Abstract
The hydrogen evolution reaction (HER) is a crucial step in electrochemical water splitting and demands an efficient, durable and cheap catalyst if it is to succeed in real applications1,2,3. For an energy-efficient HER, a catalyst must be able to trigger proton reduction with minimal overpotential4 and have fast kinetics5,6,7,8,9. The most efficient catalysts in acidic media are platinum-based, as the strength of the Pt–H bond10 is associated with the fastest reaction rate for the HER11,12. The use of platinum, however, raises issues linked to cost and stability in non-acidic media. Recently, non-precious-metal-based catalysts have been reported, but these are susceptible to acid corrosion and are typically much inferior to Pt-based catalysts, exhibiting higher overpotentials and lower stability13,14,15. As a cheaper alternative to platinum, ruthenium possesses a similar bond strength with hydrogen (∼65 kcal mol–1)16, but has never been studied as a viable alternative for a HER catalyst. Here, we report a Ru-based catalyst for the HER that can operate both in acidic and alkaline media. Our catalyst is made of Ru nanoparticles dispersed within a nitrogenated holey two-dimensional carbon structure (Ru@C2N). The Ru@C2N electrocatalyst exhibits high turnover frequencies at 25 mV (0.67 H2 s−1 in 0.5 M H2SO4 solution; 0.75 H2 s−1 in 1.0 M KOH solution) and small overpotentials at 10 mA cm–2 (13.5 mV in 0.5 M H2SO4 solution; 17.0 mV in 1.0 M KOH solution) as well as superior stability in both acidic and alkaline media. These performances are comparable to, or even better than, the Pt/C catalyst for the HER.
Similar content being viewed by others
References
Vesborg, P. C. K., Seger, B. & Chorkendorff, I. Recent development in hydrogen evolution reaction catalysts and their practical implementation. J. Phys. Chem. Lett. 6, 951–957 (2015).
Turner, J. A. Sustainable hydrogen production. Science 305, 972–974 (2004).
Dresselhaus, M. S. & Thomas, I. L. Alternative energy technologies. Nature 414, 332–337 (2001).
Norskov, J. K. & Christensen, C. H. Toward efficient hydrogen production at surfaces. Science 312, 1322–1323 (2006).
Parsons, R. & Bockris, J. O. Calculation of the energy of activation of discharge of hydrogen ions at metal electrodes. Trans. Faraday Soc. 47, 914–928 (1951).
Rüetschi, P. & Delahay, P. Hydrogen overvoltage and electrode material. A theoretical analysis. J. Chem. Phys. 23, 195–199 (1955).
Conway, B. E. & Bockris, J. O. Electrolytic hydrogen evolution kinetics and its relation to the electronic and adsorptive properties of the metal. J. Chem. Phys. 26, 532–541 (1957).
Parsons, R. The rate of electrolytic hydrogen evolution and the heat of adsorption of hydrogen. Trans. Faraday Soc. 54, 1053–1063 (1958).
Thomas, J. G . Kinetics of electrolytic hydrogen evolution and the adsorption of hydrogen by metals. Trans. Faraday Soc. 57, 1603–1611 (1961).
Gross, A., Schnur, S., Santos, E. & Schmickler, W. Catalysis in Electrochemistry: From Fundamental Aspects to Strategies for Fuel Cell Development (Wiley, 2011).
McKone, J. R. et al. Evaluation of Pt, Ni, and Ni-Mo electrocatalysts for hydrogen evolution on crystalline Si electrodes. Energy Environ. Sci. 4, 3573–3583 (2011).
Popczun, E. J. et al. Nanostructured nickel phosphide as an electrocatalyst for the hydrogen evolution reaction. J. Am. Chem. Soc. 135, 9267–9270 (2013).
Zeng, M. & Li, Y. Recent advances in heterogeneous electrocatalysts for the hydrogen evolution reaction. J. Mater. Chem. A 3, 14942–14962 (2015).
Zheng, Y. et al. Hydrogen evolution by a metal-free electrocatalyst. Nat. Commun. 5, 3783 (2014).
Cobo, S. et al. A Janus cobalt-based catalytic material for electro-splitting of water. Nat. Mater. 11, 802–807 (2012).
Mitchell, W. J., Xie, J., Jachimowski, T. A. & Weinberg, W. H. Carbon monoxide hydrogenation on the Ru(001) surface at low temperature using gas-phase atomic hydrogen: spectroscopic evidence for the carbonyl insertion mechanism on a transition metal surface. J. Am. Chem. Soc. 117, 2606–2617 (1995).
Mahmood, J., Kim, D., Jeon, I.-Y., Lah, M. S. & Baek, J.-B. Scalable synthesis of pure and stable hexaaminobenzene trihydrochloride. Synlett 24, 246–248 (2013).
Mahmood, J. et al. Nitrogenated holey two-dimensional structures. Nat. Commun. 6, 6486 (2015).
Jaramillo, T. F. et al. Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007).
Liang, H. W. et al. Molecular metal-Nx centres in porous carbon for electrocatalytic hydrogen evolution. Nat. Commun. 6, 7992 (2015).
Laursen, A. B. et al. Nanocrystalline Ni5P4: a hydrogen evolution electrocatalyst of exceptional efficiency in both alkaline and acidic media. Energy Environ. Sci. 8, 1027–1034 (2015).
McKone, J. R., Sadtler, B. F., Werlang, C. A., Lewis, N. S. & Gray, H. B. Ni-Mo nanopowders for efficient electrochemical hydrogen evolution. ACS Catal. 3, 166–169 (2013).
Popczun, E. J., Read, C. G., Roske, C. W., Lewis, N. S. & Schaak, R. E. Highly active electrocatalysis of the hydrogen evolution reaction by cobalt phosphide nanoparticles. Angew. Chem. Int. Ed. 53, 5427–5430 (2014).
Fei, H. et al. Atomic cobalt on nitrogen-doped graphene for hydrogen generation. Nat. Commun. 6, 8668 (2015).
Kibsgaard, J., Jaramillo, T. F. & Besenbacher, F. Building an appropriate active-site motif into a hydrogen-evolution catalyst with thiomolybdate [Mo3S13]2- clusters. Nat. Chem. 6, 248–253 (2014).
Le Goff, A. et al. From hydrogenases to noble metal-free catalytic nanomaterials for H2 production and uptake. Science 326, 1384–1387 (2009).
Ma, L., Ting, L. R. L., Molinari, V., Giordano, C. & Yeo, B. S. Efficient hydrogen evolution reaction catalyzed by molybdenum carbide and molybdenum nitride nanocatalysts synthesized via the urea glass route. J. Mater. Chem. A 3, 8361–8368 (2015).
Quiroz, M. A., Meas, Y., Lamy-Pitara, E. & Barbier, J. Characterization of a ruthenium electrode by underpotential deposition of copper. J. Electroanal. Chem. Interfacial Electrochem. 157, 165–174 (1983).
Green, C. L. & Kucernak, A. Determination of the platinum and ruthenium surface areas in platinum−ruthenium alloy electrocatalysts by underpotential deposition of copper. I. Unsupported catalysts. J. Phys. Chem. B 106, 1036–1047 (2002).
Trasatti, S. & Petrii, O. Real surface area measurements in electrochemistry. Pure Appl. Chem. 63, 711–734 (1991).
Kohn, W. & Sham, L. J. Self-consistent equations including exchange and correlation effects. Phys. Rev. 140, A1133–A1138 (1965).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Acknowledgements
This work was supported by the Creative Research Initiative (CRI, 2014R1A3A2069102), BK21 Plus (10Z20130011057), Science Research Center (SRC, 2016R1A5A1009405) and Creative Materials Discovery Program (2016M3D1A1900035) programmes through the National Research Foundation (NRF) of Korea.
Author information
Authors and Affiliations
Contributions
J.-B.B. conceived the project and oversaw all the research phases. J.-B.B. and J.M. designed the project, and collected and analysed data. F.L. carried out all the electrochemical experiments and data analysis. I.A. and S.-J.K. were involved in the BET measurements and monomer synthesis. S.-M.J. and H.Y.J. performed the detailed TEM and HR-TEM characterizations. N.P. and M.S.O. carried out the theoretical studies. J.-B.B., J.M., F.L., N.P. and H.Y.J. wrote the paper and discussed the results. All the authors contributed to and commented on this paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary information
Supplementary information (PDF 3798 kb)
Rights and permissions
About this article
Cite this article
Mahmood, J., Li, F., Jung, SM. et al. An efficient and pH-universal ruthenium-based catalyst for the hydrogen evolution reaction. Nature Nanotech 12, 441–446 (2017). https://doi.org/10.1038/nnano.2016.304
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/nnano.2016.304
- Springer Nature Limited
This article is cited by
-
Oxophilic gallium single atoms bridged ruthenium clusters for practical anion-exchange membrane electrolyzer
Nature Communications (2024)
-
Active site engineering accelerates water electrolysis
Nature Synthesis (2024)
-
A strongly coupled Ru–CrOx cluster–cluster heterostructure for efficient alkaline hydrogen electrocatalysis
Nature Catalysis (2024)
-
Laser-assisted synthesis of PtPd alloy for efficient ethanol oxidation
Nano Research (2024)
-
Supporting IrOx nanosheets on hollow TiO2 for highly efficient acidic water splitting
Nano Research (2024)