Abstract
Carbon nanotubes (CNT) with exceptional mechanical and physical properties are the prime candidate materials for metal matrix composites. But the dispersion of CNTs in the metal matrix is affected by attractive van der Waals forces. In this study, we have adopted ultrasonication and mechanical alloying to achieve homogenous dispersion of multiple reinforcements namely B4C and CNTs within the commercial purity aluminium powder. The ultrsonication of all the starting materials was followed mechanical alloying process which was carried out in a planetary ball mill up to 480 min. The milling process was systematically studied by taking a small amount of milled powder at different milling time of 60, 120, 240 and 480 min respectively. The effect of ultrasonication and mechanical alloying on both morphology of the powders and dispersion of B4C and CNTs was studied using scanning electron microscopy. The results showed uniform dispersion of both B4C and CNTs within the pure aluminium powders without any agglomeration. Both the pure aluminium and hybrid nanocomposite powder showed decrease in particle size from 20.89 µm to 5.67 µm and 2.72 µm respectively after 480 minutes of ball milling.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Suryanarayana C, Al-Aqeeli N (2013) Mechanically alloyed nanocomposites. Prog Mater Sci 58:383–502
Kashyap KT, Puneeth KB, Ram HRA, Koppad PG (2012) Ageing kinetics in Carbon nanotube reinforced aluminium alloy AA6063. Mater Sci Forum 710:780–785
Varol T, Canakci A, Yalcin ED (2017) Fabrication of nano SiC-reinforced Al2024 matrix composites by a novel production method. Arab J Sci Eng 42:1751–1764
Chen Z, Sun GA, Wu Y, Mathon MH, Borbely A, Chen D, Ji G, Wang ML, Zhong SY, Wang HW (2017) Multi-scale study of microstructure evolution in hot extruded nano-sized TiB2 particle reinforced aluminum composites. Mater Des 116:577– 590
Mirjavadi SS, Alipour M, Hamouda AMS, Matin A, Kord S, Afshari BM, Koppad PG (2017) Effect of multi-pass friction stir processing on the microstructure, mechanical and wear properties of AA5083/ZrO2 nanocomposites. J Alloys Compd 726:1262–1273
Mirjavadi SS, Alipour M, Emamiand S, Kord S, Hamouda AMS, Koppad PG, Keshavamurthy R (2017) Influence of TiO2 nanoparticles incorporation to friction stir welded 5083 aluminum alloy on the microstructure, mechanical properties and wear resistance. J Alloys Compd 712:795–803
Canakci A, Varol T, Erdemir F (2016) The effect of flake powder metallurgy on the microstructure and densification behavior of B4C nanoparticle-reinforced Al–Cu–Mg alloy matrix nanocomposites. Arab J Sci Eng 41:1781–1796
Iijima S (1991) Helical microtubules of graphitic carbon. Nature 354:56–58
Kashyap KT, Koppad PG, Puneeth KB, Ram HRA, Mallikarjuna HM (2011) Elastic modulus of multiwalled carbon nanotubes reinforced aluminium matrix nanocomposite - a theoretical approach. Comput Mater Sci 50:2493–2495
Salvetat JP, Bonard JM, Thomson NH, Kulik AJ, Forró L, Benoit W, Zuppiroli L (1999) Mechanical properties of carbon nanotubes. Appl Phys A 69:255–260
Treacy MMJ, Ebbesen TW, Gibson JM (1996) Exceptionally high Young’s modulus observed for individual carbon nanotubes. Nature 381:678–680
Bakshi SR, Agarwal A (2011) An analysis of the factors affecting strengthening in carbon nanotube reinforced aluminum composites. Carbon 49:533–544
Goh CS, Wei J, Lee LC, Gupta M (2006) Development of novel carbon nanotube reinforced magnesium nanocomposites using the powder metallurgy technique. Nanotechnology 17:7– 12
Munir KS, Kingshott P, Wen C (2015) Carbon nanotube reinforced titanium metal matrix composites prepared by powder metallurgy-A review. Crit Rev Solid State Mater Sci 40:38– 55
Kuzumaki T, Miyazawa K, Ichinose H, Ito K (1998) Processing of carbon nanotube reinforced aluminum composite. J Mater Res 13:2445–2449
Koppad PG, Singh VK, Ramesh CS, Koppad RG, Kashyap KT (2014) Metal matrix nanocomposites reinforced with carbon nanotubes. In: Tiwari A, Shukla S K (eds) Advanced carbon materials and technology. Wiley, Hoboken, pp 331–376
Esawi A, Morsi K (2007) Dispersion of carbon nanotubes (CNTs) in aluminium powder. Compos Part A 38:646–650
Varol T, Canakci A (2013) Effect of particle size and ratio of B4C reinforcement on properties and morphology of nanocrystalline Al2024-B4C composite powders. Powder Technol 246:462– 472
Varol T, Canakci A (2013) Synthesis and characterization of nanocrystalline Al 2024–B4C composite powders by mechanical alloying. Philos Mag Lett 93:339–345
Yang X, Shi C, He C, Liu E, Li J, Zhao N (2011) Synthesis of uniformly dispersed carbon nanotube reinforcement in Al powder for preparing reinforced Al composites. Compos Part A 42:1833–1839
Cha SI, Kim KT, Arshad SN, Mo CB, Hong SH (2005) Extraordinary strengthening effect of carbon nanotubes in metal matrix nanocomposites by molecular-level mixing. Adv Mater 17:1377–1381
Mallikarjuna HM, Ramesh CS, Koppad PG, Keshavamurthy R, Sethuram D (2017) Nanoindentation and wear behaviour of copper based hybrid composites reinforced with SiC and MWCNTs synthesized by spark plasma sintering. Vacuum 145:320–333
Ye J, He J, Schoenung JM (2006) Cryomilling for the fabrication of a particulate B4C reinforced Al nanocomposite: Part I. Effects of process conditions on structure. Metall Mater Trans A 37:3099–3109
Alizadeh A, Taheri-Nassaj E, Baharvandi HR (2011) Preparation and investigation of Al–4 wt% B4C nanocomposite powders using mechanical milling. Bull Mater Sci 34:1039–1048
Varol T, Canakci A (2013) Effect of particle size and ratio of B4C reinforcement on properties and morphology of nanocrystalline Al2024-B4C composite powders. Powder Technol 246:462– 472
Abdoli H, Salahi E, Farnoush H, Pourazrang K (2008) Evolutions during synthesis of Al–AlN-nanostructured composite powder by mechanical alloying. J Alloys Compd 461:166–172
Yoo SJ, Han SH, Kim WJ (2013) A combination of ball milling and high-ratio differential speed rolling for synthesizing carbon nanotube/copper composites. Carbon 61:487–500
Wang L, Choi H, Myoung J, Lee W (2009) Mechanical alloying of multi-walled carbon nanotubes and aluminium powders for the preparation of carbon/metal composites. Carbon 47:3427–3433
Basariya MR, Srivastava VC, Mukhopadhyay NK (2014) Microstructural characteristics and mechanical properties of carbon nanotube reinforced aluminum alloy composites produced by ball milling. Mater Des 64:542–549
Perez-Bustamante R, Perez-Bustamante F, Estrada-Guel I, Licea-Jimene L, Miki-Yoshida M, Martinez-Sanchez R (2013) Effect of milling time and CNT concentration on hardness of CNT/al2024 composites produced by mechanical alloying. Mater Charac 75:13–19
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Gowda, A.C., Koppad, P.G., Sethuram, D. et al. Morphology Studies on Mechanically Milled Aluminium Reinforced with B4C and CNTs. Silicon 11, 1089–1098 (2019). https://doi.org/10.1007/s12633-018-9905-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12633-018-9905-1