Abstract
Simple and effective generation of transition metal chalcogenides (TMCs) in a single-layer form has been a challenging task. Here we present a tandem molecular intercalation (TMI) as a new exfoliation concept for producing single-layer TMCs from multi-layer colloidal TMC nanostructures in solution phase. TMI requires tandem Lewis base intercalates, where short ‘initiator’ molecules first intercalate into TMCs to open up the interlayer gap, and the long ‘primary’ molecules then bring the gap to full width so that a random mixture of intercalates overcomes the interlayer force. Spontaneous exfoliation then yields single-layer TMCs. The TMI process is uniquely advantageous because it works in a simple one-step process under safe and mild conditions (that is, room temperature without sonication or H2 generation). With the appropriate intercalates, we have successfully generated single-layer nanostructures of group IV (TiS2, ZrS2), group V (NbS2) and VI (WSe2, MoS2) TMCs.
Similar content being viewed by others
Introduction
Two-dimensional (2D) layered materials including transition metal chalcogenides (TMCs) with strong in-plane covalent bonds and weak interlayer van der Waals interactions exhibit a wide range of interesting anisotropic phenomena from charge transport to catalytic and optical properties1,2,3,4,5,6,7,8,9. Similar to graphene, such interesting effects are centred on single-layer TMCs and, as an example, when MoS2, an indirect band gap semiconductor in bulk, is thinned to a single layer, a strong photoluminescence is observed due to the indirect-to-direct band gap change6,7.
Single-layer or few-layer nanosheets can be obtained from bulk TMCs by several exfoliation techniques such as dry mechanical cleavage with Scotch tape10,11 or solution-based exfoliation processes12,13,14,15,16,17,18,19,20,21,22,23,24,25,26. Intercalation of alkali metals by using elemental metals12,13 (for example, potassium) or organo-alkali compounds (for example, butyllithium14,15,16 and more recently sodium naphthalenide17) has been a widely used method for the exfoliation of layered materials. Such exfoliation and disintegration methods with K, air and EtOH-H2O along with sonication of layered flakes have successfully generated monolayer nanoparticles of WS2, BN and graphene9,12,13. Although quite effective, the use of reactive chemicals during exfoliation conditions and H2 generation through multiple exfoliation processes has drawbacks17. While the electrochemical exfoliation method has been developed as a faster and controllable exfoliation protocol, complicated electrochemical set-ups present challenges for the mass production of single-layer nanosheets18,19,20,21. Alternatively, a sonication method in the presence of solvents22,23 such as N-methyl-pyrrolidone has been demonstrated for the successful exfoliation of wide range of TMCs, but the products are often mixed with single- and multi-layer TMCs with potential degradation of samples due to the harsh sonication conditions required to overcome the interlayer interactions24,25,26. As stated here, current methodologies have their own advantages and disadvantages, but none of them are yet perfect17,26, although it is true that these are effective for large-size layered nanostructures. The development of mild exfoliation strategies that can circumvent the key harsh process conditions (for example, sonication and H2 gas formation) has been challenging and, therefore, new and better routes to obtain single-layer TMCs in a simple, efficient and reproducible manner are currently being pursued. In this study, we introduce the ‘tandem molecular intercalation (TMI)’ process as a mild and effective exfoliation strategy for single-layer 2D TMC nanosheets from multi-layer colloidal TMC nanostuctures. Our TMI process utilizes two different Lewis base intercalates for the initiative and primary roles. Relatively short length ‘initiator’ Lewis base molecules are introduced into the interlayer space of 2D TMCs to start the gap-widening process, and a simultaneous influx of ‘primary’ intercalate molecules with longer chains creates randomly mixed bilayers of intercalates to overcome the interlayer interactions and eventually generate single-layer nanosheets (Fig. 1). Although the host–guest chemistry for the intercalation of Lewis bases into bulk TMCs has been well documented27,28, its successful extension to an exfoliation strategy has not been demonstrated yet.
Results
Intercalation of alkylamine in TiS2 colloidal nanostructure
We first examined the group IV TiS2 colloidal nanostructure (60 nm in diameter with a dozen layers) with an interlayer distance of 5.7 Å and with each single-layer TiS2 comprising a S-Ti-S tri-atomic plate of 1T-type CdI2 structure29 (Fig. 2a). The intercalation and gap-widening capability of Lewis base molecular intercalates were investigated depending on the alkyl chain length of primary amines such as propyl-, butyl- and hexyl-amine (Fig. 2b)29,30. Here, an excess amount of intercalate is added to TiS2 nanoparticle in dimethyl sulphoxide (DMSO) at room temperature, and the reaction mixture is stirred for 30 min to 5 h depending on the chain length of the intercalate molecules. Subsequently, the colloidal suspension is precipitated by centrifugation and washed with chloroform. The initial interlayer distance of pristine TiS2 is 5.7 Å, but after intercalation with propyl- butyl- and hexyl-amine, it increases to 9.5, 10.5 and 14.3 Å, respectively, according to TEM analysis (Fig. 2c–f).
XRD analysis also confirms the widening interlayer distance (Fig. 2h). Interlayer gap dependent c axis peaks, such as (001), (002) and (003), are shifted to lower angles as the intercalate size increases. Pronounced effects are observed for the (001) peak position, where the 2θ angle changes from 15.5° to 9.0°, 8.7° and 6.3° for propylamine, butylamine and hexylamine, respectively. From the 2θ values, the interlayer distances are calculated to be 5.7, 9.8, 10.2 and 14.0 Å, and the expansion of the c axis is 4.1 Å for propylamine, 4.5 Å for butylamine and 8.3 Å for hexylamine (Fig. 2j), respectively. This (001) peak shift trend and TEM analysis confirm that the interlayer gap widening of TiS2 is proportional to the alkylamine length. As the lengths of propyl-, butyl- and hexyl-amine are ~4.1, 5.1 and 7.7 Å (Fig. 2i), respectively, the observed expansion of the interlayer gap suggests a head-to-tail monolayer arrangement of alkylamines between the layers31.
This alkylamine intercalation process proceeds through a monolayer arrangement at the initial stage, but after lengthened intercalation time, the intercalates start to adopt a bilayer arrangement between the layers. With the use of propylamine, the 2θ angle of the (001) peak position of TiS2 shifts from 15.5° to 8.9° at 45 min and 6.4° at 7 h (Fig. 3a). At the intermediate time of 3 h, the two peaks at 8.9° and 6.4° are simultaneously observed. These XRD results suggest that the TiS2 interlayer distance of 9.9 Å corresponds to a monolayer of propylamine, which subsequently changes to a bilayer formation (13.8 Å) through an intermediate state (3 h) (Fig. 3b). The intercalation modes of alkylamines follow monolayer to bilayer arrangements, and the interlayer gap widening can be controlled using different alkylamine intercalates. However, none of the layered TiS2 show spontaneous exfoliation even though the London-dispersion-corrected DFT calculation estimates a critical interlayer distance of ~11 Å to overcome the interlayer van der Waals interaction between two layers of pristine TiS2 (Fig. 3c). Our observation of non-exfoliation phenomenon is presumably due to the additional energy needed to overcome partially or fully interdigitated interactions between the alkyl chains of the intercalates (Fig. 3b)30,32,33.
Exfoliation of TMCs via TMI method
Here, we devised the TMI concept, where two different lengths of intercalates are utilized for the exfoliation of layered nanostructures. This TMI process has distinctive features, namely a short ‘initiator’ alkylamine first expands the interlayer gap for efficient intercalation of the ‘primary’ long alkylamine; the difference in the chain length, then, generates a bilayer arrangement with empty space between intercalates to reduce van der Waals force between them; and finally spontaneous exfoliation occurs (Fig. 4a). We examined the TMI concept for the exfoliation of multi-layer TiS2. By adding propylamine and hexylamine to colloidal TiS2 nanostructure in DMSO at room temperature, the intercalation of propylamine is observed with an expanded interlayer distance of 9.5 Å in 30 min (Fig. 4b), and the presence of intercalated propylamine is confirmed by 1H-NMR. Then, further expansion of the layer distance to 21 Å is observed in 6 h (Fig. 4c), and the coexistence of propylamine and hexylamine is confirmed by 1H-NMR. At this stage, the layers spontaneously begin to separate, and single-layer TiS2 nanosheets are obtained. Figure 4d,e show TEM images of single-layer TiS2 nanosheets after exfoliation. A top-view high-resolution TEM (HRTEM) image of a single-layer TiS2 nanosheet shows lattice fringes with interplanar spacings of 2.9 and 1.7 Å, corresponding to the (100) and (110) planes of the TiS2, respectively (Fig. 4f). The single-layer thickness of 8.0 Å is confirmed by AFM analysis (Fig. 4g). Additional XRD analysis shows single peak of (110) plane at 53.7° without any peaks in c axis direction, which confirms that final products are fully exfoliated single-layer TiS2 (Supplementary Figs 1a and 2b). Such experimental observations are in good agreement with the calculations based on density-functional tight-binding theory, which confirms that mixed intercalates of different chain lengths decrease the total interaction energy below 2kBT to have an effective exfoliation (Supplementary Fig. 3, Supplementary Tables 1–3).
Our tandem molecular exfoliation method can be applied to other colloidal nanoparticles of group IV, V and VI TMCs, such as ZrS2, NbS2 and WSe2. First, the exfoliation of multi-layer ZrS2 nanostructure (17 nm in lateral size and three layers) is examined (Fig. 5a,b). Although less explored than group VI counterparts, group IV TMCs also exhibit interesting single-layer properties such as enhanced thermoelectric property and electrical conductivity for TiS2 and strain-driven indirect-to-direct band gap transition of ZrS2 (refs 34, 35, 36). Similar to the case of TiS2, propylamine and hexylamine are added to ZrS2 nanostructure in DMSO with stirring at room temperature. After 4 h, the interlayer distance is expanded from 5.8 Å (Fig. 5b) to 20.5 Å (Fig. 5c). After 9 h, single-layer ZrS2 nanosheets are obtained after centrifugation (Fig. 5d). The thickness measured by TEM is ~6.0 Å, which is consistent with the estimated thickness of single-layer ZrS2 (Fig. 5e). A top-view HRTEM image of a single-layer ZrS2 nanosheet shows lattice fringes with interplanar spacings of 3.1 and 1.8 Å, corresponding to the (100) and (110) planes of the hexagonal 1T-ZrS2, respectively (Fig. 5f and Supplementary Fig. 2c). This TMI method with propyl- and hexylamine intercalates is also effective to group V NbS2 nanoparticles (Supplementary Fig. 4).
For the exfoliation of multi-layer WSe2 nanostructure, tandem intercalates with high Lewis basicity are chosen. Two different-length intercalates of sodium ethoxide and sodium hexanolate are added to multi-layer WSe2 nanostructure in DMSO. After stirring for 7 h at room temperature, single-layer WSe2 nanosheets are isolated by centrifugation. During the course of intercalation, the expansion of the 6.5 Å interlayer spacing of WSe2 (Fig. 6g) to 12.2 Å (Fig. 6h) suggests that ethoxide intercalation proceeds to form a bilayer arrangement between the layers. Figure 6f,i show low-magnification and magnified TEM images of single-layer WSe2 nanosheets after exfoliation, where a side view of standing single-layer WSe2 nanosheets is observed. This exfoliation process can be scaled up to sub-gram scale (Supplementary Fig. 5).
The choice of proper intercalates is critical to have their effective intercalation into TMCs. Intercalates act as Lewis base with highest occupied molecular orbital (HOMO) and TMCs act as Lewis acid with lowest unoccupied molecular orbital (LUMO). Therefore, as the HOMO–LUMO energy difference (ΔEHOMO–LUMO) is smaller, the more favoured their interaction becomes. Such HOMO–LUMO Lewis acid–base interaction can be generally applied to group IV and VI TMCs. LUMO of group VI TMCs (for example, MoS2, MoSe2, MoTe2, WS2, WSe2 and WTe2) is between −4.2 and −3.5 eV, which is in close energy level with HOMO (approximately −4.2 eV) of strong base alkoxides to have favoured interactions between them37,38. Similarly, LUMO of group IV TMCs (for example, TiS2, ZrS2, ZrSe2, HfS2 and HfSe2) is ranging from −6.0 to −5.5 eV, which is close to HOMO (approximately −6.2 eV) of relatively weaker base alkylamines37,38,39.
While our TMI method is most effective for the exfoliation of laterally small (<100 nm) TMC nanoparticles, it can be also extended to larger micron-size TMCs. For the exfoliation of micron-size TMCs (Fig. 7 and Supplementary Fig. 6), sodium ethoxide and hexanolate are added to a solution of MoS2 in DMSO. After stirring 48 h, single-layer MoS2 nanosheets over 1 μm are observed (Fig. 7). Similarly, micron-size multi-layer TMCs of WSe2 and TiS2 can also be exfoliated (Supplementary Figs 2a and 6). Although specific conditions (for example, time, type and concentration of intercalates, temperature and so on) should be further optimized for efficient exfoliation, this preliminary study indicates the potential of TMI method for large-size TMCs.
Discussion
In this study, we demonstrate that ‘tandem molecular intercalation (TMI)’ is an effective new concept for the exfoliation of multi-layer colloidal TMC nanostructures into single-layer TMC nanosheets. TMI is a relatively fast process for producing single-layer TMCs and is conducted at room temperature, with the clear merit of eliminating the occasional degradation of single-layer TMCs by avoiding harsh exfoliation processes. A variety of Lewis bases can be intercalated into TMC nanostructures, and group IV (TiS2 and ZrS2), group V (NbS2) and VI (WSe2, MoS2) TMCs require different types of intercalates. A relatively weaker Lewis base, such as alklyamine, works nicely for group IV and V TMCs, whereas a stronger Lewis base, such as alkoxide, is required for group VI TMCs. In principle, TMI can serve as a general strategy for the exfoliation of wide range of colloidal TMC nanostructures under mild exfoliation conditions, namely, a room-temperature process without sonication or H2 evolution.
Methods
Alkylamine chain length-dependent intercalation
Propylamine (0.07 ml, 0.91 mmol), pre-synthesized TiS2 (ref. 40; 0.05 mmol) and DMSO (5 ml) are added to a 10 ml vial. The mixture is stirred for 30 min at room temperature. The mixture is then precipitated by centrifugation at 3,000 r.p.m. for 30 min, and the precipitates are washed three times with chloroform. The intercalation conditions for other alkylamines are identical except for the intercalation time (1 h for butylamine and 5 h for hexylamine).
Exfoliation of multi-layer TMC nanostructures
Multi-layer colloidal TiS2 nanostructure (5.0 mg, 0.04 mmol)40, propylamine (3.0 ml, 36.5 mmol), hexylamine (2.0 ml, 15.1 mmol) and DMSO (5 ml) are mixed to a 10 ml vial and stirred for 10 h at room temperature. Then, the mixture is centrifuged at 3,000 r.p.m. for 30 min to precipitate non-exfoliated materials. The supernatant is re-centrifuged at 15,000 r.p.m. for 50 min to precipitate exfoliated TMCs. Then, chloroform (10 ml) is added to dissolve the precipitate and the resulting purple solution is centrifuged at 17,500 r.p.m. for 10 min. This process repeats several times and then the final product is dried under vacuum at room temperature for 2 h to afford exfoliated TiS2 (1.4 mg, 27%) as a purple powder.
The exfoliation of multi-layer ZrS2 follows similar procedures. Multi-layer colloidal ZrS2 nanostructure (5.0 mg, 0.03 mmol)40, propylamine (2.5 ml, 30.4 mmol), hexylamine (1.0 ml, 7.6 mmol) and DMSO (5 ml) are mixed to a 10 ml vial and stirred for 9 h at room temperature. Single-layer ZrS2 (1.6 mg, 32%) is obtained by following the same purification process of TiS2.
For the exfoliation of WSe2, multi-layer colloidal WSe2 nanostructure (10.0 mg, 0.03 mmol), sodium ethoxide (1.50 g, 22.0 mmol), sodium hexanolate (0.50 g, 4.03 mmol) and DMSO (15 ml) are mixed. After 7 h stirring, the mixture is centrifuged at 6,000 r.p.m. for 30 min to precipitate the non-exfoliated materials. Then the supernatant is re-centrifuged at 15,000 r.p.m. for 60 min to precipitate exfoliated TMCs. The precipitate is washed several times with ethanol via centrifugation at 17,500 r.p.m. for 20 min to give exfoliated WSe2 (3.3 mg, 33%).
Instruments
TEM and HRTEM analyses were performed using JEM 2100 at 200 kV and JEOL-ARM1300S at 1,250 kV, respectively. Atomic force microscopy (AFM) images were obtained in non-contact mode using a scanning probe microscope (Veeco). X-ray diffraction (XRD) studies were conducted using Rigaku-G2005304 equipped with a Cukα radiation source (30 kV, 15 mA). 1H-NMR spectra were obtained using a 400 MHz FT-NMR Spectrometer (Bruker Biospin).
Density-functional theory calculations
The DFT calculations were performed using the Amsterdam Density-Functional (ADF2013-BAND) package41,42. We used the local VWN exchange-correlation potential with nonlocal Perdew–Burke–Ernzerhof exchange-correlation correction and empirical D3 treatment of London dispersion interactions (PBE-D3-BJ)43.
Additional information
How to cite this article: Jeong, S. et al. Tandem intercalation strategy for single-layer nanosheets as an effective alternative to conventional exfoliation processes. Nat. Commun. 6:5763 doi: 10.1038/ncomms6763 (2015).
References
Yoffe, A. D. Layer compounds. Annu. Rev. Mater. Sci. 3, 147–170 (1973).
Frienda, R. H. & Yoffe, A. D. Electronic properties of intercalation complexes of the transition metal dichalcogenides. Adv. Phys. 36, 1–94 (1987).
Jaramillo, T. et al. Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Lukowski, M. A. et al. Enhanced hydrogen evolution catalysis from chemically exfoliated metallic MoS2 nanosheets. J. Am. Chem. Soc. 135, 10274–10277 (2013).
Splendiani, A. et al. Emerging photoluminescence in monolayer MoS2 . Nano Lett. 10, 1271–1275 (2010).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805-1–136805-4 (2010).
Kuc, A., Zibouche, N. & Heine, T. Influence of quantum confinement on the electronic structure of the transition metal sulfide TS2 . Phys. Rev. B 83, 245213-1–245213-4 (2011).
Lin, L. et al. Fabrication of luminescent monolayered tungsten dichalcogenides quantum dots with giant spin-valley coupling. ACS Nano 7, 8214–8223 (2013).
Novoselov, K. S. et al. Two-dimensional atomic crystals. Proc. Nat Acad. Sci. USA 102, 10451–10453 (2005).
Radisavljevic, B., Whitwick, M. B. & Kis, A. Integrated circuits and logic operations based on single-layer MoS2 . ACS Nano 5, 9934–9938 (2011).
Lin, L. et al. Fabrication and luminescence of monolayered boron nitride quantum dots. Small 10, 60–65 (2014).
Lin, L. & Zhang, S. Creating high yield water soluble luminescent graphene quantum dots via exfoliating and disintegrating carbon nanotubes and graphite flakes. Chem. Commun. 48, 10177–10179 (2012).
Dines, M. B. Lithium interacalation via n-butyllithium of the layered transition metal dichalcogenides. Mater. Res. Bull. 10, 287–292 (1975).
Joensen, P., Frindt, R. F. & Morrison, S. R. Single-layer MoS2 . Mater. Res. Bull. 21, 457–461 (1986).
Eda, G. et al. Photoluminescence from chemically exfoliated MoS2 . Nano Lett. 11, 5111–5116 (2011).
Zheng, J. et al. High yield exfoliation of two-dimensional chalcogenides using sodium naphthalenide. Nat. Commun. 5, 2995 (2014).
Zeng, Z. et al. An effective method for the fabrication of few-layer-thick inorganic nanosheets. Angew. Chem. Int. Ed. 51, 9052–9056 (2012).
Yuwen, L. et al. General synthesis of noble metal (Au, Ag, Pd, Pt) nanocrystal modified MoS2 nanosheets and the enhanced catalytic activity of Pd–MoS2 for methanol oxidation. Nanoscale 6, 5762–5769 (2014).
Bissessur, R., Kanatzidis, M. G., Schindlerb, J. L. & Kannewurf, C. R. Encapsulation of polymers into MoS2 and metal to insulator transition in metastable MoS2 . J. Chem. Soc. Chem. Commun. 1582–1585 (1993).
Gordon, R. A., Yang, D., Crozier, E. D., Jiang, D. T. & Frind, R. F. Structures of exfoliated single layers of WS2, MoS2, and MoSe2 in aqueous suspension. Phys. Rev. B 65, 125407-1–125407-9 (2002).
Coleman, J. N. et al. Two-dimensional nanosheets produced by liquid exfoliation of layered materials. Science 331, 568–571 (2011).
Zhou, K.-G., Mao, N.-N., Wang, H.-X., Peng., Y. & Zhang, H.-L. A mixed-solvent strategy for efficient exfoliation of inorganic graphene analogues. Angew. Chem. Int. Ed. 50, 10839–10842 (2011).
Smith, R. J. et al. Large-scale exfoliation of inorganic layered compounds in aqueous surfactant solutions. Adv. Mater. 23, 3944–3948 (2011).
Mashtalir, O. et al. Intercalation and delamination of layered carbides and carbonitrides. Nat. Commun. 4, 1716 (2013).
O’Neill, A., Umar, K. & Coleman, J. N. Preparation of high concentration dispersions of exfoliated MoS2 with increased flake size. Chem. Mater. 24, 2414–2421 (2012).
Gamble, F. R. et al. Intercalation complexes of Lewis bases and layered sulfides: a large of new superconductors. Science 174, 493–497 (1971).
Levy, F. Intercalated layered materials Springer Link (1979).
Chianelli, R. R., Scanlon, J. C. & Thompson, A. H. Structure refinement of stoichiometric TiS2 . Mater. Res. Bull. 10, 1379–1382 (1975).
Lagaly, G. Intercalation of alkylamines with different types of layered compounds. Solid State Ion 22, 43–51 (1986).
Whittingham, M. S. & Chianelli, R. R. Layered compounds and intercalation chemistry: an example of chemistry and diffusion in solids. J. Chem. Educ. 57, 569–574 (1980).
Ulman, A., Eilers, J. E. & Tillman, N. Packing and molecular orientation of alkanethiol monolayers on gold surfaces. Langmuir 5, 1147–1152 (1989).
Sieval, A. B., Hout, B. V. D., Zuilhof, H. & Sudhölter, E. J. R. Molecular modeling of covalently attached alkyl monolayers on the hydrogen-terminated Si(111) surface. Langmuir. 17, 2172–2181 (2007).
Zhang, R.-Z., Wan, C.-L., Wang, Y.-F. & Koumoto, K. Titanium sulphene: two-dimensional confinement of electrons and phonons giving rise to improved thermoelectric performance. Phys. Chem. Chem. Phys. 14, 15641–15644 (2012).
Lin., C. et al. Hydrogen-incorporated TiS2 ultrathin nanosheets with ultrahigh conductivity for stamp-transferrable electrodes. J. Am. Chem. Soc. 135, 5144–5151 (2013).
Li, Y., Kang, J. & Li, J. Indirect-to-direct band gap transition of the ZrS2 monolayer by strain: first-principles calculations. RSC Adv. 4, 7396–7401 (2014).
Gong, C. et al. Band alignment of two-dimensional transition metal dichalcogenides: application in tunnel field effect transistors. Appl. Phys. Lett. 103, 053513-1–053513-4 (2013).
NIST Standard Reference Database Number 101. http://cccbdb.nist.gov/ (accessed (25 August 2014).
Miro, P., Han, J. H., Cheon, J. & Heine, T. Hexagonal transition-metal chalcogenide nanoflakes with pronounced lateral quantum confinement. Angew. Chem. Int. Ed. 53, 12624–12628 (2014).
Jeong, S., Yoo, D., Jang, J.-t., Kim, M. & Cheon, J. Well-defined colloidal 2-D layered transition-metal chalcogenide nanocrystals via generalized synthetic protocols. J. Am. Chem. Soc. 134, 18233–18236 (2012).
Velde, G. T. & Baerends, E. J. Precise density-functional method for periodic structures. Phys. Rev. B 44, 7888–7903 (1991).
Wiesenekker, G. & Baerends, E. J. Quadratic integration over the three-dimensional Brillouin zone. J. Phys. Condens. Mater. 3, 6721–6742 (1991).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Acknowledgements
This work was financially supported by the National Creative Research Initiatives Program (2010-0018286).
Author information
Authors and Affiliations
Contributions
S.J., D.Y. and J.C. designed the experiments and analysed the data. S.J. and M.A. performed the synthesis and characterization. S.J., D.Y. and J.C. wrote the manuscript. P.M. and T.H. performed the density-functional theory calculations. All the authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-6, Supplementary Tables 1-3, Supplementary Methods and Supplementary References (PDF 309 kb)
Supplementary Data 1
TiS2-propylamine monolayer (XLS 149 kb)
Supplementary Data 2
TiS2-hexylamine bilayer (XLS 213 kb)
Supplementary Data 3
TiS2-propylamine/hexylamine bilayer (XLS 82 kb)
Rights and permissions
About this article
Cite this article
Jeong, S., Yoo, D., Ahn, M. et al. Tandem intercalation strategy for single-layer nanosheets as an effective alternative to conventional exfoliation processes. Nat Commun 6, 5763 (2015). https://doi.org/10.1038/ncomms6763
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms6763
- Springer Nature Limited
This article is cited by
-
Intercalation in 2D materials and in situ studies
Nature Reviews Chemistry (2024)
-
Synthesis of atomically thin sheets by the intercalation-based exfoliation of layered materials
Nature Synthesis (2023)
-
Engineering covalently bonded 2D layered materials by self-intercalation
Nature (2020)
-
Intercalation-assisted Exfoliation Strategy for Two-dimensional Materials Preparation
Chemical Research in Chinese Universities (2020)
-
Organically interconnected graphene flakes: A flexible 3-D material with tunable electronic bandgap
Scientific Reports (2019)