Effect of W on stress corrosion cracking behavior (SCC) of Ni-saving duplex stainless steels (Fe18Cr6Mn3Mo0.4N (2.13, 5.27)W, in wt%) was investigated in 4 M NaCl solution using a slow strain rate test method. The change in the W content from 2.13 to 5.27 wt% marginally affected the tensile properties of the investigated DSSs. Alloying W clearly improved the pitting initiation resistance and repassivation tendency of the investigated alloys, but the SCC susceptibility was not remarkably decreased by addition of W. The slight enhancement in the SCC resistance of the alloy containing 5.27 wt% W was revealed to be correlated with the accelerated galvanic corrosion between the ferrite and austenite phases as a result of the W partitioning preferentially into the ferrite phase which could encourage the propagation of pitting.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R. M. Davison and D. Redmond, Mater. Design 12, 187 (1991).
T. Maki, T. Furuhara, and K. Tsuzaki, ISIJ Int. 41, 571 (2001).
J. Charles, Steel Res. Int. 79, 455 (2008).
J. Olsson, Desalination 183, 217 (2005).
J. Olsson and M Snis, Desalination 205, 104 (2007).
I. Alvarez-Armas, Recent Patents on Mechanical Engineering 1, 51 (2008).
N. R. Baddoo, J. Constr. Steel Res. 64, 1199 (2008).
K. H. Lo, C.H. Shek, and J. K. L. Lai, Mat. Sci. Eng. R 65, 39 (2009).
M. Snis and J. Olsson, Desalination 223, 476 (2008).
J. Y. Choi, S. W. Hwang, M. C. Ha, and K.-T. Park, Met. Mater. Int. 5, 893 (2014).
R. Merello, F. J. Botana, J. Botella, M. V. Matres, and M. Marcos, Corros. Sci. 45, 909 (2003).
H. Vannevik, J. O. Nilsson, J. Frodigh, and P. Kangas, ISIJ Inter. 36, 807 (1996).
J. O. Nilsson, G. Chai, and U. Kivisäkk, Proc. 6th Stainless Steel Science and Market Conf. (ed. P. Karjalainen) p. 585, European Stainless Steel Conference, Helsinki, Finland (2008).
L. Weber and P. J. Uggowitzer, Mat. Sci. Eng. A 242, 222 (1998).
M. E. Wilms, V. J. Gadgil, J. M. Krougman, and F. P. Ijsseling, Corros. Sci. 36, 781 (1994).
H. Sieurin, R. Sandstrom, and E. M. Westin, Metall. Mater. Trans. A 37, 2975 (2006).
I. U. H. Toor, J. H. Park, and H. S. Kwon, Corros. Sci. 50, 404 (2008).
J. Li, Z. Zhang, H. Chen, X. Xiao, J. Zhao, and L. Jiang, Metall. Mater. Trans. A 43, 428 (2012).
L. Zhang, W. Zhang, Y. Jiang, B. Deng, D. Sun, and J. Li, Electrochim. Acta 54, 5387 (2009).
J. Y. Choi, J. H. Ji, S. W. Hwang, and K. T. Park, Mat. Sci. Eng. A 528, 6012 (2011).
H. Y. Ha, T. H. Lee, and B. C. Hwang, Korean Patent 10 1306263 (2013).
S. H. Kim, B. J. Song, and W. S. Ryu, Met. Mater. Int. 7, 297 (2001).
J. Zhao, Y. W. Kim, J. H. Lee, J. M. Lee, H. S. Chang, and C. S. Lee, Met. Mater. Int. 18, 217 (2012).
F. Abe and S. Nakazawa, Metall. Mater. Trans. A 23, 3025 (1992).
K. M. Kim and K.Y. Kim, J. Power Sources 173, 917 (2007).
Z. X. Zhang, Q. X. Ran, Y. L. Xu, X. J. Yu, D. W. Jiang, and X. S. Xiao, J. Iron Steel Res. Int. 21, 69 (2014).
A. Irhzo, Y. Segui, N. Bui, and F. Dabosi, Corros. Sci. 26, 769 (1986).
J. Chen and J. K. Wu, Corros. Sci. 30, 53 (1990).
W.-S. Ji, Y.-W. Jang, and J.-G. Kim, Met. Mater. Int. 17, 463 (2011).
C. J. Park and H. S. Kwon, Corros. Sci. 44, 2817 (2002).
J. S. Kim and H. S. Kwon, Corrosion 55, 512 (1999).
C. J. Park, M. K. Ahn, and H. S. Kwon, Mat. Sci. Eng. A 418, 211 (2006).
K. Y. Kim, P. Q. Zhang, T. H. Ha, and Y. H. Lee, Corrosion 54, 910 (1998).
J. S. Kim, T. H. Ha, and K.Y. Kim, Corrosion 57, 452 (2001).
ASTM Standard G129, Standard Practice for Slow Strain Rate Testing to Evaluate the Susceptibility of Metallic Materials to Environmentally Assisted Cracking, vol. 03.02, Annual book of ASTM standards, PA, USA (2000).
R. Nishimura and Y. Maeda, Corros. Sci. 46, 769 (2004).
Y. S. Yoon, H. Y. Ha, T. H. Lee, and S. S. Kim, Corros. Sci. 80, 28 (2014).
Y. S. Yoon, H. Y. Ha, T. H. Lee, and S. S. Kim, Corros. Sci. 88, 337 (2014).
E. Novak and J. Schmit, Proc. XVII IMEKO World Congress Metrology in the 3rd Millennium, p. 183, HMD, Croatian Metrology Soc. Dubrovnik, Croatia (2003).
H. Y. Ha, M. H. Jang, T. H. Lee, and J. Moon, Corros. Sci. 89, 154 (2014).
G. S. Frankel, J. Electrochem. Soc. 145, 2186 (1998).
T. A. Mozhi, W. A. T. Clark, and B. E. Wilde, Corros. Sci. 27, 257 (1987).
W. T. Tsai, V. Reynders, M. Stratmann, and H. J. Grabke, Corros. Sci. 34, 1647 (1993).
J. Congleton and W. Yang, Corros. Sci. 37, 429 (1995).
J. I. Son, S. S. Kim, J. H. Lee, and B. H. Choi, Metall. Mater. Trans. A 34, 1617 (2003).
Y. H. Jang, S. S. Kim, and J. H. Lee, Mat. Sci. Eng. A 396, 302 (2005).
Z. Zhang, Z. Wang, Y. Jiang, H. Tan, D. Han, and Y. Guo, Corros. Sci. 62, 42 (2012).
H. Hwang and Y. Park, Mater. Trans. 50, 1548 (2009).
H. Tan, Y. Jiang, B. Deng, T. Sun, J. Xu, and J. Li, Mater. Charact. 61, 1049 (2009).
Y. Yang, H. Tan, Z. Zhang, Z. Wang, Y. Jiang, and J. Li, Corrosion 69, 167 (2013).
Z. Wei, J. Laizhu, H. Jincheng, and S. Hongmei, Mat. Sci. Eng. A 497, 501 (2008).
M. Rosso, I. Peter, and D. Suani, J. Achiev. Mater. Manuf. Eng. 59, 26 (2013).
H. Y. Ha, M. H. Jang, T. H. Lee, and J. Moon, Mater. Charact. 106, 338 (2015).
L. F. Garfias-Mesias, J. M. Syke, and C. D. S. Tuck, Corros. Sci. 387, 1319 (1996).
S. T. Kim, I. S. Lee, J. S. Kim, S. H. Jang, Y. S. Park, K. T. Kim, and Y. S. Kim, Corros. Sci. 64, 164 (2012).
R. Newman, Electrochem. Soc. Interface 19, 33 (2010).
H. Y. Ha, T. H. Lee, and S. J. Kim, Electrochim. Acta 80, 432 (2012).
L. Q. Guo, M. Li, X. L. Shi XL, X. Yan, X. Y. Li, and L. J. Qiao, Corros. Sci. 53, 3733 (2011).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Ha, HY., Lee, TH. & Kim, S. Effect of W on stress corrosion cracking susceptibility of newly developed Ni-saving duplex stainless steels. Met. Mater. Int. 23, 115–125 (2017). https://doi.org/10.1007/s12540-017-6356-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-017-6356-y