Abstract
Hot stamping (press hardening) is widely used to fabricate safety components such as door beams and B pillars with increased strength via quenching. However, parts that are hot-stamped from ultra-high-strength steel (UHSS) have very limited elongation, i.e., low ductility. In the present study, a novel variant of hot stamping technology called quenching-and-partitioning (Q&P) hot stamping was developed. This approach was tested on several UHSS sheet metals, and it was confirmed that this method can be used to overcome the drawbacks associated with conventional hot stamping. The applicability of Q&P hot stamping to each of these steels was also assessed. The part properties and performances of three widely used ultra-high-strength sheet metals, B1500HS, 27SiMn, and TRIP780, were evaluated through tensile testing and microstructural observations. The results demonstrated that the ductility of Q&P hot-stamped sheet metals was notably higher than that of the conventionally hot-stamped parts because Q&P hot stamping gives rise to a dual-phase structure of both martensite and austenite. Further, material tests demonstrated that the Q&P treatment had positive effects on all three selected materials, of which TRIP780 had the best ductility and the highest value of the product of strength and plasticity. Scanning electron microscopy images indicated that the silicon in the steels could limit the formation of cementite and would, therefore, improve the mechanical properties of Q&P hot-stamped products.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Karbasian H, Tekkaya A E. A review on hot stamping. J Mater Processing Tech, 2010, 210: 2103–2118
Hu P, Ma N, Liu L, et al. Theories, Methods and Numerical Technology of Sheet Metal Cold and Hot Forming. London: Springer-Verlag, 2013. 35–46
Geiger M, Merklein M, Hoff C. Basic investigations on the hot stamping steel 22MnB5. AMR, 2005, 6-8: 795–804
Han X, Zhong Y, Yang K, et al. Application of hot stamping process by integrating quenching & partitioning heat treatment to improve mechanical properties. Procedia Eng, 2014, 81: 1737–1743
Rossini M, Spena P R, Cortese L, et al. Investigation on dissimilar laser welding of advanced high strength steel sheets for the automotive industry. Mater Sci Eng-A, 2015, 628: 288–296
Vandeputte S, Vanderschhuern D, Classens S, et al. Modern steel grades covering all needs of the automotive industry. In: Proceedings of Ninth International Conference on Steel Sheet Metal. Leuven, 2001. 405–414
Ying S, Dong H. The third generation auto sheet steel: Theory and practice. In: Proceedings of the FISITA 2012 World Automotive Congress. Berlin, 2013. 933–947
Naderi M, Abbasi M, Saeed-Akbari A. Enhanced mechanical properties of a hot-stamped advanced high-strength steel via tempering treatment. Metall Mat Trans A, 2013, 44: 1852–1861
Ying L, Chang Y, Hu P, et al. Influence of low tempering temperature on fracture toughness of ultra high strength boron steel for hot forming. Adv Mater Res, 2010, 146-147: 160–165
Naderi M, Ketabchi M, Abbasi M, et al. Semi-hot stamping as an improved process of hot stamping. J Mater Sci Tech, 2011, 27: 369–376
Naderi M, Ketabchi M, Abbasi M, et al. Analysis of microstructure and mechanical properties of different high strength carbon steels after hot stamping. J Mater Process Tech, 2011, 211: 1117–1125
Santofimia M J, Nguyen-Minh T, Zhao L, et al. New low carbon Q&P steels containing film-like intercritical ferrite. Mater Sci Eng-A, 2010, 527: 6429–6439
Hao L, Xiao N, Zheng C, et al. Mechanical properties and temper resistance of deformation induced ferrite in a low carbon steel. J Mater Sci Tech, 2010, 26: 1107–1113
Speer J, Matlock D K, De Cooman B C, et al. Carbon partitioning into austenite after martensite transformation. Acta Mater, 2003, 51: 2611–2622
Speer J G, De Moor E, Clarke A J. Critical assessment 7: Quenching and partitioning. Mater Sci Tech, 2015, 31: 3–9
Hsu T Y, Jin X J, Rong Y H. Strengthening and toughening mechanisms of quenching-partitioning-tempering (Q-P-T) steels. J Alloys Compd, 2013, 577: S568–S571
Chen M M, Wu R M, Liu H P, et al. An ultrahigh strength steel produced through deformation-induced ferrite transformation and Q&P process. Sci China Technol Sci, 2012, 55: 1827–1832
Liu H, Jin X, Dong H, et al. Martensitic microstructural transformations from the hot stamping, quenching and partitioning process. Mater Charact, 2011, 62: 223–227
Liu H, Lu X, Jin X, et al. Enhanced mechanical properties of a hot stamped advanced high-strength steel treated by quenching and partitioning process. Scripta Mater, 2011, 64: 749–752
Han X, Zhong Y, Xin P, et al. Research on one-step quenching and partitioning treatment and its application in hot stamping process. Proc Institution Mech Engineers Part B-J Eng Manufacture, 2015, 84: 163–182
Han X, Xin P, Hao X, et al. A new try of hot stamping process with higher strength-ductility balance. In: Proceedings of International Deep Drawing Research Group IDDRG. Zurich, 2013. 659–669
Lin T, Song H W, Zhang S H, et al. Microstructure, mechanical properties, and toughening mechanisms of a new hot stamping-bake toughening steel. Metall Mat Trans A, 2015, 46: 4038–4046
Santofimia M J, Zhao L, Petrov R, et al. Characterization of the microstructure obtained by the quenching and partitioning process in a low-carbon steel. Mater Charact, 2008, 59: 1758–1764
Paravicini Bagliani E, Santofimia M J, Zhao L, et al. Microstructure, tensile and toughness properties after quenching and partitioning treatments of a medium-carbon steel. Mater Sci Eng-A, 2013, 559: 486–495
Li H Y, Lu X W, Wu X C, et al. Bainitic transformation during the two-step quenching and partitioning process in a medium carbon steel containing silicon. Mater Sci Eng-A, 2010, 527: 6255–6259
Zhao H S, Li W, Zhu X, et al. Analysis of the relationship between retained austenite locations and the deformation behavior of quenching and partitioning treated steels. Mater Sci Eng-A, 2016, 649: 18–26
Zhong N. Research on High Strength Q&P and Q-P-T Steels. Dissertation for Doctoral Degree. Shanghai: Shanghai Jiao Tong University, 2009. 139
Han X, Cui Z, Xin P, et al. A U-shape tool desigh for one-step Q&P hot stamping process. China Patent, ZL 201310335789.1, 2015-05-20
Saleh M H, Priestner R. Retained austenite in dual-phase silicon steels and its effect on mechanical properties. J Mater Process Tech, 2001, 113: 587–593
Jacques P, Girault E, Catlin T, et al. Bainite transformation of low carbon Mn-Si TRIP-assisted multiphase steels: influence of silicon content on cementite precipitation and austenite retention. Mater Sci Eng-A, 1999, 273-275: 475–479
Mahieu J, Van Dooren D, Barbé L, et al. Influence of Al, Si and P on the kinetics of intercritical annealing of TRIP-aided steels: Thermodynamical prediction and experimental verification. Steel Res, 2002, 73: 267–273
Haga J, Mizui N, Nagamichi T, et al. Effect of boron on mechanical properties and recrystallization behavior of Ti-added ultra-low carbon cold-rolled steel sheets. Isij Int, 1998, 38: 580–586
Mohrbacher H. Martensitic automotive steel sheet-fundamentals and metallurgical optimization strategies. Adv Mater Res, 2014, 1063: 130–142
He L. Research on Key Parameter Measuring and Quenching Properties of Boron Steel B1500HS in Hot Stamping Process. Dissertation for Doctoral Degree. Jinan: Shandong University, 2012
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Han, X., Zhong, Y., Tan, S. et al. Microstructure and performance evaluations on Q&P hot stamping parts of several UHSS sheet metals. Sci. China Technol. Sci. 60, 1692–1701 (2017). https://doi.org/10.1007/s11431-016-9111-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11431-016-9111-y