Abstract
The enhanced photocatalytic performance of nanocomposite is synthesized via the hydrothermal method and characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM), Fourier transform infrared spectroscopy (FT-IR), UV–visible diffuse reflectance spectroscopy (UV–Vis DRS) and photoluminescence spectroscopy (PL). Under visible light irradiation, PVA assisted Bi2WO6–CdS nanocomposite film displayed enhanced photocatalytic efficiency and inhibition of photocorrosion as compared with pure CdS, pure Bi2WO6 and Bi2WO6–CdS composite. The PVA assisted Bi2WO6–CdS composite film catalyst showed stable catalytic performance until seven successive runs with 92% of methylene blue(MB) degradation, and easy to recover after degradation of organic pollutant. PVA assisted Bi2WO6–CdS nanocomposite film has optimal band edge position for superior photocatalytic degradation. Furthermore, the trapping experiment was carried out using different scavenger for active species. Among the active species, OH· are the most responsive species which play a vital role in the degradation of metronidazole and MB.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Dyes play a major role in various branches of dying industries such as bleaching, textile, medicine and paper industries (Chauhan et al. 2014; Shanavas et al. 2017). The dye-based industries liberating ~ 10% of non-bio degradable dye wastages with highly colored water, which are deleterious to the environment (Ahmedchekkat et al. 2011; Bazin et al. 2012). The existing dye water leads to interfere with the penetration of light and thus reducing the photosynthesis of aquatic plants which severely annihilate the aquatic ecosystem (Ni et al. 2007). Many organic dyes are toxic and carcinogenic like azo dyes; Congo red, methylene blue and Rhodamine B these may lead to the jeopardizing aquatic organism and also human health (Wong et al. 2004). Generally, the degradation of organic pollutants are mainly classified into three types such as (1) physical technologies: adsorption, reverse osmosis, ultra-filtration. (2) Chemical process: chlorination, ozonation, precipitation, catalyst-chemical oxidation. (3) Biological process: enzymatic decomposition, biodegradation.
In this regards over the past decades, photocatalytic degradation of organic pollutants and water splitting using nano heterogeneous photocatalyst have immense important due to its feasibility and low cost (Ajmal et al. 2014; Chen and Mao 2007). TiO2 is one of the most accepted photocatalysts because of biologically and chemically inert (Boobas et al. 2017) and its high photostability, nontoxicity, and low cost, but it has some drawbacks of wide band gap, low quantum yield and only under ultraviolet region (Kudo and Miseki 2009). In case of metal chalcogenides, particularly metal sulfides, have much higher photocatalytic activity (e.g., CdS, ZnS, SnS2) although metal sulfides are subjected to oxidize by photogenerated holes known as photocorrosion. Among them, various narrow band gap semiconductors, CdS (~ 2.4) can directly absorb visible light at wavelengths ~ 550 nm, which is a good candidate to apply as a photocatalyst. Even though the pure CdS suffered by rapid recombination rate of photogenerated charge carriers and photocorrosion during the catalytic action and restricting its potential application. Many researchers focused to overcome the above problem by various technologies (Wang et al. 2016a; Yu et al. 2016). Incorporation of metal sulfides into interlayer and mesoporous materials have a long time efficient for stabilizing the metal sulfides (Shangguan and Yoshida 2002; Shen and Guo 2006). In the midst of various semiconductor photocatalyst, aurivillius family and its layered structure have attractive future and much attention because of hybridized valance band O 2p and Bi 6s (Tang et al. 2007; Garcia-Perez et al. 2012; Zhu et al. 2013; Dong et al. 2014a). Aurivillius oxide photocatalytic semiconductors (Bi2 An−1 B n O3n+3) A = Ca, Sr, Ba, Pb, Na, K and B = Ti, Nb, Ta, Mo, W, Fe (Guo et al. 2013; Zhang et al. 2009; Fu et al. 2005). Bismuth oxyhalide (Chatterjee and Dasgupta 2005; Wang et al. 2011) has the abundant head of the researchers, in the midst of these, Bi2WO6 (Saison et al. 2013; Zhuo et al. 2013; Dumrongrojthanath et al. 2013; Saison et al. 2011) has much higher photocatalytic activity and stability in visible and ultraviolet light irradiation and has a wide band gap. However, it also suffered by rapid recombination of photogenerated electrons and holes and unsuitable conduction band edge position (Ren et al. 2015). Meanwhile, among various conjugated polymers, nanocomposites on the polymer substrates or polymer-assisted nanocomposites are attractive to solve the problems concerning the recovery processes during the photocatalytic action. PVA is a hydrophilic polymer which has been explored in a wide range of application including biomaterials and drug delivery system because of biocompatibility and nontoxicity (Jung and Kim 2014; Liu et al. 2015a; Moon et al. 2013; Krishnakumar et al. 2017). Coupling of one or more active components to effectively make heterostructures like CaWO4/Bi2WO6 composite, Bi2WO6/CeO2 hybrid nanoparticles and Ag2CO3/Bi2WO6 heterojunction (Guo et al. 2012a, 2014; Bao et al. 2015), are a more powerful method to overcome the demerits of all traditional photocatalyst. In the last few years, making binary nanomaterials using aurivillius oxide semiconductors (Zhang et al. 2016; Liu et al. 2015b) and ternary (CNNS/CdS/rGO), (CeO2/SnO2/rGO), (La2CuO4/CeO2/rGO) (Zhou et al. 2016; Priyadharsan et al. 2017; Shanavas et al. 2017) plays a vital role in dye degradation. The heterostructure of nanomaterials have much higher efficiency compared to above all, because of interfacial charge transfer between the heterostructure, therefore, it can highly retain the recombination of photogenerated charge carriers.
In this research work, we analyzed the structure and morphology-based many metal chalcogenides, and aurivillius family heterostructure (Kundu et al. 2017; Luo et al. 2016; Kandi et al. 2017; Xiao et al. 2016; He et al. 2011), CdS and Bi2WO6 (Tang et al. 2015) have well-matched energy levels and efficient photocatalytic degradation of organic dyes but also had some drawbacks, especially metal sulfides suffered by photocorrosion. The mixing of photocatalyst nanocomposite with the polymeric substrate is a new way to solve the current problem; recovery of photocatalyst and inhibition of photocorrosion. In our work, as-synthesized Bi2WO6–CdS heterostructures; dispersed into polymer (PVA) matrix. The cost-effective transparent PVA assisted Bi2WO6–CdS nanocomposite film exhibit a recycling stability and ease of recovery in the photodegradation process.
Experimental
Synthesis of CdS nanoparticle
All the chemical reagents and organic targets were of analytical grades and used without further purification. CdS NPs were synthesized by a previously reported hydrothermal route (Cheng et al. 2016), the required molar ratio of [Na2S·xH2O] sodium sulfide solution was added dropwise into the [CdCl2·2½ H2O] cadmium chloride solution and stirred vigorously for 8 h. The stirred solution was left aging for another 4 h to get the product. Furthermore, it was ultrasonicated with water and transferred into 100 ml Teflon-lined autoclave kept in 24 h at 180 °C. Finally, the yellow color precipitate was washed several times with ethanol and distilled water and the product was dried at 100 °C for 10 h for further characterization.
Synthesis of Bi2WO6–CdS nanocomposite
In the typical synthesis of Bi2WO6–CdS nanocomposite 0.12 g of [Bi(NO3)3·5H2O] bismuth nitrate pentahydrate was dissolved in 50 ml of ethylene glycol. On the other hand 0.06 g of [Na2WO4·2H2O] sodium tungstate was dissolved in 80 ml deionized water and stirred for 3 h, these two solutions were mixed and stirred until to obtain a homogeneous suspension. Afterwards, the required amount of CdS nanoparticles was dispersed by ultrasonication for 10 min and mixed with this solution. Then the suspension was transferred into the Teflon-lined autoclave kept at 180 °C for 20 h. The product was washed several times using ethanol and distilled water to remove moistures; the finally obtained precipitate is dried at 100 °C for 4 h. The same procedure is repeated for preparation of Bi2WO6 nanoparticles without the addition of CdS.
Synthesis of PVA assisted Bi2WO6–CdS nanocomposite film
PVA assisted Bi2WO6–CdS nanocomposite film was prepared via hydrothermal method. The cold soluble polymer was [–CH2CHOH–] n stirred for 2 h to get a homogenous solution, the prepared Bi2WO6–CdS nanocomposite was ultrasonicated for 30 min and then mixed with the polymer, continuously stirred for another hour to get a composition. It was transferred into 100 ml Teflon-lined autoclave and gave heat treatment at 180 °C for one hour. Then colloidal solution is poured into silica glass plate and dried to evaporate the solvent.
Characterization methods
Phase structure of the synthesized catalyst was examined by powder X-Ray diffraction using Rigaku X-ray diffractometer Cu-Kα radiation (K = 1.54 Å) in the 2θ range of 20°–80° at room temperature. The surface chemical elemental analysis was conducted on an X-ray photoelectron spectroscopy (XPS) (SPECS GmbH spectrometer with Phobios 100MCD Energy analyzer) depth profiling facility. Fourier transform infrared (FT-IR) spectra of all the samples were recorded using a Bruker Tensor 27 spectrophotometer with a resolution of 2 cm−1 in the range of 4000–400 cm−1 at room temperature. Whereas the morphology of the sample was analyzed by field emission scanning electron microscopy [FESEM] with the feature of energy dispersive X-ray diffraction spectrum. Optical properties namely UV–Vis DRS and photoluminescence of the all the prepared catalyst were evaluated by Ocean Optics PX-2 and Perkin Elmer LS-45 fluorescence spectrometer, respectively.
Photodegradation assessment and setup
Methylene blue and metronidazole acted as target substrates for examining the photocatalytic activity of as-synthesized photocatalyst under visible light irradiation. In a typical process 2 × 2 cm3 of nano-photocatalyst was dipped (100 ml) in 20 ppm solution of methylene blue. For metronidazole 3 × 3 cm3 for 100 ml in 0.1 mg were used, simultaneously the pH value would be monitored. Photodecomposition activity was carried out using 500 W halogen lamp as visible light source and the glassware with double walled for the purpose of circulating water system to maintain a sustained environment of temperature, before the irradiation of visible light. To ensure the formation of adsorption and desorption equilibrium of the organic pollutant with catalyst, the solution was ultrasonicated for 20 min and then stirred for 1 h in dark environment. During the process of decomposition at every 20 min, 6 ml of solution were sampled and centrifuged to remove the catalyst. The photocatalytic efficiency was investigated by the following equations (Mirhoseini and Salabat 2015):
where C0 and C are initial and variable reaction concentration, respectively. In the degradation process, the absorption intensity for all the catalyst would be A0 and the significant time interval of the reduced absorption be A, the efficiency was calculated as follows:
To get better understanding of kinetics reaction, the experimental data fitted by a pseudo-first-order model. The equation for calculation is as follows:
where C0 is the initial concentration of dye, C is the concentration at desired time interval Kapp is the apparent first-order rate constant.
Trapping of active species
The main active species produced in the photodecomposition process of MB and metronidazole confirmed by the trapping agents such as benzoquinone, ethylenediaminetetraacetate, isopropyl alcohol and silver nitrate. They were introduced into to the degradation process to trap superoxide (O ·−2 ), holes (h+), hydroxyl (OH·), and electron (e−), respectively. All these trapping agents were in the quantity of 5 mmol except BQ which was in 1 mmol to prevent the causes of dye during the reaction. Further, the hydroxyl radicals of all the samples were confirmed by the aid of photoluminescence of terephthalic acid.
Results and discussion
X-ray diffraction analysis
The crystalline structure, appropriate particle size and phase purity of as-synthesized catalysts examined by powder X-ray diffraction pattern. The prepared bare CdS, Bi2WO6, Bi2WO6–CdS and PVA assisted Bi2WO6–CdS nanocomposite film are separately shown in Fig. 1. The sharp peak in the powder X-ray diffraction pattern exposed the well crystalline nature of the prepared sample. Bare Bi2WO6 nanoparticle exhibit intense diffraction peaks at 28.16, 32.68, 35.70, 47.07, 51.08, 55.02, 58.54, 68.74, 75.89, 78.30, which corresponds to (113), (006), (115), (206), (224), (313), (226), (400), (139), (406) planes of the russellite (orthorhombic) structure and also exactly matches the JCPDS card No 73-1126. The pure CdS reveals peaks at 24.66, 26.39, 28.30, 36.42, 43.58, 47.64, 51.68, 58.02, 66.74, 69.39, 70.91, 72.35, 75.40,79.99. Which could be well indexed to the (100), (002), (101), (102), (110), (103), (200), (202), (203), (210), (211), (114), (105), (300) crystal planes of wurtzite (hexagonal) phase [JCPDS card No 06-0314]. In both cases, no additional peaks were found, which shows the absence of other phases or any other impurities. Whereas the XRD pattern of the as-synthesized Bi2WO6–CdS heterostructure, and PVA assisted Bi2WO6–CdS nanocomposites film, possess both Bi2WO6 and CdS nanomaterials with less intensity. It could be due to the synergistic effect of the two nanomaterials and additional peaks at 13.86, 16.72 were observed in PVA assisted Bi2WO6–CdS nanocomposite film due to the crystalline and semi-crystalline nature of PVA. The appropriate crystallite size of all the samples calculated using Debye–Scherrer’s equation
D mean diameter of the crystallite, K = 0.96 is constant, \( \lambda \) is wavelength (1.54 Å), β full width half maximum, θ is diffraction Braggs angle.
The structural parameters of the samples like dislocation density (δ), stacking faults (SF), intercrystalline separation (R), are calculated by the following equation (Hemalatha and Rukmani 2016). The values are tabulated in the Table 1.
The lattice parameters calculated using Eqs. (5) and (6) and their values are tabulated in Table 2:
Thus, the hexagonal phases of CdS possess a longer absorption in the visible light region and higher activity compared to cubic phases (Silva et al. 2008; Tian et al. 2012). The bare CdS nanoparticles have to aggregate due to their instabilities; therefore, reducing the aggregation by their heterostructures and doping would enhance the surface area and thus would help to improve the catalytic performance (Kumar and Ojha 2016). Composites show less crystalline nature compared to the pure CdS and Bi2WO6 thus it could enhance the crystal surface imperfection like dislocation, stacking faults which turn to increase reaction centers (Zhang et al. 2007). The rate of structural defects could increase the number of chemically reactive sites, and the defects and disorders could change the equilibrium coordination number, that’s why chemical reaction would increase further defects tend to lower the bandgap because of the introduction of new band position (Li et al. 2017).
XPS analysis
The oxidation states and surface chemical composition of the nanocomposite film were characterized by X-ray photoelectron spectroscopy (XPS). Typical survey XPS spectrum of Bi2WO6–CdS/PVA indicates that Bi, W, Cd, S, C and O elements could all be detected as shown in Fig. 2a. The high-resolution XPS spectra of Bi 4f, W 4f, Cd 3d, S 2p, C 1s and O 1s is shown in Fig. 2b–g. Figure 2b shows the two bands at 159.15 and 164.16 eV ascribed to Bi 4f7/2 and Bi 4f5/2, respectively, which can be attributed to Bi3+ in the crystal structure. The peak at 36.2 and 37.6 eV as shown in Fig. 2c, corresponding to W 4f7/2 and W 4f5/2, respectively, can assign to be a W6+ oxidation state of Bi2WO6–CdS/PVA (Zhang et al. 2006). Figure 2d represents the binding energies of 405.28 and 412.60 eV corresponds to the Cd 3d5/2 and Cd 3d3/2 respectively (Li et al. 2013). The S 2p spectrum was divided into two different peaks is shown in Fig. 2e. The peak at 161.15 eV could be a credit to the S2− anion, and the other one at 167.12 eV could be assigned to the oxidized SO42− form (Bandyopadhyay et al. 1997). From Fig. 2f, it was observed that the peaks with binding energies of 284.2 and 287.65 could be assigned to the C 1s spectra of C–C and C–O, respectively. The C–C bond bond confirm the main chain of PVA (Wei et al. 2011). Furthermore, Fig. 2g show that two peaks fitted the O 1s spectrum. The peak at 530.35 eV can be due to the metal oxides, the broad peak at 533.04 eV indicates the binding energy of C–OH bond in PVA (Gu et al. 2012). Based on these observations and analyses the results exhibit that the formation of Bi2WO6–CdS/PVA composite occurs, which is in better agreement with the results of the EDX and XRD analysis.
FT-IR analysis
The chemical state of as-synthesized Bi2WO6, CdS, Bi2WO6–CdS and PVA assisted Bi2WO6–CdS nanocomposite film explored via FT-IR spectroscopy and their spectrograms are shown in Fig. 3. The spectrum reveals the band absorption peak at 3000–3600 cm−1 in bare nanoparticles is assigned to the OH stretching vibration of a physically observed water molecule. In Bi2WO6 several characteristic peaks were observed at wavenumbers 1395, 725, 583 cm−1 are due to the W–O–W bridging, W–O stretching, Bi–O stretching vibration, respectively (Liu et al. 2015c; Wei et al. 2014; Guo et al. 2012b). In the case of CdS, Cd–S stretching vibration occurred below 700 cm−1. Meanwhile, PVA assisted Bi2WO6–CdS nanocomposite film shows vibrations at 3000–3109 cm−1 are due to the O–H stretching vibration hydroxyl groups due to polymeric or water molecules, and then CH, C=O, C=C, and C–C stretching, rocking vibrations are assigned at 2970, 1746, 1605, 1525 and 900 cm−1, respectively (Krishnakumar and Shanmugam 2012; Chen 2002; Rao et al. 2015; Mallakpour and Vahabi 2015). In PVA assisted Bi2WO6–CdS nanocomposite film, the content of nanoparticle loading is very low, therefore, the interaction of nano heterostructures with nanostructured polymer was unpredictable from the FT-IR spectrum.
Morphology analysis
The surface morphology of all prepared samples was characterized by FESEM and their micrographs are shown in Fig. 4. It was observed that the bismuth tungstate shows spheroid structure. CdS show loosely agglomerated well-defined spherical shape with the high surface area, meanwhile, in the case of Bi2WO6–CdS nanocomposite CdS nanospheres were sprinkled on the core Bi2WO6 structure. The CdS nanosphere agglomeration get suppressed when it is adhered to the surface of Bi2WO6 and their particle size could enhance by deposition of CdS. In the case of PVA assisted Bi2WO6–CdS nanocomposite film, the dark spot shows a shapeless surface passivated structure which is attributed to the crystalline nature of polymer in nanoscale, the bright spot indicates the surface modified agglomerated Bi2WO6–CdS nano-heterostructures. This type of morphology might enhance the photocatalytic degradation performance.
EDX analysis
The representative EDX spectra of synthesized samples examined by the integrated feature of FESEM, and their graphs are shown in Fig. 5. In Bi2WO6 the Bi, W, O elements were confirmed and their wt% are 48.15, 35.09, 16.76, respectively. The established CdS spectra show Cd, S element with 76.10, 23.10 wt% correspondingly. Whereas the Bi2WO6–CdS shows the presence of above-mentioned all elements with slight changes in wt% (Cd, Bi, W, O, S with 29.78, 26.98, 25.55, 9.08, 8.60 wt% singly). But PVA assisted Bi2WO6–CdS nanocomposite film confirms the presence of H, C, O, Cd, Bi, W, S elements with 51.73, 23.57, 15.97, 1.65, 0.26, 6.15, 0.69 wt%, respectively. No other impurities are found in all the samples.
UV–Vis diffuse reflectance spectra
All the prepared photocatalysts subjected to optical characterization of UV–Vis DRS techniques using Ocean Optics PX-2 spectrophotometer, and the results are shown in Fig. 6. The Bi2WO6 nanoparticle exhibited the strong absorption edge ultraviolet and visible region approximately 420 nm is owing to the band gap photoexcitation of Bi2WO6. On the other hand, CdS exhibit the intensive absorption edge around 600 nm due to its response to visible light. When adding CdS to Bi2WO6 the absorption edge shows blue shifts 575 nm and it could gather few number of photons compared to bare Bi2WO6 and CdS (Zou et al. 2016). Then the PVA assisted Bi2WO6–CdS composite film also exhibited absorption edge in visible region 560 nm. This blue shift of absorption indicates that the composites exhibit quantum confinement effect (Jing and Guo 2007). From above obtained results PVA assisted Bi2WO6–CdS nanocomposite film has higher absorption maximum in the visible region. The band gaps of all the samples were calculated with the help of tauc plot and shown in inset Fig. 6 using the following equation (Zheng and Liu 2007)
α is the absorption coefficient, h is the plank constant, ν is the frequency of light, Eg is the band gap, A is the proportionality constant, respectively, n = (1, 4) depend on the type of optical transition whether direct or indirect. Therefore, plotting between (αhν)2 and (hν) by extrapolating the linear portion of the curve to zero absorption coefficient. The band gap of pure Bi2WO6, CdS, Bi2WO6–CdS and PVA assisted Bi2WO6–CdS nanocomposite film calculated, and their values are given by 3.32, 2.16, 2.25 and 2.41 eV, respectively. The PVA assisted Bi2WO6–CdS nanocomposites film show low band gap compared to that of Bi2WO6 materials, because of changes in optical properties suffered by the interaction between the pure CdS and Bi2WO6 nanomaterials (Guo et al. 2016). Although the band gap of PVA assisted Bi2WO6–CdS nanocomposites film, due to the intermediate transaction of electrons in between the composite materials the recombination rate will be declined and the observed result is further confirmed through PL study. These results illustrate that the PVA assisted Bi2WO6–CdS nanocomposite film can be excited in visible light region due to the deposition of CdS nanoparticles on its surface.
Photoluminescence spectroscopy
Photoluminescence spectroscopy is used to assess the recombination efficiency of photogenerated electrons and holes in photocatalytic reaction. Photoluminescence properties of all the products are shown in Fig. 7. The more intense peak assigned to CdS and thus more emission occurs due to a large amount of recombination of photogenerated charge carriers. The Bi2WO6 and PVA could reduce the photoemission, and the composite often indicates a drastic decrease in its intensity and confirmed the sensible suppression and recombination of electron and hole which improved photocatalytic activity. PVA/Bi2WO6–CdS has narrow optical band gap than Bi2WO6, this could give highly harvesting photons from UV–Vis light, and it could retain the recombination of generated charge carriers. The PL intensity of PVA assisted nanocomposite film shows less intensity compared to all other prepared photocatalyst, thus result from most of the surface states are passivated by making the availability of the electron for catalytic action (Wang et al. 2016b). The weaker PL intensity is, the higher separation efficiency of photoinduced charge (electron–hole separation), so that higher photocatalytic degradation behavior was preferred. Thus, the result indicates that compared with pure CdS and Bi2WO6 samples, the photocatalytic efficiency of PVA/Bi2WO6–CdS photocatalyst may be greatly improved.
Photocatalytic degradation of metronidazole
Drugs occupy an important place in the water pollution due to the availability of many healthcare products such as antibiotics, analgesics, anti-inflammatories and hypnotics, and high consumption rate of a human being and veterinary medication (Kansal et al. 2014). The drugs occupy the aquatic environment from various ways such as pharmaceuticals, industrial effluents and domestic effluents, the disposal of rude discarding of extra drugs in households, medicinal care, and healing treatment of livestock (Farzadkia et al. 2014). High concentration of antibiotics can involve serious risk for the human being and natural system because high solubility causes them, long-term presence, more toxic, cancerogenic, less adsorption, non-biodegradability nature. The effluent of wastewater from pharmaceuticals industries must be treated adequately before entry into natural water streams, to remove the contaminant caused by antibiotics. In over the past decades antibiotic effluents from industries act as a target pollutants to degrade using photocatalyst such as quinoline content and levofloxacin (Kansal et al. 2014), amoxicillin, glycopeptide, macrolide, sulphonamide (Kummerer 2009), tetracycline (Safari et al. 2015; Zhao et al. 2013), sulfamethoxazole (Abellan et al. 2009; Abellan et al. 2007), chloramphenicol (Chatzitakis et al. 2008) and metronidazole (Farzadkia et al. 2014). Among them metronidazole has been studied by many researchers, metronidazole antibiotics (2-methyl-5-nitro-imidazole-1-ethanol) was a derivative of nitroimidazole, which was widely used in the treatment of infectious diseases like anaerobic bacteria, protozoans, Bacteroides. Continuos and increasing the content of metronidazole is more carcinogenic and mutagenic, researchers have been paid mandatory to remove this type of contaminants completely before they are discharged from industries (Farzadkia et al. 2014; Liu et al. 2013; Dong et al. 2014b) here by all the problems aforementioned we choose metronidazole as a target organic contaminants.
The photocatalytic activities of pure CdS, Bi2WO6, binary Bi2WO6–CdS and PVA–Bi2WO6–CdS nanocomposite were evaluated by the metronidazole shown in Fig. 8a. From the result, PVA–Bi2WO6–CdS nanocomposite shows enhanced photocatalytic efficiency when compared to other binary composites such as Bi2WO6–CdS and parent photocatalysts like Bi2WO6 and CdS. The parent photocatalyst shows the limited amount of catalytic efficiency, but after coupling PVA with of CdS–Bi2WO6, the photocatalytic degradation of metronidazole significantly enhanced, achieving almost 70% after the irradiation of visible light for 100 min. Due to the composition of CdS–Bi2WO6 with PVA can serve as charge traps thus could retarding electron–hole combination rate and thereafter enhancing the interfacial charge transfer for metronidazole degradation. In addition to this connection, PVA coupled with binary Bi2WO6–CdS composite the photocorrosion phenomenon would be minimized, so that the durability and photostability increased. To understand the photocatalytic activity of pure CdS, Bi2WO6, binary Bi2WO6–CdS, and PVA–Bi2WO6–CdS nanocomposite can be described by pseudo-first-order kinetics, in Fig. 8b shows a linear relationship between ln(C0/C) and reaction time, indicating that the photodegradation of metronidazole follows first-order kinetics. The calculated values of Kapp or K were given by 0.0120, 0.0110, 0.0090 and 0.0070 for PVA assisted Bi2WO6–CdS, Bi2WO6–CdS, Bi2WO6, and CdS, respectively. Indeed thus from the values of K it is clear that the PVA assisted Bi2WO6–CdS nanocomposite film shows highest photocatalytic activity. A nanocomposite film possesses more activity 1.7142, 1.333 and 1.0909 times higher than CdS, Bi2WO6 and Bi2WO6–CdS, respectively; this is due to highly suppressed photogenerated carriers. Furthermore, UV–visible spectra confirmed the enhanced photocatalytic degradation efficiency of PVA–Bi2WO6–CdS nanocomposite film an antibiotic solution of metronidazole. The absorption spectrum of efficient PVA–Bi2WO6–CdS nanocomposite film are shown in Fig. 9. The absorption spectra of metronidazole show the characteristic peak (absorption maximum) at approximately λmax 320 nm. The photocatalytic degradation of metronidazole observed for every 20 min time interval at constant irradiation of UV–visible light. From the observation of absorption spectrum, drastically decrease the absorption maximum, it strongly indicates decomposition nature of metronidazole solution. So that, PVA–Bi2WO6–CdS nanocomposite film has an excellent photocatalytic activity compared to the CdS, Bi2WO6, Bi2WO6–CdS catalyst.
Photocatalytic degradation MB
On basis of all aforementioned photocatalytic performance of catalysts like individuals and their composites were evaluated by the degradation of MB exposed to visible light irradiation, before that the adsorption test was carried. There was no degradation observed in the absence of catalysts, which was obviously the stability of MB under self-photolysis. For comparison purpose, the photocatalytic activity of bare CdS, Bi2WO6, binary Bi2WO6–CdS and PVA–Bi2WO6–CdS nanocomposite against MB is shown in Fig. 10. Where net visible, light irradiating time was to be 100 min, and the absorption intensity was measured peak position at 664 nm, during the reaction absorption intensity was monitored for every 20 min. The results show that the bare CdS and Bi2WO6 shows low activity against degradation MB for 100 min that was 72 and 86%, respectively. Meanwhile, PVA assisted Bi2WO6–CdS nanocomposite film gave much higher efficiency (92%) compared to binary Bi2WO6–CdS and neat catalysts. Further, the higher degradation efficiency of PVA assisted Bi2WO6–CdS nanocomposite film, confirmed in Fig. 11a. Clearly, the photocatalytic activity of binary Bi2WO6/CdS composites boosts with the addition of CdS when compared to pure Bi2WO6. The difference in photocatalytic activity may relate to visible light absorption properties, the separation efficiency of photogenerated electrons and holes and efficient charge transfer. CdS are normally charge carriers, both electrons and holes quickly recombine and only a fraction are contributed in the photocatalytic reaction process causing low reactivity and also Bi2WO6 nanoparticles exhibit the lowest photocatalytic activity, which may result from its large band gap. According to the band gap calculation above, the band gap of Bi2WO6 is 3.32 eV, indicating poor absorbance of light in the visible region. The degradation rate of MB was analyzed by the pseudo-first-order kinetic process over CdS, Bi2WO6, Bi2WO6–CdS and PVA assisted Bi2WO6–CdS nanocomposite film and the results shown in Fig. 11b. Photoreaction kinetics rate of the CdS, Bi2WO6, Bi2WO6–CdS and PVA assisted Bi2WO6–CdS nanocomposite film were 0.012, 0.015, 0.022 and 0.024, respectively. The PVA assisted Bi2WO6–CdS nanocomposite film were 1.0909 times higher than Bi2WO6–CdS heterostructures and 1.6, 2 times higher than bare Bi2WO6, CdS.
Proposed possible mechanism
Based on the above discussion, the possible photocatalytic mechanism for PVA assisted Bi2WO6–CdS nanocomposite film was proposed and shown in Fig. 12. Under the visible light, irradiation of CdS was excited and produced the photogenerated charge carriers. When the excited electron in the CB of CdS where transferred into the CB of Bi2WO6. While excited holes in the VB of Bi2WO6 shifted to the CB of CdS. There was a suppression of photogenerated charge carriers and free transfer of separated electron and holes towards the surface for the availability of carriers for oxidation and reduction. The conduction band (CB) and valence band (VB) edges were determined using the following equations:
χ is the absolute electronegativity of semiconductor which is geometric mean of constitute of atoms Ee is the energy free electrons on the hydrogen scale (~ 4.5 eV), the absolute electronegativity was 5.19 for CdS (Zou et al. 2016) and 6.36 for Bi2WO6 (Wang et al. 2017) and the calculated band edge positions are tabulated in Table 3. The degradation of model pollutants such as metronidazole and MB described in the following reaction
From the mechanism pathway, PVA assisted Bi2WO6–CdS nanocomposite film produced a large amount of highly reactive species like OH˙ than that of less reactive species such as ·O2− radical. So that photocatalytic activity drastically increases PVA assisted Bi2WO6–CdS nanocomposite film, because of the large amount and highly reactive OH· radical production. Meanwhile, the contribution of PVA on Bi2WO6–CdS composite immense fashion, due to the special character of minimizing photocorrosion and photostability.
Trapping of active species
The active species trapping measurements is significant to examine the active species in the photocatalytic process for a better understanding of photocatalytic mechanism. In degradation of dyes, several active radical species such as hole (h+), hydroxyl radicals (OH·), superoxide anion radical (·O2−) and electron (e−) plays major contribution. The active species trapping experiments toward PVA assisted Bi2WO6–CdS nanocomposite film are carried out, and the results are shown in Fig. 13. Primarily, all the four established species with a photogenerated hole (h+), hydroxyl (OH·) radical superoxide anion radical (·O2−) and electron (e−) are active during the photocatalytic process. Almost adverse change exist in the presence of IPA, implying that OH· radicals had a large effect on the degradation process under visible light illumination. In contrast, an apparent reduction was observed upon the addition of BQ compared to the case IPA, and a radical inhibition was superficial after the addition of EDTA, suggesting that ·O2− radicals and/or h+ were the main reactive species of the PVA assisted Bi2WO6–CdS nanocomposite film and played significant roles in the photocatalytic process under visible light illumination. Moreover, the photocatalytic degradation rate of model pollutants solution using EDTA and AgNO3 was lower than that using IPA, revealing that OH· played the most significant role in the photocatalytic process under visible light illumination.
Detection experiment for hydroxyl radicals
In general, the hydroxyl radicals (OH·), a highly reactive species with strong oxidation ability, were considered mainly responsible for the degeneration of pollutant molecules in the photocatalytic reaction. The concentration of hydroxyl radicals was detected during the reaction with the help of terephthalic acid by photoluminescence spectra. The taken terephthalic acid is reacting with OH· radicals when produced at the reaction and convert into a highly luminescent 2-hydroxy terephthalic acid. The intensity of PL spectra is directly proportional to the formation of 2-hydroxy terephthalic acid in the reaction of terephthalic acid with OH· in photocatalysis system (Sarkar et al. 2016; Zeng et al. 2017). The UV–Vis absorbance and detection of OH· radicals for PVA assisted Bi2WO6–CdS nanocomposite film using PL spectra is shown in Fig. 14. The UV–Vis absorbance gives a strong absorbance at 233 nm, then PL spectra of the produced 2-hydroxy terephthalic acid were monitored two peaks at approximately 345, 420 nm, respectively. PVA Bi2WO6–CdS show more PL intensity, due to producing a significant amount of OH· radicals. The same experiment was carried out with the bare photocatalyst like CdS and Bi2WO6. From the OH· radical detection processes, the PL intensity of Bi2WO6 and CdS has low when compared with PVA assisted Bi2WO6–CdS nanocomposite film. Figure 14b–d shows the PL intensity of formation of 2-hydroxy terephthalic acid in presence of Bi2WO6 and CdS.
Recycling exploration
In the practical applications of photocatalysis, the reusability, as well as stability, had a more important which when act as a catalyst. The recycling experiment was carried out for the prepared PVA assisted Bi2WO6–CdS nanocomposite film under an aforementioned same reaction condition; here the nanocomposite film was separated after the degradation of organic pollutant. Then it was dipped into another 100 ml of MB solution. The efficiency of Photodegradation of MB for every cycle is shown in Fig. 15. There was no obvious loss until seven cycles after that obviously minimum decline in photocatalytic activity.
Conclusion
In summary, PVA assisted Bi2WO6–CdS nanocomposite film photocatalyst was successfully synthesized through hydrothermal method. The PVA assisted Bi2WO6–CdS nanocomposite film showed better photocatalytic activity and photostability than that of pure CdS and pure Bi2WO6 toward the degradation of both MB and metronidazole under visible-light irradiation. The attractive nature of PVA assisted Bi2WO6–CdS nanocomposite film was easy to recover from the degradation system after the photocatalytic degradation performance. The PVA play a vital role in the retired recombination rate of photon-generated carriers, accordingly promote the activity and stability of the catalyst. This work will deliver a new way for efficient photocatalyst and reduced photocorrosion.
References
Abellan MN, Bayarri B, Gimenez J, Costa J (2007) Photocatalytic degradation of sulfamethoxazole in aqueous suspension of TiO2. Appl Catal B 74:233–241
Abellan MN, Gimenez J, Esplugas S (2009) Photocatalytic degradation of antibiotics: the case of sulfamethoxazole and trimethoprim. Catal Today 144:131–136
Ahmedchekkat F, Medjram MS, China M, Al-Bsoul AMA (2011) Sono photocatalytic degradation of Rhodamine B using a novel reactor geometry: effect of operating conditions. Chem Eng J 178:244–251
Ajmal A, Majeed I, Malik RN, Idriss H, Nadeem MA (2014) Principles and mechanisms photocatalytic dye degradation on TiO2 based photocatalysts: a comparative overview. RSC Adv 43:7003–37026
Bandyopadhyay K, Mayya KS, Vijayamohanan K, Sastry M (1997) Spontaneously organized molecular assembly of an aromatic organic disulfide on silver/platinum alloy surfaces: an angle dependent X-ray photoemission investigation. J Electron Spectrosc Relat Phenom 87:101–107
Bao J, Guo S, Gao J, Hu T, Yang L, Liu C, Peng J, Jiang C (2015) Synthesis of Ag2CO3/Bi2WO6 heterojunctions with enhanced photocatalytic activity and cycling stability. RSC Adv 5:97195–97204
Bazin I, Hassine AIH, Hamouda YH, Mnif W, Bartegi A, Lopez-Ferber M, De Waard M, Gonzalez C (2012) Estrogenic and anti-estrogenic activity of 23 commercial textile dyes. Ecotoxicol Environ Saf 85:131–136
Boobas S, Krishnakumar V, Jayaprakash J, Ranjith R, Vijayan J (2017) Preparation of cerium and sulfur codoped TiO2 nanoparticles based photocatalytic activity with enhanced visible light. J Photochem Photobiol A 349:91–99
Chatterjee D, Dasgupta S (2005) Visible light induced photocatalytic degradation of organic pollutants. J Photochem Photobiol C 6:186–205
Chatzitakis A, Berberidou C, Paspaltsis I, Kyriakou G, Sklaviadis T, Poulios I (2008) Photocatalytic degradation and drug activity reduction of chloramphenicol. Water Res 42:386–394
Chauhan R, Kumar A, Chaudhary RP (2014) Photocatalytic degradation of methylene blue with Cu doped ZnS nanoparticles. J Lumin 145:6–12
Chen X (2002) Preparation and property of TiO2 nanoparticle dispersed polyvinyl alcohol composite materials. J Mater Sci Lett 21:1637–1639
Chen X, Mao SS (2007) Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications. Chem Rev 107:2891–2959
Cheng H, Lv XJ, Cao S, Zhao ZY, Chen Y, Fu WF (2016) Robustly photogenerating H2 in water using FeP/CdS catalyst under solar irradiation. Sci Rep 6:19846
Dong S, Feng J, Li Y, Hu L, Liu M, Wang Y, Pi Y, Sun J, Sun J (2014a) Shape-controlled synthesis of BiVO4 hierarchical structures with unique natural-sunlight-driven photocatalytic activity. Appl Catal B 152:413–424
Dong S, Sun J, Li Y, Yu C, Li Y, Sun J (2014b) ZnSnO3 hollow nanospheres/reduced graphene oxide nanocomposites as high-performance photocatalysts for degradation of metronidazole. Appl Catal B 144:386–393
Dumrongrojthanath P, Thongtem T, Phuruangrat A, Thongtem S (2013) Hydrothermal synthesis of Bi2WO6 hierarchical flowers with their photonic and photocatalytic properties. Superlattices Microstruct 54:71–77
Farzadkia M, Esrafili A, Baghapour MA, Shahamat YD, Okhovat N (2014) Degradation of metronidazole in aqueous solution by nano-ZnO/UV photocatalytic process. Desalination Water Treat 52:4947–4952
Fu H, Pan C, Yao W, Zhu Y (2005) Visible-light-induced degradation of rhodamine B by nanosized Bi2WO6. J Phys Chem C 109:22432–22439
Garcia-Perez UM, Sepulveda-Guzman S, Martinez-De La Cruz A (2012) Nanostructured BiVO4 photocatalysts synthesized via a polymer-assisted coprecipitation method and their photocatalytic properties under visible-light irradiation. Solid State Sci 14:293–298
Gu W, Liao LS, Cai SD, Zhou DY, Jin ZM, Shi XB, Lei YL (2012) Adhesive modification of indium-tin-oxide surface for template attachment for deposition of highly ordered nanostructure arrays. Appl Surf Sci 258:8139–8145
Guo Y, Zhang G, Gan H, Zhang Y (2012a) Micro/nano-structured CaWO4/Bi2WO6 composite: synthesis, characterization and photocatalytic properties for degradation of organic contaminants. Dalton Trans 41:12697–12703
Guo Y, Zhang G, Gan H (2012b) Synthesis, characterization and visible light photocatalytic properties of Bi2WO6/rectorite composites. J Colloid Interface Sci 369:323–329
Guo Y, Zhang G, Liu J, Zhang Y (2013) Hierarchically structured α-Fe2O3/Bi2WO6 composite for photocatalytic degradation of organic contaminants under visible light irradiation. RSC Adv 3:2963–2970
Guo H, Guo Y, Liu L, Li T, Wang W, Chen W, Chen J (2014) Designed hierarchical synthesis of ring-shaped Bi2WO6@CeO2 hybrid nanoparticle aggregates for photocatalytic detoxification of cyanide. Green Chem 16:2539–2545
Guo N, Cao Y, Rong Y, Jia D (2016) Green synthesis of BiOBr modified Bi2O2CO3 nanocomposites with enhanced visible-responsive photocatalytic properties. RSCAdv 6:106046–106053
He D, Wang L, Li H, Yan T, Wang D, Xie T (2011) Self-assembled 3D hierarchical clew-like Bi2WO6 microspheres: synthesis, photo-induced charges transfer properties, and photocatalytic activities. CrystEngCommun 13:4053–4059
Hemalatha KS, Rukmani K (2016) Synthesis, characterization and optical properties of polyvinyl alcohol–cerium oxide nanocomposite films. RSC Adv 6:74354–74366
Jing D, Guo L (2007) Efficient hydrogen production by a composite CdS/mesoporous zirconium titanium phosphate photocatalyst under visible light. J Phys Chem C F111:13437–13441
Jung G, Kim HI (2014) Synthesis and photocatalytic performance of PVA/TiO2/graphene MWCNT nanocomposites for dye removal. J Appl Polym Sci 131:40715
Kandi D, Martha S, Thirumurugan A, Parida KM (2017) Modification of BiOI microplates with CdS QDs for enhancing stability, optical property, electronic behavior toward Rhodamine B decolorization, and photocatalytic hydrogen evolution. J Phys Chem C 121:4834–4849
Kansal SK, Kundu P, Sood S, Lamba R, Umar A, Mehta SK (2014) Photocatalytic degradation of the antibiotic levofloxacin using highly crystalline TiO2 nanoparticles. New J Chem 38:3220–3226
Krishnakumar V, Shanmugam G (2012) Structural, optical and dielectric properties of PbS PVA-PEG nanocomposite film. Sci Adv Mater 4:1247
Krishnakumar V, Ranjith R, Jayaprakash J, Boobas S, Venkatesan J (2017) Enhancement of photocatalytic degradation of methylene blue under visible light using transparent Mg-doped CdS–PVA nanocomposite films. J Mater Sci Mater Electron 28:13990–13999
Kudo A, Miseki Y (2009) Heterogeneous photocatalyst materials for water splitting. Chem Soc Rev 38:253–278
Kumar S, Ojha AK (2016) In-situ synthesis of reduced graphene oxide decorated with highly dispersed ferromagnetic CdS nanoparticles for enhanced photocatalytic activity under UV irradiation. Mater Chem Phys 171:126–136
Kummerer K (2009) Antibiotics in the aquatic environment—a review—part I. Chemosphere 75:417–434
Kundu J, Khilari S, Pradhan D (2017) Shape-dependent photocatalytic activity of hydrothermally synthesized cadmium sulfide nanostructures. ACS Appl Mater Interfaces 9:9669–9680
Li W, Li M, Xie S, Zhai T, Yu M, Liang C, Ouyang X, Lu X, Li H, Tong Y (2013) Improving the photoelectron chemical and photocatalytic performance of CdO nanorods with CdS decoration. CrystEngComm 15:4212–4216
Li Y, Li YL, Sa B, Ahuja R (2017) Review of two-dimensional materials for photocatalytic water splitting from a theoretical perspective. Catal Sci Technol 7:545–559
Liu J, Zhang G, Jimmy CY, Guo Y (2013) In situ synthesis of Zn2GeO4 hollow spheres and their enhanced photocatalytic activity for the degradation of antibiotic metronidazole. Dalton Trans 42:5092–5099
Liu X, Chen Q, Lv L, Feng X, Meng X (2015a) Preparation of transparent PVA/TiO2 nanocomposite films with enhanced visible-light photocatalytic activity. Catal Commun 58:30–33
Liu CM, Liu JW, Zhang GY, Zhang JB, Wu QS, Xu YY, Sun YQ (2015b) Facile room temperature precipitation strategy for Ag2O/Bi2WO6 heterojunction with high simulated sunlight photocatalytic performance via bi-directed electron migration mechanism. RSC Adv 5:32333–32342
Liu L, Qi Y, Lu J, Lin S, An W, Hu J, Liang Y, Cui W (2015c) Dramatic activity of a Bi2WO6@gC3N4 photocatalyst with a core@ shell structure. RSC Adv 5:99339–99346
Luo M, Lu P, Yao W, Huang C, Xu Q, Wu Q, Kuwahara Y, Yamashita H (2016) Shape and composition effects on photocatalytic hydrogen production for Pt–Pd alloy cocatalysts. ACS Appl Mater Interfaces 8:20667–20674
Mallakpour S, Vahabi M (2015) Preparation of poly(vinyl alcohol) nanocomposite films reinforced with poly(amide–imide)/CuO having N-trimellitylimido-l-valine linkages for the improvement of mechanical and thermal properties. Polym Plast Technol Eng 54:1625–1633
Mirhoseini F, Salabat A (2015) Ionic liquid based microemulsion method for the fabrication of poly (methyl methacrylate)-TiO2 nanocomposite as a highly efficient visible light photocatalyst. RSC Adv 5:12536–12545
Moon YE, Jung G, Yun J, Kim HI (2013) Poly(vinyl alcohol)/poly(acrylic acid)/TiO2/graphene oxide nanocomposite hydrogels for pH-sensitive photocatalytic degradation of organic pollutants. Mater Sci Eng B 178:1097–1103
Ni ZM, Xia SJ, Wang LG, Xing FF, Pan GX (2007) Treatment of methyl orange by calcined layered double hydroxides in aqueous solution: adsorption property and kinetic studies. J Colloid Interface Sci 316:284–291
Priyadharsan A, Vasanthakumar V, Karthikeyan S, Raj V, Shanavas S, Anbarasan PM (2017) Multi-functional properties of ternary CeO2/SnO2/rGO nanocomposites: visible light driven photocatalyst and heavy metal removal. J Photochem Photobiol A Chem 346:32–35
Rao JK, Raizada A, Ganguly D, Mankad MM, Satayanarayana SV, Madhu GM (2015) Investigation of structural and electrical properties of novel CuO–PVA nanocomposite films. J Mater Sci 50:7064–7074
Ren F, Zhang J, Wang Y (2015) Enhanced photocatalytic activities of Bi2WO6 by introducing Zn to replace Bi lattice sites: a first-principles study. RSC Adv 5:29058–29065
Safari GH, Hoseini M, Seyedsalehi M, Kamani H, Jaafari J, Mahvi AH (2015) Photocatalyticdegradation of tetracycline using nanosized titanium dioxide in aqueous solution. Environ Sci Technol 12:603–616
Saison T, Chemin N, Chaneac C, Durupthy O, Ruaux V, Mariey L, Mauge F, Beaunier P, Jolivet JP (2011) Bi2O3, BiVO4, and Bi2WO6: impact of surface properties on photocatalytic activity under visible light. J Phys Chem C 115:5657–5666
Saison T, Gras P, Chemin N, Chaneac C, Durupthy O, Brezova V, Colbeau-Justin C, Jolivet JP (2013) New insights into Bi2WO6 properties as a visible-light photocatalyst. J Phys Chem C 117:22656–22666
Sarkar AK, Saha A, Tarafder A, Panda AB, Pal S (2016) Efficient removal of toxic dyes via simultaneous adsorption and solar light driven photodegradation using recyclable functionalized amylopectin–TiO2–Au nanocomposite. ACS Sustain Chem Eng 4:1679–1688
Shanavas S, Priyadharsan A, Ramesh R, Anbarasan PM (2017a) Optimization and detailed stability study on Pb doped ceria nano cubes for enhanced photodegradation of several anionic and cationic organic pollutants. Arab J Chem. https://doi.org/10.1016/j.arabjc.2017.11.001
Shanavas S, Priyadharsan A, Vasanthakumar V, Arunkumar A, Anbarasan PM, Bharathkumar S (2017b) Mechanistic investigation of visible light driven novel La2CuO4/CeO2/rGO ternary hybrid nanocomposites for enhanced photocatalytic performance and antibacterial activity. J Photochem Photobiol A 340:96–108
Shangguan W, Yoshida A (2002) Photocatalytic hydrogen evolution from water on nanocomposites incorporating cadmium sulfide into the interlayer. J Phys Chem B 106:12227–12230
Shen S, Guo L (2006) Structural, textural and photocatalytic properties of quantum-sized In2S 3-sensitized Ti-MCM-41 prepared by ion-exchange and sulfidation methods. J Solid State Chem 179:2629–2635
Silva LA, Ryu SY, Choi J, Choi W, Hoffmann MR (2008) Photocatalytic hydrogen production with visible light over Pt-interlinked hybrid composites of cubic-phase and hexagonal-phase CdS. J Phys Chem C 112:12069–12073
Tang J, Zou Z, Ye J (2007) Efficient photocatalysis on BaBiO3 driven by visible light. J Phys Chem C 111:12779–12785
Tang R, Su H, Duan S, Sun Y, Li L, Zhang X, Zeng S, Sun D (2015) Enhanced visible light driven photocatalytic performances using Bi2WO6/MS (M = Cd, Zn) heterostructures: facile synthesis and photocatalytic mechanisms. RSC Adv 5:41949–41960
Tian Y, Fu J, Chang B, Xi F, Dong X (2012) Synthesis of mesoporous CdS/titania composites with visible light photocatalytic activities. Mater Lett 81:95–98
Wang Y, Deng K, Zhang L (2011) Visible light photocatalysis of BiOI and its photocatalytic activity enhancement by in situ ionic liquid modification. J Phys Chem C 115:14300–14308
Wang C, Wang L, Jin J, Liu J, Li Y, Wu M, Chen L, Wang B, Yang X, Su BL (2016a) Probing effective photocorrosion inhibition and highly improved photocatalytic hydrogen production on monodisperse PANI@CdS core–shell nanospheres. Appl Catal B 188:351–359
Wang Y, Wu Y, Qin Y, Rao J, Chen G, Lv C, Liu B (2016b) The synthesis of elegant hierarchical CdS via a facile hydrothermal method assisted by inorganic salt, with photo corrosion inhibition. CrystEngComm 18:7523–7529
Wang J, Tang L, Zeng G, Liu Y, Zhou Y, Deng Y, Wang J, Peng B (2017) Plasmonic Bi metal deposition and g-C3N4 coating on Bi2WO6 microspheres for efficient visible-light photocatalysis. ACS Sustain Chem Eng 5:1062–1072
Wei YT, Zheng YM, Chen JP (2011) Enhanced adsorption of arsenate onto a natural polymer based sorbent by surface atom transfer radical polymerization. J Colloid Interface Sci 356:234–239
Wei W, Xie J, Lu X, Osei PB, Yan Z, Meng S, Cui H (2014) CTAB-assisted synthesis and characterization of Bi2WO6 photocatalysts grown from WO3·0.33 H2O nanoplate precursors. Monatshefte für Chemie Chem Mon 145:47–59
Wong YC, Szeto YS, Cheung W, McKay G (2004) Adsorption of acid dyes on chitosan equilibrium isotherm analyses. Process Biochem 39:695–704
Xiao X, Wei J, Yang Y, Xiong R, Pan C, Shi J (2016) Photoreactivity and mechanism of g-C3N4 and Ag co-modified Bi2WO6 microsphere under visible light irradiation. ACS Sustain Chem Eng 4:3017–3023
Yu H, Huang X, Wang P, Yu J (2016) Enhanced photoinduced-stability and photocatalytic activity of CdS by dual amorphous cocatalysts: synergistic effect of Ti(IV)-hole cocatalyst and Ni (II)-electron cocatalyst. J Phys Chem C 120:3722–3730
Zeng C, Hu Y, Huang H (2017) BiOBr0.75I0.25/BiOIO3 as a novel heterojunctional photocatalyst with superior visible-light-driven photocatalytic activity in removing diverse industrial pollutants. ACS Sustain Chem Eng 5:3897–3905
Zhang KL, Liu CM, Huang FQ, Zheng C, Wang WD (2006) Study of the electronic structure and photocatalytic activity of the BiOCl photocatalyst. Appl Catal B Environ 68:125–129
Zhang H, Chen X, Li Z, Kou J, Yu T, Zou Z (2007) Preparation of sensitized ZnS and its photocatalytic activity under visible light irradiation. J Phys D Appl Phys 40:6846
Zhang LW, Wang YJ, Cheng HY, Yao WQ, Zhu YF (2009) Synthesis of porous Bi2WO6 thin films as efficient visible-light-active photocatalysts. Adv Mater 21:1286–1290
Zhang L, Tian W, Chen Y, Chen J, Teng H, Zhou J, Shi J, Sun Y (2016) Light-driven removal of rhodamine B over SrTiO3 modified Bi2WO6 composites. RSC Adv 6:83471–83481
Zhao C, Pelaez M, Duan X, Deng H, O’Shea K, Fatta-Kassinos D, Dionysiou DD (2013) Roleof pH on photolytic and photocatalytic degradation of antibiotic oxytetracycline in aqueous solution under visible/solar light: kinetics and mechanism studies. Appl Catal B 134:83–92
Zheng L, Liu X (2007) Solution-phase synthesis of CuO hierarchical nanosheets at near-neutral pH and near-room temperature. Mater Lett 61:2222–2226
Zhou C, Yan J, Chen B, Li P, Dong X, Xi F, Liu J (2016) Synthesis and application of ternary photocatalyst with a gradient band structure from two-dimensional nanosheets as precursors. Rsc Adv. 6:108955–108963
Zhu Z, Zhang L, Li J, Du J, Zhang Y, Zhou J (2013) Synthesis and photocatalytic behavior of BiVO4 with decahedral structure. Ceram Int 39:7461–7465
Zhuo Y, Huang J, Cao L, Ouyang H, Wu J (2013) Photocatalytic activity of snow-like Bi2WO6 microcrystalline for decomposition of Rhodamine B under natural sunlight irradiation. Mater Lett 90:107–110
Zou L, Wang H, Wang X (2016) High efficient photodegradation and photocatalytic hydrogen production of CdS/BiVO4 heterostructure through Z-scheme process. ACS Sustain Chem Eng 5:303–309
Acknowledgements
The authors thank Department of Physics, Indian Institute of Science, Bangalore for XPS Analysis. One of the authors Ranjith Rajendran acknowledges Periyar University for providing financial support in the form of University Research Fellowship (URF) grant.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Rajendran, R., Varadharajan, K., Jayaraman, V. et al. Photocatalytic degradation of metronidazole and methylene blue by PVA-assisted Bi2WO6–CdS nanocomposite film under visible light irradiation. Appl Nanosci 8, 61–78 (2018). https://doi.org/10.1007/s13204-018-0652-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13204-018-0652-9