Abstract
The catalytic conversion of CO2 to CO via a reverse water gas shift (RWGS) reaction followed by well-established synthesis gas conversion technologies may provide a potential approach to convert CO2 to valuable chemicals and fuels. However, this reaction is mildly endothermic and competed by a strongly exothermic CO2 methanation reaction at low temperatures. Therefore, the improvement in the low-temperature activities and selectivity of the RWGS reaction is a key challenge for catalyst designs. We reviewed recent advances in the design strategies of supported metal catalysts for enhancing the activity of CO2 conversion and its selectivity to CO. These strategies include varying support, tuning metal–support interactions, adding reducible transition metal oxide promoters, forming bimetallic alloys, adding alkali metals, and enveloping metal particles. These advances suggest that enhancing CO2 adsorption and facilitating CO desorption are key factors to enhance CO2 conversion and CO selectivity. This short review may provide insights into future RWGS catalyst designs and optimization.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
The concentration of carbon dioxide (CO2) in the atmosphere has increased dramatically, triggering a series of severe environmental problems, such as global warming, glacier melting, and ocean acidification [1,2,3,4,5]. These problems seriously threaten the human living environment. Therefore, CO2 concentration in the atmosphere must be reduced. Many researchers have tried to solve these problems through carbon dioxide capture and storage (CCS) and carbon dioxide capture and utilization (CCU) [6,7,8,9,10]. However, CCS poses a risk of CO2 leakage and causes unknown effects on the environment [11]. Thus, developing the CCU technology appears to be more meaningful than simply storing CO2 [12, 13].
The conversion of CO2 to CO via a reverse water gas shift (RWGS) reaction [Eq. (1)] has been widely explored because the produced CO can be further converted to valuable chemicals and fuels through well-developed synthesis gas (CO and H2) conversion technologies, such as Fischer–Tropsch (FT) synthesis and methanol synthesis. However, the RWGS reaction is competed by Sabatier reaction or CO2 methanation [Eq. (2)] and methanol formation, resulting in a decreased CO yield [11, 14, 15]. Under atmospheric pressure, the yield of methanol is rather low or absent [16] and thus can be ignored. However, the strongly exothermic methanation reaction is thermodynamically more favored over the mildly endothermic RWGS reaction at low reaction temperatures [17,18,19,20,21]; as such, minimizing the methanation during RWGS becomes a great challenge. Therefore, active RWGS catalysts operated at low temperatures with enhanced CO selectivity and minimized CH4 selectivity should be developed. CO may evolve as an intermediate in the hydrogenation of CO2 to CH4, methanol, and other hydrocarbons [11, 16, 17, 22, 23], so understanding the mechanism of CO formation is also important for the rational design of catalysts for these processes.
Based on reaction kinetics, spectroscopy, and density functional theory (DFT) calculations, two mechanisms of RWGS have been proposed [24,25,26,27,28,29]. One is redox mechanism: CO2 is reduced to CO with the catalyst being oxidized directly, and then H2 reduces the catalyst again to complete the catalytic turnover [24]. This mechanism was originally proposed for Cu-based catalysts, where Cu is oxidized by CO2 and reduced again by H2 [24, 25, 30, 31]. This mechanism has also been proposed for catalysts containing reducible oxides, which can be readily reduced and oxidized under reaction conditions [32,33,34,35,36].
Another is association mechanism: CO2 adsorbs on the surface of catalysts and reacts with dissociated H to form an intermediate species, such as formate (*HCOO), carboxyl (*COOH), carbonate (CO32−), and bicarbonate (HCO3−), which is decomposed to CO and H2O [27, 37]. This mechanism was originally proposed for metal/reducible support catalysts [27, 38,39,40], such as Pt/CeO2. For this mechanism, the key intermediate proposed for the RWGS reaction may vary among different catalysts or the same catalyst operating under different conditions [41,42,43,44]. However, redox and association mechanisms have been debated. The mechanism of RWGS reaction is strongly dependent on catalyst types and reaction conditions; as such, no consensus has been reached.
Regardless of the mechanism of the RWGS reaction, an active catalyst requires two functionalities: (a) adsorption of CO2 and disruption of one C–O bond of CO2; (b) dissociation of H2 and hydrogenation of O to form H2O. A selective RWGS catalyst needs a mild C–O dissociation ability and a weak CO adsorption ability to avoid the dissociation of CO and the further hydrogenation of CO to CH4 and methanol. Therefore, the balance between C–O dissociation and hydrogenation is a key factor for the development of highly active and selective RWGS catalysts operating under mild conditions. The hydrogenation ability can be provided by a typical transition metal (e.g., Pt and Pd), whereas the C–O breaking ability can be achieved by a mildly oxophilic transition metal (e.g., Ru and Rh) [45,46,47] and may be further enhanced by a support or a promoter to improve CO2 adsorption. The balance between hydrogenation and C–O bond dissociation abilities is evidently dependent on the properties and interactions of metals and supports (or promoters).
The development of the RWGS reaction has been briefly reviewed in several reviews focusing on the catalytic conversion of CO2 to fuels and chemicals [12, 48,49,50]. For instance, Porosoff et al. [48] reviewed various catalysts for the conversion of CO2 to CO, methanol, and hydrocarbon fuels. Kattel et al. [51] reviewed the conversion of CO2 to C1 products of CO, methanol, and methane and focused on the role of the interface of metal/oxide catalysts in these reactions. Two reviews on the RWGS reaction have been conducted [12, 37]. Daza and Kuhn [12] analyzed the feasibility of converting CO2 to liquid fuels through the RWGS reaction. They also explored the supported metal catalysts and oxide catalysts for RWGS, and their reaction mechanisms. Su et al. [37] reviewed the reaction mechanism and more types of catalysts (supported metal catalysts, mixed oxide catalysts, and transition metal carbide catalysts) for the RWGS reaction.
In contrast to previous reviews providing a detailed overview of various types of catalysts for the RWGS reaction, this short review aims to present the recent advances in strategies developed to improve the selectivity and activity of a RWGS reaction. Although other types of catalysts have been widely studied [52,53,54], our review focuses on supported metal catalysts, which are the most intensively investigated catalyst for the RWGS reaction. In particular, this review considers the role of a support (or a promoter) and its interaction with transition metals in tuning the activity and selectivity of the RWGS reaction.
Strategies to Improve the Activity and Selectivity of the RWGS Reaction
Supported transition metal catalysts have been widely explored for CO2 reduction. Depending on metal properties, Pd- and Pt-based catalysts are selective for producing CO, whereas catalysts based on oxophilic metals, such as Ni, Rh, and Ru, are more selective for producing CH4 [55,56,57,58,59]. CH4 can be a minor or major product under a RWGS reaction condition in the presence of these catalysts [55,56,57,58,59]. Thus, in addition to improving activities, tuning the selectivity of catalysts toward the RWGS reaction is important.
Transition metals, such as Pd and Pt, are highly active for activating H2. However, they weakly adsorb and activate CO2. Although DFT work has shown that CO2 electrochemical reduction by H2 on Pt (111) is possible [60], Kattel et al. [58] theoretically demonstrated that even a Pt nanoparticle (Pt46 cluster) with low coordination surface sites is unable to catalyze the RWGS reaction because of a weak CO2 adsorption. Kinetic Monte Carlo simulations have revealed that CO production is possible only when the CO2 adsorption strength is further improved (Fig. 1a), and the weak adsorption of CO facilitates CO desorption while strong adsorption of CO produces more CH4 (Fig. 1b) [58]. In addition, Kwak et al. [61] experimentally showed that even Pd atomically dispersed on a multiwall carbon nanotube (Pd/MWCNT) is inactive (Table 1) for CO2 reduction under mild conditions (< 500 °C) because neither Pd nor MWCNT can strongly adsorb and activate CO2 under their reaction conditions. These works have indicated that bare transition metals are inefficient for the RWGS reaction because of their low abilities in CO2 activation. Therefore, a support or a promoter and its interaction with a transition metal are essential for tuning the activity and selectivity of the RWGS reaction.
Varying Support
The reducibility and acid–base properties of a support can greatly influence reaction intermediates and CO2 adsorption and activation. Hence, supports play an important role in the activity and selectivity of the RWGS reaction. Choosing an appropriate support is important to tune the activity and selectivity of this reaction.
SiO2 and Al2O3 are irreducible supports. Their major role is to disperse the supported species, and they are not expected to directly activate CO2. Even though SiO2 is considered an inert support, it can play a role in the RWGS reaction. As shown in Fig. 2a, CO2 adsorbs at the interface of Pt/SiO2; in particular, C adsorbs on Pt, and O bonds with the hydroxyl of SiO2 via hydrogen bonding [58]. The adsorption strength of CO2 in the presence of SiO2 enhances by 0.21 eV compared with that of a bare Pt nanoparticle, thus enabling the RWGS reaction [58]. Al2O3 is another widely used irreducible support with weak acidity. In comparison with Pd/MWCNT, which cannot catalyze the RWGS reaction, 0.5% Pd atomically dispersed on Al2O3 converts CO2 to CO and yields CH4 as a minor product (Table 1) [61]. Using operando diffuse reflectance infrared Fourier transformed spectroscopy (DRIFTS), Bobadilla et al. [62] suggested that CO2 reacts with the hydroxyl of Al2O3 to form bicarbonate species (Fig. 3a), which then reacts with H spilled over from Au to form formate. Formate eventually decomposes to CO. These studies have indicated that SiO2 and Al2O3 indirectly participate in the RWGS reaction by enhancing CO2 adsorption. Normally, the activities of SiO2- and Al2O3-supported catalysts in a RWGS reaction are relatively low (Table 1), and they are mainly used to benchmark the activity of supported metals.
In contrast to SiO2 and Al2O3, TiO2 and CeO2 are reducible supports, which readily generate oxygen vacancies, particularly in the presence of a metal to activate H2. An oxygen vacancy participates in a RWGS reaction through the strong adsorption of CO2 and may directly activate CO2. Although different reaction pathways are proposed, the oxygen vacancy in proximity to a metal site plays a crucial role in enhancing the activity of the RWGS reaction.
The activity of metal catalysts supported on TiO2 is normally higher in a RWGS reaction than that on an irreducible support. Kim et al. [32] conducted a kinetic study and proposed that a RWGS reaction follows a redox mechanism on Pt/TiO2 catalysts. They performed H2 temperature-programmed reduction and temperature-programmed desorption experiments and suggested that Pt–Ov–Ti3+ sites, in addition to Pt and TiO2 sites, are active sites for a RWGS reaction [32]. The turnover frequency (TOF) of CO2 conversion on reducible Pt/TiO2 improves by approximately eight times compared with that on irreducible Pt/Al2O3 (Table 1) [32]. Kattel et al. [58] carried out DFT calculation and indicated that CO2 adsorbs at the interface of Pt/TiO2 (Fig. 2b); C adsorbs on Pt, and one O adsorbs on an oxygen vacancy (coordinatively unsaturated Ti cation), resulting in an enhanced CO2 adsorption by 0.11 eV compared with that on Pt/SiO2. This process facilitates the cleavage of the C–O bond to form the adsorbed CO and fill the oxygen vacancy. Their experimental work has further confirmed that the stronger CO2 adsorption on Pt/TiO2 than that on Pt/SiO2 improves the TOF of CO2 conversion in the RWGS reaction by 4–5 times (Table 1) [58]. Bobadilla et al. [62] reported that the activation energy of a RWGS reaction on Au/TiO2 is 30 kJ/mol, which is much lower than that of 79 kJ/mol on Au/Al2O3; as a result, the RWGS activity on Au/TiO2 is higher than that on Au/Al2O3. As shown in Fig. 4, under identical reaction conditions (0.2 g of catalyst, H2/CO2 = 4/1, gas hourly space velocity [GHSV] is 12,000 h−1), the conversion of CO2 for Au/TiO2 approaches the thermodynamic equilibrium of CO2 conversion, while it is much lower on Au/Al2O3 (Table 1) [62]. Bobadilla et al. [62] further performed DRIFTS and UV–vis spectroscopy studies and proposed that the presence of oxygen vacancies (or Ti3+ cations) during the reaction facilitates the formation of a surface hydroxycarbonyl (OCOH) intermediate, which decomposes to form CO and H2O (Fig. 3b).
CeO2 is also a reducible support whose oxygen storage capacity (OSC) is higher than that of TiO2. CeO2-supported transition metal catalysts have been widely investigated for the mechanism of a RWGS reaction under various conditions [27, 73, 74]. An early work showed that CO2 adsorption on Pt/CeO2 at room temperature produces CO adsorbed on Pt and suggested that an oxygen vacancy in the vicinity of a Pt particle is responsible for CO2 reduction to CO [75]. Performing DRIFT and mass spectroscopy (MS) during steady-state isotopic transient kinetic analysis, Goguet et al. [27] suggested that surface carbonate is an active intermediate, and formate is a spectator during the RWGS reaction on Pt/CeO2 under their reaction condition. Wang et al. [74] conducted a quantitative transient analysis of products and showed that the surface oxygen vacancy in the vicinity of a Au particle in Au/CeO2 can be replenished by an interaction with CO2 and proposed that the RWGS reaction may follow a redox mechanism via the Au-assisted deposition and removal of active surface O. They also compared the OSC properties of Au/CeO2 and Au/TiO2 and suggested that oxygen vacancies away from an Au particle may be involved in the RWGS reaction on Au/CeO2, because of the higher oxygen mobility in CeO2 than in TiO2. However, Chen et al. [38] combined Fourier transform infrared (FTIR) experiments and a temperature-programmed surface reaction and proposed that redox and associate mechanisms exist on a Pt/CeO2 catalyst via a related mechanism that involves a surface formate species as the major path under their reaction condition. These works have indicated that oxygen vacancies play an important role in the RWGS reaction, even though its reaction mechanism may vary depending on reaction conditions.
The RWGS activity of transition metals on CeO2 is higher than that of metals supported on irreducible supports. Porosoff and Chen [76] compared the RWGS reaction on 1.7% Pt supported on reducible CeO2 and irreducible Al2O3 at 573 K (H2/CO2 = 3/1, total pressure 30.0 Torr) and found that the forward reaction rate constant based on the mass of a catalyst and the amount of CO uptake (a measure of Pt metal dispersion) on Pt/CeO2 are ~ 1.7 and ~ 5.7 times higher than those on Pt/Al2O3 [76]. Yang et al. [63] prepared ~ 2 nm Cu supported on CeO2 and mesoporous SiO2 to exclude the effect of the particle size of Cu. They observed that Cu/CeOx is about four times more active than Cu/SiO2 at 573 K (Table 1; 0.2 g of catalyst, H2/CO2 = 3/1, 1 bar, weight hourly space velocity of 1.08 h−1) and assigned this improvement to the formation of oxygen vacancies on the Cu/CeOx catalyst.
In summary, the activity of metal catalysts on reducible supports (CeO2 and TiO2) in a RWGS reaction is higher than that on irreducible supports (SiO2 and Al2O3; Table 1), but they may form more CH4. No CH4 forms on Au- and Cu-based catalysts, whereas CH4 may form on Pt and Pd catalysts [62, 63]. For Pt catalysts, CH4 selectivity is higher on reducible supports (TiO2 and CeO2) than on irreducible supports (SiO2 and Al2O3) possibly because of the removal of both O atoms from CO2 by oxygen vacancies and the hydrogenation of the formed C species to CH4 [76]. The deposited carbon species on a support may lead to catalyst deactivation. Indeed, Goguet et al. [73] reported the deactivation of a 2% Pt/CeO2 catalyst during a RWGS reaction. They subjected the used catalysts to temperature-programmed oxidation and found that deactivation is closely related to the amount of deposited carbon. Thus, carbon species deposited on partially reduced CeO2 around a Pt particle is the major reason for this deactivation.
Although metal/reducible support catalysts show higher activity in RWGS, the work of direct comparison between different reducible supports and their consequences on the varied activity and selectivity for RWGS reaction is rare. Sakurai et al. [64] studied CO2 hydrogenation on Au/CeO2, Au/ZrO2, and Au/TiO2 catalysts. Under identical reaction conditions [250 °C, H2/CO2 = 3, 8 atom pressure, 3000 mL/(gcat h)], these catalysts show similar CO selectivity (> 90%), whereas conversion is quite different: 3.4%, 9.2%, and 16.1% for Au/CeO2, Au/ZrO2, and Au/TiO2, respectively (Table 1). This high activity on Au/TiO2 is attributed to the higher acidity of TiO2 than those of ZrO2 and CeO2. Kattel et al. [65] compared CO2 hydrogenation on bimetallic PtCo supported on CeO2, ZrO2, and TiO2. Similar CO2 conversion (7.8%–9.1%) is observed on these catalysts under identical condition (0.1 g of catalyst, 300 °C, H2/CO2 = 2/1, feed flow rate of 60 mL/min), whereas the highest TOF and the highest CO selectivity are found on a PtCo/TiO2 catalyst (Table 1). These ascribed this change to the strength of C, O-bound, and O-bound species are enhanced on PtCo/CeO2 and PtCo/ZrO2 interfaces with respect to that of PtCo/TiO2. As a result, different reaction intermediates form, and CH4 selectivity increases. We note that the surface area of these reducible supports are different, perhaps resulting in a comparison with different bases. Therefore, how the redox and acid–base properties of different supports influence the activity and selectivity of RWGS reaction should be further studied.
Tuning Metal–Support Interactions
A RWGS reaction occurs at the interface of a metal and a support, so finely tuning metal–support interactions and maximizing metal–support interfacial sites can greatly improve activity and enhance selectivity toward CO. Maximizing metal–support interfacial sites can be achieved by reducing the particle size of metals, adjusting pretreatment procedures, and tuning the property of supports. Tuning metal–support interactions is particularly important for Ni-, Rh-, and Ru-based catalysts, which are more selective to the production of CH4 rather than CO.
Reducing the particle size of transition metals not only provides more surface sites for a reaction but also increases the number of metal–support interfacial sites and has been investigated by several groups. Kwak et al. [66] tested CO2 hydrogenation on 0.1%–5% Ru/Al2O3 catalysts. CH4 is the major product on a 5% Ru sample (mainly Ru particles), while CO is the major product on a 0.1% Ru sample (mainly atomically dispersed Ru; Table 1). On the 0.1% Ru/Al2O3 catalyst at 350 °C (Fig. 5), CO is the only product at the beginning of a reaction, whereas CH4 becomes the major product with time on stream. This is because the sintering of atomically dispersed Ru on particles occurs with time on stream possibly due to a weak Ru–Al2O3 interaction. Matsubu et al. [56] prepared 2% Rh/TiO2 catalyst with both Rh particles and isolated Rh sites. They removed the Rh particles without removing isolated Rh species that strongly interacts with TiO2 by leaching with HCl/H2O2 (Fig. 6a). In comparison with a fresh Rh/TiO2 catalyst with Rh particles exhibiting the major product of CH4, the leached Rh/TiO2 catalyst with only the isolated Rh sites produces CO at 200 °C and CO2/H2 of 3 (15–30 mg of catalyst, 0.1 MPa, CO2/H2/N2 = 3/1/96, feed flow rate of 100 mL/min; Fig. 6). Therefore, they concluded that an isolated Rh site is the active site for a RWGS reaction, while Rh particle is the active site for CH4 formation. Combining DFT and experiments, Chen et al. [77] also demonstrated that a single Ir atom interacting with TiO2 is selective for CO formation, whereas Ir particle is active for CH4 formation. These works have mainly focused on the particle size of metals but have rarely explored the role of metal–support interactions.
However, one may expect that metal–support interactions can be enhanced by decreasing the particle size of metals because of an increased metal–support interface. Recently, Li et al. [67] prepared 5% Ir/CeO2 catalyst with an Ir particle size of approximately 1 nm and 0.7% Ir/CeO2 with atomically dispersed Ir. Although an Ir/CeO2 catalyst with large Ir particles (> 2.5 nm) shows the dominant product of CH4, the 5% and 0.7% Ir/CeO2 catalysts have the dominant product of CO. The activity based on the mole of Ir improves when the size of an Ir particle is smaller than 1 nm (Table 1; 300 °C, 1 MPa, H2/CO2/Ar = 76/19/5). Li et al. [67] also conducted X-ray adsorption spectroscopy (XAS) and found that 1 nm Ir particle and atomically dispersed Ir become partially oxidized because of the strong interaction with CeO2, whereas a large Ir particle (> 2.5 nm) is mainly reduced. Thus, they argued that the main active site for a RWGS reaction is the partially oxidized Ir that strongly interacts with CeO2 support irrespective of Ir particles or atomically dispersed Ir species.
Varying treatment conditions can tune the metal–support interactions of metal/reducible support catalysts. Aitbekova et al. [55] prepared ~ 2.6 nm Ru uniformly dispersed on Al2O3, TiO2, and CeO2 supports and tested in a CO2 reduction reaction. They found that TiO2- and CeO2-supported Ru are more active than Al2O3-supported Ru catalyst and that CH4 is the major product in all catalysts. However, the mild oxidation of catalysts at 230 °C and followed by low-temperature (230 °C) reduction results in the redispersion of Ru particles to form a single RuOx site on CeO2, which causes an almost complete shift of the product selectivity from CH4 to CO (Fig. 7). This enhanced selectivity is attributed to the weakened adsorption of CO on the single RuOx site. However, this redispersion partially occurs in Al2O3- and TiO2-supported Ru possibly because of the weaker interaction of Al2O3 and TiO2 than that of CeO2 with RuOx to disperse the single RuOx site. The mild oxidation at 230 °C and followed by the high-temperature (500 °C) reduction of Ru/TiO2 favor the formation of a strong metal–support interaction (SMSI). That is, the partially reduced TiOx covers Ru particles, resulting in a decreased CO2 conversion and an enhanced CO selectivity due to the loss of a surface Ru site by covering. Interestingly, the redispersed Ru/CeO2 catalyst via a mild oxidizing treatment is stable in a RWGS reaction for 12–14 h, and CO selectivity increases further from 90% to 99%. Similarly, the high-temperature (500 °C) reduction of a Ni/TiO2 catalyst results in a SMSI effect with a decreased activity, but this reaction shifts the selectivity from CH4 to CO (Table 1) because Ni is covered, and more Ni–TiO2 interface sites are produced [57]. However, for the supported Ni catalysts prepared from NH3 or H2-pretreated TiO2 support, reduction at 500 °C only induces a SMSI effect to a limited extent; thus, CH4 is the dominant product on these catalysts (Table 1).
In addition to changing metal particle sizes or pretreatment conditions, varying the property of a support can also be used to tune metal–support interactions. Kim et al. [78] prepared a series of Pt/TiO2 catalysts with a varying crystallite size of TiO2. They found that decreasing the crystallite size of TiO2 significantly improves the reducibility of Pt/TiO2, produces more Pt–Ov–Ti3+ interfacial sites, and eventually improves the activity in a RWGS reaction (Fig. 8).
Addition of Reducible Transition Metal Oxide Promoters
The addition of a promoter can also change the adsorption and activation of CO2 and may further change the activity and selectivity for a RWGS reaction. One type of a promoter is reducible transition metal oxide, which can also form oxygen vacancies upon reduction. Similar to oxygen vacancies on reducible TiO2 and CeO2, oxygen vacancies at the interface of a metal-reducible metal oxide promoter may play an important role in CO2 activation. Adjusting the interaction between a metal and a promoter may significantly improve the activity and tune selectivity in a RWGS reaction.
Kwak et al. [61] compared the CO2 reduction on 1% Pd/MWCNT and 1% Pd-2.3% La2O3/MWCNT catalysts (0.05 g of catalyst, H2/CO2/He = 3/1/16, feed flow rate of 60 mL/min). In contrast to the inactivity of 1% Pd/MWCNT for CO2 reduction, addition of La2O3 to the catalyst improves the activity, and CO is observed as the only product (< 500 °C; Table 1). This observation highlights the role of La2O3 in CO2 activation. Ro et al. [79] prepared a MoOx-modified Pt/SiO2 catalyst via a controlled surface reaction. MoOx is selectively deposited on surface Pt at a Mo/Pt ratio of < 0.3, thereby creating Pt–MoOx interfacial sites. The intrinsic reaction rate and TOF of the optimized PtMo/SiO2 (Mo/Pt = 0.3) for the RWGS reaction at 473 K improve by ~ 11 and ~ 39 times compared with those of Pt/SiO2 (Fig. 9), respectively (H2/CO2 = 2, 7.1 bar). The activation energy decreases from 67.9 kJ/mol for Pt/SiO2 to 60.0 kJ/mol for PtMo/SiO2. The reaction orders are altered upon MoOx loading. Interestingly, the activity of the RWGS reaction can be further improved when Pt-MoOx is exposed to light irradiation. Yan et al. [68] investigated CO2 reduction on NiFe/ZrO2 catalysts with varying amounts of Fe loadings. As shown in Fig. 10, at low Fe loadings (Ni/Fe > 1), the major active site is the Ni–ZrO2 interface, which selectively produces CH4 (selectivity > 88%) through methanation (673 K, H2/CO2/Ar = 2/1/5). At high Fe loadings (Ni/Fe = 1/3), the major active site is a Ni–FeOx interfacial site, producing CO with selectivity higher than 95% (Table 1). DFT calculations have indicated that the CO adsorption energies at Ni–ZrO2 and Ni–FeOx interfaces are −2.92 and −1.93 eV, respectively. Therefore, CO adsorbed at the Ni–ZrO2 interface is too strong, so it favors CH4 formation. Conversely, CO adsorbed at the Ni–FeOx interface is weaker, so it promotes CO desorption.
Bimetallic Alloy Formation
Another type of promoter can be completely reduced to form a bimetallic alloy with a major metal [80,81,82]. Depending on the property of promoters, bimetallic alloy properties, such as H2 dissociation, CO2 adsorption, and C–O cleavage, may be changed. For example, Yuan et al. [81] performed a DFT study on CO2 hydrogenation on Ni (111) and Re-doped Ni (111) surfaces. The adsorption energies of CO2 on Ni (111) and Re@Ni (111) surfaces are 0.20 and −0.28 eV, respectively. This result indicates the stronger adsorption of CO2 on the latter surface. Furthermore, the activation energy of CO2 dissociation to CO* and O* decreases from 0.41 eV on Ni (111) to 0.18 eV on Re@Ni (111). These results suggest that the presence of oxophilic Re on Ni (111) favors one O atom of CO2 adsorption on Re and promotes the C–O bond dissociation. Thus, a bimetallic alloy may also change the activity and selectivity of a RWGS reaction.
Alayoglu et al. [80] showed that Pt is segregated on the surface of a PtCo alloy, and the selectivity of CO increases from ~ 82% on Co/MCF-17 to ~ 100% on PtCo/MCF-17 at a CO2 conversion of ~ 5% (reaction conditions: 0.05 g of catalyst, 300 °C, 5.5 bar, H2/CO2/He = 33.3/11.1/5.6, feed flow rate of 50 mL/min). Porosoff and Chen [76] compared CO2 reduction on bimetallic PtCo, PtNi, and PdNi supported on Al2O3 or CeO2 catalysts. PdNi/CeO2 is the most active catalyst, but it forms the highest amount of CH4. By comparison, PtCo/Al2O3 shows the highest selectivity toward CO. They suggested that selectivity can be correlated with the electronic properties of catalysts by using values of the d-band center. As shown in Fig. 11, the Pt–Co bimetallic catalyst with a d-band center value away from the Fermi level and toward the more negative direction yields the highest CO:CH4 ratio. The advantage of establishing this trend is that it can provide a direction for the future selection of single-metal or bimetallic catalysts that efficiently activate CO2. Further studies have indicated that PtCo/TiO2 is more selective than PtCo/CeO2 and PtCo/ZrO2 catalysts for CO because of the weak bonding strength of CO at the Pt–Co/TiO2 catalyst interface site [65]. Ye et al. [59] compared CO2 reduction on Pd/SiO2 and PdIn/SiO2 catalysts. A Pd/SiO2 catalyst is much more active than other catalysts, but it produces CH4 as a minor product. By comparison, PdIn/SiO2 is much less active than other catalysts, but it only produces CO (Table 1). Characterizations have shown the formation of a PdIn bimetallic alloy (Fig. 12). A DFT study has revealed that a PdIn alloy is less active than Pd for H2 dissociation, CO adsorption on the PdIn alloy is weaker than that on Pd, and PdIn is energetically less favorable to the hydrogenation of CO to CH4 than Pd. Specifically, the H2 dissociation energy on a PdIn alloy increases by 1.56 eV, whereas the linear CO adsorption energy on a PdIn alloy decreases by 0.77 eV. These changes shift the formation of CH4 on Pd/SiO2 to the formation of CO on bimetallic PdIn/SiO2.
Addition of Alkali Metals
The addition of alkali metals to Pt- and Au-based catalysts can greatly improve the activity of a water gas shift (WGS) reaction [83,84,85]. The addition of an appropriate amount of Na to Pt/TiO2 can improve reducibility and surface basicity and form strong Pt-O-Na interactions by donating electrons from Pt to NaOx, which creates an active site at the interface of Pt–NaOx for the WGS reaction [83]. The increased basicity may improve the adsorption of acidic CO2. Furthermore, electronically modified Pt may alter interactions with CO, enhance activity, and tune the selectivity for the RWGS reaction.
Chen et al. [69] showed that the addition of a small amount of K2O to a Cu/SiO2 catalyst improves its activity for a RWGS reaction by more than 2.4 times (Table 1). Specifically, the CO2 conversion is 12.8% on a Cu/K2O/SiO2 catalyst, while it is only 5.3% on Cu/SiO2 catalyst at 600 °C (0.02 g of catalyst, 0.1 MPa, H2/CO2 = 1/1, feed flow rate of 100 mL/min). K likely enhances CO2 adsorption and facilitates the decomposition of the formate species to CO. Liang et al. [70] studied the effect of the addition of 2% K to 2% Pt/mullite on the RWGS reaction. The TOF of RWGS at 340 °C improves by seven times with the addition of K (Table 1; H2/CO2/N2 = 4.5/4.5/1, feed flow rate of 50 mL/min) with a reduced selectivity to CH4 (Fig. 13). The activation energy of CO2 conversion decreases from 62 ± 2.3 kJ/mol to 34 ± 1.3 kJ/mol upon K addition. This result suggests that the interface between KOx and Pt serves as an active site for the decomposition of formate to CO, and the presence of KOx weakens CO adsorption on Pt and thus hinders CH4 formation. Yang et al. [86] investigated the role of K addition in the activity and selectivity of Pt on zeolite L (Pt/L) for a RGWS reaction. K addition (K/Pt = 80) improves the reaction rate from 0.021 mol/(gcat h) to 0.080 mol/(gcat h) at 500 °C compared with that of Pt/L (0.1 g of catalyst, H2/CO2/N2 = 4.5/4.5/1, feed flow rate of 50 mL/min), while CH4 formation decreases. On the basis of XAS and X-ray photoelectron spectra (XPS) results, Yang et al. [86] proposed the formation of a Pt–O(OH)–Pt interface, which serves as an active site to adsorb CO2 and form an active intermediate of bridge-bonded formate. Similarly, Santos et al. [84] reported that the addition of Na to Pt/C can improve the RWGS reaction with a reduced activation energy. They suggested that the addition of Na modifies the electronic structure of Pt and favors CO2 dissociation.
In addition to improving the activity of the RWGS reaction, changing product selectivity can be achieved by adding alkali metals. Bando et al. [71] investigated the effect of Li modification on Rh-exchanged Y zeolite for CO2 hydrogenation (1 g of catalyst, 250 °C, 3 MPa, H2/CO2 = 3/1, feed flow rate of 100 mL/min). They found that CH4 is the major product of Rh-Y, whereas adding Li to Rh-Y mainly produces CO (Table 1). This change is attributed to Li that provides new active sites for CO2 adsorption and stabilizes the adsorbed CO.
Enveloping Metal Particles
These above strategies are based on tuning metal–support (promoter) interactions. The local environment of metal particles is also important for various reactions and may be finely tuned by enveloping with nanoporous materials. Wang et al. [72] reported a new strategy to tune the local environment of metals by enveloping a metal particle with different zeolites for CO2 reduction reaction. The Rh particles of 4.2–5.0 nm are either supported on zeolite (Rh/HZSM-5, Rh/S-1) or enveloped in HZSM-5, KZSM-5, and pure silica zeolite of S-1 (Rh@HZSM-5, Rh@KZSM-5, and Rh@S-1). CO2 reduction reaction tests (0.5 g of catalyst, 1 MPa, H2/CO2/Ar = 3/1/1, feed flow rate of 30 mL/min, 250–500 °C) showed that Rh/HZSM-5, Rh/S-1, and Rh@HZSM-5 favor CH4 formation, whereas Rh@S-1 produces CO as a major product (Table 1) and CH4 as a minor product (Fig. 14). The selectivity behavior of Rh particles enveloped in S-1 is similar to that of the single Rh site on TiO2 [56]. FTIR and H2 spillover experiments showed that proton form HZSM-5 favors stronger CO adsorption on Ru and facilitates hydrogen spillover, while pure silica zeolite favors weaker CO adsorption and limited hydrogen spillover. The weak CO adsorption favors desorption, and the limited hydrogen spillover decreases the Rh hydrogenation ability toward the CH4 formation. A stability test at 400 °C has demonstrated that Rh/S-1 is stable for 150 h with a CO selectivity of 96%.
Conclusions and Outlooks
The catalytic conversion of CO2 to CO via the RWGS reaction followed by well-established synthesis gas conversion technologies may provide a potential approach to convert CO2 to valuable chemicals and fuels. The improvement in the low-temperature activity and selectivity of the RWGS reaction is a key challenge for this reaction. We reviewed recent advances in the strategies of catalyst designs that can enhance the activity and selectivity of the RWGS reaction. These strategies include varying support, tuning metal–support interactions, adding reducible transition metal oxide promoters, forming bimetallic alloys, adding alkali metals, and enveloping metal particles. The analysis of these advances suggests that enhancing CO2 adsorption and facilitating CO desorption appear to be the key factors for enhancing CO2 conversion and CO selectivity.
Although significant efforts have been made, studies have shown that the RWGS reaction is accompanied with a methanation side reaction on various catalysts. As a result, a mixture of CO and CH4 products forms, thereby burdening subsequent separation processes. Thus, RWGS catalysts with 100% CO selectivity should be designed. In the future, combining different metals with supports/promoters and tailoring the fine structure of supported metal catalysts should be considered the important directions for designing highly selective catalysts of the RWGS reaction.
Future work may focus on the reaction mechanism of catalysts in a RWGS reaction. The reaction mechanism and even active sites have been strongly debated, and these aspects are essential for the rational design of highly efficient and selective RWGS catalysts. With the development of in situ and operando spectroscopy technologies, such as in situ XPS and in situ XRD, as well as the capability of DFT calculations, the reaction mechanism on various catalysts operating under various reaction conditions may be clarified in the future. With better understanding on the reaction mechanism and structure–activity/selectivity relationship, more efficient catalysts may be designed in the future.
Future work may also focus on the stability of catalysts in a RWGS reaction. The stability of catalysts in this reaction has been rarely explored. Several stability tests have been performed under conditions near the thermodynamic equilibrium of CO2 conversion, which may mask the unstable nature of catalysts. The stability of catalysts is an important issue for a commercial process, so this parameter should be extensively investigated. Understanding the deactivation mechanism may also provide useful information for the rational design of stable catalysts in the RWGS reaction.
References
Knutson TR, Tuleya RE (2004) Impact of CO2-induced warming on simulated hurricane intensity and precipitation: sensitivity to the choice of climate model and convective parameterization. J Climate 17(18):3477–3495
Hansen J, Sato M, Ruedy R et al (2006) Global temperature change. Proc Natl Acad Sci USA 103(39):14288–14293
Yang J, Cai W, Ma MD et al (2020) Driving forces of China’s CO2 emissions from energy consumption based on Kaya-LMDI methods. Sci Total Environ 711:134569
Ahmed R, Liu GJ, Yousaf B et al (2020) Recent advances in carbon-based renewable adsorbent for selective carbon dioxide capture and separation—a review. J Clean Prod 242:118409
Ansaloni L, Salas-Gay J, Ligi S et al (2017) Nanocellulose-based membranes for CO2 capture. J Membr Sci 522:216–225
Quarton CJ, Samsatli S (2020) The value of hydrogen and carbon capture, storage and utilisation in decarbonising energy: insights from integrated value chain optimisation. Appl Energy 257:113936
Mac Dowell N, Fennell PS, Shah N et al (2017) The role of CO2 capture and utilization in mitigating climate change. Nat Clim Change 7(4):243–249
Hadjadj R, Deák C, Palotás ÁB et al (2019) Renewable energy and raw materials—the thermodynamic support. J Clean Prod 241:118221
De Ras K, van de Vijver R, Galvita VV et al (2019) Carbon capture and utilization in the steel industry: challenges and opportunities for chemical engineering. Curr Opin Chem Eng 26:81–87
Wang ZJ, Song H, Liu HM et al (2020) Coupling of solar energy and thermal energy for carbon dioxide reduction: status and prospects. Angew Chem Int Ed 59:2–22
Kaiser P, Unde R, Kern C et al (2013) Production of liquid hydrocarbons with CO2 as carbon source based on reverse water-gas shift and Fischer-tropsch synthesis. Chemie Ingenieur Tech 85(4):489–499
Daza YA, Kuhn JN (2016) CO2 conversion by reverse water gas shift catalysis: comparison of catalysts, mechanisms and their consequences for CO2 conversion to liquid fuels. RSC Adv 6(55):49675–49691
Ali N, Bilal M, Nazir MS et al (2020) Thermochemical and electrochemical aspects of carbon dioxide methanation: a sustainable approach to generate fuel via waste to energy theme. Sci Total Environ 712:136482
Zhuang YC, Currie R, McAuley KB et al (2019) Highly-selective CO2 conversion via reverse water gas shift reaction over the 0.5 wt% Ru-promoted Cu/ZnO/Al2O3 catalyst. Appl Catal A: Gen 575:74–86
He YL, Yang KR, Yu ZW et al (2019) Catalytic manganese oxide nanostructures for the reverse water gas shift reaction. Nanoscale 11(35):16677–16688
Xu XD, Moulijn JA (1996) Mitigation of CO2 by chemical conversion: plausible chemical reactions and promising products. Energy Fuels 10(2):305–325
Xu JH, Su X, Duan HM et al (2016) Influence of pretreatment temperature on catalytic performance of rutile TiO2-supported ruthenium catalyst in CO2 methanation. J Catal 333:227–237
Nityashree N, Price CAH, Pastor-Perez L et al (2020) Carbon stabilised saponite supported transition metal-alloy catalysts for chemical CO2 utilisation via reverse water-gas shift reaction. Appl Catal B: Environ 261:118241
Dias YR, Perez-Lopez OW (2020) Carbon dioxide methanation over Ni-Cu/SiO2 catalysts. Energy Convers Manag 203:112214
Konsolakis M, Lykaki M, Stefa S et al (2019) CO2 hydrogenation over nanoceria-supported transition metal catalysts: role of ceria morphology (nanorods versus nanocubes) and active phase nature (Co versus Cu). Nanomaterials 9(12):1739
Wang YJ, Xu Y, Liu QK et al (2019) Enhanced low-temperature activity for CO2 methanation over NiMgAl/SiC composite catalysts. J Chem Technol Biotechnol 94(12):3780–3786
Qiu M, Tao HL, Li Y et al (2019) Insight into the mechanism of CO2 and CO methanation over Cu(100) and Co-modified Cu(100) surfaces: a DFT study. Appl Surf Sci 495:143457
Li WH, Zhang GH, Jiang X et al (2019) CO2 hydrogenation on unpromoted and M-promoted Co/TiO2 catalysts (M = Zr, K, Cs): effects of crystal phase of supports and metal–support interaction on tuning product distribution. ACS Catal 9(4):2739–2751
Ginés MJL, Marchi AJ, Apesteguía CR (1997) Kinetic study of the reverse water-gas shift reaction over CuO/ZnO/Al2O3 catalysts. Appl Catal A: Gen 154(1–2):155–171
Fujita SI, Usui M, Takezawa N (1992) Mechanism of the reverse water gas shift reaction over Cu/ZnO catalyst. J Catal 134(1):220–225
Chen C, Cheng WH, Lin S (2000) Mechanism of CO formation in reverse water-gas shift reaction over Cu/Al2O3 catalyst. Catal Lett 68(1–2):45–48
Goguet A, Meunier FC, Tibiletti D et al (2004) Spectrokinetic investigation of reverse water-gas-shift reaction intermediates over a Pt/CeO2 catalyst. J Phys Chem B 108(52):20240–20246
Zhang M, Zijlstra B, Filot IAW et al (2020) A theoretical study of the reverse water-gas shift reaction on Ni(111) and Ni(311) surfaces. Can J Chem Eng 98(3):740–748
Fornero EL, Chiavassa DL, Bonivardi AL et al (2017) Transient analysis of the reverse water gas shift reaction on Cu/ZrO2 and Ga2O3/Cu/ZrO2 catalysts. J CO2 Util 22:289–298
Ernst K (1992) Kinetics of the reverse water–gas shift reaction over Cu(110). J Catal 134(1):66–74
Hadden RA, Vandervell HD, Waugh KC et al (1988) The adsorption and decomposition of carbon dioxide on polycrystalline copper. Catal Lett 1(1–3):27–33
Kim SS, Lee HH, Hong SC (2012) A study on the effect of support’s reducibility on the reverse water-gas shift reaction over Pt catalysts. Appl Catal A: Gen 423–424:100–107
Widmann D, Behm RJ (2011) Active oxygen on a Au/TiO2 catalyst: formation, stability, and CO oxidation activity. Angew Chem Int Ed 50(43):10241–10245
Kotobuki M, Leppelt R, Hansgen DA et al (2009) Reactive oxygen on a Au/TiO2 supported catalyst. J Catal 264(1):67–76
Sharma S, Hilaire S, Vohs JM et al (2000) Evidence for oxidation of ceria by CO2. J Catal 190(1):199–204
Bernal S, Blanco G, Gatica JM et al (2001) Effect of mild Re-oxidation treatments with CO2 on the chemisorption capability of a Pt/CeO2 catalyst reduced at 500 °C. J Catal 200(2):411–415
Su X, Yang XL, Zhao B et al (2017) Designing of highly selective and high-temperature endurable RWGS heterogeneous catalysts: recent advances and the future directions. J Energy Chem 26(5):854–867
Chen XD, Su X, Liang BL et al (2016) Identification of relevant active sites and a mechanism study for reverse water gas shift reaction over Pt/CeO2 catalysts. J Energy Chem 25(6):1051–1057
Jacobs G, Davis BH (2005) Reverse water-gas shift reaction: steady state isotope switching study of the reverse water-gas shift reaction using in situ DRIFTS and a Pt/ceria catalyst. Appl Catal A: Gen 284(1–2):31–38
Shido T, Iwasawa Y (1993) Reactant-promoted reaction mechanism for water-gas shift reaction on Rh-doped CeO2. J Catal 141(1):71–81
Chen XD, Su X, Duan HM et al (2017) Catalytic performance of the Pt/TiO2 catalysts in reverse water gas shift reaction: controlled product selectivity and a mechanism study. Catal Today 281:312–318
Kim SS, Park KH, Hong SC (2013) A study of the selectivity of the reverse water–gas-shift reaction over Pt/TiO2 catalysts. Fuel Process Technol 108:47–54
Meunier FC, Tibiletti D, Goguet A et al (2005) On the reactivity of carbonate species on a Pt/CeO2 catalyst under various reaction atmospheres: application of the isotopic exchange technique. Appl Catal A: Gen 289(1):104–112
Goguet A, Shekhtman S, Burch R et al (2006) Pulse-response TAP studies of the reverse water–gas shift reaction over a Pt/CeO2 catalyst. J Catal 237(1):102–110
Dou J, Sheng Y, Choong C et al (2017) Silica nanowires encapsulated Ru nanoparticles as stable nanocatalysts for selective hydrogenation of CO2 to CO. Appl Catal B: Environ 219:580–591
Panagiotopoulou P (2017) Hydrogenation of CO2 over supported noble metal catalysts. Appl Catal A: Gen 542:63–70
Park JN, McFarland EW (2009) A highly dispersed Pd–Mg/SiO2 catalyst active for methanation of CO2. J Catal 266(1):92–97
Porosoff MD, Yan BH, Chen JG (2016) Catalytic reduction of CO2 by H2 for synthesis of CO, methanol and hydrocarbons: challenges and opportunities. Energy Environ Sci 9(1):62–73
Saeidi S, Najari S, Fazlollahi F et al (2017) Mechanisms and kinetics of CO2 hydrogenation to value-added products: a detailed review on current status and future trends. Renew Sustain Energy Rev 80:1292–1311
Wang W, Wang SP, Ma XB et al (2011) Recent advances in catalytic hydrogenation of carbon dioxide. Chem Soc Rev 40(7):3703–3727
Kattel S, Liu P, Chen JG (2017) Tuning selectivity of CO2 hydrogenation reactions at the metal/oxide interface. J Am Chem Soc 139(29):9739–9754
Tao Y, Zhu YM, Liu CJ et al (2018) A highly selective Cr/ZrO2 catalyst for the reverse water-gas shift reaction prepared from simulated Cr-containing wastewater by a photocatalytic deposition process with ZrO2. J Environ Chem Eng 6(6):6761–6770
Porosoff MD, Yang XF, Boscoboinik JA et al (2014) Molybdenum carbide as alternative catalysts to precious metals for highly selective reduction of CO2 to CO. Angew Chem Int Ed 53(26):6705–6709
Daza YA, Maiti D, Kent RA et al (2015) Isothermal reverse water gas shift chemical looping on La0.75Sr0.25Co(1−Y)FeYO3 perovskite-type oxides. Catal Today 258:691–698
Aitbekova A, Wu LH, Wrasman CJ et al (2018) Low-temperature restructuring of CeO2-supported Ru nanoparticles determines selectivity in CO2 catalytic reduction. J Am Chem Soc 140(42):13736–13745
Matsubu JC, Yang VN, Christopher P (2015) Isolated metal active site concentration and stability control catalytic CO2 reduction selectivity. J Am Chem Soc 137(8):3076–3084
Li J, Lin YP, Pan XL et al (2019) Enhanced CO2 methanation activity of Ni/anatase catalyst by tuning strong metal–support interactions. ACS Catal 9(7):6342–6348
Kattel S, Yan BH, Chen JG et al (2016) CO2 hydrogenation on Pt, Pt/SiO2 and Pt/TiO2: importance of synergy between Pt and oxide support. J Catal 343:115–126
Ye JY, Ge QF, Liu CJ (2015) Effect of PdIn bimetallic particle formation on CO2 reduction over the Pd-In/SiO2 catalyst. Chem Eng Sci 135:193–201
Shi C, O’Grady CP, Peterson AA et al (2013) Modeling CO2 reduction on Pt(111). Phys Chem Chem Phys 15(19):7114
Kwak JH, Kovarik L, Szanyi J (2013) Heterogeneous catalysis on atomically dispersed supported metals: CO2 reduction on multifunctional Pd catalysts. ACS Catal 3(9):2094–2100
Bobadilla LF, Santos JL, Ivanova S et al (2018) Unravelling the role of oxygen vacancies in the mechanism of the reverse water–gas shift reaction by operando DRIFTS and ultraviolet–visible spectroscopy. ACS Catal 8(8):7455–7467
Yang SC, Pang SH, Sulmonetti TP et al (2018) Synergy between ceria oxygen vacancies and Cu nanoparticles facilitates the catalytic conversion of CO2 to CO under mild conditions. ACS Catal 8(12):12056–12066
Sakurai H, Tsubota S, Haruta M (1993) Hydrogenation of CO2 over gold supported on metal oxides. Appl Catal A: Gen 102(2):125–136
Kattel S, Yu WT, Yang XF et al (2016) CO2 hydrogenation over oxide-supported PtCo catalysts: the role of the oxide support in determining the product selectivity. Angew Chem Int Ed 55(28):7968–7973
Kwak JH, Kovarik L, Szanyi J (2013) CO2 reduction on supported Ru/Al2O3 catalysts: cluster size dependence of product selectivity. ACS Catal 3(11):2449–2455
Li SW, Xu Y, Chen YF et al (2017) Tuning the selectivity of catalytic carbon dioxide hydrogenation over iridium/cerium oxide catalysts with a strong metal–support interaction. Angew Chem Int Ed 56(36):10761–10765
Yan BH, Zhao BH, Kattel S et al (2019) Tuning CO2 hydrogenation selectivity via metal-oxide interfacial sites. J Catal 374:60–71
Chen CS, Cheng WH, Lin SS (2003) Study of reverse water gas shift reaction by TPD, TPR and CO2 hydrogenation over potassium-promoted Cu/SiO2 catalyst. Appl Catal A: Gen 238(1):55–67
Liang BL, Duan HM, Su X et al (2017) Promoting role of potassium in the reverse water gas shift reaction on Pt/mullite catalyst. Catal Today 281:319–326
Bando KK, Soga K, Kunimori K et al (1998) Effect of Li additive on CO2 hydrogenation reactivity of zeolite supported Rh catalysts. Appl Catal A: Gen 175(1–2):67–81
Wang CT, Guan EJ, Wang L et al (2019) Product selectivity controlled by nanoporous environments in zeolite crystals enveloping rhodium nanoparticle catalysts for CO2 hydrogenation. J Am Chem Soc 141(21):8482–8488
Goguet A, Meunier F, Breen J et al (2004) Study of the origin of the deactivation of a Pt/CeO2 catalyst during reverse water gas shift (RWGS) reaction. J Catal 226(2):382–392
Wang LC, Tahvildar Khazaneh M, Widmann D et al (2013) TAP reactor studies of the oxidizing capability of CO2 on a Au/CeO2 catalyst—a first step toward identifying a redox mechanism in the Reverse Water-Gas Shift reaction. J Catal 302:20–30
Jin T, Zhou Y, Mains GJ et al (1987) Infrared and X-ray photoelectron spectroscopy study of carbon monoxide and carbon dioxide on platinum/ceria. J Phys Chem 91(23):5931–5937
Porosoff MD, Chen JG (2013) Trends in the catalytic reduction of CO2 by hydrogen over supported monometallic and bimetallic catalysts. J Catal 301:30–37
Chen XD, Su X, Su HY et al (2017) Theoretical insights and the corresponding construction of supported metal catalysts for highly selective CO2 to CO conversion. ACS Catal 7(7):4613–4620
Kim SS, Lee HH, Hong SC (2012) The effect of the morphological characteristics of TiO2 supports on the reverse water–gas shift reaction over Pt/TiO2 catalysts. Appl Catal B: Environ 119–120:100–108
Ro I, Sener CN, Stadelman TM et al (2016) Measurement of intrinsic catalytic activity of Pt monometallic and Pt-MoOx interfacial sites over visible light enhanced PtMoOx/SiO2 catalyst in reverse water gas shift reaction. J Catal 344:784–794
Alayoglu S, Beaumont SK, Zheng F et al (2011) CO2 hydrogenation studies on Co and CoPt bimetallic nanoparticles under reaction conditions using TEM. XPS NEXAFS. Top Catal 54(13–15):778–785
Yuan HJ, Zhu XL, Han JY et al (2018) Rhenium-promoted selective CO2 methanation on Ni-based catalyst. J CO2 Util 26:8–18
Kharaji AG, Shariati A, Takassi MA (2013) A novel γ-alumina supported Fe-Mo bimetallic catalyst for reverse water gas shift reaction. Chin J Chem Eng 21(9):1007–1014
Zhu XL, Shen M, Lobban LL et al (2011) Structural effects of Na promotion for high water gas shift activity on Pt–Na/TiO2. J Catal 278(1):123–132
Santos J, Bobadilla L, Centeno M et al (2018) Operando DRIFTS-MS study of WGS and rWGS reaction on biochar-based Pt catalysts: the promotional effect of Na. C 4(3):47
Yang M, Li S, Wang Y et al (2014) Catalytically active Au-O(OH)x-species stabilized by alkali ions on zeolites and mesoporous oxides. Science 346(6216):1498–1501
Yang XL, Su X, Chen XD et al (2017) Promotion effects of potassium on the activity and selectivity of Pt/zeolite catalysts for reverse water gas shift reaction. Appl Catal B: Environ 216:95–105
Acknowledgements
The authors are grateful to the National Key Research and Development Program of China (No. 2016YFB0600900) and the National Natural Science Foundation of China (Nos. 21676194 and 21873067) for their support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhu, M., Ge, Q. & Zhu, X. Catalytic Reduction of CO2 to CO via Reverse Water Gas Shift Reaction: Recent Advances in the Design of Active and Selective Supported Metal Catalysts. Trans. Tianjin Univ. 26, 172–187 (2020). https://doi.org/10.1007/s12209-020-00246-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12209-020-00246-8