Abstract
Dye-sensitized solar cell, known as an emergent technology, has been attracted attention around the world. It has been easily produced by a mesoporous semiconductor oxide (SO), with a dye. On the other hand, some unexpected reactions as the back-electron recombination, reducing the solar cell efficiency. The presence of some molecules to act as an oxide passivation might rise up the collection reaction rate, and enhance the photoelectrochemical solar system parameters. The molecule used as a dye additive, must effortlessly adsorb in SO and potentiate the dye deaggregation. This work aims to study the benzotriazole (BTAH) insertion in DSSC with TiO2, evaluating its capability as a passivator molecule in such PV technology. The electrochemical results showed better electrochemical energy conversion efficiency with lower resistance with BTAH at 2.0 mg mL−1, achieving a jsc = 9.92 ± 0.26, Voc = 0.770 ± 0.022, FF = 0.557 ± 0.014, ɳ = 4.26 ± 0.13 with superior electron lifetime and amazing recombination prevention.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
The use of semiconductor oxides with solar incidence is a promising technology to energy conversion [1,2,3]. Recent application of chenodeoxycholic acid-substituted dyes, in the third generation of dye-sensitized solar cells (DSSCs) raised up a new study area in PV systems [4]. The capability of suppressing dye-dye interactions and anchoring in the oxide surface become an excellent alternative in DSSCs development.
Dye-sensitized solar cells are made by the use of an electron transport material on transparent conductor oxide (TCO), acting as a scaffold material. There is also the presence of a dye, a photosensitive molecule that inject electron by solar irradiation, providing a charge flow responsible for the solar energy conversion [1,2,3].
Simply, the solar cell operating is based on the dye ability to inject electrons in the conduction band of scaffold oxide, usually TiO2 [5], ZnO [6], and SnO2 [7] with solar energy incidence. The injected electrons, moves through a TCO to a cathode catalyst, generating a charge flow as demonstrated in Reaction 1, (where SO is the semiconductor oxide).
The intermediation of redox species is provided by an electrolyte that has been able to capture the electron in the cathode, reducing the dye [8, 9]. However, another reaction has been able to occur in the oxide/dye/electrolyte interface, the back-electron recombination (Reaction 2) [5, 10].
Suppressing the oxide-electrolyte recombination is one of the most studied ways to produce DSSC with improved photoelectrochemical parameters [11]. From this standpoint, many technologies have been used to reduce Reaction 2: push–pull dyes [12], using mix oxides [13, 14], and electrolyte additives [15]. Recently, Rodrigues and co-workers, [11] applied the poly (4-vinyl pyridine), observing a TiO2 surface passivation, able to suppress the back-electron recombination and increasing the current, even at low dye loading [16, 17]. This related study shows that is possible to use organic additives in dye solar cells, such as benzotriazole (BTAH).
Benzotriazole is used as an effective inhibitor for several metal alloys and demonstrates high solubility in many aqueous media, good thermal stability, and has been able to chemical adsorbed in metal surface, due to nitrogen presence. In other words, some impressive advantages over the use of chenodeoxycholic acid. Furthermore, the equilibrium involving BTAH− and BTAH2− can contribute to physisorption and modulation of a space charge layer in a semiconductor/electrolyte interface [15, 16].
With a dye, BTAH might act efficiently avoiding dye aggregation, and shifting the oxide fermi level (Ef), influencing the charge separation and photoelectrochemical values of the cells [15, 17, 18]. Regarding toxicity and recent applications, concentrations lower than 2.10–2 mol L−1 are not toxic and relate to its use, beyond the corrosion inhibitor, BTAH has been used as protease inhibitor to several virus classes, such as Corona Virus (SARS-CoV) [19, 20].
This work aims to first report the application of BTAH as an additive to DSSC and understand their role in photoanode/electrolyte interface, as a new alternative to produce systems with superior photoelectrochemical parameters.
Experimental
The oxide paste was produced with 3 g the TiO2 (Aldrich® 25 nm 100% anatase), 1 ml of polyethylene glycol, 0.1 mL of acetylacetone, 4 mL of deionized water, and 0.1 mL of Triton-X. TiO2 suspension was coated by Doctor Blading method under FTO (~ 7 Ω sq−1 Aldrich®). After deposition, the films were sintered at 450 °C for 30 min followed by immersion for 12 h in N719 commercial dye solution (2.5 × 10–4 mol L in ethanol) containing 0.148 mg mL−1; 2 mg mL−1 and 20 mg mL−1 of BTAH [10].
The electrolyte was fabricated by mixing 0.5 mol L−1 tert-butylpiridine, 0.6 mol L−1 tetrabutylammonium, 0.1 mol L−1 lithium iodide, and 0.1 mol L−1 of resublimate iodine, in methoxypropionitrile [5]. The cathode catalyst was produced by Pt electrodeposition under FTO, using a three-electrode system, with FTO as a working electrode, Pt as a counter electrode, and Ag/AgCl as a reference electrode, using K2PtCl6 dissolved in HCl as electrolyte [18].
The solar cells were assembled in sandwich format, in an active area of 0.2 cm2. The electrochemical measurements of j-V curves were taken in Zhenium Zahner@ potentiostat with a solar simulator provided by a Xenon lamp at 100 mW cm−2. Electrochemical Impedance Spectroscopy (10 mHz–10 kHz at 10 mV of perturbation), Intensity Modulated Photovoltage Spectroscopy (IMVS), and Intensity Modulated Photocurrent Spectroscopy (IMPS) (100 mHz–1 kHz at 10 mW of perturbation) were performed in an auto lab potentiostat from Metrohm®, coupled with a led lamp of 530 nm at 50 mW cm−2.
Results and discussion
In Fig. 1 it is depicted the j-V curves to dye solar cells analyzed, and the photoelectrochemical results in Table 1.
It is well observed a reduced open circuit potential (Voc) to the cells with the BTAH amounts. It can be explained by the reduction of TiO2 conduction band edge, due to the protonation of oxide by N group contained in BTAH molecules [19, 20]. The reduced Voc can be seen as a negative point to solar cell working, by potentiated charge recombination reaction [21]. On the other hand, some papers demonstrated no relation between lower Voc with back-electron recombination suppression, as showed by Guimaraes and co-workers [12].
As the Voc is the difference between the quasi-Fermi level and the standard redox potential to the electrolyte, it is noted that BTAH amount in N719 dye has been able to shift the Ef level to more positive potentials [22]. One possible key to improve Voc values is synthesizing new dyes containing BTAH in their own composition, not acting only as a spacer, even to composing the sensitizing material [4].
The photoconversion energy efficiency (ɳ) was obtained using Eq. 1, where jsc is the short circuit current, FF fill factor, and Pin the incident power [23].
It has been observed superior ɳ value (4.26 ± 0.03) to the cell prepared with BTAH in 2.0 mg mL−1 condition when compared to the standard cell (3.78 ± 0.09). It demonstrated an efficiency boost of 12.8% in the energy conversion, due to superior photocurrent to the same BTAH condition. The ɳ values, when compared to literature were reduced since it was not made TiCl4 treatment and the scattering TiO2 layer was not used [24].
It is also observed, that BTAH in the concentration of 0.148 mg mL−1 has not demonstrated a different behavior when compared to bare cells (due to deviation values). In higher concentrations of 20.0 mg mL−1 and superior, it is expected an inhibition process of the charge collection, because BTAH molecules must occupy all the TiO2 active layer, reducing the current and PCE values [25]. The space charge region in TiO2/electrolyte interface (SCR) should be undergoing changes, improving electron collection rate (Reaction 1), and reducing the recombination reaction demonstrated by Reaction 2 [26]. For a better analysis of its supposed behavior, EIS measurements were taken and Bode diagram is depicted in Fig. 2.
In Bode diagram of Fig. 2, it is observed two different regions. Higher frequencies are related to Pt/Electrolyte interface and in lower frequencies, SCR interface [12]. It is noted a shift to reduced frequency values to the region of working electrode. As frequency and time are inversely proportional, lower frequencies mean a slowness in the charge transfer process, and to confirm this resistance, Nyquist plots (Fig. 3) were fitted using a simplified equivalent circuit (Fig. 1.SI) [11, 27,28,29]. The resistance values of TiO2/Dye, BTAH interface (RWE), and Pt/Electrolyte with the chemical capacitance (Cμ) were estimated in Table 2.
By adding BTAH in 2.0 mg mL−1 concentration, it is noted a great minimization of charge transfer resistance in TiO2/dye, BTAH/electrolyte interface. This behavior demonstrates a more conductive and less resistive system which should facilitate the charge transport mechanism, being a great advantage when compared to similar additives applications, that showed an increase in RWE [8]. At higher values of added benzotriazole, RWE starts to rise up, proving that at high amounts (> 20 mg mL−1) it is obtained a solar system with a charge process transfer minimized. Nyquist diagrams in Fig. 3 also demonstrate the same reduction in Zi values, with BTAH addition, which corroborates the jsc and ɳ values obtained from j-V curves (Table 1).
For the chemical capacitance (Cμ), it is observed proportional decreased values with the amounts of BTAH added, as also verified in Cμ versus f curves of Fig. 2.SI. This behavior has been shown a reduce in the electrical double layer formed at working electrode interface.
With equal or higher amounts of BTAH (> 20.0 mg mL−1), it is supposed to obtain an increased resistance value, due to TiO2 pores filling that would be filled by the photosensitive molecule, decumulating the Cμ. It is clear that there is a concentration threshold that potentiates the solar cell photoelectrochemical parameters which must be well analyzed. A schematic overview about these discussions is shown in Fig. 4.
As shown in Fig. 4, a vacancy site, due to dye absence is an active site of recombination reaction, caused by electrolyte filling [30]. With BTAH insertion, there is a deaggregation of the dye, due to a competition for a TiO2 surface site. As benzotriazole molecules present a reduced size, it is able to fill the vacancy sites, avoiding by a steric hindrance and oxide adsorption effect, the contact of TiO2 and oxidized electrolyte. As demonstrated in some papers, BTAH has been able to easily adsorb in several materials [19, 20]. The charge recombination process should still occur, due to conjugated duple bonds, however with a slower speed.
As Reaction 1 and 2 occurs in TiO2/electrolyte interface, it is not feasible to study the processes separately by EIS diagram. To well analyze the back-electron recombination and charge collection the IMVS and IMPS diagram were performed on cells and are depicted in Fig. 5A-B.
As the IMVS operates in open circuit condition and IMPS in short circuit, it is possible to calculate the electron lifetime ( e) and collection lifetime ( c) using Eq. 2 [29, 31, 32]. The calculated results are shown in Table 3.
In Fig. 5A, it is observed a shift to lower frequencies of the maximum frequency point to 2.0 mg mL−1 of BTAH when compared to an unmodified device. This condition suggested a superior electron lifetime, which is a positive point to dye solar device and was confirmed by values in Table 2 [10, 32]. It is seen a e = 0.041 s and a e = 0.034 s to 2.0 mg mL−1 and 0 mg mL−1 of BTAH, respectively, showing a prevention of charge recombination between I3− with TiO2 [5]. The presence of the organic structure in BTAH difficult to access of I3− species and these molecules also can occupy the vacancy sites in TiO2 semiconductors, developing a slow back-electron recombination. On the other hand, the 20 mg mL−1 BTAH addition has not been presented the best ɳ values to conditions tested, and despite superior e, its present low Cμ.
In the IMPS diagram, it is also noted a shift to higher frequencies with BTAH insertion, suggesting faster collection reactions. Using Eq. 2c was calculated and an improvement in collection time was observed when BTAH was added to the dye. This behavior, evidence that the used additive has been able to boost the collection in TiO2 semiconductor oxide [18]. Again, the steric effect is caused by benzene presence in a molecule, and also the N719 dye deaggregation, as the BTAH molecules might be positioning themselves between the dye molecules, rising up the charge separation and transportation in the semiconductor electrolyte interface. To 20 mg mL−1 of BTAH, despite amazing e and c presumably reduce the number of dye molecules anchored in TiO2 surface, supplying less electron under solar energy incidence, supported by jsc value in Table 1 [4, 11].
Then, it is important to emphasize that BTAH inserted in N719 dye solution is an amazing additive to be used in dye solar devices to enhance photoelectrochemical parameters.
Conclusions
BTAH molecules are effective additives in dye solar devices, able to enhance the photoelectrochemical parameters of the cell.
The back-electron recombination (e) can be restricted and the collection time (c) can be raised by BTAH presence. e and c enhancing are proportional to additive concentration, due to decreasing in recombination TiO2/electrolyte sites. On the other hand, higher BTAH amounts, difficult the dye anchoring, reducing the photoelectrochemical parameters.
The best solar cell was achieved at concentration of 2.0 mg mL−1 of BTAH, reaching a jsc = 9.92 ± 0.26, Voc = 0.770 ± 0.022, FF = 0.557 ± 0.014, ɳ = 4.26 ± 0.13, e = 0.034 s and c = 0.082 s with lower charge transfer resistance.
References
Karimi-nazarabad M, Goharshadi EK, Sajjadizadeh H (2022) Copper−azolate framework coated on g ‑ C3N4 nanosheets as a core−shell heterojunction and decorated with a Ni (OH)2 Cocatalyst for efficient photoelectrochemical water splitting. https://doi.org/10.1021/acs.jpcc.2c01570
M. Karimi-nazarabad, H. Ahmadzadeh, E.K. Goharshadi, Porous perovskite-lanthanum cobaltite as an efficient cocatalyst in photoelectrocatalytic water oxidation by bismuth doped g-C 3 N 4. Sol Energy 227, 426–437 (2021). https://doi.org/10.1016/j.solener.2021.09.028
B. O’Regan, Grätzel M (1991) A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films. Nat 3536346(353), 737–740 (1991). https://doi.org/10.1038/353737a0
A.F. Buene, D.M. Almenningen, A. Hagfeldt, O.R. Gautun, B.H. Hoff, First report of chenodeoxycholic acid-substituted dyes improving the dye monolayer quality in dye-sensitized solar cells. Sol RRL (2020). https://doi.org/10.1002/solr.201900569
Tractz GT, Viomar A, Dias BV, De Lima CA, Banczek EP, Da Cunha MT, Antunes SRM, Rodrigues PRP (2019) Recombination study of dye sensitized solar cells with natural extracts. J Braz Chem Soc. https://doi.org/10.21577/0103-5053.20180186
R. Vittal, K.C. Ho, Zinc oxide based dye-sensitized solar cells: A review. Renew Sustain Energy Rev 70, 920–935 (2017). https://doi.org/10.1016/j.rser.2016.11.273
J. Lee, N. Park, Y. Shin, Solar energy materials & solar cells nano-grain SnO2 electrodes for high conversion efficiency SnO 2 – DSSC. Sol Energy Mater Sol Cells 95, 179–183 (2011). https://doi.org/10.1016/j.solmat.2010.04.027
B. O’Regan, M. Grätzel, A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films. Nature 353, 737–740 (1991). https://doi.org/10.1038/353737a0
Gratzel M (2001) Photoelectrochemical Cells. Nature 414:
T. Tractz, F. Staciaki, S. Regina, M. Antunes, P. Banczek, M. Taras, P. Rog, Nb2O5 synthesis and characterization by Pechini method to the application as electron transport material in a solar device. Sol Energy 216, 1–6 (2021). https://doi.org/10.1016/j.solener.2021.01.029
D.F.S. Rodrigues, F. Santos, C.M. Abreu, J.F. Coelho, A. Serra, D. Ivanou, A. Mendes, Passivation of the TiO2 surface and promotion of N719 dye anchoring with poly(4-vinylpyridine) for efficient and stable dye- sensitized solar cells. ACS Sustain Chem Eng 9, 5981–5990 (2021). https://doi.org/10.1021/acssuschemeng.1c00842
R.R. Guimaraes, A.L.A. Parussulo, T.A. Matias, H.E. Toma, K. Araki, Electrostatic blocking barrier as an effective strategy to inhibit electron recombination in DSSCs. Electrochim Acta 255, 92–98 (2017). https://doi.org/10.1016/j.electacta.2017.09.096
B. Boro, B. Gogoi, B.M. Rajbongshi, A. Ramchiary, Nano-structured TiO2/ZnO nanocomposite for dye-sensitized solar cells application: a review. Renew Sustain Energy Rev 81, 2264–2270 (2018). https://doi.org/10.1016/j.rser.2017.06.035
R.T. Ako, D.S.U. Peiris, P. Ekanayake, A.L. Tan, D.J. Young, Z. Zheng, V. Chellappan, DSSCs with ZnO@TiO2 core-shell photoanodes showing improved Voc: Modification of energy gradients and potential barriers with Cd and Mg ion dopants. Sol Energy Mater Sol Cells 157, 18–27 (2016). https://doi.org/10.1016/j.solmat.2016.05.009
G. Boschloo, L. Häggman, A. Hagfeldt, Quantification of the effect of 4-tert-butylpyridine addition to I -/I3- redox electrolytes in dye-sensitized nanostructured TiO2 solar cells. J Phys Chem B 110, 13144–13150 (2006). https://doi.org/10.1021/jp0619641
P.R. Rodrigues, I. Aoki, A.H. De Andrade, E. De Oliveira, S.M. Agostinho, Effect of benzotriazole on electrochemical and corrosion behaviour of type 304 stainless steel in 2M sulphuric acid solution. Br Corros J 31, 305–308 (2014). https://doi.org/10.1179/bcj.1996.31.4.305
M.T. da Cunha, P.R.P. Rodrigues, G.G.O. Cordeiro, E. D’Elia, S.M.L. Agostinho, Electrochemical studies of the interface Fe/0.5 mol L-1 H2SO4 in the presence of benzotriazole and tolytriazole. Mater Chem Phys 116, 469–473 (2009). https://doi.org/10.1016/j.matchemphys.2009.04.025
T. Valerio, G.T. Tractz, G.A.R. Maia, E.P. Banczek, P.R.P. Rodrigues, Minimizing of charge recombination by Nb 2 O 5 addition in dye-sensitized solar cells. Opt Mater (2020). https://doi.org/10.1016/j.optmat.2020.110310
E.P. Banczek, P.R.P. Rodrigues, I. Costa, Investigation on the effect of benzotriazole on the phosphating of carbon steel. Surf Coat Technol 201, 3701–3708 (2006). https://doi.org/10.1016/j.surfcoat.2006.09.003
M.M. Mennucci, E.P. Banczek, P.R.P. Rodrigues, I. Costa, Evaluation of benzotriazole as corrosion inhibitor for carbon steel in simulated pore solution. Cem Concr Compos 31, 418–424 (2009). https://doi.org/10.1016/j.cemconcomp.2009.04.005
A. Viomar, G.A.R. Maia, F.R. Scremin, N.M. Khalil, M.T. Cunha, A.C. Antunes, P.R.P. Rodrigues, Influence of obtaining method of Nb2O5 particles used in dye sensitized solar cells consisting of TiO 2 / Nb 2 O 5. Rev Virtual Química (2016). https://doi.org/10.5935/1984-6835.20160064
A. Gopalraman, S. Karuppuchamy, S. Vijayaraghavan, High efficiency dye-sensitized solar cells with: V OC- J SC trade off eradication by interfacial engineering of the photoanode|electrolyte interface. RSC Adv 9, 40292–40300 (2019). https://doi.org/10.1039/c9ra08278f
S. Kundu, P. Sarojinijeeva, R. Karthick, G. Anantharaj, G. Saritha, R. Bera, S. Anandan, A. Patra, P. Ragupathy, M. Selvaraj, D. Jeyakumar, K.V. Pillai, Enhancing the efficiency of DSSCs by the modification of TiO2 photoanodes using N, F and S, co-doped graphene quantum dots. Electrochim Acta 242, 337–343 (2017). https://doi.org/10.1016/j.electacta.2017.05.024
G.G. Sonai, A. Tiihonen, K. Miettunen, P.D. Lund, A.F. Nogueira, Long-term stability of dye-sensitized solar cells assembled with cobalt polymer gel electrolyte. J Phys Chem C 121, 17577–17585 (2017). https://doi.org/10.1021/acs.jpcc.7b03865
Tractz T, Paula A, Matheus C, Fernanda L, Larsson G, Rodrigues P (2022) The use of 2-Mercaptobenzothiazole as a new co-adsorbent in dye-sensitized solar cells. 131: . https://doi.org/10.1016/j.optmat.2022.112658
K. Ocakoglu, F. Yakuphanoglu, J.R. Durrant, S. Icli, The effect of temperature on the charge transport and transient absorption properties of K27 sensitized DSSC. Sol Energy Mater Sol Cells 92, 1047–1053 (2008). https://doi.org/10.1016/j.solmat.2008.03.006
S. Kushwaha, S. Mandal, S. Subramanian, S. Aryasomayajul, K. Ramanujam, A DSSC with an efficiency of ∼10 %: fermi level manipulation impacting the electron transport at the photoelectrode-electrolyte interface. ChemistrySelect 1, 6179–6187 (2016). https://doi.org/10.1002/slct.201601461
C. Longo, M.A. De Paoli, Dye-sensitized solar cells: a successful combination of materials. J Braz Chem Soc 14, 889–901 (2003). https://doi.org/10.1590/S0103-50532003000600005
J. Bisquert, V.S. Vikhrenko, Interpretation of the time constants measured by kinetic techniques in nanostructured semiconductor electrodes and dye-sensitized solar cells. J Phys Chem B 108, 2313–2322 (2004). https://doi.org/10.1021/jp035395y
Hagfeldt A, Boschloo G, Sun L, Kloo L, Pettersson H (2010) 2010 ChemReview_Hagfeldt.pdf. 6595–6663
P. Xiang, F. Lv, T. Xiao, L. Jiang, X. Tan, T. Shu, Improved performance of quasi-solid-state dye-sensitized solar cells based on iodine-doped TiO2 spheres photoanodes. J Alloys Compd 741, 1142–1147 (2018). https://doi.org/10.1016/j.jallcom.2018.01.220
L.L. Li, Y.C. Chang, H.P. Wu, E.W.G. Diau, Characterisation of electron transport and charge recombination using temporally resolved and frequency-domain techniques for dye-sensitised solar cellse. Int Rev Phys Chem 31, 420–467 (2012). https://doi.org/10.1080/0144235X.2012.733539
Acknowledgements
This study was financed in part by the Coordenação de Aperfeiçoamento de Pessoal e Nível Superior-Brasil (CAPES). The authors are also grateful to CNPq, SETI/UGF, Fundação Araucária, UNICENTRO-PR and UTFPR.
Author information
Authors and Affiliations
Corresponding author
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Springer Nature or its licensor holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Tractz, G.T., Matheus, A.P.C., Larsson, L.F.G. et al. First application of benzotriazole as a dye additive to dye-sensitized solar cells: electrochemical device characterization. J IRAN CHEM SOC 20, 79–85 (2023). https://doi.org/10.1007/s13738-022-02645-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13738-022-02645-1