Abstract
Ultra-high molecular weight polyethylene (UHMWPE) has been broadly utilized in hip and knee artificial implant due to its low friction coefficient, high wear resistance and good biocompatibility. However, some disadvantage properties such as low young’s modulus and low load bearing, anti-fatigue capacity limit application areas and wear debris of UHMWPE components cause implant failure. For this reason, reduced graphene oxide (RGO) filler was produced by green synthesis with vitamin C and the influences of RGO filler content on the tribological performance under distilled water lubrication condition were investigated and had been correlated with microstructure. RGO filled UHMWPE biocomposites were fabricated by firstly liquid phase ultrasonic mixing and then hot press molding. The characterization and experiment results revealed that the wear behavior of UHMWPE/RGO biocomposites were not only affected by the lubricant and binder properties of RGO, but also restricted by the content of RGO filler. The RGO filled UHMWPE biocomposites exhibited a lower wear rate and friction coefficient in comparison to the unfilled UHMWPE. The biocomposite with 0.7 wt% of RGO showed good interfacial bonding strength and excellent wear resistance. Furthermore, fatigue wear tracks reduced significantly on the same biocomposite surface. High crystallite size and microhardness value of UHMWPE/RGO-0.7 biocomposite was caused destroy the tribofilm formed on the Al2O3 counterface.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
Recently, polymer matrix composites were found ever-rising tribological applications such as gears, bearings, seals and artificial joints instead of metals due to their advantages such as low density, easy manufacturability, superior shock, high vibration and self-lubrication [1, 2]. UHMWPE has been widely used for artificial joints due to its clinical performances in the last two decades [3, 4]. On the other hand, UHMWPE has low Young’s modulus, low load bearing and anti-fatigue capacity [5]. Therefore, efforts have been put on to improve tribological performances of UHMWPE. Incorporation of fillers to overcome shortcomings of the UHMWPE matrix is a promising solution [6]. For this purpose, composite materials were produced using inorganic fillers such as kaolin, zirconium, nano zinc oxide and also, various organic fillers, including carbon fiber, carbon black and carbon nanotubes have been investigated in UHMWPE matrix due to their good surface adherence and better solid lubrication properties. However, these fillers limited their application at UHMWPE composites because of high cost and inadequate performance of composites in artificial joints [5]. Graphene has attracted as an ideal filler recently because of its special properties graphene has potential applications in many fields such as composite materials [7]. Commonly, graphene derivatives such as graphene oxide (GO), reduced graphene oxide (RGO), graphene nanoplates (GNP) and multi-layer graphene (MLG) are widely used as fillers for polymer composite materials [8]. GO is prepared from oxidation of graphite powder by Hummers method and RGO is synthesized from the reduction process of GO. Usually, GO and RGO are more preferred than other graphene derivatives due to their hydrophilicity, ease of formation of stable colloidal suspensions and easy-inexpensive synthesis [9]. At the same time, they have antibacterial properties and they were often used for biomedical applications recently [10]. There are studies to investigate tribological properties of UHMWPE composites by using GO [5, 11,12,13] and GNP [14, 15] but to the best of our knowledge, there are no report on the green synthesis of RGO for UHMWPE and their effects on the tribological properties of UHMWPE biocomposites, in the literature. Bhattacharyya et al. reported that UHMWPE nanocomposite films was produced with RGO using two different process routes. But they used phenylhydrazine as reduction agent. Phenylhydrazine that hydrazine derivative is highly toxic and instability. Therefore, it is not suitable for biomaterial application areas whether excess hydrazine is not removed [16]. In this paper, RGO filler was produced by green synthesis with vitamin C. RGO filled UHMWPE biocomposites were prepared, and the effect of the RGO content of the biocomposites on the structural and tribological properties under distilled water lubrication conditions were investigated. As a consequence, tribological and mechanical properties of UHMWPE can be altered by changing loading content of RGO. Moreover, the synthesized RGO may be a good candidate for UHMWPE based biomaterials.
2 Experimental methods
Firstly, GO was prepared by oxidizing the graphite powder according to a modified Hummers’ method [8, 17]. The detailed information about the reduction process of GO was described in previous literature [18]. UHMWPE/RGO biocomposites of different weight percentage of RGO to UHMWPE were prepared as follows: In brief, as-prepared powder RGO were sonicated for 30 min in ethyl alcohol using a homogenizer to form a well dispersed suspension. After that, UHMWPE powders were added into the suspension and the mixture was stirred for 30 min and then sonicated for 1 h. Then the ethyl alcohol was removed at 60–70 °C in an oil bath and the biocomposite powders were dried in an oven at 60 °C. Finally, the unfilled UHMWPE and biocomposite powders were molded by hot-pressing at 180 °C under a 10 MPa pressure and holding at this pressure for 30 min. In order to investigate the effects of RGO on the tribological properties of the biocomposites with the RGO content of unfilled, 0.7 and 3.0 wt% RGO were prepared. The codes of unfilled UHMWPE and these two biocomposites were UHMWPE, UHMWPE/RGO-0.7 and UHMWPE/RGO-3.0. The crystallinity of the biocomposites were represented by X-ray diffraction (XRD) patterns acquired by a PAN analytical, Empyrean diffractometer using Cu Kα radiation in the angle range 2θ = 5–30°. The molecular structure of the biocomposites were characterized by Fourier transfer infrared spectroscopy (FTIR) spectra which is recorded by a Spectrum 100, Perkin Elmer between 400 and 4000 cm−1. Shimadzu microhardness tester was used to measure the hardness of the biocomposites prepared. The hardness values were calculated based on the Vickers method with a load of 25 g. At least ten successive measurements were performed for each condition. The scanning electron microscope (SEM) (Zeiss, Supra 40VP) and energy-dispersive X-ray spectrometry (EDS) were used to observe morphology and worn surfaces of the biocomposites. A ball-on-disc reciprocating tribometer was used for all friction and wear tests. Wear tests were performed in a reciprocating mode with a 1.7 cm s−1 sliding rate under 5 N applied load for 45 min. The counter body was an Al2O3 ball with 10 mm diameter. Following the wear tests, the Al2O3 counterface surfaces were examined under an optical microscope (OM) in order to investigate the wear mechanisms.
3 Results and discussion
Figure 1 showed the XRD diffractograms of unfilled UHMWPE and UHMWPE/RGO biocomposites. The two peaks at 2θ° = 21.56 and 2θ° = 23.92, that appear in all diffractograms, correspond to the (110) and (200) planes of the orthorhombic crystal [19]. Inclusion of 0.7 wt% and 3.0 wt% RGO filling reduced the intensity of both UHMWPE peaks, which could be attributed to modification of matrix crystallinity [20]. The values of crystallite size of unfilled UHMWPE and UHMWPE/RGO biocomposites for 2θ = 23.92°, were shown in Fig. 1. It is observed that 0.7 wt% RGO contents results in increase of crystallite size achieving 100%, for comparison biocomposite with 3.0 wt% RGO and unfilled polymer. The increase of crystalline size in the UHMWPE/RGO-0.7 biocomposite and subsequently will affect the wear behavior of the biocomposite. Because the low RGO amount was act as nucleation centers and not disruptive reorganization and chain folding during crystallization process [21]. Additionaly, there is no new diffraction peak were observed in the patterns of biocomposites except the orthorhombic crystal peaks of unfilled polymer. This clearly indicated that RGO was exfoliated in the UHMWPE matrix [4, 22].
Figure 2 showed the FTIR spectra of the UHMWPE and UHMWPE/RGO biocomposites. The peaks of 2915.92 cm−1, 2848.69 cm−1, 1463.04 cm−1 and 718.47 cm−1 were attributed to the CH asymmetric vibration, the CH symmetric vibration, the CH2 the bending vibration and CH2 rocking vibration, respectively, for the unfilled UHMWPE. The strength of the peaks at 2915.92 cm−1, 2848.69 cm−1, 1463.04 cm−1 and 718.47 cm−1 enhanced with low and high amounts of RGO, which possibly indicated that more interaction between RGO and UHMWPE matrix [23].
Figure 3 showed the SEM images of the surfaces of UHMWPE/RGO biocomposites with different amounts of RGO and EDS elemental map of carbon and oxygen. It could be seen that the surface of UHMWPE/RGO-0.7 was relatively flat but also it had uneven regions. The image of this biocomposite showed RGO were embedded into the UHMWPE matrix so that good interfacial bonding strength exhibited between RGO and UHMWPE [14]. Furthermore, as the content of RGO increased to 3.0 wt%, the morphology of the surface was totally different. The UHMWPE/RGO-3.0 biocomposite exhibited an obviously rough and deformed morphology. As a result, the reorganization and chain folding of the polymer was hindered by the increasing content of RGO. In the XRD analysis section discussed the low amount of the RGO that caused nucleation centers by using crystallite size data. The EDS elemental mapping of biocomposites confirms that oxygen was uniformly distributed in the biocomposites. The dispersion of oxygen is very important because only RGO have oxygen containing functional groups. The results obtained from the EDS are compatible with XRD results.
Table 1 showed that the microhardness, wear rate and friction coefficient values of unfilled UHMWPE and biocomposites under distilled water lubricating condition. Hardness of the biocomposites increased at all RGO loading content and when the loading content is 0.7 wt%, biocomposite had the best microhardness value in contrast to that of unfilled UHMWPE. The distribution of RGO in polymer matrix, as discussed in EDS analysis and XRD sections, may result in an increase of resistance to indentation [18]. It could be seen that the wear rate of all the biocomposites filled with RGO were lower than that of unfilled UHMWPE. Also, it was observed that the low amount of RGO that resulted in the maximum wear resistance. These results may be attributed to the excellent mechanical properties and high specific surface area of RGO, which facilitates good load transfer to the RGO network [12]. It could be seen that after adding the content of RGO into UHMWPE matrix, the friction coefficient of biocomposites decreased significantly. Both RGO and distilled water displayed lubricant properties because of homogeneous dispersion of RGO in the UHMWPE matrix and good interaction of filler and polymer matrix according to XRD, EDS and FTIR analysis results [15, 24].
Figure 4 showed the effects of different amount of RGO on the worn surface of biocomposites. In the low magnified image, it could be seen that the worn surface of unfilled UHMWPE were thin and superficial grooves under deionized water. The fatigue wear was found dominant where the cracked surface layer of the unfilled UHMWPE in the high magnified image. The low and high magnified images of UHMWPE/RGO-0.7 showed that the wear marks due to the grooves were disappeared and lead to severe adhesive wear. When the RGO filler loading was increased to 3.0 wt% the worn surfaces seemed to be severe adhesive wear in the low magnified image. Additionally, from the high magnified image shown in Fig. 4, it is clear that adhesive wear tracks and significant fatigue tear increased on surface of biocomposite. As a result, with the decrease in friction surface temperature, plastic deformation was not observed on the surface of biocomposites in the distilled water condition [25].
OM analyses of the morphologies of Al2O3 counterface under distilled water lubricated conditions were evaluated in Fig. 5a, c. Interfacial interactions between the polymer and filler played an important role in tribofilms formation [26]. Unfilled UHMWPE have a thin and uniform transfer film on the Al2O3 ball (Fig. 5a). When sliding occurred under distilled water lubricated condition, a robust tribofilm generated from UHMWPE/RGO-3.0 (Fig. 5c) and a patchy tribofilm produced from UHMWPE/RGO-0.7 were observed (Fig. 5b), which led to a lower wear rate of biocomposite with 0.7 wt% of RGO than that of biocomposite with 3.0 wt% of RGO. The strongly interfacial interactions between UHMWPE with RGO and high crystallite size amount of UHMWPE/RGO-0.7 biocomposite under distilled water condition was prone to destroy the tribofilm formed on Al2O3 surface.
4 Conclusions
RGO filled UHMWPE biocomposites were successfully fabricated and assessed in terms of tribological performance under distilled water lubrication condition. The following conclusions can be obtained from above studies.
-
FTIR results showed that there was interaction between the RGO and UHMWPE. It could be affirmed homogenous dispersion of the RGO in the UHMWPE matrix and crystallite size achieving 100% in UHMWPE/RGO-0.7 biocomposite as confirmed by XRD analysis.
-
SEM images showed that RGO were embedded into the UHMWPE matrix so that good interfacial bonding strength exhibited between RGO and UHMWPE in UHMWPE/RGO-0.7 biocomposite. The EDS elemental mapping of biocomposites confirms that oxygen was uniformly distributed in the all biocomposites.
-
The addition of RGO with small amounts was obviously increased the microhardness and the biocomposite with 0.7 wt% RGO had the best microhardness value.
-
The fatigue wear tracks and wear rate were significantly reduced when RGO was added up to 0.7 wt%.
-
With the RGO content increases, the frictional coefficient of the biocomposites were decreased. It is due to an efficient load transfer from the matrix to the filler.
References
Shi G, Cao Z, Yan X, Wang Q (2019) In-situ fabrication of a UHMWPE nanocomposite reinforced by SiO2 nanospheres and its tribological performance. Mater Chem Phys 236:1–9. https://doi.org/10.1016/j.matchemphys.2019.121778
Zoo Y-S, An J-W, Lim D-P, Lim D-S (2004) Effect of carbon nanotube addition on tribological behavior of UHMWPE. Tribol Lett 16:305–309. https://doi.org/10.1023/B:TRIL.0000015206.21688.87
Melk L, Emami N (2018) Mechanical and thermal performances of UHMWPE blended vitamin E reinforced carbon nanoparticle composites. Compos B 146:20–27. https://doi.org/10.1016/j.compositesb.2018.03.034
Pang W, Ni Z, Chen G, Huang G, Huang H, Zhao Y (2015) Mechanical and thermal properties of graphene oxide/ultrahigh molecular weight polyethylene nanocomposites. RSC Adv 77:63063–63072. https://doi.org/10.1039/C5RA11826C
Tai Z, Chen Y, An Y, Yan X, Xue Q (2012) Tribological behavior of UHMWPE reinforced with graphene oxide nanosheets. Tribol Lett 46:55–63. https://doi.org/10.1007/s11249-012-9919-6
Salari M, Taromsari SM, Reza Bagheri, Sani MAF (2019) Improved wear, mechanical, and biological behavior of UHMWPE-HAp-zirconia hybrid nanocomposites with a prospective application in total hip joint replacement. J Mater Sci 54:4259–4276. https://doi.org/10.1007/s10853-018-3146-y
Guo Y, Sun X, Liu Yu, Wang W, Qiu H, Gao J (2012) One pot preparation of reduced graphene oxide (RGO) or Au (Ag) nanoparticle-RGO hybrids using chitosan as a reducing and stabilizing agent and their use in methanol electrooxidation. Carbon 50:2513–2523. https://doi.org/10.1016/j.carbon.2012.01.074
Mindivan F (2015) The synthesis, thermal and structural characterization of polyvinylchloride/graphene oxide (PVC/GO) composites. Mater Sci Non-Equilib Phase Transform 3:33–36
Vadukumpully S, Paul J, Mahanta N, Valiyaveettil S (2011) Flexible conductive graphene/poly(vinyl chloride) composite thin films with high mechanical strength and thermal stability. Carbon 49:198–205. https://doi.org/10.1016/j.carbon.2010.09.004
Sandhya PK, Jose J, Sreekala MS, Padmanabhan M, Kalarikkal N (2018) Reduced graphene oxide and ZnO decorated graphene for biomedical applications. Ceram Int 44:15092–15098. https://doi.org/10.1016/j.ceramint.2018.05.143
Vadivel HS, Golchin A, Emami N (2018) Tribological behaviour of carbon filled hybrid UHMWPE composites in water. Tribol Int 124:169–177. https://doi.org/10.1016/j.triboint.2018.04.001
Pang W, Ni Z, Wu JL, Zhao Y (2018) Investigation of tribological properties of graphene oxide reinforced ultrahigh molecular weight polyethylene under artificial seawater lubricating condition. Appl Surf Sci 434:273–282. https://doi.org/10.1016/j.apsusc.2017.10.115
Golchin A, Wikner A, Emami N (2016) An investigation into tribological behaviour of multi-walled carbon nanotube/graphene oxide reinforced UHMWPE in water lubricated contacts. Tribol Int 95:156–161. https://doi.org/10.1016/j.triboint.2015.11.023
Chih A, Anson-Casaos A, Puertolas JA (2017) Frictional and mechanical behaviour of graphene/UHMWPE composite coatings. Tribol Int 116:295–302. https://doi.org/10.1016/j.triboint.2017.07.027
Aliyu IK, Mohammed AS, Al-Qutub A (2018) Tribological performance of ultra high molecular weight polyethylene nanocomposites reinforced with graphene nanoplatelets. Polym Compos 40:1301–1311. https://doi.org/10.1002/pc.24975
Bhattacharyya A, Chen S, Zhu M (2014) Graphene reinforced ultra high molecular weight polyethylene with improved tensile strength and creep resistance properties. Express Polym Lett 8(2):74–84. https://doi.org/10.3144/expresspolymlett.2014.10
Hummers WS, Offeman RE (1958) Preparation of graphitic oxide. J Am Chem Soc 6(80):1339. https://doi.org/10.1021/ja01539a017
Mindivan F, Göktaş M (2019) Preparation of new PVC composite using green reduced graphene oxide and its effects in thermal and mechanical properties. Polym Bull 2019:1–21. https://doi.org/10.1007/s00289-019-02831-x
Mohammed AS, Ali A, Nesar M (2017) Evaluation of tribological properties of organoclay reinforced UHMWPE nanocomposites. J Tribol 139:1–6. https://doi.org/10.1115/1.4033188
Ahmad M, Uzir Wahit M, Rafiq Abdul Kadir M, Zaman Mohd Dahlan K (2012) Mechanical, rheological, and bioactivity properties of ultra high-molecular-weight polyethylene bioactive composites containing polyethylene glycol and hydroxyapatite. Sci World J 2012:1–13. https://doi.org/10.1100/2012/474851
Amangah M, Salami-Kalajahi M, Roghani-Mamaqani H (2018) Nanoconfinement effect of graphene on thermophysical properties and crystallinity of matrix-grafted graphene/crosslinked polysulfide polymer nanocomposites. Diam Relat Mater 83:177–183. https://doi.org/10.1016/j.diamond.2018.02.012
Bahrami H, Ramazani SAA, Kheradmand A, Shafiee M, Baniasadi H (2015) Investigation of thermomechanical properties of UHMWPE/Graphene oxide nanocomposites prepared by in situ Ziegler-Natta polymerization. Adv Polym Technol. https://doi.org/10.1002/adv.21508
Kandhol G, Wadhwa H, Chand S, Mahendia S, Kumar S (2019) Study of dielectric relaxation behavior of composites of Poly(vinyl alchohol) (PVA) and reduced graphene oxide (RGO). Vacuum 160:384–393. https://doi.org/10.1016/j.vacuum.2018.11.051
Huang G, Ni Z, Chen G, Zhao Y (2016) The influence of irradiation and accelerated aging on the mechanical and tribological properties of the graphene oxide/ultra-high-molecular-weight polyethylen nanocomposites. Int J Polym Sci 2016:1–9. https://doi.org/10.1155/2016/2618560
Dong P, Long C, Peng Y, Peng X, Guo F (2019) Effect of coatings on thermal conductivity and tribological properties of aluminum foam/polyoxymethylene interpenetrating composites. J Mater Sci 54:13135–13146. https://doi.org/10.1007/s10853-019-03826-9
Qi H, Hu C, Zhang G, Yu J, Zhang Y, He H (2019) Comparative study of tribological properties of carbon fibers and aramid particles reinforced polyimide composites under dry and sea water lubricated conditions. Wear 436–437:1–9. https://doi.org/10.1016/j.wear.2019.203001
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Çolak, A., Göktaş, M. & Mindivan, F. Effect of reduced graphene oxide amount on the tribological properties of UHMWPE biocomposites under water-lubricated conditions. SN Appl. Sci. 2, 375 (2020). https://doi.org/10.1007/s42452-020-2179-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s42452-020-2179-4