Abstract
The damage process and corrosion ion distribution in concrete, which was exposed to 60 and 170 drying-immersion cycles of sulfate solution, were systematically investigated. The effects of plain concrete, plain concrete mixed with 4 and 8 kg/m3 modified PP fiber and high-performance concrete (HPC) mixed with 0.8 kg/m3 fine PP fiber on the damage process were also studied. The experimental results showed that thenardite-induced surface scaling, as well as gypsum- and ettringite-induced cracks, were the main degradation forms of concrete under attack of sulfate solution and drying–immersion cycles. The relative dynamic modulus of elasticity of concrete initially increased, then reached stability and finally decreased to failure. The sulfate diffusion coefficients of plain and HPC were 10-12 and 10-13 m2/s, respectively. The concentration of sodium ion increased with depth, then maintained stability and finally decreased rapidly with concrete depth. The content of calcium ion on the concrete surface was 110%-150% of that in the interior of specimens. Although fiber worsened the surface scaling of concrete, better resistance capacity of sulfate ion penetration into concrete was observed in plain concrete with 4 kg/m3 modified PP fiber and HPC.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Rasheeduzzafar. Influence of Cement Composition on Concrete Durability[J]. J. ACI Material, 1992, 89(6): 574–586
Monteiro PJM, Kurtis KE. Time to Failure for Concrete Exposed to Severe Sulfate Attack [J]. Cement and Concrete Research, 2003, 33(7): 987–993
Zuo XB, Sun W, Li H, et al. Modeling of Diffusion-reaction Behavior of Sulfate Ion in Concrete under Sulfate Environments [J]. Computers and Concrete, 2012, 10(1): 79–93
Qiao HX, He ZM, Zhu YP, et al. Durability Study of High Performance Concrete in Salt Region[J]. China Railway science, 2007, 27(4): 32–37
Ma BG, Gao XG, Byars EA, et al. Thaumasite Formation in a Tunnel of Bapanxia Dam in Western China[J]. Cement and Concrete Research, 2006, 36(4): 716–722
Nehdi ML, Hayek M. Behavior of Blended Cement Mortars Exposed to Sulfate Solutions Cycling in Relative Humidity[J]. Cement and Concrete Research, 2005, 35(4): 731–742
Zhang MH, Jiang MQ, Chen JK. Variation of Flexural Strength of Cement Mortar Attacked by Sulfate Ions[J]. Engineering Fracture Mechanics, 2005, 75(17): 4948–4957
Jin ZQ, Sun W, Jiang JY, et al. Damage of Concrete Attacked by Sulfate and Sustained Loading[J]. Journal of Southeast University (English edition), 2008, 24(1): 69–73
Bassuoni MT, Nehdi ML. Durability of Self-consolidating Concrete to Sulfate Attack under Combined Cyclic Environments and Flexural Loading[J]. Cement and Concrete Research, 2009, 39(3): 206–226
Rozière E, Loukili A, Hachem RE, et al. Durability of Concrete Exposed to Leaching and External Sulphate Attacks[J]. Cement and Concrete Research, 2009, 39(12): 1188–1198
Xie YJ, Zhong XH, Zhu CH, et al. Durability of HPC for Bridge and Tunnel Structure on Qinghai-Tibet Railway[J]. China Railway Science, 2003, 24(1): 108–112
Irassar EF, Maio AD, Batie OR. Sulfate Attack on Concrete with Mineral Admixtures[J]. Cement and Concrete Research, 1996, 26(1): 113–123
Vahid A, Togay O. Mechanical and Durability Properties of Highstrength Concrete Containing Steel and Polypropylene Fibers[J]. Construction and Building Materials, 2015, 94(30): 73–82
Saeid K, Hazizan MA, Morteza J, et al. The Effects of Polypropylene Fibers on the Properties of Reinforced Concrete Structures[J]. Construction and Building Materials, 2012, 27(1): 73–77
Atkinson A, Hearne JA. Mechanistic Model for the Durability of Concrete Barriers Exposed to Sulfate-bearing Groundwater[C]. In: Materials Research Society Symposium Proceedings, 1990(176): 149–156
Long GC, Xie YJ, Tang XG. Evaluating Deterioration of Concrete by Sulfate Attack[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2007, 22(3): 572–576
Jin ZQ, Sun W, Zhang YS, et al. Interaction Between Sulfate and Chloride Solution Attack of Concrete With and Without Fly Ash[J]. Cement and Concrete Research, 2007, 37(8): 1223–1232
Yuan XL, Li BX, Cui G, et al. Effect of Fly Ash and Early Strength Agent on Durability of Concrete Exposed to the Cyclic Sulfate Environment[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2010, 25(6): 1065–1069
Zhang JS, Zhang YH, Feng LP. Corrosion Resistance Coefficient for Concrete Compressive Strength under Sulfate Environment[J]. Journal of Building Materials, 2014, 17(3): 369–377
Carlos RN, Eric D, Eduardo S. How Does Sodium Sulfate Crystallize Implications for the Decay and Testing of Building Materials[J]. Cement and Concrete Research, 2000, 30(10): 1527–1534
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the National Natural Science Foundation of China (Nos. 51378269 and 5142010501), the Chinese National Basic Research Program of China(No. 2015CB655100) and the 111 Program
Rights and permissions
About this article
Cite this article
Geng, Y., Jin, Z., Hou, B. et al. Long-term behavior of fiber reinforced concrete exposed to sulfate solution cycling in drying-immersion. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 32, 875–881 (2017). https://doi.org/10.1007/s11595-017-1683-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-017-1683-x