Abstract
This paper investigates the interfacial reaction between Sn and Sn3Ag0.5Cu (SAC305) solder on n-type Bi2Te3 thermoelectric material. An electroless Ni-P layer successfully suppressed the formation of porous SnTe intermetallic compound at the interface. The formation of the layers between Bi2Te3 and Ni-P indicates that Te is the dominant diffusing species. Shear tests were conducted on both Sn and SAC305 solder on n- and p-type Bi2Te3 with and without a Ni-P barrier layer. Without a Ni-P layer, porous SnTe would result in a more brittle fracture. A comparison of joint strength for n- and p-type thermoelectric modules is evaluated by the shear test. Adding a diffusion barrier increases the mechanical strength by 19.4% in n-type and 74.0% in p-type thermoelectric modules.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
L.E. Bell, Science 321, 1457 (2008).
G.J. Snyder and E.S. Toberer, Nat. Mater. 7, 105 (2008).
M.G. Kanatzidis, S.D. Mahanti, and T.P. Hogan, Chemistry, Physics, and Materials Science of Thermoelectric Materials—Beyond Bismuth Telluride (New York: Kluwer/Plenum, 2003), p. 1.
S.W. Chen and C.N. Chiu, Scr. Mater. 56, 97 (2007).
C.N. Chiu, C.H. Wang, and S.W. Chen, J. Electron. Mater. 37, 40 (2008).
Y.C. Lan, D.Z. Wang, G. Chen, and Z.F. Ren, Appl. Phys. 92, 101910 (2008).
O.D. Iyore, T.H. Lee, R.P. Gupta, J.B. White, H.N. Alshareef, M.J. Kim, and B.E. Gnade, Surf. Interface Anal. 41, 440 (2009).
W.S. Liu, H.Z. Wang, L.J. Wang, X.W. Wang, G. Joshi, G. Chen, and Z.F. Ren, J. Mater. Chem. A 1, 13093 (2013).
P.Y. Chien, C.H. Yeh, H.H. Hsu, and A.T. Wu, J. Electron. Master. 43, 284 (2014).
S.W. Chen, T.R. Yang, C.Y. Wu, H.W. Hsiao, H.S. Chu, J.D. Huang, and T.W. Liou, J. Alloys Compd. 686, 847 (2016).
T.Y. Lin, C.N. Liao, and A.T. Wu, J. Electron. Mater. 41, 153 (2012).
W.H. Chao, Y.R. Chen, S.C. Tseng, P.H. Yang, R.J. Wu, and J.Y. Hwang, Thin Solid Films 570, 172 (2014).
R.P. Gupta, K. Xiong, J.B. White, K. Cho, H.N. Alshareef, and B.E. Gnade, J. Electrochem. Soc. 157, H666 (2010).
C.Y. Ko and A.T. Wu, J. Electron. Mater. 41, 3320 (2012).
J. Jiang, L. Chen, Q. Yao, S. Bai, and Q. Wang, Mater. Chem. Phys. 92, 39 (2005).
J.W.G. Bos, H.W. Zandbergen, M.-H. Lee, N.P. Ong, and R.J. Cava, Phys. Rev. B 75, 195203 (2007).
L.C. Lo and A.T. Wu, J. Electron. Mater. 41, 3325 (2012).
C.N. Liao, C.H. Lee, and W.J. Chen, Electrochem. Solid State Lett. 10, 23 (2007).
S.W. Chen, C.Y. Wu, H.J. Wu, and W.T. Chiu, J. Alloys Compd. 611, 313 (2014).
Y.C. Lin, K.J. Wang, and J.G. Duh, J. Electron. Mater. 39, 283 (2010).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lin, WC., Li, YS. & Wu, A.T. Study of Diffusion Barrier for Solder/n-Type Bi2Te3 and Bonding Strength for p- and n-Type Thermoelectric Modules. J. Electron. Mater. 47, 148–154 (2018). https://doi.org/10.1007/s11664-017-5906-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-017-5906-x