Abstract
Using silica sol as a binder for titanium investment casting is very attractive due to its good stability and reasonable cost as compared with yttrium sol and zirconium sol. However, the mechanism of interface reaction in the related system remains unclear. In this investigation, the interface reaction between Y2O3-SiO2 (Y-Si) shell mold and titanium alloys was studied. A group of shell molds were prepared by using Y2O3 sand and silica sol with different contents of SiO2. Ti-6Al-4V alloy was cast under vacuum by gravity casting through cold crucible induction melting (CCIM) method. Scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS) were employed to characterize the micromorphology and composition of the reaction area, respectively. X-ray photoelectron spectroscopy (XPS) was used to confirm the valence state of relevant elements. White light interferometer (WLI) was used to obtain the surface topography of Y-Si shells. The results show that the thickness of reaction layers is below 3 μm when the SiO2 content of silica sol is below 20wt.%. Whereas, when the SiO2 content increases to 25wt.%, the thickness of the reaction layer increases sharply to about 15 μm. There is a good balance between chemical inertness and mechanical performance when the SiO2 content is between 15 and 20wt.%. Moreover, it was found that the distribution of SiO2 and the roughness at the surface of the shell are the key factors that determine the level of reaction.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Saha R L, Jacob K T. Casting of Titanium and its Alloys. Defence Science Journal, 2014, 36(2): 121–141.
Nastac L, Gungor M N, Klug K L, et al. Advances in investment casting of Ti-6Al-4V alloy: A review. International Journal of Cast Metals Research, 2006, 19(2): 73.
Sung S Y, Kim Y J. Alpha-case formation mechanism on titanium investment castings. Mater Sci Eng A, 2005, 405(1):173.
Lin K, Lin C. Interfacial reactions between zirconia and titanium. Scripta Materialia, 1998, 39(10): 1333.
Kim M G, Kim S K, Kim Y J. Effect of Mold Material and Binder on Metal-Mold Interfacial Reaction for Investment Casting of Titanium Alloys. Materials Transactions, 2002, 43(4): 745.
Liu H B, Shen B, Zhu M, et al. Reaction between Ti and boron nitride based investment shell molds used for casting titanium alloys. Rare Metals, 2008, 27(6): 617.
Huang D, Xie C M, Nan H, et al. The research and development on titanium and titanium alloy investment casting coating system at abroad. Foundry, 2004, 53(3): 179. (In Chinese)
Cui R J, Gao M, Zhang H, et al. Interactions Between TiAl Alloys and Yttria Refractory Material In Casting Process. Journal of Materials Processing Technology, 2010, 210(9): 1195.
Zhao E T, Kong F T, Chen Y Y. Effect of different primary coating materials and mold temperatures on fluidity of high-temperature titanium alloy. Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture, 2012, 226(11): 1862.
Sturgis D H, Branscomb T M. Mold system for casting of reactive alloys: US Patent 8980778, 2015.
Frueh C, Poirier D R, Maguire M C. The effect of silica-containing binders on the titanium/face coat reaction. Metallurgical and Materials Transactions B, 1997, 28(5): 919–926.
Papadopoulos T R, Zinelis S, Vardavoulias M. A metallurgical study of the contamination zone at the surface of dental Ti castings, due to the phosphate-bonded investment material: the protection efficacy of a ceramic coating. Journal of Materials Science, 1999, 34(15): 3639–3646.
Kim M G, Kim S K, Kim Y J. Effect of mold material and binder on metal-mold interfacial reaction for investment castings of titanium alloys. Materials Transactions, 2002, 43(4): 745–750.
Horton R A. Method of casting a reactive metal against a surface formed from an improved slurry containing yttria: U.S. Patent No. 4, 947, 927, 1990–8–14.
Wei Y M, Lu Z G, Wu G P, et al. Reaction between Ti-6Al-4V and Y2O3–SiO2 based face shell for investment casting. Rare Metals, 2016, 35(12): 901–908.
Guo X, Lu Z G. Influence of AMT on Diacetatozirconic Acidbonded Yttria Shell and Titanium Alpha-Layer. Rare Metal Materials and Engineering, 2014, 43(12): 3013–3017.
Washburn E W. The dynamics of capillary flow. Physical Review, 1921, 17(3): 273.
Naidich Y V, Zhuravlev V S. Adhesion, wettability and reaction of titanium-containing melts with high-melting oxides. Refractories, 1974, 15(1-2): 55–60.
Li B S, Liu A H, Hai NAN, et al. Wettability of TiAl alloy melt on ceramic moulds in electromagnetic field. Transactions of Nonferrous Metals Society of China, 2008, 18(3): 518–522.
Zhu J, Kamiya A, Yamada T, et al. Surface tension, wettability and reactivity of molten titanium in Ti/yttria-stabilized zirconia system. Materials Science and Engineering: A, 2002, 327(2): 117–127.
Author information
Authors and Affiliations
Corresponding author
Additional information
Zhi-gang Lu Male, born in 1972, Ph.D., Associate Professor. Research interests: investment casting and ceramic additive manufacturing. He has published more than 50 papers.
Rights and permissions
About this article
Cite this article
Wei, Ym., Hu, Kh. & Lu, Zg. Effect of SiO2 concentration in silica sol on interface reaction during titanium alloy investment casting. China Foundry 15, 23–30 (2018). https://doi.org/10.1007/s41230-018-7066-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-018-7066-x