Abstract
Ferronickel enrichment and extraction from nickel laterite ore were studied through reduction and magnetic separation. Reduction experiments were performed using hydrogen and carbon monoxide as reductants at different temperatures (700–1000°C). Magnetic separation of the reduced products was conducted using a SLon-100 cycle pulsating magnetic separator (1.2 T). Composition analysis indicates that the nickel laterite ore contains a total iron content of 22.50wt% and a total nickel content of 1.91wt%. Its mineral composition mainly consists of serpentine, hortonolite, and goethite. During the reduction process, the grade of nickel and iron in the products increases with increasing reduction temperature. Although a higher temperature is more favorable for reduction, the temperature exceeding 1000°C results in sintering of the products, preventing magnetic separation. After magnetic separation, the maximum total nickel and iron concentrations are 5.43wt% and 56.86wt%, and the corresponding recovery rates are 84.38% and 53.76%, respectively.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
G.G. Charles, Mineral Commodity Summaries, United States Geological Survey, Virginia, 2003, p. 14.
T. Norgate and S. Jahanshahi, Low grade ores: smelt, leach or concentrate, Miner. Eng., 23(2010), p. 65.
C.T. Harris, J.G. Peacey, and C.A. Pickles, Selective sulphidation of a nickeliferous lateritic ore, Miner. Eng., 24(2011), p. 657.
T. Norgate and S. Jahanshahi, Assessing the energy and greenhouse gas footprints of nickel laterite processing, Miner. Eng., 24(2010), p. 698.
J.H. Zhu, Exploration laterite-nickel ore and analysis on utilization technology, World Nonferrous Met., 10(2007), p. 7.
Y. Liu and Z.F. Cong, Atmospheric sulphuric acid leaching of saprolitic nickel laterites, Nonferrous Min. Metall., 24(2008), No. 2, p. 34.
J.H. Li, W. Chen, and Z.H. Xiao, Review on process technologies of laterite-nickel ore, Hydrometall. China, 23(2004), No. 4, p. 191.
B. Li, H. Wang, and Y.G. Wei, The reduction of nickel from low-grade nickel laterite ore using a solid-state deoxidization method, Miner. Eng., 24(2011), p. 1556.
G.H. Li, M.J. Rao, T. Jiang, Q.Q. Huang, T.M. Shi, and Y.B. Zhang, Innovative process for preparing ferronickel materials from laterite ore by reduction roasting-magnetic separation, Chin. J. Nonferrous Met., 21(2011), No. 12, p. 3137.
M. Jiang, T.C. Sun, Z.G. Liu, J. Kou, N. Liu, and S.Y. Zhang, Mechanism of sodium sulfate in promoting selective reduction of nickel laterite ore during reduction roasting process, Int. J. Miner. Process., 123(2013), p. 32.
W. Liang, H. Wang, J.G. Fu, and Z.X. He, High recovery of ferro-nickel from low grade nickel laterite ore, J. Cent. South Univ. Sci. Technol., 42(2011), No. 8, p. 2173.
J. Onodera, T. Inoue, and T. Imaizumi, Attempts at the beneficiation of laterite nickel ore, Int. J. Miner. Process., 19(1987), p. 25.
S. Agatzini-Leonardou, I.G. Zafiratos, and D. Spathis, Beneficiation of a Greek serpentinic nickeliferous ore: Part I. Mineral processing, Hydrometallurgy, 74(2004), p. 259.
B.K. Loveday, The use of oxygen in high pressure acid leaching of nickel laterites, Miner. Eng., 21(2008), p. 533.
S.F. Ruan, P.H. Jiang, C.Y. Wang, F. Yin, and Y.Q. Chen, Experimental study on low grade nickelferrous laterite ore with selective reduction roasting technology, Min. Metall., 16(2007), No. 2, p. 31.
J. Kim, D. Dodbiba, H. Tanno, K. Okaya, S. Matsuo, and T. Fujita, Calcination of low-grade laterite for concentration of Ni by magnetic separation, Miner. Eng., 23(2010), p. 282.
P.Y. Chen, J.T. Gao, S.Q. Li, Y.T. Zhang, R.Z. Liu, and J.L. Zhang, A new technic experimental study on precise reduction of iron oxide-separation of non-molten of iron oxide, J. Sichuan Univ. Eng. Sci. Ed., 43(2011), No. 5, p. 195.
X.H. Huang, Theory of Ferrous Metallurgy, Metallurgy Industry Press, Beijing, 2010, p. 285.
H.K. Mohamed, Isothermal reduction kinetics at 900–1100°C of NiFe2O4 sintered at 1000–1200°C, J. Anal. Appl. Pyrol., 73(2005), p. 123
J.H. Li, X.H. Li, Q.Y. Hu, Z.X. Wang, Y.Y. Zhou, J.C. Zheng, W.R. Liu, and L.J. Li, Effect of pre-roasting on leaching of laterite, Hydrometallurgy, 99(2009), p. 84.
J. Lu, S.J. Liu, J.S. Guan, W.G. Du, F. Pan, and S. Yang, The effect of sodium sulphate on the hydrogen reduction process of nickel laterite ore, Miner. Eng., 49(2013), p. 154.
C.A. Pickles, C.T. Harris, J. Peacey, and J. Forster, Thermodynamic analysis of the Fe-Ni-Co-Mg-Si-O-H-S-C-Cl system for selective sulphidation of a nickeliferous limonitic laterite ore, Miner. Eng., 54(2013), p. 52.
Z.K. Li, X.Z. Yuan, and C.C. Lin, A simulation study on the pre-reduction and calcination process of laterite ore in rotary kiln, Ferro-alloys, 40(2009), p. 24.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Tang, Xh., Liu, Rz., Yao, L. et al. Ferronickel enrichment by fine particle reduction and magnetic separation from nickel laterite ore. Int J Miner Metall Mater 21, 955–961 (2014). https://doi.org/10.1007/s12613-014-0995-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-014-0995-5