, D. & Zhang, B. Metallic WO2–carbon mesoporous nanowires as highly efficient electrocatalysts for hydrogen evolution reaction. J. Am. Chem. Soc. 137, 6983–6986 (2015).
Ling, T. et al. Activating cobalt (II) oxide nanorods for efficient electrocatalysis by strain engineering. Nat. Commun. 8, 1509 (2017).
Gong, M. et al. Nanoscale nickel oxide/nickel heterostructures for active hydrogen evolution electrocatalysis. Nat. Commun. 5, 4695 (2014).
Zheng, T. et al. Conductive tungsten oxide nanosheets for highly efficient hydrogen evolution. Nano Lett. 17, 7968–7973 (2017).
Spataru, N., Le Helloco, J. G. & Durand, R. A study of RuO2 as an electrocatalyst for hydrogen evolution in alkaline solution. J. Appl. Electrochem. 26, 397–402 (1996).
Kötz, E. R. & Stucki, S. Ruthenium dioxide as a hydrogen-evolving cathode. J. Appl. Electrochem. 17, 1190–1197 (1987).
Luo, Z. et al. Mesoporous MoO3-x material as an efficient electrocatalyst for hydrogen evolution reactions. Adv. Energy Mater. 6, 1600528 (2016).
Wang, H. et al. Bifunctional non-noble metal oxide nanoparticle electrocatalysts through lithium-induced conversion for overall water splitting. Nat. Commun. 6, 7261 (2015).
Maeno, Y. et al. Superconductivity in a layered perovskite without copper. Nature 372, 532–534 (1994).
Seitz., L. C. et al. A highly active and stable IrOx/SrIrO3 catalyst for the oxygen evolution reaction. Science 353, 1011–1014 (2016).
Zhu, Y., Zhou, W. & Shao, Z. Perovskite/carbon composites: applications in oxygen electrocatalysis. Small 13, 1603793 (2017).
Bak, J., Bae, H. B., Kim, J., Oh, J. & Chung, S. Y. Formation of two-dimensional homologous faults and oxygen electrocatalytic activities in a perovskite nickelate. Nano Lett. 17, 3126–3132 (2017).
Goodenough, J. Electronic and ionic transport properties and other physical aspects of perovskites. Rep. Prog. Phys. 67, 1915–1993 (2004).
Du, J. et al. Nonstoichiometric perovskite CaMnO3-δ for oxygen electrocatalysis with high activity. Inorg. Chem. 53, 9106–9114 (2014).
Halwidl, D. et al. Adsorption of water at the SrO surface of ruthenates. Nat. Mater. 15, 450–455 (2016).
Suntivich, J., May, K. J., Gasteiger, H. A., Goodenough, J. B. & Shao-Horn, Y. A perovskite oxide optimized for oxygen evolution catalysis from molecular orbital principles. Science 334, 1383–1385 (2011).
Suntivich, J., Gasteiger, H. A., Yabuuchi, N. & Shao-Horn, Y. Electrocatalytic measurement methodology of oxide catalysts using a thin-film rotating disk electrode. J. Electrochem. Soc. 157, B1263–B1268 (2010).
Zhu, Y. et al. SrNb0.1Co0.7Fe0.2O3-δ perovskite as a next-generation electrocatalyst for oxygen evolution in alkaline solution. Angew. Chem. Int. Ed. 54, 3897–3901 (2015).
Xu, X. et al. A perovskite electrocatalyst for efficient hydrogen evolution reaction. Adv. Mater. 28, 6442–6448 (2016).
Miao, R. et al. Mesoporous iron sulfide for highly efficient electrocatalytic hydrogen evolution. J. Am. Chem. Soc. 139, 13604–13607 (2017).
Seh, Z. W. et al. Combining theory and experiment in electrocatalysis: Insights into materials design. Science 355, eaad4998 (2017).
Zheng, Y. et al. High electrocatalytic hydrogen evolution activity of an anomalous ruthenium catalyst. J. Am. Chem. Soc. 138, 16174–16181 (2016).
Kibsgaard, J. & Jaramillo, T. F. Molybdenum phosphosulfide: an active, acid-stable, earth-abundant catalyst for the hydrogen evolution reaction. Angew. Chem. Int. Ed. 53, 14433–14437 (2014).
Kibsgaard, J. et al. Designing an improved transition metal phosphide catalyst for hydrogen evolution using experimental and theoretical trends. Energy Environ. Sci. 8, 3022–3029 (2015).
Cao, X. et al. Highly catalytic active PtNiCu nanochains for hydrogen evolution reaction. Nano Energy 9, 301–308 (2014).
Katsounaros, I., Cherevko, S., Zeradjanin, A. R. & Mayrhofer, K. J. J. Angew. Chem. Int. Ed. 53, 102–121 (2014).
Subbaraman, R. et al. Enhancing hydrogen evolution activity in water splitting by tailoring Li+-Ni(OH)2-Pt interfaces. Science 334, 1256–1260 (2011).
Zheng, Y. et al. Hydrogen evolution by a metal-free electrocatalyst. Nat. Commun. 5, 3783 (2014).
Su, J. et al. Ruthenium-cobalt nanoalloys encapsulated in nitrogen-doped graphene as active electrocatalysts for producing hydrogen in alkaline media. Nat. Commun. 8, 14969 (2017).
Nørskov, J. K., Rossmeisl, J., Logadottir, A. & Lindqvist, L. Origin of the overpotential for oxygen reduction at a fuel-cell cathode. J. Phys. Chem. B 108, 17886–17892 (2004).
Feibelman, P. J. Partial dissociation of water on Ru (0001). Science 295, 99–102 (2002).
Stoerzinger, K. A., Qiao, L., Biegalski, M. D. & Shao-Horn, Y. Orientation-dependent oxygen evolution activities of rutile IrO2 and RuO2. J. Phys. Chem. Lett. 5, 1636–1641 (2014).
Chang, S. H. et al. Hydrogen functional links between stability and reactivity of strontium ruthenate single crystals during oxygen evolution. Nat. Commun. 5, 4191 (2014).
Matzdorf, R. et al. Ferromagnetism stabilized by lattice distortion at the surface of the p-wave superconductor Sr2RuO4. Science 289, 746–748 (2000).
Wu, Y. et al. Electron density modulation of NiCo2S4 nanowires by nitrogen incorporation for highly efficient hydrogen evolution catalysis. Nat. Commun. 9, 1425 (2018).
Tsai, C., Chan, K., Abild-Pedersen, F. & Nørskov, J. K. Active edge sites in MoSe2 and WSe2 catalysts for the hydrogen evolution reaction: a density functional study. Phys. Chem. Chem. Phys. 16, 13156–13164 (2014).
Chen, G. et al. Efficient and stable bifunctional electrocatalysts Ni/NixMy (M=P,S) for overall water splitting. Adv. Funct. Mater. 26, 3314–3323 (2016).
Laursen, J. et al. Nanocrystalline Ni5P4: a hydrogen evolution electrocatalyst of exceptional efficiency in both alkaline and acidic media. Energy Environ. Sci. 8, 1027–1034 (2015).
Danilovic, N. et al. Enhancing the alkaline hydrogen evolution reaction activity through the bifunctionality of Ni(OH)2/metal catalysts. Angew. Chem. Int. Ed. 51, 12495–12498 (2012).
Zhu, Y. et al. Synergistically enhanced hydrogen evolution electrocatalysis by in situ exsolution of metallic nanoparticles on perovskites. J. Mater. Chem. A 6, 13582–13587 (2018).
Hu, C. et al. In situ electrochemical production of ultrathin nickel nanosheets for hydrogen evolution electrocatalysis. Chem 3, 122–133 (2017).
Zhu, Y., Zhou, W., Sunarso, J., Zhong, Y. & Shao, Z. Phosphorus-doped perovskite oxide as highly efficient water oxidation electrocatalyst in alkaline solution. Adv. Funct. Mater. 26, 5862–5872 (2016).
Yang, C. et al. In-situ activation of self-supported 3D hierarchically porous Ni3S2 films grown on nanoporous copper as excellent pH-universal electrocatalysts for hydrogen evolution reaction. Nano Energy 36, 85–94 (2017).
Li, Q., Xing, Z., Wang, D., Sun, X. & Yang, X. In situ electrochemically activated CoMn-S@NiO/CC nanosheets array for enhanced hydrogen evolution. ACS Catal. 6, 2797–2801 (2016).
Jiang, P. et al. Pt-like electrocatalytic behavior of Ru-MoO2 nanocomposites for the hydrogen evolution reaction. J. Mater. Chem. A 5, 5475–5485 (2017).
Yoon, D. et al. Cactus-like hollow Cu2-xS@Ru nanoplates as excellent and robust electrocatalysts for the alkaline hydrogen evolution reaction. Small 13, 1700052 (2017).
Xu, J. et al. Boosting the hydrogen evolution performance of ruthenium clusters through synergistic coupling with cobalt phosphides. Energy Environ. Sci. 11, 1819–1827 (2018).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comp. Mater. Sci. 6, 15–50 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).
Grimme, S. Semiempirical GGA‐type density functional constructed with a long‐range dispersion correction. J. Comput. Chem. 27, 1787–1799 (2006).
Nørskov, J. K. et al. Trends in the exchange current for hydrogen evolution. J. Electrochem. Soc. 152, J23–J26 (2005).
Henkelman, G. et al. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. Chem. Phys. 113, 9901 (2000).
Acknowledgements
This work was financially supported by the National Nature Science Foundation of China under contract No. 21576135, the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD), the Major Project of Educational Commission of Jiangsu Province of China under contract No. 13KJA430004, the Program for Jiangsu Specially-Appointed Professors, and the Youth Fund in Jiangsu Province under contract No. BK20150945. Computational work was supported by resources provided by the Pawsey Supercomputing Centre with funding from the Australian Government and the Government of Western Australia.
Author information
Authors and Affiliations
Contributions
Z.S. and Y.Z. conceived and designed the research. Y.Z. conducted characterizations and electrochemical measurements. H.A.T. and S.C.S. performed DFT calculations. Z.H. and H.S. performed XAS characterization. Y.C. performed XRD refinements. J.D. and W.Z. were involved in the structural and electrochemical analysis. All authors discussed and analyzed the data. Y.Z., W.Z., M.L., H.W. and Z.S. co-wrote the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Journal peer review information: Nature Communications thanks the anonymous reviewers for their contributions to the peer review of this work. Peer Reviewer Reports are available.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhu, Y., Tahini, H.A., Hu, Z. et al. Unusual synergistic effect in layered Ruddlesden−Popper oxide enables ultrafast hydrogen evolution. Nat Commun 10, 149 (2019). https://doi.org/10.1038/s41467-018-08117-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-08117-6
- Springer Nature Limited
This article is cited by
-
Facilitating alkaline hydrogen evolution reaction on the hetero-interfaced Ru/RuO2 through Pt single atoms doping
Nature Communications (2024)
-
Recent advances in Ir/Ru-based perovskite electrocatalysts for oxygen evolution reaction
Rare Metals (2024)
-
Ru-doped functional porous materials for electrocatalytic water splitting
Nano Research (2024)
-
Monometallic interphasic synergy via nano-hetero-interfacing for hydrogen evolution in alkaline electrolytes
Nature Communications (2023)
-
A Quaternary mixed oxide protective scaffold for ruthenium during oxygen evolution reaction in acidic media
Communications Engineering (2023)