Abstract
Here, a systematic experimental study on indium tin oxide (ITO) films is presented to investigate the effects of oxygen partial pressure on the film's electrical properties. The results of Hall measurements show that adding more oxygen in the sputtering gas has negative influences on the electrical conductivity of ITO films. As O2/(O2 + Ar)% in the sputtering gas is increased from 0 to 6.98%, the resistivity of ITO film rises almost exponentially from 7.9 × 10−4 to 4.1 × 10−2 Ω cm, with the carrier density decreasing from 4.8 × 1020 to 5.4 × 1018 cm−3. The origins of these negative effects are discussed with focuses on the concentration of ionized impurities and the scattering of grain barriers. Extensive x-ray photoelectron spectroscopy (XPS) analyses were employed to gain insight into the concentration of ionized impurities, demonstrating a strong correlation between the oxygen vacancy concentration and the carrier density in ITO films as a function of sputtering O2 partial pressure. Other microstructural characterization techniques including x-ray diffraction (XRD), high-magnification scanning electron microscopy (SEM) and scanning transmission electron microscopy (STEM) analyses were used to evaluate the average grain size of ITO films. For ITO films that have carrier density above 1019 cm−3, scattering on grain boundaries and other crystallographic defects show negligible effects on the carrier transport. The results point to the oxygen vacancy concentration that dictates the carrier density and, thus, the resistivity of magnetron-sputtered ITO films.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
T. Minami, Thin Solid Films 516, 5822 (2008).
E. Fortunato, D. Ginley, H. Hosono, and D.C. Paine, MRS Bulletin 32, 242 (2007).
R.K. Pandey, S. Mishra, and P.K. Bajpai, J. Electron. Mater. 45, 5822 (2016).
M.A. Green, K. Emery, Y. Hishikawa, W. Warta, and E.D. Dunlop, Prog. Photovolt: Res. Appl. 24, 905 (2016).
A.E. Delahoy and S. Guo, Handbook of Photovoltaic Science and Engineering, ed. A. Luque and S. Hegedus (Chichester: Wiley, 2011), p. 716.
K. Jeyadheepan, M. Thamilselvan, K. Kim, J. Yi, and C. Sanjeeviraja, J. Alloys Compds. 620, 185 (2015).
Z. Ghorannevis, E. Akbarnejad, A. Salar Elahi, and M. Ghoranneviss, J. Inorg. Organomet. Polym. 25, 1486 (2015).
J.J. Wang, T. Ling, S.Z. Qiao, and X.W. Du ACS Appl. Mater. Interfaces 6, 14718 (2014).
J.L. Pena, E. Hernandez-Rodriguez, V. Rejon, R. Mis-Fernandez, and I. Riech, PVSC IEEE 42nd (2015). doi:10.1109/PVSC.2015.7355894.
D.M. Meysing, C.A. Wolden, M.M. Griffith, H. Mahabaduge, J. Pankow, M.O. Reese, J.M. Burst, W.L. Rance, and T.M. Barnes, J. Vac. Sci. Technol. A 33, 021203 (2015).
D.A. Duncan, J.M. Kephart, K. Horsley, M. Blum, M. Mezher, L. Weinhardt, M. Haming, R.G. Wilks, T. Hofmann, W. Yang, M. Bar, W.S. Sampath, and C. Heske, ACS Appl. Mater. Interfaces 7, 16382 (2015).
J.M. Kephart, R.M. Geisthardt, and W.S. Sampath, Prog. Photovolt: Res. Appl. 23, 1484 (2015).
K. Ellmer, Nat. Photonics 6, 809 (2012).
Q. Gao, M. Li, X. Li, Y. Liu, C.L. Song, J.X. Wang, Q.Y. Liu, J.B. Liu, and G.R. Han, J. Alloys Compds. 550, 144 (2013).
Y. Zhu, R.J. Mendelsberg, J. Zhu, J. Han, and A. Anders, J. Mater. Sci. 48, 3789 (2013).
D. Panda and T.Y. Tseng, J. Mater. Sci. 48, 6849 (2013).
H. Mahdhi, Z. Ben Ayadi, J.L. Gauffier, and K. Djessas, J. Electron. Mater. 45, 557 (2016).
Y. Lu, S. Khan, C.L. Song, K.K. Wang, G.Z. Yuan, W. Li, G.R. Han, and Y. Liu, J. Alloys Compds. 663, 413 (2016).
T. Minami, Semicond. Sci. Technol. 20, S35 (2005).
T.H. Tsai and Y.F. Wu, Microelectron. Eng. 83, 536 (2006).
V. Linss, Surf. Coat. Tech. 290, 43 (2016).
S.M. Joshi and R.A. Gerhardt, J. Mater. Sci. 48, 1465 (2013).
M. Wegener, M. Kato, K. Kakimoto, S. Spallek, E. Spiecker, and A. Roosen, J. Mater. Sci. 50, 6124 (2015).
Y. Hu, X. Diao, C. Wang, W. Hao, and T. Wang, Vacuum 75, 183 (2004).
E. Terzini, P. Thilakan, and C. Minarini, Mater. Sci. Eng. B 77, 110 (2000).
F. Kurdesau, G. Khripunov, A.F. da Cunha, M. Kaelin, and A.N. Tiwari, J. Non-Cryst. Solids 352, 1466 (2006).
K.S. Tseng and Y.L. Lo, Appl. Surf. Sci. 285P, 157 (2013).
C.G. Choi, K. No, W.J. Lee, H.G. Kim, S.O. Jung, W.J. Lee, W.S. Kim, S.J. Kim, and C. Yoon, Thin Solid Films 258, 274 (1995).
Y.J. Kim, S.B. Jin, S.I. Kim, Y.S. Choi, I.S. Choi, and J.G. Han, Thin Solid Films 518, 6241 (2010).
A. Chen, K. Zhu, H. Zhong, Q. Shao, and G. Ge, Sol. Energy Mater. Sol. Cells 120, 157 (2014).
H. Kim, C.M. Gilmore, A. Piqué, J.S. Horwitz, H. Mattoussi, H. Murata, Z.H. Kafafi, and D.B. Chrisey, J. Appl. Phys. 86, 6451 (1999).
C. Ophus, E. Luber, and D. Mitlin, Acta Mater. 57, 1327 (2009).
C. Ophus, T. Ewalds, E.J. Luber, and D. Mitlin, Acta Mater. 58, 5150 (2010).
K. Okada, S. Kohiki, S. Luo, D. Sekiba, S. Ishii, M. Mitome, A. Kohno, T. Tajiri, and F. Shoji, Thin Solid Films 519, 3557 (2011).
J. Gwamuri, M. Marikkannan, J. Mayandi, P.K. Bowen, and J.M. Pearce, Materials 9, 63 (2016).
Y.Y. Chen, J.C. Hsu, C.Y. Lee, and P.W. Wang, J. Mater. Sci. 48, 1225 (2013).
C. Li, J. Li, S.S. Li, J.B. Xia, and S.H. Wei, Appl. Phys. Lett. 100, 262109 (2012).
S.V. Pammi, A. Chanda, J.K. Ahn, J.H. Park, C.R. Cho, W.J. Lee, and S.G. Yoon, J. Electrochem. Soc. 157, H937 (2010).
F.M. Simanjuntak, D. Panda, T.L. Tsai, C.A. Lin, K.H. Wei, and T.Y. Tseng, J. Mater. Sci. 50, 6961 (2015).
M. Chen, X. Wang, Y.H. Yu, Z.L. Pei, X.D. Bai, C. Sun, R.F. Huang, and L.S. Wen, Appl. Surf. Sci. 158, 134 (2000).
J.S. Kim, P.K.H. Ho, D.S. Thomas, R.H. Friend, F. Cacialli, G.W. Bao, and S.F.Y. Li, Chem. Phys. Lett. 315, 307 (1999).
T. Stapinski, E. Leja, and T. Pisarkiewicz, J. Phys. D: Appl. Phys. 17, 407 (1984).
K. Ellmer and R. Mientus, Thin Solid Films 516, 4620 (2008).
W. Wohlmuth and I. Adesida, Thin Solid Films 479, 223 (2005).
Acknowledgements
The authors acknowledge the China Triumph International Engineering Co. Ltd. (CTIEC), Shanghai, China, which offers generous financial support for this work. The authors thank the Evans Analytical Group's Materials Characterization Division for the FIB-STEM analysis.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no competing financial interest.
Rights and permissions
About this article
Cite this article
Peng, S., Cao, X., Pan, J. et al. X-ray Photoelectron Spectroscopy Study of Indium Tin Oxide Films Deposited at Various Oxygen Partial Pressures. J. Electron. Mater. 46, 1405–1412 (2017). https://doi.org/10.1007/s11664-016-5136-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-016-5136-7