Abstract
Binary polythiophene/multiwalled carbon nanotube (PTh/MWCNT) and ternary PTh/SnSe/MWCNT composites with different weight proportions have been successfully prepared by solution mixing, ultrasonic dispersion, and mechanical ball milling. The morphology, microstructure, and thermal stability of all the samples were studied by x-ray diffraction analysis, Fourier-transform infrared spectroscopy, field-emission scanning electron microscopy, and thermogravimetric analysis. The electrical conductivity of both the binary PTh/MWCNT and ternary PTh/SnSe/MWCNT composites was increased by nearly five orders of magnitude compared with pure PTh across the whole measurement temperature range. However, the Seebeck coefficient at room temperature decreased sharply from \(453.4\,\mu {{\text {V K}}}^{-1}\) for pure PTh to \(11{-}20\,\mu {{\text {V K}}}^{-1}\) for the composites. The thermal conductivity of all the composites was lower than 0.6 \({{\text {W m}}}^{-1}\,{{\text {K}}}^{-1}\), being slightly higher than that of pure PTh. As a result, the ZT values of all the composites were much higher than that of pure PTh (\(0.032 \times 10^{-4}\)), reaching \(1.3 \times 10^{-4}\) and \(1.62 \times 10^{-4}\) at room temperature for the binary PTh/MWCNT and ternary PTh/SnSe/MWCNT composites, respectively. The maximum ZT value reached \(3.05 \times 10^{-4}\) at 433 K for the binary PTh/MWCNT composite with MWCNT content of 40 wt.%. These results suggest that the thermoelectric performance of PTh/MWCNT composites can be greatly enhanced compared with pure PTh.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
M. He, F. Qiu, and Z. Lin, Energy Environ. Sci. 6, 1352 (2013).
B. Russ, A. Glaudell, J.J. Urban, M.L. Chabinyc, and R.A. Segalman, Nat. Rev. Mater. 1, 16050 (2016).
H. Yao, Z. Fan, H. Cheng, X. Guan, C. Wang, K. Sun, and J. Ouyang, Macromol. Rapid Commun. 39, 1700727 (2018).
B.T. McGrail, A. Sehirlioglu, and E. Pentzer, Angew. Chem. Int. Ed. 54, 1710 (2015).
Y. Li, Y. Du, Y. Dou, K. Cai, and J. Xu, Synth. Met. 226, 119 (2017).
G.H. Kim, L. Shao, K. Zhang, and K.P. Pipe, Nat. Mater. 12, 719 (2013).
R. Kroon, D.A. Mengistie, D. Kiefer, J. Hynynen, J.D. Ryan, L. Yu, and C. Muller, Chem. Soc. Rev. 45, 6147 (2016).
N. Toshima, Synth. Met. 225, 3–21 (2017).
A.M. Glaudell, J.E. Cochran, S.N. Patel, and M.L. Chabinyc, Adv. Energy Mater. 5, 1401072 (2015).
J. Zhao, D. Tan, and G. Chen, J. Mater. Chem. C 5, 47 (2017).
X. Hu, G. Chen, X. Wang, and H. Wang, J. Mater. Chem. A 3, 20896 (2015).
H. Ju, D. Park, and J. Kim, Chem. Eng. J 356, 950 (2019).
Y. Li, F. Li, J. Dong, Z. Ge, F. Kang, J. He, H. Du, B. Li, and J.-F. Li, J. Mater. Chem. C 4, 2047 (2016).
M. He, J. Ge, Z. Lin, X. Feng, X. Wang, H. Lu, Y. Yang, and F. Qiu, Energy Environ. Sci. 5, 8351 (2012).
C. Chang, M. Wu, D. He, Y. Pei, C.F. Wu, X. Wu, H. Yu, F. Zhu, K. Wang, Y. Chen, L. Huang, J.F. Li, J. He, and L.D. Zhao, Science 360, 778 (2018).
T. Zhang, K. Zhou, and Z.Q. Chen, Phys. Status Solidi B 252, 2179 (2015).
H.F. He, X.F. Li, Z.Q. Chen, Y. Zheng, D.W. Yang, and X.F. Tang, J. Phys. Chem. C 118, 22389 (2014).
X. Zhang and L.-D. Zhao, J. Materiomics 1, 92 (2015).
H. Wang and C. Yu, Joule 3, 53 (2019).
Y. Du, S.Z. Shen, W.D. Yang, K.F. Cai, and P.S. Casey, Synth. Met. 162, 375 (2012).
C. Lai, J. Li, C. Pan, L. Wang, and X. Bai, J. Electron. Mater. 45, 5246 (2016).
K. Hiraishi, A. Masuhara, H. Nakanishi, H. Oikawa, and Y. Shinohara, Jpn. J. Appl. Phys. 48, 071501 (2009).
J. Liu, J. Sun, and L. Gao, Nanoscale 3, 3616–3619 (2011).
L. Fan and X. Xu, RSC Adv. 5, 78104 (2015).
M. Famili, I.M. Grace, Q. Al-Galiby, H. Sadeghi, and C.J. Lambert, Adv. Funct. Mater. 28, 1703135 (2018).
B. Zhang, K. Wang, D. Li, and X. Cui, RSC Adv. 5, 33885 (2015).
G.-H. Kim, J. Kim, and K.P. Pipe, Appl. Phys. Lett. 108, 093301 (2016).
O. Bubnova, Z.U. Khan, A. Malti, S. Braun, M. Fahlman, M. Berggren, and X. Crispin, Nat. Mater. 10, 429 (2011).
K. Wei, T. Stedman, Z.-H. Ge, L.M. Woods, and G.S. Nolas, Appl. Phys. Lett. 107, 153301 (2015).
M.R. Karim, C.J. Lee, and M.S. Lee, J. Polym. Sci. A Polym. Chem. 44, 5283 (2006).
W. Zheng, P. Bi, H. Kang, W. Wei, F. Liu, J. Shi, L. Peng, Z. Wang, and R. Xiong, Appl. Phys. Lett. 105, 023901 (2014).
H. Wang, J.-H. Hsu, S.-I. Yi, S.L. Kim, K. Choi, G. Yang, and C. Yu, Adv. Mater. 27, 6855 (2015).
H. Wang, S.-I. Yi, X. Pu, and C. Yu, ACS Appl. Mater. Interfaces 7, 9589 (2015).
L. Liang, C. Gao, G. Chen, and C.-Y. Guo, J. Mater. Chem. C 4, 526 (2016).
F. Erden, H. Li, X. Wang, F. Wang, and C. He, Phys. Chem. Chem. Phys. 20, 9411 (2018).
T.P. Kaloni, P.K. Giesbrecht, G. Schreckenbach, and M.S. Freund, Chem. Mater. 29, 10248 (2017).
G. Han, S.R. Popuri, H.F. Greer, J.W. Bos, W. Zhou, A.R. Knox, A. Montecucco, J. Siviter, E.A. Man, M. Macauley, D.J. Paul, W.G. Li, M.C. Paul, M. Gao, T. Sweet, R. Freer, F. Azough, H. Baig, N. Sellami, T.K. Mallick, and D.H. Gregory, Angew. Chem. Int. Ed. 55, 6433 (2016).
L.D. Zhao, S.H. Lo, Y. Zhang, H. Sun, G. Tan, C. Uher, and C. Wolverton, Nature 508, 373 (2014).
L.D. Zhao, G. Tan, S. Hao, J. He, Y. Pei, H. Chi, H. Wang, S. Gong, H. Xu, V.P. Dravid, C. Uher, G.J. Snyder, C. Wolverton, and M.G. Kanatzidis, Science 351, 141 (2016).
X.G. Li, J. Li, Q.K. Meng, and M.R. Huang, J. Phys. Chem. B 113, 9718 (2009).
X. She, X. Su, H. Xie, J. Fu, Y. Yan, W. Liu, P.F. Poudeu Poudeu, and X. Tang, ACS Appl. Mater. Interfaces 10, 25519 (2018).
M.R. Karim, K.T. Lim, C.J. Lee, and M.S. Lee, Synth. Met. 157, 1008 (2007).
M.-D. Lu and S.-M. Yang, Synth. Met. 154, 73 (2005).
X.G. Li, J. Li, and M.R. Huang, Chemistry 15, 6446 (2009).
A. Agarwal, S.H. Chaki, and D. Lakshminarayana, Mater. Lett. 61, 5188 (2007).
S. Mallakpour, A. Abdolmaleki, and S. Borandeh, Prog. Org. Coat. 77, 1966 (2004).
D. Wang, L. Wang, W. Wang, X. Bai, and J. Li, in Third International Conference on Smart Materials and Nanotechnology in Engineering (2012).
L. Wang, X. Jia, D. Wang, G. Zhu, and J. Li, Synth. Met. 181, 79 (2013).
Acknowledgments
This work was supported by the National Natural Science Foundation of China under Grant Nos. 11575131, 11775163, and 11875208, and the Natural Science Foundation of Hubei Province under Grant No. 2016CFA080.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of Interest
There are no conflicts of interest to declare.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Jiang, X.Y., Zhang, Q.K., Deng, S.P. et al. Enhanced Thermoelectric Performance of Polythiophene/Carbon Nanotube-Based Composites. J. Electron. Mater. 49, 2371–2380 (2020). https://doi.org/10.1007/s11664-019-07935-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-019-07935-8