Abstract
Two-dimensional (2D) materials possess outstanding lubrication property with their thicknesses down to a few atomic layers, but they are easily susceptible to sliding induced degradation or ubiquitous chemical modification. Maintaining the superior lubricating performance of 2D materials in a harsh working environment is highly desirable yet grandly challenging. Here we show that by proper alignment of graphene on a Ge(111) substrate, friction of graphene could be well preserved at an ultra-low level even after fluorination or oxidation. This behaviour is experimentally found to be closely related to the suppression of molecular-level deformation of graphene within the moiré superlattice structure. Atomistic simulations reveal that the formation of an interconnected meshwork with enhanced interfacial charge density imposes a strong anchoring effect on graphene even under chemical modification. Modulating molecular-level deformation by interfacial confinements may offer a unique strategy for tuning the mechanical or even chemical properties of 2D materials.
Similar content being viewed by others
Introduction
Friction exists almost in every mechanical system with moving parts, and it becomes more prominent for small-scale devices due to their high surface to volume ratio. For many applications, it is often desirable to control and, in many cases, to minimize friction1. Unfortunately, lubricating solid contacts robustly remains a long-standing challenge especially at the micro- and nanoscale1,2. Recently, 2D materials have attracted much attention as they still exhibit superior lubrication property even with only a few atomic layers3,4,5. Despite the great potential as atomically thin lubricants, the lubrication performance of these 2D materials is easily deteriorated when subjected to chemical modifications stemming from the working environments or contact sliding6,7,8,9,10. For example, oxidation8, hydrogenation8 or fluorination9,10 from the external circumstance can easily lead to the dramatically increased friction of 2D materials. Preservation of ultra-low-friction state of 2D materials in various environments has become necessary and essential for practical tribological applications. Previous study has suggested that adhesive interaction between 2D materials and their substrates could influence the contact configuration via the puckering effect, thereby affecting friction4,11. In particular, it has shown that, compared with a weakly adherent substrate (silicon oxide), a highly adhesive and ultra-flat mica substrate can significantly reduce friction of graphene by suppressing the laminar-level puckering effect4.
In this work, we demonstrate that the moiré superlattice formed between graphene and germanium can impose a strong anchoring to cement the graphene to Ge substrate at the atomic scale. The interfacial confinement effectively suppresses the molecular-level deformation of graphene, and preserves the ultra-low-friction state even when the surface is actively fluorinated or oxidized. Therefore, our study suggests that the mechanical or even chemical properties of 2D materials can be tuned through interfacial confinements by modulating molecular-level deformation of 2D materials.
Results
Preservation of ultra-low-friction state on fluorinated graphene
In this work, a continuous film of monolayer polycrystalline graphene with a weak domain orientation preference12 was grown on Ge(111) through chemical vapour deposition. After growth, the graphene was exposed to SF6 plasma and its top surface was fluorinated as confirmed by Raman and X-ray photoelectron spectroscopies (see Supplementary Figs 1 and 2 and Supplementary Note 1). Lateral (friction) force images were taken with an atomic force microscope at ambient conditions, as schematically shown in Fig. 1a. The topographic image of the as-grown graphene is dominated by the morphology of the underlying Ge(111) surface with clear atomic steps (Fig. 1b). Friction on as-grown graphene (Fig. 1c) is ultra-low and rather uniform with its magnitude close to the previous reports4. In contrast, friction on graphene after fluorination becomes inhomogeneous and a clear contrast is observed. More specifically, friction of most areas (denoted as base) is significantly increased (Fig. 1d,f), which has been commonly observed in chemically functionalized graphene8,9,10. However, there coexist some randomly distributed islands (denoted as island), where surface friction remains ultra-low and is comparable to that of as-grown graphene (Fig. 1d,f). These low-friction island regions have no obvious morphological contrast compared with those high-friction base regions (Fig. 1e). This preservation of ultra-low-friction state of graphene after energetic functionalization (for example, fluorination) has not been reported based on our knowledge. The low-friction state on islands is reproducible for all fluorinated graphene(FGr)/Ge(111) samples tested (see Supplementary Fig. 3). In addition, similar friction contrast between island and base is always observed for different scanning velocities or under various normal loads (see Supplementary Fig. 4).
To explore the origin of the friction contrast on the FGr/Ge(111) heterostructure, we have taken detailed friction measurements across the base (high friction) and the island (low friction) regions, respectively. As shown in the lateral force image in Fig. 2a and the line traces in Fig. 2c, no regular atomic stick-slip can be observed in the high-friction base region suggesting a disordered nature of the surface10. However, in the island regions where the ultra-low-friction behaviour is preserved, atomic stick-slip can be clearly observed with a superposed long-range variation forming a sixfold symmetric superlattice structure, see Fig. 2b and the dotted trend lines in Fig. 2c. We also performed high-resolution friction measurements on as-grown graphene. Although clear stick-slip behaviour is always observed, the lateral force images on the as-grown graphene reveal two distinct types of regions: one without visible superlattice (Fig. 2d) and one with visible superlattice (Fig. 2e,f). Although the detailed mechanism for the long-range variation is less clear, it can originate from a periodically undulated energy corrugation13 or stiffness14. Intuitively, the contrast between Fig. 2a,b seems to associate with the presence of the superlattice structure.
Moiré pattern and evolution of molecular structure revealed by STM
The impact of superlattice structure on friction was further investigated by scanning tunnelling microscopy (STM). The STM image from the island region (see Fig. 3a) indicates that the superlattice structure in the lateral force image (Fig. 2e) coincides with the moiré pattern formed between graphene and Ge(111). Moiré pattern often appears for single crystal surfaces with periodic overlayers15,16,17. Considering the lattice mismatch (38.5%) between graphene and Ge(111), the moiré pattern will have a periodical length of ∼4 nm when graphene is aligned on Ge(111). Because increasing relative rotation angle leads to rapid decrease of its periodical length, moiré patterns are only visible in STM images for regions where graphene and Ge(111) lattices are nearly aligned (see Supplementary Fig. 5 and Supplementary Note 2). Representative three dimensional (3D) STM topographic images collected at constant-current mode on both as-grown and fluorinated films are compared in Fig. 3a,b. Large out-of-plane deformation of the graphene surface can be clearly observed in the base regions of the fluorinated samples, while the morphology of the island regions with moiré pattern barely changes after fluorination (see more in Supplementary Fig. 6). The atomically resolved STM images of the base regions indicate that the molecular-level deformation occurs (comparing with as-grown graphene in Fig. 3d) with severe non-uniform lattice distortion and wrinkles or even ridges (Fig. 3f and the inset). In contrast, similar to the as-grown graphene (Fig. 3c), only negligible lattice distortion or wrinkling is found in the island regions with visible moiré pattern after fluorination (Fig. 3e). Extensive tribological studies5,18,19,20,21 have shown that sliding on a disordered and corrugated surface or interface usually leads to higher friction and more energy dissipation. Therefore, we speculate that the preservation of ultra-low-friction state may be attributed to less degree of fluorination or strongly suppressed molecular-level deformation of graphene in regions with a moiré pattern.
Recent studies have reported that presence of moiré pattern may noticeably affect the self-assembly process of adatom clusters22 and change the catalytic activity on surfaces23. To check whether the less molecular deformation in regions with moiré pattern was due to less degree of fluorination, we performed further STM measurements to distinguish the fluorination levels for the fluorinated samples. Theoretical works have predicted that various CnF structures formed during fluorination process could open the energy bandgap of graphene24, resulting in local density of states with different energy levels. The tunnelling current at CnF structures with narrower energy bandgap can be induced by relatively low-bias voltages of STM, while high-bias voltages are required for the tunnelling of CnF structures with wider energy bandgap. For as-grown graphene on Ge(111), a moiré pattern is clearly visible by STM with sweeping bias voltages (100–500 mV) (Fig. 4a). However, the STM tunnelling current mapping of FGr (both with/without moiré pattern regions) under variable bias voltages Vb (100–800 mV) shows obvious tunnelling protrusions (increased tunnelling current) induced by fluorine attachment and the protrusion density increases markedly with increasing sample bias as show in Fig. 4b,c. From the comparison between Fig. 4b,c, it appears that the number of fluorination sites in the regions with a moiré pattern is not significantly different from that in the regions without a moiré pattern, although the distribution seems to be slightly more regular in the former case22,25. The STM results, together with adhesion measurements from regions with and without a moiré pattern (see Supplementary Figs 7 and 8 and Supplementary Note 3), essentially exclude different degree of fluorination as a primary mechanism for the observed friction contrast in the two regions.
Discussion
To investigate the possible confinement effect from the moiré pattern, density functional theory (DFT) calculations of graphene on Ge(111) substrate were performed. The relaxed morphology (Fig. 5a-I) shows a moiré pattern consisting of domain regions (peak) isolated by domain walls (valley) when a rotation angle of 2.2° (nearly aligned case with the periodical length of 3.2 nm, close to the experimental value) is imposed. The morphological undulation coincides with the periodic distribution (Fig. 5a-III) of interfacial charge density, which is an essential indication of the interaction strength between graphene and Ge substrate26. Consistent with the experimental observations (see Supplementary Fig. 9), the interfacial charge density is more enhanced in domain wall compared with that in the domain region. This enhanced interaction at the domain wall region is associated with the local interlayer stacking geometry: larger projected overlaps between C atoms of graphene and Ge atoms of substrate results in stronger interaction, as highlighted by the dotted circle in domain wall regions (Fig. 5b). In contrast, when the interface is highly misaligned at a large rotation angle, for example, 30°, the morphological undulation and moiré pattern becomes barely visible (Fig. 5a-II)27 and the corresponding charge density is sparsely distributed at the interface (Fig. 5a-IV). In the nearly aligned case, the interconnected domain wall regions with enhanced interfacial charge density spread collectively over the substrate, which acts as an extended meshwork to tightly anchor the graphene onto the substrate26,28. This unique anchoring effect becomes more evident when a fluorine atom is added to mimic the fluorination process. As shown in Fig. 5b, adding F atom tends to pull the neighbouring C atoms up due to the sp2–sp3 rehybridization. In the nearly aligned case, the local out-of-plane deformation is noticeably suppressed due to the anchoring effect; while the anchoring effect is attenuated in the misaligned case, resulting in a larger deformation (see lower panel of Fig. 5b). We have to note here that the periodic boundary condition for relatively small unit cell imposed in the DFT calculations and the limitation of adding single fluorine atom may underestimate the difference in deformation between the two cases. In real experiments, the molecular-level deformation of graphene lattice without moiré pattern can be much more pronounced than that with moiré pattern as exhibited by the STM images (Fig. 3e,f), which is schematically depicted in Fig. 5c. Previously, both experimental and theoretical studies have shown that disordered and defective surfaces usually exhibit larger friction compared with an ordered and defect-free surfaces, primarily due to the increase of the number and type of low-energy modes or stronger corrugation of the lateral potential19,29,30. Therefore, sliding on the misaligned regions will result in a much higher friction because of the disordered and the highly corrugated nature of the surface, while friction in the aligned regions could be much lower due to suppression of molecular-level deformation by the anchoring effect (Fig. 5c).
Different anchoring effect in the regions with and without moiré pattern might result in different dynamic responses when the graphene surface was slid by a tip. This in turn might cause different velocity dependence of friction on different regions. However, as shown in Supplementary Fig. 4, we did not see a clear variation trend of friction on sliding speed, which may be due to the relatively small domain size and/or high speeds adopted in our tests. In addition, because friction on as-grown samples was rather low with relatively large uncertainties, a more compliant/sensitive probe might also be needed to better distinguish the subtle variation in future study. Nevertheless, our work clearly demonstrates that the friction contrast between regions with and without a moiré pattern after graphene fluorination was always high and did not change qualitatively with the tip scanning speed.
The anchoring effect, which originates from the interconnected domain wall meshwork of the moiré pattern in the graphene/Ge(111) heterostructure, may be generally applied to preserve the ultra-low-friction state of graphene when utilized in other chemically aggressive environments. This was indeed confirmed by the friction behaviour of oxidized graphene/Ge(111) structure: the regions with moiré superlattice did preserve ultra-low-friction state of graphene as well (see Supplementary Figs 10 and 11 and Supplementary Note 4). Therefore, the formation of moiré superlattice between 2D material and a substrate is an effective strategy to maintain the superior lubrication property of 2D material in a harsh chemical environment. With recent advances in synthesis of large-scale 2D films with precisely controlled interfacial structures for various materials27,31,32,33,34, our finding potentially opens a unique route of tuning the nanomechanical properties of 2D materials systems for a wide variety of applications.
Methods
Samples preparation
P-type Ge(111) (175 μm thick, AXT) substrates with resistivity of 0.01–0.05 Ohm cm were used in the experiments. The graphene film was synthesized by chemical vapour deposition in a horizontal tube furnace with H2: CH4: Ar=0.73: 23: 230 s.c.c.m. at the growth temperature of 916 °C for 300 min. Fluorination of graphene was performed by exposing the sample into the SF6 plasma for 3 min in the OXFORD Plasma Lab system-100. To suppress the effect of ion bombardment to graphene, the sample was placed ‘face down’ (graphene faced towards the bottom electrode) using a quartz holder. The SF6 flow rate was set as 40 s.c.c.m. and the plasma power was 50 W (bias voltage ∼23 V). During fluorination, the chamber pressure and temperature of the sample stage were 96 mTorr and 60 °C, respectively.
Samples measurements
Bruker Multimode 8 system was applied to perform the friction, height, pull-off force measurements and STM at ambient conditions (temperature ∼22 °C, relative humidity ∼30%). During lateral force microscopy measurements, silicon probes with nominal tip radius of curvature ∼2 nm (SNL-10, Bruker) were chosen. Deflection sensitivity of the probe is 33.66 nm V−1 and the spring constant at the room temperature is 0.35 N m−1. Lateral force microscopy images were obtained simultaneously with the topographic images. The friction force was calculated by subtracting the forward and backward friction signals on each scan line and divided by two. The normal and lateral force were calibrated using the ramp mode35 and the diamagnetic levitation spring system36. High-resolution lateral force images in Fig. 2 in the main text were acquired with an atomic force microscope (NT-MDT spectrum Instruments) in a dry N2 environment with a Si tip (CSC37, MikroMasch). STM images were acquired with a platinum–iridium (Pt–Ir) alloy tip in normal ambient under the constant-current mode.
First-principles calculations
The DFT calculations with a non-local optB86b-vdW exchange-correlation functional37,38 were performed using the Vienna ab initio Simulation Package39. The projector-augmented-wave method was utilized to model the core electrons. The energy cutoff of the expanded wave functions was set to 400 eV. A 32 × 32 × 30 Å slab supercell containing three-layer Ge(111) atoms and monolayer graphene with a vacuum gap of more than 19 Å was used. The rotation angles between graphene and Ge(111) substrate were selected as 2.2° and 30°. The graphene and top Ge(111) layer were allowed to relax until the forces on all the relaxed atoms were less than 0.02 eV Å−1. All the calculations were done using experimental Ge lattice constant (a=5.6575 Å).
Data availability
The data that support the findings of this study are available from the corresponding authors on request.
Additional information
How to cite this article: Zheng, X. et al. Robust ultra-low-friction state of graphene via moiré superlattice confinement. Nat. Commun. 7, 13204 doi: 10.1038/ncomms13204 (2016).
References
Carpick, R. W. Controlling friction. Science 313, 184–185 (2006).
Vanossi, A. et al. Colloquium: modeling friction: from nanoscale to mesoscale. Rev. Mod. Phys. 85, 529–552 (2013).
Spear, J. C., Ewers, B. W. & Batteas, J. D. 2D-nanomaterials for controlling friction and wear at interfaces. Nano Today 10, 301–314 (2015).
Lee, C. et al. Frictional characteristics of atomically thin sheets. Science 328, 76–80 (2010).
Filleter, T. et al. Friction and dissipation in epitaxial graphene films. Phys. Rev. Lett. 102, 086102 (2009).
Won, M.-S., Penkov, O. V. & Kim, D.-E. Durability and degradation mechanism of graphene coatings deposited on Cu substrates under dry contact sliding. Carbon 54, 472–481 (2013).
Gardos, M. N. The synergistic effects of graphite on the friction and wear of MoS2 films in air. Tribol. Trans. 31, 214–227 (1988).
Ko, J.-H. et al. Nanotribological properties of fluorinated, hydrogenated, and oxidized graphenes. Tribol. Lett. 50, 137–144 (2013).
Kwon, S. et al. Enhanced nanoscale friction on fluorinated graphene. Nano Lett. 12, 6043–6048 (2012).
Li, Q. et al. Fluorination of graphene enhances friction due to increased corrugation. Nano Lett. 14, 5212–5217 (2014).
Li, Q. Y., Lee, C., Carpick, R. W. & Hone, J. Substrate effect on thickness-dependent friction on graphene. Phys. Status Solidi B 247, 2909–2914 (2010).
Lee, J.-H. et al. Wafer-scale growth of single-crystal monolayer graphene on reusable hydrogen-terminated germanium. Science 344, 286–289 (2014).
Li, Q., Dong, Y., Martini, A. & Carpick, R. W. Atomic friction modulation on the reconstructed Au(111) surface. Tribol. Lett. 43, 369–378 (2011).
Koch, S. et al. Elastic response of graphene nanodomes. ACS Nano 7, 2927–2934 (2013).
Xue, J. et al. Scanning tunnelling microscopy and spectroscopy of ultra-flat graphene on hexagonal boron nitride. Nat. Mater. 10, 282–285 (2011).
Yankowitz, M. et al. Emergence of superlattice Dirac points in graphene on hexagonal boron nitride. Nat. Phys. 8, 382–386 (2012).
Ponomarenko, L. A. et al. Cloning of Dirac fermions in graphene superlattices. Nature 497, 594–597 (2013).
Wang, X. et al. Uniaxial strain redistribution in corrugated graphene: clamping, sliding, friction, and 2D band splitting. Nano Lett. 15, 5969–5975 (2015).
Dong, Y. L., Wu, X. W. & Martini, A. Atomic roughness enhanced friction on hydrogenated graphene. Nanotechnology 24, 375701 (2013).
Ouyang, W., Ma, M., Zheng, Q. & Urbakh, M. Frictional properties of nanojunctions including atomically thin sheets. Nano Lett. 16, 1878–1883 (2016).
Filleter, T. & Bennewitz, R. Structural and frictional properties of graphene films on SiC(0001) studied by atomic force microscopy. Phys. Rev. B 81, 155412 (2010).
N’Diaye, A. T., Bleikamp, S., Feibelman, P. J. & Michely, T. Two-dimensional Ir cluster lattice on a graphene moiré on Ir(111). Phys. Rev. Lett. 97, 215501 (2006).
Deng, D. et al. Catalysis with two-dimensional materials and their heterostructures. Nat. Nano 11, 218–230 (2016).
Sahin, H., Topsakal, M. & Ciraci, S. Structures of fluorinated graphene and their signatures. Phys. Rev. B 83, 115432 (2011).
Boukhvalov, D. W. & Katsnelson, M. I. Enhancement of chemical activity in corrugated graphene. J. Phys. Chem. C 113, 14176–14178 (2009).
Busse, C. et al. Graphene on Ir(111): physisorption with chemical modulation. Phys. Rev. Lett. 107, 036101 (2011).
Woods, C. R. et al. Commensurate-incommensurate transition in graphene on hexagonal boron nitride. Nat. Phys. 10, 451–456 (2014).
Martoccia, D. et al. Graphene on Ru(0001): A 25*25 supercell. Phys. Rev. Lett. 101, 126102 (2008).
Gosvami, N. N., Egberts, P. & Bennewitz, R. Molecular order and disorder in the frictional response of alkanethiol self-assembled monolayers. J. Phys. Chem. A 115, 6942–6947 (2011).
Lio, A., Charych, D. H. & Salmeron, M. Comparative atomic force microscopy study of the chain length dependence of frictional properties of alkanethiols on gold and alkylsilanes on mica. J. Phys. Chem. B 101, 3800–3805 (1997).
Haigh, S. J. et al. Cross-sectional imaging of individual layers and buried interfaces of graphene-based heterostructures and superlattices. Nat. Mater. 11, 764–767 (2012).
van Wijk, M. M., Schuring, A., Katsnelson, M. I. & Fasolino, A. Moiré patterns as a probe of interplanar interactions for graphene on h-BN. Phys. Rev. Lett. 113, 135504 (2014).
Kim, C.-J. et al. Chiral atomically thin films. Nat. Nanotechnol. 11, 520–524 (2016).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Hutter, J. L. & Bechhoefer, J. Calibration of atomic-force microscope tips. Rev. Sci. Instrum. 64, 1868–1873 (1993).
Li, Q., Kim, K.-S. & Rydberg, A. Lateral force calibration of an atomic force microscope with a diamagnetic levitation spring system. Rev. Sci. Instrum. 77, 065105 (2006).
Klimeš, J., Bowler, D. R. & Michaelides, A. Van der Waals density functionals applied to solids. Phys. Rev. B 83, 195131 (2011).
Klimeš, J., Bowler, D. R. & Michaelides, A. chemical accuracy for the van der Waals density functional. J. Phys. Condens. Matter 22, 022201 (2010).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Acknowledgements
We acknowledge the financial support from Creative Research Groups of National Natural Science Foundation of China (No. 61321492), National Natural Science Foundation of China under Grant (No. 61274136, 11422218, 11272177 and 51527901), the National Basic Research Program of China (2013CB933003, 2013CB934201 and 2015CB351903), Postdoctoral Science Foundation of China (No. 2015M581678), the Tsinghua University Initiative Scientific Research Program (2014Z01007) and the Cyrus Tang Foundation (No. 202003) and Program of Shanghai Academic/Technology Research Leader (16XD1404200).
Author information
Authors and Affiliations
Contributions
X.Z. and Q.Y. performed the friction test experiments. X.Z. performed the fluorination and STM experiments. L.G. carried out the first-principles calculations. Z.D., Q.L. and T.M. supervised the research. X.Z., L.G., Q.L., T.M. and Z.D. wrote the paper. All authors contributed to discussions of the results.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-11, Supplementary Notes 1-4 and Supplementary References (PDF 1928 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zheng, X., Gao, L., Yao, Q. et al. Robust ultra-low-friction state of graphene via moiré superlattice confinement. Nat Commun 7, 13204 (2016). https://doi.org/10.1038/ncomms13204
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms13204
- Springer Nature Limited
This article is cited by
-
A Comparative Study on the Anti-Friction Performance of Amorphous Silicon Films Enhanced by WS2 Nanoflakes
Silicon (2023)
-
Phononic origin of structural lubrication
Friction (2023)
-
Electronic friction and tuning on atomically thin MoS2
npj 2D Materials and Applications (2022)
-
Tip-Based Nanomachining on Thin Films: A Mini Review
Nanomanufacturing and Metrology (2022)
-
Electro-lubrication in Janus transition metal dichalcogenide bilayers
Friction (2022)