Abstract
The preparation of polymer nanocomposites combined with high strength, toughness, and high transparency remains a challenge. Aramid fibers are often used as fiber-reinforced materials for their superior mechanical and thermal properties, but the weak interfacial force between aramid fibers and matrix polymer limits the application in composite materials. In this work, aramid nanofibers were prepared by a two-step process, which included deprotonation and acid hydrothermal treatment to obtain better dispersions in general solvents. The hydrothermal aramid nanofibers (HANFs) were used as reinforcing materials and blended with polyacrylonitrile (PAN) to prepare polyacrylonitrile/aramid nanofibers (PAN/HANFs) composite films with different mass fractions of HANFs. The morphologies of HANFs and the thermal, optical, and mechanical properties of composite films were investigated. Interestingly, when the mass fraction of aramid nanofibers was less than 1.0%, the composite films were synchronously strengthened and toughened. When the mass fraction of HANFs was 0.5%, the tensile strength and toughness of the PAN/HANFs composite film reached 62.04 MPa and 22.56 MJ/m3, which were 74.23% and 162.31% higher than the pure PAN film, respectively. Besides, its average transmittance in the visible light region remained 76.34%. This work may offer a novel and facile strategy for high transparent reinforced polymer composites, which have potential applications in high strength fiber or optical film.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
X. F. Zhang, Q. W. Li, T. G. Holesinger, P. N. Arendt, J. Y. Huang, P. D. Kirven, T. G. Clapp, R. F. DePaula, X. Z. Liao, Y. H. Zhao, L. X. Zheng, D. E. Peterson, and Y. T. Zhu, Adv. Mater., 19, 4198 (2007).
N. Behabtu, C. C. Young, D. E. Tsentalovich, O. Kleinerman, X. Wang, A. W. K. Ma, E. A. Bengio, R. F. ter Waarbeek, J. J. de Jong, R. E. Hoogerwerf, S. B. Fairchild, J. B. Ferguson, B. Maruyama, J. Kono, Y. Talmon, Y. Cohen, M. J. Otto, and M. Pasquali, Science, 339, 182 (2013).
M. Khalifa, S. Janakiraman, S. Ghosh, A. Venimadhav, and S. Anandhan, Polym. Compos., 40, 2320 (2019).
S. Eksi and K. Genel, Acta Phys. Pol. A, 132, 879 (2017).
R. Sen, B. Zhao, D. Perea, M. E. Itkis, H. Hu, J. Love, E. Bekyarova, and R. C. Haddon, Nano Lett., 4, 459 (2004).
Z. H. Wang, Y. Si, C. Y. Zhao, D. Yu, W. Wang, and G. Sun, ACS Appl. Mater. Interfaces, 11, 27200 (2019).
S. Ifuku, H. Maeta, H. Izawa, M. Morimoto, and H. Saimoto, RSC Adv., 4, 40377 (2014).
M. Mortier, P. Moldenaers, and J. Mewis, Rheol. Acta, 35, 57 (1996).
J. C. Fan, Z. X. Shi, L. Zhang, J. L. Wang, and J. Yin, Nanoscale, 4, 7046 (2012).
J. M. Zhang, Z. Mousavi, N. Soykeabkaew, P. Smith, T. Nishino, and T. Peijs, ACS Appl. Mater. Interfaces, 2, 919 (2010).
I. O’Connor, H. Hayden, J. N. Coleman, and Y. K. Gun’ko, Small, 5, 466 (2009).
J. J. Lin, S. H. Bang, M. H. Malakooti, and H. A. Sodano, ACS Appl. Mater. Interfaces, 9, 11167 (2017).
W. Chen, X. M. Qian, X. Q. He, Z. Y. Liu, and J. P. Liu, J. Appl. Polym. Sci., 123, 1983 (2012).
S. Zhou, G. Zhou, S. Jiang, P. Fan, and H. Hou, Mater. Lett., 200, 97 (2017).
C. B. Huang, S. L. Chen, D. H. Reneker, C. L. Lai, and H. Q. Hou, Adv. Mater., 18, 668 (2006).
Z. J. Ma, Z. L. Hu, H. Zhang, M. Y. Peng, X. He, Y. Li, Z. M. Yang, and J. R. Qiu, J. Mater. Chem. C, 4, 1029 (2016).
B. Zaarour, L. Zhu, C. Huang, X.Y. Jin, H. Alghafari, J. Fang, and T. Lin, J. Ind. Text., https://doi.org/10.1177/1528083719870197 (2019).
Z. M. Huang, Y. Z. Zhang, M. Kotaki, and S. Ramakrishna, Compos. Sci. Technol., 63, 2223 (2003).
B. M. Wang and C. C. Fan, J. Nanosci. Nanotechnol., 20, 113 (2020).
M. A. Abdelwahab, M. Misra, and A. K. Mohanty, Ind. Crops Prod., 132, 497 (2019).
S. H. Jiang, H. Q. Hou, A. Greiner, and S. Agarwal, ACS Appl. Mater. Interfaces, 4, 2597 (2012).
K. Devarayan, D. Y. Lei, H. Y. Kim, and B. S. Kim, Chem. Eng. J., 273, 603 (2015).
M. Yang, K. Q. Cao, L. Sui, Y. Qi, J. Zhu, A. Waas, E. M. Arruda, J. Kieffer, M. D. Thouless, and N. A. Kotov, ACS Nano, 5, 6945 (2011).
K. Q. Cao, C. P. Siepermann, M. Yang, A. M. Waas, N. A. Kotov, M. D. Thouless, and E. M. Arruda, Adv. Funct. Mater., 23, 2072 (2013).
J. Lyu, X. Z. Wang, L. H. Liu, Y. Kim, E. K. Tanyi, H. Chi, W. C. Feng, L. Z. Xu, T. H. Li, M. A. Noginov, C. Uher, M. D. Hammig, and N. A. Kotov, Adv. Funct. Mater., 26, 8435 (2016).
J. W. Guo, C. F. Wang, S. H. Chen, J. Y. Lai, C. H. Lu, and J. K. Chen, Sep. Purif. Technol., 234, 116106 (2020).
H. S. Chen, M. H. Huang, Y. B. Liu, L. J. Meng, and M. D. Ma, Sci Total Environ., 739, 139944 (2020).
X. Li, C. Li, G. Y. Gao, B. S. Lv, L. S. Xu, Y. Lu, and G. L. Zhang, Sci. Total Environ., https://doi.org/10.1016/j.scitotenv.2019.134910 (2020).
J. S. B. Melbiah, D. Nithya, and D. Mohan, Colloids Surf., A, 516, 147 (2017).
S. Morimune, M. Kotera, T. Nishino, K. Goto, and K. Hata, Macromolecules, 44, 4415 (2011).
L. L. Lv, X. S. Han, L. Zong, M. J. Li, J. You, X. C. Wu, and C. X. Li, ACS Nano, 11, 8178 (2017).
Y. H. Zhao, S. H. Zhang, F. Hu, J. J. Li, H. Chen, J. Y. Lin, B. Yan, Y. C. Gu, and S. Chen, J. Mater. Sci.: Mater. Electron., 30, 12718 (2019).
F. Wang, Y. D. Wu, Y. D. Huang, and L. Liu, Compos. Sci. Technol., 156, 269 (2018).
J. J. Luo, M. Y. Zhang, B. Yang, G. D. Liu, and S. X. Song, Appl. Nanosci., 9, 631 (2019).
J. D. Liu, C. X. Jin, and C. Wang, J. Colloid Interface Sci., 561, 449 (2020).
S. S. Zhang, J. J. Li, Z. P. Yin, X. F. Zhang, S. C. Kundu, and S. Z. Lu, J. Appl. Polym. Sci., 132, 42407 (2015).
C. W. Hu, T. Kawamoto, H. Tanaka, A. Takahashi, K. M. Lee, S. Y. Kao, Y. C. Liao, and K. C. Ho, J. Mater. Chem. C, 4, 10293 (2016).
G. M. Cai and W. D. Yu, J. Therm. Anal. Calorim., 104, 757 (2011).
Y. Janowska, T. Mikolajczyk, and M. Bogun, J. Therm. Anal. Calorim., 89, 613 (2007).
H. P. Karki, L. Kafle, D. P. Ojha, J. H. Song, and H. J. Kim, Sep. Purif. Technol., 210, 913 (2019).
Y. Xue, J. Liu, and J. Y. Liang, Polym. Degrad. Stabil., 98, 219 (2013).
Y. Furushima, M. Nakada, H. Takahashi, and K. Ishikiriyama, Polymer, 55, 3075 (2014).
A. Kausar and J. Plast, Film Sheeting, 35, 295 (2019).
R. O. Ritchie, Nat. Mater., 10, 817 (2011).
Y. Hou, G. L. Zhang, X. P. Tang, Y. Si, X. M. Song, F. X. Liang, and Z. Z. Yang, Macromolecules, 52, 3863 (2019).
B. W. Yu, C. Z. Geng, M. Zhou, H. W. Bai, Q. Fu, and B. B. He, Composites, Part B, 92, 413 (2016).
A. Jamil, Z. W. Guan, W. J. Cantwell, X. F. Zhang, G. S. Langdon, and Q. Y. Wang, Int. J. Impact Eng., 127, 31 (2019).
Y. T. Zhu, J. A. Valdez, I. J. Beyerlein, S. J. Zhou, C. Liu, M. G. Stout, D. P. Butt, and T. C. Lowe, Acta Mater., 47, 1767 (1999).
D. A. Norman and R. E. Robertson, J. Appl. Polym. Sci., 90, 2740 (2003).
J. W. Shin, J. P. Jeun, and P. H. Kang, J. Ind. Eng. Chem., 15, 555 (2009).
R. Gupta, K. Pancholi, R. De Sa, D. Murray, D. H. Huo, G. Droubi, M. White, and J. Njuguna, Jom, 71, 3119 (2019).
L. He and S. C. Tjong, RSC Adv., 5, 15070 (2015).
Acknowledgement
This work was supported by the Science and Technology Cooperation Project of Sichuan University and Zigong City (2019CDZG-3), the Science and Technology Foundation of Sichuan province (2020YFG0094 and 2020YFG0104), and Miaozi Project in Science and Technology Innovation Program of Sichuan Province (No.20-YCG045). We would like to thank the Analytical & Testing Center of Sichuan University for structured illumination microscopy work, and we are grateful to Shanlin Wang for her help with TEM images. We thank Erhui Ren for the experimental assistance.
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Bai, X., Zhao, Y., Song, Z. et al. Aramid Nanofibers Reinforced Polyacrylonitrile Nanocomposite Films with High Transparency and High Mechanical Properties. Fibers Polym 23, 711–719 (2022). https://doi.org/10.1007/s12221-022-3218-0
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-022-3218-0