This study aims to evaluate the performance of silica fume (SF) and nano-silica (NS) on enhancing the sulfuric acid resistance of mortar mixtures. The NS and SF were added as substitutions for cement at various dosages. The cured samples were immersed in the sulfuric acid solution with a pH of 2 for 75 d. A compressive strength test and absorption and voids tests were conducted before sulfuric acid immersion. It was found that the addition of SF and NS reduced the volume of permeable voids and increased compressive strength. A thermo-gravimetric analysis was carried out to investigate the hydration of mixtures. The mixtures with SF showed a higher level of pozzolanic reaction compared with mixtures with NS. After the 75 d of immersion, the mixtures with 5% SF and 1% NS showed the best resistance against sulfuric acid because they showed the lowest mass change and length change.
摘要
为了研究硅粉与纳米硅粉作为添加剂对水泥砂浆耐酸性的影响, 本文将标准养护后的样品浸泡于 pH=2 的硫酸溶液中, 并分析了样品在浸泡实验前后的性能变化. 实验结果表明, 添加硅粉及纳米硅粉能有效提高浸泡前水泥砂浆的单轴抗压强度, 降低可渗透孔隙的体积率. 相较于纳米硅粉, 硅粉对水泥砂浆的性能影响更为显著. 在硫酸溶液中浸泡 75 d 后, 样品出现了不同程度的腐蚀. 其中, 掺 5%硅粉及 1%纳米硅粉的样品展现了最低的质量损失及长度损失.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
DORION J F, HADJIGEORGIOU J. Microbiologically influenced corrosion (MIC) of ground support [J]. Geotechnical and Geological Engineering, 2020, 38(1): 375–387. DOI: https://doi.org/10.1007/s10706-019-01028-3.
WU L, HU C, LIU V W. The sustainability of concrete in sewer tunnel—A narrative review of acid corrosion in the city of Edmonton, Canada [J]. Sustainability, 2018, 10(2). DOI: https://doi.org/10.3390/su10020517.
CARATELLI A, MEDA A, RINALDI Z, ROMUALDI P, Structural behaviour of precast tunnel segments in fiber reinforced concrete [J]. Tunnelling and Underground Space Technology, 2011. 26(2): 284–291. DOI: https://doi.org/10.1016/j.tust.2010.10.003.
YU H, WU L, LIU W, POURRAHIMIAN Y. Effects of fibers on expansive shotcrete mixtures consisting of calcium sulfoaluminate cement, ordinary Portland cement, and calcium sulfate [J]. Journal of Rock Mechanics and Geotechnical Engineering, 2018, 10(2): 212–221. DOI: https://doi.org/10.1016/j.jrmge.2017.12.001.
ERGÜLER G K. Investigation the applicability of eggshell for the treatment of a contaminated mining site [J]. Minerals Engineering, 2015, 76: 10–19. DOI: https://doi.org/10.1016/j.mineng.2015.02.002.
JONES S N, CETIN B. Remediation of acid mine drainages with recycled concrete aggregates [J]. Geotechnical Frontiers, 2017, 2017. DOI: https://doi.org/10.1061/9780784480434.049.
JEON I K, QUDOOS A, JAKHRANI S H, KIM H G, RYOU J S. Investigation of sulfuric acid attack upon cement mortars containing silicon carbide powder [J]. Powder Technology, 2020, 359: 181–189. DOI: https://doi.org/10.1016/j.powtec.2019.10.026.
LI J, ZHANG T, LIU T. Corrosion of cement-based support system by acidic water in a deep copper mine [J]. Mordern Mining, 2018(591): 226–229. (in Chinese)
KAUFMANN J. Durability performance of fiber reinforced shotcrete in aggressive environment [C]// World Tunnelling Congress. 2014: Foz do Iguaçu, Brazil. p. 7.
EKOLU S O, DIOP S, AZENE F, MKHIZE N. Disintegration of concrete construction induced by acid mine drainage attack [J]. Journal of the South African Institution of Civil Engineers, 2016, 58(1): 34–42. DOI: https://doi.org/10.17159/2309-8775/2016/v58n1a4.
ERCIKDI B, KESIMAL A, CIHANGIR F, DEVECI H, ALP 1. Cemented paste backfill of sulphide-rich tailings: Importance of binder type and dosage [J]. Cement and Concrete Composites, 2009. 31(4): 268–274. DOI: https://doi.org/10.1016/j.cemconcomp.2009.01.008.
YIN S, SHAO Y, WU A, RAO Y, CHEN X. Deformation behaviors of cemented backfill using sulphide-content tailings [C]// Proceedings of the 20th International Seminar on Paste and Thickened Tailings, 2017. Beijing: University of Science and Technology Beijing, 315–327. DOI: https://doi.org/10.36487/ACG_REP/1752_35_YIN.
TARIQ A, YANFUL E K. A review of binders used in cemented paste tailings for underground and surface disposal practices [J]. Journal of Environmental Management, 2013, 131: 138–149. DOI: https://doi.org/10.1016/j.jenvman.2013.09.039.
HAGELIA P. Durability development in sprayed concrete for rock support; Is it possible to establish a basis for modelling? [J]. Heron, 2019, 64(1/2): 75.
TORII K, KAWAMURA M. Effects of fly ash and silica fume on the resistance of mortar to sulfuric acid and sulfate attack [J]. Cement and Concrete Research, 1994, 24(2): 361–370. DOI: https://doi.org/10.1016/0008-8846(94)90063-9.
MEHTA P. Studies on chemical resistance of low water/cement ratio concretes [J]. Cement and Concrete Research, 1985, 15(6): 969–978. DOI: https://doi.org/10.1016/0008-8846(85)90087-0.
WU L, HU C, LIU W V. Effects of pozzolans on acid resistance of shotcrete for sewer tunnel rehabilitation [J]. Journal of Sustainable Cement-Based Materials, 2019, 8(1): 55–77. DOI: https://doi.org/10.1080/21650373.2018.1519645.
MEHTA P K. Properties of blended cements made from rice husk ash [J]. Journal of the American Concrete Institute, 1977, 74(9): 440–442. DOI: https://doi.org/10.14359/11022.
GUTBERLET T, HILBIG H, BEDDOE R. Acid attack on hydrated cement—Effect of mineral acids on the degradation process [J]. Cement and Concrete Research, 2015, 74: 35–43. DOI: https://doi.org/10.1016/j.cemconres.2015.03.011.
AMIN M, BASSUONI M T. Response of concrete with blended binders and nanoparticles to sulfuric acid attack [J]. Magazine of Concrete Research, 2017, 70(12): 617–632. DOI: https://doi.org/10.1680/jmacr.17.00081.
DUAN P, SHUI Z, CHEN W, SHEN C. Effects of metakaolin, silica fume and slag on pore structure, interfacial transition zone and compressive strength of concrete [J]. Construction and Building Materials, 2013, 44: 1–6. DOI: https://doi.org/10.1016/j.conbuildmat.2013.02.075.
DIAB A M, ELYAMANY H E, ELMOATY A E M A, SREH M M. Effect of nanomaterials additives on performance of concrete resistance against magnesium sulfate and acids [J]. Construction and Building Materials, 2019, 210: 210–231. DOI: https://doi.org/10.1016/j.conbuildmat.2019.03.099.
MAHDIKHANI M, BAMSHAD O, FALLAH SHIRVANI M. Mechanical properties and durability of concrete specimens containing nano silica in sulfuric acid rain condition [J]. Construction and Building Materials, 2018. 167: 929–935. DOI: https://doi.org/10.1016/j.conbuildmat.2018.01.137.
BIRICIK H, SARIER N. Comparative study of the characteristics of nano silica-, silica fume-and fly ash-incorporated cement mortars [J]. Materials Research, 2014, 17(3): 570–582. DOI: https://doi.org/10.1590/S1516-14392014005000054
QUERCIA BIANCHI G. Application of nano-silica in concrete [D]. Eindhoven: Technische Universiteit Eindhoven, 2014. DOI: https://doi.org/10.6100/IR780551.
ASSI L N. Cost and fuel usage optimization of activating solution based silica fume geopolymer concrete [D]. University of South Carolina. 2017.
HENDI A, RAHMANI H, MOSTOFINEJAD D, TAVAKOLINIA A, KHOSRAVI M. Simultaneous effects of microsilica and nanosilica on self-consolidating concrete in a sulfuric acid medium [J]. Construction and Building Materials, 2017. 152: 192–205. DOI: https://doi.org/10.1016/j.conbuildmat.2017.06.165.
MAHMOUD M, BASSUONI M T. Response of concrete to incremental aggression of sulfuric acid [J]. Journal of Testing and Evaluation, 2020, 48(4): 19. DOI: https://doi.org/10.1520/JTE20180114.
HEWAYDE E, ALLOUCHE E, NAKHLA G. Experimental investigations of the effect of selected admixtures on the resistance of concrete to sulfuric acid attack [J]. New Pipeline Technologies, Security, and Safety, 2003. DOI: https://doi.org/10.1061/40690(2003)33.
RAHMANI H, RAMAZANIANPOUR A, PARHIZKAR T, HILLEMEIER B. Contradictory effects of silica fume concretes in sulfuric acid environments [C]// 3rd International Conference on Concrete & Development. Tehran, Iran, 2009: 761–774.
WAFA F. Accelerated sulfate attack on concrete in a hot climate [J]. Cement, Concrete and Aggregates, 1994, 16(1): 31–35. DOI: https://doi.org/10.1520/CCA10558J.
ATTIOGBE E K, RIZKALLA S H. Response of concrete to sulfuric acid attack [J]. ACI Materials Journal, 1988, 85(6): 481–488.
TOKYAY M. Cement and concrete mineral admixtures [M]. Boca Raton, Florida: CRC Press, 2016.
ACI COMMITTEE, 506R-16: Guide to Shotcrete [R]. American Concrete Institute: Farmington Hills, MI, United States. 2016.
BERRA M, CARASSITI F, MANGIALARDI T, PAOLINI A E, SEBASTIANI M. Effects of nanosilica addition on workability and compressive strength of Portland cement pastes [J]. Construction and Building Materials, 2012, 35: 666–675. DOI: https://doi.org/10.1016/j.conbuildmat.2012.04.132.
SIDDIQUE R. Utilization of silica fume in concrete: Review of hardened properties [J]. Resources, Conservation and Recycling, 2011, 55(11): 923–932. DOI: https://doi.org/10.1016/j.resconrec.2011.06.012.
KHALOO A, MOBINI M H, HOSSEINI P. Influence of different types of nano-SiO2 particles on properties of high-performance concrete [J]. Construction and Building Materials, 2016, 113: 188–201. DOI: https://doi.org/10.1016/j.conbuildmat.2016.03.041.
WONG H S, ABDUL RAZAK H. Efficiency of calcined kaolin and silica fume as cement replacement material for strength performance [J]. Cement and Concrete Research, 2005, 35(4): 696–702. DOI: https://doi.org/10.1016/j.cemconres.2004.05.051.
ASTM C192/C192M-16a. Standard practice for making and curing concrete test specimens in the laboratory [S]. ASTM International: West Conshohocken, PA. United States. 2016.
ASTM C642-13. Standard test method for density, absorption, and voids in hardened concrete [S]. ASTM International: West Conshohocken, PA. United States, 2013. DOI: https://doi.org/10.1520/c0642-13.
ASTM C39/C39M-18. Standard test method for compressive strength of cylindrical concrete specimens [S]. ASTM International: West Conshohocken, PA. United States, 2018.
HOSSAIN M M, KARIM M R, HASAN M, HOSSAIN M K, ZAIN M F M. Durability of mortar and concrete made up of pozzolans as a partial replacement of cement: A review [J]. Construction and Building Materials, 2016, 116: 128–140. DOI: https://doi.org/10.1016/j.conbuildmat.2016.04.147.
WANG J, NIU D, DING S, MI Z, LUO D. Microstructure, permeability and mechanical properties of accelerated shotcrete at different curing age [J]. Construction and Building Materials, 2015, 78: 203–216. DOI: https://doi.org/10.1016/j.conbuildmat.2014.12.111.
SUPIT S W M, SHAIKH F U A. Durability properties of high volume fly ash concrete containing nano-silica [J]. Materials and Structures, 2015, 48(8): 2431–2445. DOI: https://doi.org/10.1617/s11527-014-0329-0.
POON C S, KOU S C, LAM L. Compressive strength, chloride diffusivity and pore structure of high performance metakaolin and silica fume concrete [J]. Construction and Building Materials, 2006, 20(10): 858–865. DOI: https://doi.org/10.1016/j.conbuildmat.2005.07.001.
ABBASS W, KHAN M I, MOURAD S. Experimentation and predictive models for properties of concrete added with active and inactive SiO2 fillers [J]. Materials, 2019, 12(2): 299. DOI: https://doi.org/10.3390/ma12020299.
YAJUN J, CAHYADI J H. Simulation of silica fume blended cement hydration [J]. Materials and Structures, 2004, 37(6): 397–404. DOI: https://doi.org/10.1007/BF02479636.
RUPASINGHE M, SAN NICOLAS R, MENDIS P, SOFI M, NGO T. Investigation of strength and hydration characteristics in nano-silica incorporated cement paste [J]. Cement and Concrete Composites, 2017, 80: 17–30. DOI: https://doi.org/10.1016/j.cemconcomp.2017.02.011.
DODSON V H. Pozzolans and the pozzolanic reaction [M]//Concrete Admixtures, Boston, MA: Springer US, 1990. DOI: https://doi.org/10.1007/978-1-4757-4843-77.
RICHARDSON I G. The nature of C-S-H in hardened cements [J]. Cement and Concrete Research, 1999, 29(8): 1131–1147. DOI: https://doi.org/10.1016/S0008-8846(99)00168-4.
BASSUONI M T, NEHDI M L. Resistance of self-consolidating concrete to sulfuric acid attack with consecutive pH reduction [J]. Cement and Concrete Research, 2007, 37(7): 1070–1084. DOI: https://doi.org/10.1016/j.cemconres.2007.04.014.
PELISSER F, GLEIZE P J P, MIKOWSKI A. Effect of the Ca/Si molar ratio on the micro/nanomechanical properties of synthetic C-S-H measured by nanoindentation [J]. The Journal of Physical Chemistry C, 2012, 116(32): 17219–17227. DOI: https://doi.org/10.1021/jp302240c.
BAHAFID S, GHABEZLOO S, DUC M, FAURE P, SULEM J. Effect of the hydration temperature on the microstructure of Class G cement: C-S-H composition and density [J]. Cement and Concrete Research, 2017, 95: 270–281. DOI: https://doi.org/10.1016/j.cemconres.2017.02.008.
TORII K, KAWAMURA M. Pore structure and chloride ion permeability of mortars containing silica fume [J]. Cement and Concrete Composites, 1994, 16(4): 279–286. DOI: https://doi.org/10.1016/0958-9465(94)90040-X.
MEHTA P K, MONTEIRO P J. Concrete microstructure, properties and materials [M]. New York: McGraw-Hill Education, 2014.
QUERCIA G, SPIESZ P, HÜSKEN G, BROUWERS H. SCC modification by use of amorphous nano-silica [J]. Cement and Concrete Composites, 2014, 45: 69–81. DOI: https://doi.org/10.1016/j.cemconcomp.2013.09.001.
ZHANG M H, ISLAM J, PEETHAMPARAN S. Use of nano-silica to increase early strength and reduce setting time of concretes with high volumes of slag [J]. Cement and Concrete Composites, 2012, 34(5): 650–662. DOI: https://doi.org/10.1016/j.cemconcomp.2012.02.005.
YAJUUN J, CAHYADI J. Investigation on microstructure of silica fume cement pastes [J]. WIT Transactions on the Built Environment, 2002, 59: 9.
LI H, YAN D, CHEN G, XU S, LIU J, HU Y. Porosity, pore size distribution and chloride permeability of shotcrete modified with nano particles at early age [J]. Journal of Wuhan University of Technology-Mater Sci Ed, 2016, 31(3): 582–589. DOI: https://doi.org/10.1007/s11595-016-1413-9.
WU Z, SHI C, KHAYAT K H, WAN S. Effects of different nanomaterials on hardening and performance of ultra-high strength concrete (UHSC) [J]. Cement and Concrete Composites, 2016, 70: 24–34. DOI: https://doi.org/10.1016/j.cemconcomp.2016.03.003.
JALAL M, POULADKHAN A, HARANDI O F, JAFARI D. Comparative study on effects of class F fly ash, nano silica and silica fume on properties of high performance self compacting concrete [J]. Construction and Building Materials, 2015, 94: 90–104. DOI: https://doi.org/10.1016/j.conbuildmat.2015.07.001.
KONG D, DU X, WEI S, ZHANG H, YANG Y, SHAH S P. Influence of nano-silica agglomeration on microstructure and properties of the hardened cement-based materials [J]. Construction and Building Materials, 2012, 37: 707–715. DOI: https://doi.org/10.1016/j.conbuildmat.2012.08.006.
FOROOD T I, REDAELLI E, LOLLINI F, LI W, BERTOLINI L. Effects of nanosilica on compressive strength and durability properties of concrete with different water to binder ratios [J]. Advances in Materials Science and Engineering, 2016: 16. DOI: https://doi.org/10.1155/2016/8453567.
LIM S, MONDAL P. Effects of incorporating nanosilica on carbonation of cement paste [J]. Journal of Materials Science, 2015, 50(10): 3531–3540. DOI: https://doi.org/10.1007/s10853-015-8910-7.
SARGENT P. The development of alkali-activated mixtures for soil stabilisation [M]// Handbook of alkali-activated cements, mortars and concretes. Elsevier, 2015. DOI: https://doi.org/10.1533/9781782422884.4.555.
ABID K, GHOLAMI R, ELOCHUKWU H, MOSTOFI M, BING C H, MUKTADIR G. A methodology to improve nanosilica based cements used in CO2 sequestration sites [J]. Petroleum, 2018, 4(2): 198–208. DOI: https://doi.org/10.1016/j.petlm.2017.10.005.
DU H, DU S, LIU X. Durability performances of concrete with nano-silica [J]. Construction and Building Materials, 2014, 73: 705–712. DOI: https://doi.org/10.1016/j.conbuildmat.2014.10.014.
AYDıN A C, NASL V J, KOTAN T. The synergic influence of nano-silica and carbon nano tube on self-compacting concrete [J]. Journal of Building Engineering, 2018, 20: 467–475. DOI: https://doi.org/10.1016/j.jobe.2018.08.013.
SADRMOMTAZI A, FASIHI A, BALALAEI F, HAGHI A. Investigation of mechanical and physical properties of mortars containing silica fume and nano-SiO2 [C]//Proceedings of the Third International Conference on Concrete and Development. Tehran, Iran, 2009: 27–29.
DYER T. Influence of cement type on resistance to attack from two carboxylic acids [J]. Cement and Concrete Composites, 2017, 83: 20–35. DOI: https://doi.org/10.1016/j.cemconcomp.2017.07.004.
LIN-PING W, GUANG-PING H, CHAO-SHI H, WEI VICTOR L. Effects of cellulose nanocrystals on improving the acid resistance of cementitious composites in mining [J]. International Journal of Minerals, Metallurgy and Materials. DOI: https://doi.org/10.1007/s12613-020-2087-z.
MAKHLOUFI Z, BEDERINA M, BOUHICHA M, KADRI E H. Effect of mineral admixtures on resistance to sulfuric acid solution of mortars with quaternary binders [J]. Physics Procedia, 2014, 55: 329–335. DOI: https://doi.org/10.1016/j.phpro.2014.07.048.
RAHMANI H, RAMZANIANPOUR A. Effect of silica fume and natural pozzolanas on sulfuric acid resistance of dense concretes [J]. Asian Journal of Civil Engineering, 2008, 9(3): 303–319.
FENG J, SUN J, YAN P. The influence of ground fly ash on cement hydration and mechanical property of mortar [J]. Advances in Civil Engineering, 2018. DOI: https://doi.org/10.1155/2018/4023178.
AL-SWAIDANI A M, ALIYAN S D, ADARNALY N. Mechanical strength development of mortars containing volcanic scoria-based binders with different fineness [J]. Engineering Science and Technology, 2016, 19(2): 970–979. DOI: https://doi.org/10.1016/jjestch.2015.12.006.
TSUBONE K, YAMAGUCHI Y, OGAWA Y, KAWAI K. Deterioration of concrete immersed in sulfuric acid for a long term [J]. Key Engineering Materials, 2016, 711: 659–664. DOI: https://doi.org/10.4028/www.scientific.net/KEM.711.659.
CHENG-YI H, FELDMAN R F. Hydration reactions in portland cement-silica fume blends [J]. Cement and Concrete Research, 1985, 15(4): 585–592. DOI: https://doi.org/10.1016/0008-8846(85)90056-0.
KADRI E H, KENAI S, EZZIANE K, SIDDIQUE R, de SCHUTTER G. Influence of metakaolin and silica fume on the heat of hydration and compressive strength development of mortar [J]. Applied Clay Science, 2011, 53(4): 704–708. DOI: https://doi.org/10.1016/j.clay.2011.06.008.
SIAD H, LACHEMI M, SAHMARAN M, HOSSAIN K M A. Effect of glass powder on sulfuric acid resistance of cementitious materials [J]. Construction and Building Materials, 2016, 113: 163–173. DOI: https://doi.org/10.1016/j.conbuildmat.2016.03.049.
NEMATZADEH M, FALLAH-VALUKOLAEE S. Erosion resistance of high-strength concrete containing forta-ferro fibers against sulfuric acid attack with an optimum design [J]. Construction and Building Materials, 2017, 154: 675–686. DOI: https://doi.org/10.1016/j.conbuildmat.2017.07.180.
LESLIE J, CHEESMAN W. An ultrasonic method of studying deterioration and cracking in concrete structures [J]. Journal of the American Concrete Institute, 1949, 21(1): 17–36.
FELDMAN R F. Non-destructive testing of concrete [J]. Canadian Building Digest, 1977, 187: 4.
KHAN H A, CASTEL A, KHAN M S H, MAHMOOD A H. Durability of calcium aluminate and sulphate resistant Portland cement based mortars in aggressive sewer environment and sulphuric acid [J]. Cement and Concrete Research, 2019, 124: 105852. DOI: https://doi.org/10.1016/j.cemconres.2019.105852.
GRANDCLERC A, DANGLA P, GUEGUEN-MINERBE M, CHAUSSADENT T. Modelling of the sulfuric acid attack on different types of cementitious materials [J]. Cement and Concrete Research, 2018, 105: 126–133. DOI: https://doi.org/10.1016/j.cemconres.2018.01.014.
GU L, BENNETT T, VISINTIN P. Sulphuric acid exposure of conventional concrete and alkali-activated concrete: Assessment of test methodologies [J]. Construction and Building Materials, 2019, 197: 681–692. DOI: https://doi.org/10.1016/j.conbuildmat.2018.11.166.
Acknowledgment
The authors are thankful for the financial support by the Natural Sciences and Engineering Research Council of Canada (NSERC RGPIN-2017-05537) and the generous donation of Aerosol-fumed silica from Evonik Industries.
Author information
Authors and Affiliations
Contributions
WU Lin-ping was responsible for experimental design, data collection and analysis, and manuscript writing. LIU Wei Victor was involved in concept formation and contributed to manuscript composition and edits. HUANG Guang-ping helped in data collection and manuscript edits.
Corresponding author
Ethics declarations
The authors declare that they have no conflict of interest.
Additional information
Foundation item: Project(NSERC RGPIN-2017-05537) supported by the Natural Sciences and Engineering Research Council of Canada
Rights and permissions
About this article
Cite this article
Wu, Lp., Huang, Gp. & Liu, W.V. Performance evaluation of nano-silica and silica fume on enhancing acid resistance of cement-based composites for underground structures. J. Cent. South Univ. 27, 3821–3838 (2020). https://doi.org/10.1007/s11771-020-4473-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11771-020-4473-0