Abstract
Aluminium alloys are materials of choice for structural applications with remarkable mechanical and corrosion properties but prone to premature failure under the combined action of stress and corrosive environment. Over the years, several efforts including surface modifications and thermomechanical treatments have been made to address this shortcoming. The present work reviews the corrosion, stress corrosion cracking (SCC), and corrosion fatigue (CF) behaviour of nanostructured Al alloys especially the Al–Mg (5xxx-series) and Al–Zn–Mg (7xxx-series), after surface modifications. To a large extent, the SCC behaviour of Al alloys could be influenced by the microstructure, heat treatments, stress, pre-strain, alloy compositions, and environments. The CF properties of surface-modified Al alloys were reviewed with a view to finding a relation between the nanostructured Al alloys and their aftermath corrosion fatigue properties. The fatigue behaviour of Al alloys can be influenced by the corrosion behaviour via various mechanisms including hydrogen embrittlement, prompt crack growth in aggressive environment, and crack initiation at pits. The strengthening mechanisms in nanostructured Al alloys are also briefly explained. For further study, some insights are then provided to avail the readers on options for future research.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Aluminum alloys, especially the Al–Mg (5xxx-series) and Al–Zn–Mg (7xxx-series) are presently receiving wide attention and interests as potential structural materials which find applications in most aerospace and automotive industries [1,2,3]. The uncommon interests cannot only be attributed to their high toughness and specific strength, but their low density and outstanding corrosion resistance performance [1, 2]. However, they are susceptible to stress corrosion cracking (SCC) especially in aggressive environments and this still remain a bottleneck limiting their applications in some areas. Efforts have been made to address the current SCC challenge, and research is still ongoing to explore several feasible options.
Stress corrosion cracking (SCC) in Al alloys (an advanced generation of cracks leading to vital failure) often takes place when susceptible Al materials are subjected to the combined action of stress (above the limit) and corrosive environment. In short, a tensile stress condition beyond the limit, a specific environment and a susceptible Al metal are the three main factors influencing the occurrence of SCC in Al alloys i.e., SCC cannot probably occur if the three factors are not simultaneously present [2, 3]. The combination of these three factors often results in total failure and hence it should be avoided by all means for Al alloys. Moreover, SCC of Al alloys in corrosive environments occurs in three stages [4,5,6]: (a) crack initiation, originating from a smooth surface and depends to a large extent on the environment properties such as temperature, pH and salinity; metal structure and crack nucleation mechanism, (b) crack propagation, from the point of crack initiation to the core part of the materials under the combined action of applied tensile stress and corrosion mechanism, and (c) failure, which occurs when the limit has been exceeded by the combined corrosion—applied stress forces. It should be noted that both Al–Mg (5xxx-series) and Al–Zn–Mg (7xxx-series) are susceptible to SCC, and this often causes a catastrophic failure anytime it occurs in Al alloys especially the Al–Zn–Mg (7xxx-series). However, the imminent failure can be avoided or reduced to the lowest level by enhancing the SCC resistance via surface modifications [4, 7,8,9,10,11,12,13,14] and thermomechanical treatments. More details about these methods are given in section two.
The corrosion fatigue behaviors of Al alloys differ from each other in different environments and processing parameters after surface modifications [15,16,17,18,19,20,21,22,23,24,25,26,27,28,29,30]. Firstly, using the Pearson correlation analysis [15] and Trantina-Jonson model [16] by correlating parameters between the corrosion pits and equivalent cracks, the pre-corrosion fatigue lifetime [15] and corrosion fatigue crack growth rate [16] as well as the pit growth [17] in Al alloys can easily be predicted. Unravelling the effects of pre-corrosion on the fatigue lifetime of Al 8011 alloy [18], a significant decrease in the fatigue strength was observed due to the occurrence of corrosion pits on the sample surface. In addition, due to exfoliation, pit clustering, and pitting leading to localized corrosion damage characterized with crack initiation at corrosion defects, a similar decrease in fatigue lifetime was reported for AA6061 Al alloy [19] after surface treatment by friction stir welding (FSW) process. However, decreasing the pH value and increasing the corrosion solution flow rate, temperature, and corrosion time could reduce the fatigue lifetime of Al alloys, as illustrated for 2024-T4 Al alloy by Chen et al. [20].
In both 3.5% NaCl solution and air, there is an improvement in the corrosion fatigue properties of 7A85 Al alloy [21] after shot peening and plasma electrolytic oxidation, which can be linked to the compressive residual stress (CRS) induced by the shot peening treatment. Meanwhile, a large size of pits can occur by increasing the pre-corrosion time, resulting in reduced multiaxial fatigue lifetime, just as the case of 2024-T4 Al alloy [22, 23] in different corrosive environments. As indicated by Leon and Aghion [24] for Al alloy processed via selective laser melting (SLM), the corrosion fatigue resistance could be greatly improved in different corrosive environments by reducing the surface roughness. By this, surface defects like cavities and holes can be greatly reduced. All efforts must be made to reduce the surface and corrosion defects/pits [25] since they negatively affect the corrosion fatigue performance by causing premature crack initiation [26] and accelerating the rate of crack growth [27]. Investigating the effects of surface modifications by ball-burnishing and shot peening on the corrosion fatigue properties of AA5083 [28] in chloride environment, a significant improvement in the fatigue lifetime is obtained. Shot peening and ball-burnishing process also enhances the corrosion fatigue resistance of AA7075-T73 alloy [29]. The improvement in the corrosion fatigue performance can be accrued to the residual stress induced by the surface modification process, heat treatment and hardness increase through the addition of nano-clay particles [30], reducing the surface defects as well as the corrosion defects and pits in the process.
The present work reviews the corrosion, SCC, and CF properties of surface-modified Al alloys with a view to finding a relation between the nanostructured Al alloys and their aftermath corrosion fatigue properties, and most importantly proffer possible solutions to addressing the common catastrophic failure experienced by Al alloys under the combined actions of stress and corrosive environments.
2 SCC of Surface-Modified Al Alloys
For structural applications, Al alloys are very sought-after materials due to their versatility, strength, and corrosion properties. However, their applications and usability are often limited due to their susceptibility to SCC in aggressive environments. Several surface modifications including equal-channel angular pressing (ECAP), dynamic plastic deformation (DPD), shot peening or surface mechanical attrition treatment (SMAT) techniques have been successfully applied in the past to enhance the SCC resistance of different Al alloys in different environmental conditions [4, 7,8,9,10,11,12,13,14]. For instance, the SCC resistance of nanostructured AA 7075-T6 Al alloy via shot peening process [4] was significantly increased, although the surface roughness also increased in the process which promotes localized corrosion pitting. Here, the CRS induced by shot peening and refined microstructure inhibits the formation of pits and propagation of crack thereby enhancing the resistance to SCC, but at the expense of the corrosion behaviour because the microstructural change often acts as a pitting corrosion site during the process. The negative effects of the surface roughness may be checked and addressed by adjusting the shot peening intensity and shot diameter during the process.
Similarly, the fatigue resistance of 7075 Al alloy [7] was reportedly enhanced after ultrasonic rolling which can again be accrued to the large values of CRS induced during the process on the surface layer of the Al alloy. It can be said here that the higher the induced CRS, the higher the resistance to fatigue and SCC. At the same time, the maximum CRS and CRS thickness layer increases with increasing roller radius, amplitude, and static load. In addition, Pan et al. [8] reported a significant increment in the localized corrosion resistance for surface modified AA7075 alloys due to the precipitation mechanism, unique surface properties and microstructures [1] which gives room for improvement of surface properties, however, the effects of nanoparticles during the treatment on the fatigue and SCC of AA7075 Al alloys could not be ascertained.
As reported by Xu et al. [9], after sensitization, the nanostructured Al–5Mg via DPD process experienced a significant increase in resistance to SCC and intergranular corrosion (IC) as well as an improved ductility and strength, when compared with its coarse-grained counterpart. This is in relation with the generation of a high volume of low-angle grain boundaries (LAGBs) through the DPD process. Meanwhile, estimating the SCC susceptibility of nanostructured AA5083 via friction stir processing (FSP) in 0.6 M NaCl solution [10] using slow strain rate testing (SSRT) method [10, 11], the FSP-processed AA5083 revealed no susceptibility while the ultrafine grained Al–Mg–Sc–Zr showed high SCC susceptibility. A similar case was reported for Al–Zn–Mg–Cu alloy (AA7075) [12,13,14] especially after surface treatment by high pressure torsion method [14].
Just like shot peening process, SMAT technique has also be widely adopted to influence the general corrosion properties of materials without tampering with their inherent properties [31,32,33,34,35,36,37,38]. More importantly, the positive influence of SMAT on the SCC resistance of Al alloys has been reported [39,40,41,42,43]. After surface modification via SMAT technique, Li et al. [39] reported a significant increase in SCC resistance of alloy 690 in alkaline steam generator environments. This may be related to the remarkable CRS induced by SMAT technique and the aftermath formation of stable film. In addition, the ultra-fine microstructures play a vital role in the improvement of pitting corrosion resistance observed for nanostructured Al–8.6Mg and Al–7.5Mg Al alloys [40] in artificial and natural environments, as well as other Al alloys [41,42,43]. In short, the SCC behaviour of nanostructured Al alloys could be influenced by the environments, alloy compositions, pre-strain, stress, heat treatments, and microstructure.
3 Corrosion Fatigue Properties of Nanostructured Al Alloys
Among the mechanical properties of materials, the fatigue property has always been one of the most important issues defining the ability of materials to resist failure in very-high-cycle fatigue (VHCF) and high-cycle fatigue (HCF) conditions [44,45,46,47,48,49,50]. Obviously, the mechanical properties of Al alloys are enhanced after surface modifications in terms of yield strength (σ0.2 (MPa)), ultimate tensile strength (UTS) (σb (MPa)), and percentage elongation (δ (%)) [26, 51,52,53,54,55,56,57,58,59,60,61,62,63,64,65], as summarized in Table 1. The formation of nanostructured layer via grain refinement mostly prevents the fatigue crack initiation and propagation. This is made possible by the presence of the larger volume fraction of grain boundaries impeding the dislocation sliding and hence preventing the initiation of cracks, and the nanostructured layer is believed to be the primary factor hindering the creation of stress concentrator for initiation of crack [66,67,68,69,70,71,72,73]. The surface quality goes a long way in determining the strength of the materials after surface treatment. In addition, plastic deformation could induce microcracks on the sample surface reducing the fatigue strength of materials resulting in the stress concentration and initiation of cracks [74,75,76,77,78,79]. In short, microcracks induced by severe plastic deformation (SPD) can lead to micro damage on sample surface leading to multi-crack initiation phenomenon [54]. However, it is important to note that once the crack breaks through the SPD layer and reaches a baser metal structure, then the SPD layer will have no significance influence again—this is a known issue with laser surface modified layers. Furthermore, the fatigue strength of severely plastic deformed materials is expected to improve via the CRS by hindering crack initiation and propagation [80,81,82,83,84,85], i.e., CRS can enhance the resistance of crack initiation and propagation.
Interestingly, the SMAT technique has been in the frontline among other SPD methods in significantly enhancing the fatigue strength as well as the corrosion resistance of materials [90,91,92,93,94,95,96]. Several factors such as phase transformation, nanocrystalline layer, surface layer, and residual stress and its relaxation [54] could contribute to the effects of SMAT on the fatigue strength of Al alloys. The deformation-induced phase transformation has significant influence on the properties of materials of Al alloys and steels in particular. Under the effect of plastic deformation, a transition of a fraction of austenitic phase to martensitic phase can occur. By this, the fatigue strength of materials can be enhanced by the martensitic transformation induced by SMAT together with the formation of gradient-structured layers since the martensitic phase tends to have higher mechanical strength than the austenitic phase.
Studies on the fatigue crack growth and tensile properties of the nanostructured and ultrafine-grained Al alloys have been carried out in the past [54,55,56,57, 97,98,99,100,101,102,103,104,105,106]. As a function of environment, the corrosion fatigue properties of nanostructured Al alloys can be grouped into crack initiation, low-rate growth, high-rate growth, and rupture. And it can be studied in line with corrosion product, crack propagation, pit location and initiation. The corrosion fatigue strengths of Al alloys can be significantly enhanced with the adoption of SPD techniques such as SMAT [41, 42, 54] and shot peening [4, 21]. The fatigue behaviour of Al alloys can be influenced by the corrosion behaviour via various mechanisms including hydrogen embrittlement/SCC [57, 97,98,99,100,101], prompt crack growth in aggressive environment [102], and crack initiation at pits [102,103,104,105,106]. In the case of nanostructured 2024 Al alloy processed via SMAT technique, the enhancement in the corrosion resistance property is related to the formation of a dense passive film as a result of nano structuring effect of SMAT and protective coating from microarc oxidation process (post-SMAT) [107]. The fabrication of the nanostructured layer at the bottom of the coating is expected to significantly enhance the general corrosion resistance property.
As summarized in Table 2, the corrosion fatigue mechanisms of nanostructured Al alloys in different corrosive environments and applications can be categorized in terms of induced CRS, cleavage and fracture, nucleation of pores, precipitate-free zone width, pitting kinetics, quench rate, distribution of precipitates, grain boundary precipitates, matrix precipitate, and enhanced passivation [1, 52, 55, 56, 108,109,110,111]. Under corrosion fatigue conditions, attributed to the premature crack initiation on corrosion defects, the conventionally processed alloys exhibit a reduced fatigue lifetime. The reduced fatigue strength can be explained based on different mechanisms including hydrogen embrittlement at defect and plastic deformation localization around the corrosion defects [56].
As revealed in Fig. 1a–f, the corrosion fatigue performance of Al alloys is influenced by the gradient-structured layers produced on the top layers, in different environment and conditions. For instance, the nanostructured 7B50-T7751 Al alloy processed by USRP (Fig. 1a, b, e) [59, 60] exhibits an improved corrosion fatigue life with optimal surface integrity in air and 3.5% NaCl as compared with the conventional Al alloy [59]. This is achievable due to the microstructure refinement and CRS induced by USRP, inhibiting the appearance and formation of intergranular and pitting corrosion thereby preventing the initiation of corrosion fatigue cracks. As a matter of fact, gradient structure is a contributing factor for the improvement in corrosion fatigue performance [60]. Hence, the study on the influence of surface integrity as well as the combined effect of surface nanocrystallization and CRS is important as far as the corrosion fatigue life of Al alloy is concerned. As indicated in Fig. 1c [1], the fatigue fracture morphology can occur in corrosion pitting, fatigue crack propagation, and rapid fatigue fracture regions. In addition, the fatigue life increases mostly with surface nanocrystallization [59], and corrosion fatigue can set in for conventional Al alloys without gradient structures (Fig. 1f) [108]. Generally, reduction in fatigue strength of Al alloys, for instance 7075-T651 [26] and AlLi alloy 2090 [98], can mainly be attributed to the combined effects of hydrogen embrittlement and anodic dissolution at the crack tip, as well as the formation of corrosion pits [26]. Hence, hydrogen embrittlement remains one of the primary mechanisms for the corrosion fatigue process of Al alloys.
There is a direct relationship between the corrosion and mechanical properties of Al alloys as illustrated in Fig. 2. In the process of enhancing the corrosion resistance performance, it is necessary to ensure that the strength is not affected. However, the yield strength vs corrosion current density (icorr) varies among the Al alloys. The 7055 Al alloy [89] experiences high yield strength together with the lowest icorr (possibly signifying a good corrosion resistance property), but the case is different for 1050 Al alloy [86] with low yield strength even though a good corrosion resistance property is obtained. A similar improvement in both the strength and corrosion resistance can be observed for 7085 [67] and 7075-T6 [86] Al alloys. It can be seen that Al–0.07Fe–0.007La and Al–0.07Fe–0.007La Al alloys [87] possessed the highest icorr, indicating a possible poor corrosion resistance performance and lowest yield strengths. The difference in behaviour of the yield strength vs corrosion resistance among the different types of Al alloys may be linked to the nature and extent of heat treatment, alloying compositions, or environmental factors [67, 71, 78, 81, 86,87,88,89].
On the other hand, thermomechanical treatments including the step-quench aging (SQA) and slow quench rate methods as well as electrodeposition/coatings and heat treatments, are widely receiving great attention as alternative methods of enhancing the overall properties of materials [112,113,114,115,116,117,118,119], especially the resistance of Al alloys to SCC [44,45,46,47,48,49,50]. To be specific, the SQA heat treatment reportedly increased the resistance of AA7097 Al alloy to SCC, which is probably due to the discontinuous distribution, large size, and high Cu content grain boundary precipitates [44]. In addition, the thermomechanical treatment via slow quench rate decreases the rate of crack propagation thereby improving the resistance of AlZnMgCu alloy [45] to SCC.
4 Strengthening Mechanisms in Nanostructured Al Alloys
The susceptibility to corrosion of Al alloy differs among the various classes. For example, Al–Mg (5xxx-series) and Al–Zn–Mg (7xxx-series) have very different behaviors under the same electrolyte and applied electrochemical potential conditions due to differences in the underlying mechanisms responsible for susceptibility.
4.1 Al–Mg (5xxx-Series)
Due to their excellent corrosion resistance and mechanical properties, good weldability, high strength/weight ratio, and low cost, non-heat treatable Al–Mg 5xxx alloys have been widely accepted as the preferred materials of choice for structural applications especially in aggressive marine conditions. They also find applications in forging, transport, and shipbuilding industries, as well in aerospace and building sectors. Aluminium (Al) and magnesium (Mg) are the two main alloying elements in these alloys, and the presence of Mg plays a vital role in achieving the stated properties by enhancing the mechanical properties and stimulating solid solution and work hardening strengthening. However, the Mg element in the alloy does not alter the deformation features and tamper with the SFE of Al–Mg 5xxx, but can result in lattice distortion, hasting the strain hardening in the process. Under standard service temperatures (60–200 °C), over a long period of time, these alloys often experience sensitization and more susceptibility to intergranular stress corrosion cracking (IGSCC) when the Mg content in them is above 3 wt%, compared to the standard alloy composition. The sensitivity to IGSCC can be established by constant-extension-rate tests (CERTs) and be assessed based on the mass losses via nitric acid mass loss test (NAMLT). Furthermore, findings revealed that the IGSCC in Al–Mg–5xxx is arguably related to the occurrence of the Mg-rich β phase—Al3Mg2 precipitates [120,121,122,123] along the grain boundaries at elevated temperatures, and it could be greatly influenced by the time and orientation of exposure/grain boundary, grain size as well as the degree of sensitization (DoS) [123,124,125].
The strengthening mechanisms of nanostructured Al Alloys majorly comprise the grain boundary, solution hardening, precipitation strengthening, and dislocation strengthening. As a matter of fact, the strain hardening, and solid solution strengthening are the major source of strength in Al–Mg–5xxx alloys [126, 127].
4.2 Al–Zn–Mg (7xxx-Series)
Al-Zn-Mg (7xxx-series) are known for their high strength, moderate heat and electrical conductivities, high strength/density ratio, good workability, and enhanced corrosion properties, which makes them promising materials for aluminium sheets for different applications as well as extrusions for aircrafts and automotive parts [128,129,130]. This remarkable feat can be linked to the presence of considerable and desired alloying elements—Mg and Zn, which improves the mechanical properties and stimulates the precipitation hardening mechanism [128, 131]. However, their maximum strengths can be obtained at low temperatures because at high temperatures, they are prone to stress corrosion and over-ageing. The Al–Zn–Mg 7xxx are heat treatable alloys which can be strengthened by precipitation or age hardening, unlike the Al–Mg–5xxx series which can be reinforced by cold working process and are non-heat treatable.
5 Summary and Future Work
The corrosion, stress corrosion cracking (SCC) resistance, and corrosion fatigue (CF) behaviour of nanostructured Al alloys especially the Al–Mg (5xxx-series) and Al–Zn–Mg (7xxx-series) have been reviewed. These alloys are widely useful for aerospace and automotive applications [131,132,133,134,135,136,137,138,139] because of their high specific strength and excellent corrosion resistance but very prone to SCC especially in harsh service conditions. The imminent catastrophic failure can be avoided or reduced by enhancing the SCC resistance via surface modifications and thermomechanical treatments such as step-quench aging (SQA) and slow quench rate.
Al and Mg are the two main alloying elements in Al–Mg (5xxx-series). The presence of Mg does not alter the deformation features or tamper with the stacking fault energy (SFE) hence play a vital role in achieving the remarkable surface properties, but can result in lattice distortion, hasting the strain hardening in the process. Additionally, the improved SCC and CF resistance experienced by the Al-Zn-Mg (7xxx-series) can be linked to the presence of considerable and desired alloying elements—Mg and Zn, which improves the mechanical properties and stimulates the precipitation hardening mechanism, but they are prone to stress corrosion and over-ageing at high temperatures. Moreover, the Al–Mg–5xxx series can be reinforced by cold working process and are non-heat treatable, compared to the Al–Zn–Mg 7xxx which are heat treatable alloys and can be strengthened by precipitation or age hardening.
An improvement in the SCC and CR resistance of Al alloys is achievable due to the microstructure refinement and compressive residual stress (CRS) induced during the surface modification process, inhibiting the appearance and formation of intergranular and pitting corrosion thereby preventing the initiation of corrosion fatigue cracks. By this, gradient structure plays an important role in enhancing the corrosion fatigue performance. In addition, the rate of crack propagation can be decreased thereby increasing the resistance of Al alloys to SCC via the thermomechanical treatments, and this is probably attributed to the discontinuous distribution, large size, and high Cu content grain boundary precipitates. Hence, the SCC behaviour of nanostructured Al alloys could be influenced by the environments, alloy compositions, pre-strain, stress, heat treatments, and microstructure. Furthermore, the corrosion fatigue mechanisms of nanostructured Al alloys in different corrosive environments can be categorized in terms of induced CRS, cleavage and fracture, nucleation of pores, precipitate-free zone width, pitting kinetics, quench rate, distribution of precipitates, and enhanced passivation.
The corrosion, stress corrosion cracking (SCC), and corrosion fatigue (CF) behavior differs among the various classes of Al alloy. For example, Al–Mg (5xxx-series) and Al–Zn–Mg (7xxx-series) have very different behaviors under the same electrolyte and applied electrochemical potential conditions due to differences in the underlying mechanisms responsible for susceptibility. For future study, further works on the underlying mechanisms responsible for susceptibility in various classes of Al alloys in relation to their corrosion, SCC, and CF behaviors after surface modification can be carried out, and most importantly the influence of surface modification on the causal factors responsible for susceptibility.
Abbreviations
- CERTs:
-
Constant-extension-rate tests
- CRS:
-
Compressive residual stress
- DoS:
-
Degree of sensitization
- DPD:
-
Dynamic plastic deformation
- DSC:
-
Differential scanning calorimetry
- EIC:
-
Environment-induced cracking
- FSP:
-
Friction stir processing
- FSW:
-
Friction stir welding
- GBs:
-
Grain boundaries
- GBPs:
-
Grain boundary precipitates
- HAGBs:
-
High angle grain boundaries
- HCF:
-
High-cycle fatigue
- IGPs:
-
Intragranular precipitates
- IGSCC:
-
Intergranular stress corrosion cracking
- LAGBs:
-
Low angle grain boundaries
- NAMLT:
-
Nitric acid mass loss test
- UTS:
-
Ultimate tensile strength
- VHCF:
-
Very-high-cycle fatigue
- SCC:
-
Stress corrosion cracking
- SFE:
-
Stacking fault energy
- SLM:
-
Selective laser melting
- SMAT:
-
Surface mechanical attrition treatment
- SPD:
-
Severe plastic deformation
- SQA:
-
Step-quench and aging
- SSRT:
-
Slow strain rate testing
References
Liu C, Ma L, Zhang Z, Fu Z, Liu L (2021) Metals 11:1754
Abolhasani A, Langelier B, Worswick MJ, Wells MA, Esmaeili S (2022) J Alloy Compd 906:164344
Kayani SH, Park S, Euh K, BokSeol J, GiKim J, Sung H (2022) Mater Charact 190:112019
Bao L, Li K, Zheng J, Zhang Y, Zhan K, Yang Z, Zhao B, Ji V (2022) Surf Coat Technol 440:128481
Umamaheshwerrao AC, Vasu V, Govindaraju M, Saisrinadh KV (2016) Trans Nonferrous Met Soc China 26:1447–1471
Pedeferri P (2018) Springer, Cham. https://doi.org/10.1007/978-3-319-97625-9_13
Zheng J, Shang Y, Guo Y, Deng H, Jia L (2022) J Manuf Process 80:132–140
Pan S, Yuan J, Linsley C, Liu J, Li X (2022) Corros Sci 206:110479
Xu W, Xin YC, Zhang B, Li XY (2022) Acta Mater 225:117607
Argade G, Kumar N, Mishra R (2013) Mater Sci Eng A 565:80–89
Holroyd NH, Burnett T, Seifi M, Lewandowski JJ (2017) Mater Sci Eng A 682:613–621
Knight SP, Birbilis N, Muddle BC, Trueman AR, Lynch SP (2010) Corros Sci 52:4073–4080
Knight SP, Pohl K, Holroyd NJH, Birbilis N, Rometsch PA, Muddle BC, Goswami R, Lynch SP (2015) Corros Sci 98:50–62
Zhang Y, Jin S, Trimby PW, Liao X, Murashkin MY, Valiev RZ, Liu J, Cairney JM, Ringer SP, Sha G (2019) Acta Mater 162:19–32
Huang Y, Ye X, Hu B, Chen L (2016) Int J Fatigue 88:217–226
Wang CQ, Xiong JJ, Shenoi RA, Liu MD, Liu JZ (2016) Int J Fatigue 83:280–287
Hu P, Meng Q, Hu W, Shen F, Zhan Z, Sun L (2016) Corros Sci 113:78–90
Mishra RK (2020) Mater Today Proc 25(4):602–609
Rodriguez RI, Jordon JB, Allison PG, Rushing T, Garcia L (2019) Mater Sci Eng A 742:255–268
Chen Y, Liu Ch, Zhou J, Wang F (2019) J Alloy Compd 772:1–14
Yea Z, Liu D, Zhang X, Wu Z, Long F (2019) Appl Surf Sci 486:72–79
Chen Y, Liu CH, Zhou J, Wang X (2017) Int J Fatigue 98:269–278
Chen Y, Zhou J, Liu Ch, Wang F (2018) Int J Fatigue 108:35–46
Leon A, Aghio E (2017) Mater Charact 131:188–194
Guerin M, Alexis J, Andrieu E, Blanc C, Odemer G (2015) Mater Des 87:681–669
Chlistovsky RM, Heffernan PJ, DuQuesnay DL (2007) Int J Fatigue 29:1941–1949
Meng X, Lin Z, Wang F (2013) Mater Des 51:683–687
Abdulstaar M, Mhaede M, Wollmann M, Wagner L (2014) Surf Coat Technol 254:244
Mhaede M (2012) Mater Des 41:61–66
Aroo H, Azadi M, Azadi M (2022) Silicon 14:3749–3763
Olugbade T, Lu J (2018) In: Twelfth international conference on fatigue damage of structural materials, Cape Cod, Hyannis, USA
Olugbade TO, Lu J (2020) Nano Mater Sci 2:3–31
Olugbade T (2019) Data-in-Brief 25:104033
Olugbade T, Liu C, Lu J (2019) Adv Eng Mater 21:1900125
Olugbade TO, Lu J (2019) Anal Lett 52:2454–2471
Olugbade TO, Olutomilola EO, Olorunfemi BJ (2022) Corros Rev 40:189–203
Olugbade TO, Omiyale BO, Ojo OT (2022) J Mater Eng Perform 31:1707–1727
Olugbade TO, Lu J (2019) J Bio Tribo Corros 5:38
Li N, Shi S, Luo J, Lu J, Wang N (2016) Mater Res Lett 4:180–184
Sharma MM, Ziemian CW (2008) J Mater Eng Perform 17:870–878
DeOrio J (2020) Barrett. The Honors College Thesis/Creative Project Collection
Wen L, Wang Y, Zhou Y, Guo LX, Ouyang JH (2011) Mater Chem Phys 126:301–309
Sharma MM, Tomedi JD, Weigley TJ (2014) Mater Sci Eng A 619:35–46
Xie P, Chen S, Chen K, Jiao H, Huang L, Zhang Z, Yang Z (2019) Corros Sci 161:108184
Yuan D, Chen K, Chen S, Zhou L, Chang J, Huang L, Yi Y (2019) Mater Des 164:107558
Olugbade TO, Abioye TE, Farayibi PK, Olaiya NG, Omiyale BO, Ogedengbe TI (2021) Anal Lett 54:1588–1602
Ou BL, Yang JG, Wei MY (2007) Metall Mater Trans A 38:1760–1773
Yang JG, Ou BL (2001) Scand J Metall 30:158–167
Olugbade TO, Omoniyi OO, Omiyale BO (2022) J Inst Eng (India) Ser D 103:141–147
Lin JC, Liao HL, Jehng WD, Chang CH, Lee SL (2006) Corros Sci 48:3139–3156
Strehblow HH (1995) Mechanisms of pitting corrosion. Corrosion mechanisms in theory and practice, Marcel Dekker, New York, pp 201–238
Olugbade T, Lu J (2020) In: International conference on nanostructured materials (NANO 2020), vol 117, Australia
Gupta RK, Fabijanic D, Dorin T, Qiu Y, Wang JT, Birbilis N (2015) Mater Des 84:270–276
Suresh S (1998) Fatigue of materials, 2nd edn. Cambridge University Press, Cambridge
Olugbade TO (2020) Corros Rev 38:473–488
Rochet C, Andrieu E, Arfaei B, Harouard JP, Laurino A, Lowe TC, Odemer G, Blanc C (2020) Int J Fatigue 140:105812
Pao PS, Jones HN, Cheng SF, Feng CR (2005) Int J Fatigue 27:1164–1169
Tellkamp VL, Lavernia EJ (1999) Nanostruct Mater 12:249–254
Xu X, Liu D, Zhang X, Liu C, Liu D, Zhang W (2019) Int J Fatigue 125:237–248
Xu X, Liu D, Zhang X, Liu C, Liu D (2020) J Mater Sci Technol 40:88–98
Ebrahimi M, Gode C, Attarilar S et al (2021) Trans Indian Inst Met 74:753–766
Liddicoat PV, Liao XZ, Zhao YH, Zhu YT, Murashkin MY, Lavernia EJ, Valiev RZ, Ringer SP (2010) Nat Commun 1:63
Cepeda-Jimenez CM, Garcia-Infanta JM, Ruano OA, Carreno F (2011) J Alloys Compd 509:8649–8656
Panigrahi SK, Jayaganthan R (2011) Mater Des 32:3150–3160
Ning AL, Liu ZY, Peng BS, Zeng SM (2007) Trans Nonferrous Met Soc China 17:1005–1011
Li J, Birbilis N, Li C, Jia Z, Cai B, Zheng Z (2009) Mater Char 60:1334–1341
Chen S, Chen K, Peng G, Jia L, Dong P (2012) Mater Des 35:93–98
Xu D, Birbilis N, Rometsch P (2012) Corrosion Sci 54:17–25
Ranganatha R, Kumar VA, Nandi VS, Bhat R, Muralidhara B (2013) Trans Nonferrous Met Soc China 23:1570–1575
Xie L, Lei Q, Wang M, Sheng X, Li Z (2017) J Mater Res 32:1105–1117
Jeshvaghani RA, Zohdi H, Shahverdi H, Bozorg M, Hadavi S (2012) Mater Char 73:8–15
Lei C, Li H, Fu J, Shi N, Zheng G, Bian T (2018) Metals 8:285
Wang Y, Jiang H, Li Z, Yan D, Zhang D, Rong L (2017) J Mater Sci Technol 34:1250–1257
Peng X, Li Y, Liang X, Guo Q, Xu G, Peng Y, Yin Z (2018) J Alloys Compd 735:964–974
Peng X, Guo Q, Liang X, Deng Y, Gu Y, Xu G, Yin Z (2017) Mater Sci Eng A 688:146–154
Liu Y, Liang S, Jiang D (2016) J Alloys Compd 689:632–640
Jiang J, Tang Q, Yang L, Zhang K, Yuan S, Zhen L (2016) J Mater Process Technol 227:110–116
Jiang D, Liu Y, Liang S, Xie W (2016) J Alloys Compd 681:57–65
Liu Y, Jiang D, Li B, Yang W, Hu J (2014) Mater Des 57:79–86
Wen K, Fan Y, Wang G, Jin L, Li X, Li Z, Zhang Y, Xiong B (2017) Prog Nat Sci Mater Int 27:217–227
Chen S, Li J, Hu GY, Chen K, Huang L (2018) J Alloys Compd 757:259–264
Zhang M, Liu T, He C, Ding J, Liu E, Shi C, Li J, Zhao N (2016) J Alloys Compd 658:946–951
Gao T, Zhang Y, Liu X (2014) Mater Sci Eng A 598:293–298
Wen K, Xiong B, Zhang Y, Li Z, Li X, Huang S, Yan L, Yan H, Liu H (2018) Met Mater Int 24:1–12
Li C, Pan Q, Shi Y, Wang Y, Li B (2014) Mater Des 55:551–559
Kim SJ, Ko JY (2006) Korean J Chem Eng 23:847–853
Yang X, Ding D, Xu Y, Zhang W, Gao Y, Wu Z, Chen G, Chen R, Huang, Tang J (2019) Metals 9: 706
Chuvil’deev VN, Nokhrin AV, Kopylov VI, Gryaznov MY, Shotin SV, Likhnitskii CV, Kozlova NA, Shadrina YS, Berendeev NN, Melekhin NV, Nagicheva GS, Smetanina KE, Tabachkova NY (2022) J Alloy Compd 891:162110
Zhong H, Li S, Zhang Z, Dehua Li, Deng H, Chen J, Qi L, Ojo OA (2022) Mater Today Commun 31:103732
Olugbade TO (2020) PhD thesis. Department of Mechanical Engineering, City University of Hong Kong
Olugbade TO (2022) MRS Adv 7:886
Olugbade TO, Omiyale BO (2021) Anal Techn Szegedinensia 15:9
Olugbade TO (2022) In: Singh M (ed) Stainless steel. IntechOpen Publisher, London
Olugbade TO (2021) Anal Lett 54:1055
Olugbade TO, Omiyale BO (2022) Chem Afr 5:1663
Olugbade TO (2022) Chem Afr 5:333
Ebtehaj K, Hardie D, Parkins RN (1989) Br Corros J 24:183–188
Dervenis CP, Meletis EI, Hochman RF (1988) Mater Sci Eng A 102:151–160
Pao PS, Jones HN, Gill SJ, Feng CR (2003) MRS Symp Proc 740:15–20
Haase I, Nocke K, Worch H, Zouhar G, Tempus G (2001) Prakt Metallogr 38:119–137
Elboujdaini M, Shehata MT (1997) Microstruct Sci 25:41–49
Wei RP, Harlow GD (1998) Corrosion and corrosion fatigue of aluminum alloys: chemistry, micromechanics, and reliability. Air Force Office of Scientific Research
Zamber JE, Hillberry BM (1999) AIAA J 37:1311–1317
Harlow DG, Wei RP (1998) Eng Fract Mech 59:305–325
Genel K (2007) Scr Mater 57:297–300
Tsai TC, Chuang TH (1997) Mater Sci Eng A 225:135–144
Wen L, Wang Y, Zhou Y, Guo L, Ouyang J (2011) Corros Sci 53:473–480
Sharma MM, Tomedi JD, Parks JM (2015) Corros Sci 93:180–190
Olugbade TO, Ojo OT, Omiyale BO, Olutomilola EO, Olorunfemi BJ (2021) J Braz Soc Mech Sci Eng 43:421
Zupanc U, Grum J (2010) J Mater Process Technol 210:1197–1202
Wei RP, Liao CM, Gao M (1998) Metall Mater Trans A 29A:1153–1160
Dang C, Yao Y, Olugbade TO, Li J, Wang L (2018) Thin Solid Films 653:107
Zu K, Chau K, Olugbade TO, Pan L, Chow DH, Huang L, Zheng L, Tong W, Li X, Chen Z, He X, Zhang R, Mi J, Li Y, Dai B, Wang J, Xu J, Liu K, Lu J, Qin L (2020) J Mater Sci Technol 63:145
Abioye TE, Olugbade TO, Ogedengbe TI (2017) J Emerg Trends Eng Appl Sci 8:225
Dang C, Olugbade TO, Fan S, Zhang H, Gao LL, Li J, Lu Y (2018) Vacuum 156:310
Abioye TE, Omotehinse IS, Oladele IO, Olugbade TO, Ogedengbe TI (2020) World J Eng 17:87
Ogedengbe T, Olugbade TO, Olagunju O (2015) Br J Appl Sci Technol 10:1
Sassi W, Boubaker H, Bahar S, Othman M, Ghorbal A, Zrelli R, Hihn JY (2020) J Alloy Compd 828:154437
Mohammed T, Olugbade TO, Nwankwo I (2016) J Sci Res Rep 10:1–9
Searles JL, Gouma P, Buchheit RG (2001) Metall Mater Trans A 32:2859–2867
Engler O, Kuhnke K, Krupp H, Hentschel T (2020) Pract Metallogr 57:545–568
Crane CB, Gangloff RP (2015). Corrosion. https://doi.org/10.5006/1766
Khullar P, Badilla JV, Kelly RG (2017) Paper presented at the CORROSION 2017, New Orleans, Louisiana, USA
Engler O, Hentschel T, Brinkman HJ (2015) IOP Conf Ser Mater Sci Eng 82:012111
Sukiman NL, Zhou X, Birbilis N, Hughes A, Mol JMC, Garcia SJ, Zhou X, Thompson GE (2012). IntechOpen. https://doi.org/10.5772/53752
Rebecca MB, David J, Allison MA, Leslie GB, Ramgopal T, Jenifer SWL (2019) Int J Fatigue 124:1–9
Mofarrehi MM, Javidani XG (2022) J Alloy Compd 781:945–983
Pang J, Liu F, Liu J, Tan M, Blackwood D (2016) Corrosion Sci 106:217–228
Azarniya A, Hosseini HRM (2015) J Alloys Compd 643:64–73
Azarniya A, Hosseini HRM, Jafari M, Bagheri N, Shan D, Zhen L (2012) Aging behavior and microstructure evolution in the processing of aluminum alloys. Microstruct Evol Metal Form, Processes, p 267
Omiyale BO, Olugbade TO, Abioye TE, Farayibi PK (2022) Mater Sci Technol 38:391–408
Bankong BD, Abioye TE, Olugbade TO, Gbadeyan OO, Zuhailawati H, Ogedengbe TI (2023) Mater Sci Technol 39:129–146
Omiyale BO, Ogedengbe II, Olugbade TO, Farayibi PK (2023). 3D Print Addit Manuf. https://doi.org/10.1089/3dp.2022.0253
Sassi W, Zrelli R, Hihn JY et al (2020) J Polym Res 27:323
Ojo OT, Olugbade TO, Omiyale BO (2021) Anal Techn Szegedinensia 15:8
Omiyale BO, Rasheed AA, Akinnusi RO, Olugbade TO (2022) In: Biotechnology—biosensors, biomaterials and tissue engineering—annual volume 2022 [working title]. IntechOpen. https://doi.org/10.5772/intechopen.104465
Udensi SC, Ekpe OE, Nnanna LA (2020) Chem Afr 3:303–316
Zhang J, Wang W (2020) Chem Afr 3:317–321
Zeghaoui S, Hanniche Z, Bouyakoub I et al (2022) Chem Afr 5:673–681
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of Interest
The authors report no conflict of interest.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Olugbade, T.O., Omiyale, B.O., Ojo, O.T. et al. Stress-Corrosion and Corrosion-Fatigue Properties of Surface-Treated Aluminium Alloys for Structural Applications. Chemistry Africa 6, 1699–1708 (2023). https://doi.org/10.1007/s42250-023-00606-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s42250-023-00606-6