Abstract
Hypoeutectic Al–xSi–0.45Mg (x = 6.5, 7.5, 8.5, 9.5) alloys were refined by Al5Ti1B containing TiB2 and Al3Ti3B containing TiB2 and AlB2, respectively. With increasing Si, Si poisoning on TiB2 results in the obvious coarsening of primary α-Al in Al5Ti1B-refined alloys from 350 ± 40 to 400 ± 50, 475 ± 50 and 560 ± 80 μm, and the competition between Si promotion on AlB2 and Si poisoning on TiB2 leads to the slight coarsening of primary α-Al in Al3Ti3B-refined alloys from 215 ± 30 to 265 ± 35, 265 ± 30 and 315 ± 25 μm. After T6 heat treatment, with increasing Si, the yield strength (YS) of Al5Ti1B-refined alloys increases from 294 ± 2 to 299 ± 2, 304 ± 1 and 309 ± 2 MPa, and the elongation first increases from 3.5 ± 0.8 to 4.5 ± 1.0 and 7.8 ± 1.4%, after decreases to 5.5 ± 1.2%, while the YS of the Al3Ti3B-refined alloys increases from 300 ± 1 to 305 ± 2, 312 ± 1 and 317 ± 2 MPa, and the elongation increases from 6.1 ± 1.1 to 8.5 ± 1.2, 11.8 ± 1.5 and 12.1 ± 1.6%. The increase in the secondary phase and precipitation strengthening results in the increase in strength with increasing Si. With increasing Si, the decrease in porosity formation by decreasing solidification interval and increasing fluidity is superior to the increase in porosity formation by slightly coarsening grain size, which leads to the increase in ductility in the Al3Ti3B-refined alloys, while the competition between porosity decreasing and increasing factors leads to the inverted ‘V’-shaped evolution of ductility in the Al5Ti1B-refined alloys.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Al–Si–Mg cast alloys have been widely used for making high-integrity castings with a combination of good castability, low density, high-strength-to-weight ratio, good corrosion resistance and low coefficient of thermal expansion, which are necessary for transport manufacturing to provide light-weighting components. Grain refinement has been proved as an important way to obtain fine primary α-Al grains, which can improve the toughness, strength, formability and machinability [1,2,3,4,5,6,7,8,9,10,11].
The most widely used grain refiner in aluminium alloys over the past several decades is the Al5Ti1B master alloy with TiB2 particles and excess Ti, which inoculates the melt with TiB2/TiAl3 particles as heterogeneous nuclei, and the sufficient free Ti solute in the melt can restrict the growth of primary α-Al grains after nucleation. The exact mechanism of grain refinement under Al5Ti1B has been well demonstrated recently; the formation of a monolayer of (112) Al3Ti two-dimensional compound on the (0001) TiB2 surface can reduce the misfit between TiB2 and α-Al from − 4.2 to 0.09%, which can efficiently enhance the nucleation potency of TiB2 particles for primary α-Al grains [12]. The Al5Ti1B master alloy offers good performance in the casting of wrought alloys, but it is hard to meet the expectations in cast Al–Si alloys, especially with a content of Si higher than 3.5 wt% [13,14,15]. The reason is that Si in the melt reacts with Ti to form Ti–Si phases, which poison the TiB2 nucleation site [16, 17]. The poisoning mechanism of Si on the TiB2 nucleation sites has been verified by experiment recently, and Al–Si–Ti particles were observed on the prism face of TiB2 particles [18].
To reduce or avoid Si poisoning, one effective way is to introduce B into the Al–Si alloys, and it is often achieved by adding Al–B master alloy, in which AlB2 resides as the source to supply B, into the melt. The use of Al–B master alloys for the grain refinement of Al–Si cast alloys dated back to 1980s, and the grain size was continually reduced even with increasing Si content [15]. AlB2 is the dominated particle in Al–B master alloys and has a small misfit between α-Al, and it was expected that AlB2 could be a potent nucleating substrate for α-Al [19]. However, a number of observations [20, 21] showed that AlB2 alone without Si cannot effectively refine α-Al, indicating that the solute Si may interfere with AlB2 to enhance its nucleating potential. There is still lack of unambiguous understanding of the mechanism. Recently, it has been proposed that the creation of a layer of SiB6 at the interface between AlB2 and Al may reduce the crystallographic mismatch, which can significantly improve the nucleating potency of AlB2, and the enhanced grain refining efficiency can be mainly attributed to the enhanced heterogeneous nucleation of AlB2 caused by Si [22]. However, an amount of ~ 0.12 wt% Ti is usually present in commercial cast aluminium alloys for grain growth restriction. It was found that the commercial Al–Si–Mg cast alloys could not enjoy the outstanding grain refinement efficiency of Al–B master alloys, with the presence of Ti, since the AlB2 particles are readily transformed to TiB2 particles and then suffering from the Si poisoning, and the grain refinement efficiency of Al–B master alloys is much similar to Al5Ti1B master alloy for commercial Al–Si–Mg cast alloys with Ti present [23].
For the grain refinement of commercial Al–Si–Mg cast alloys containing Ti, one effective way is to reduce the Ti content and increase the B content in the Al–Ti–B master alloys, and Al3Ti3B master alloy with TiB2 particles and excess B was found providing effective grain refinement [10, 11, 23, 24]. Al3Ti3B master alloy was reported containing TiB2 and AlB2 particles [10, 11, 23], and both of these particles could be potentially heterogeneous nucleation sites. The exact mechanism of grain refinement under Al3Ti3B is still quite unclear. On the one hand, Si poisons the heterogeneous nucleation of TiB2 particles; on the other hand, Si promotes the heterogeneous nucleation of AlB2 particles, so it is interesting to study the effect of Si poisoning and promotion on the grain refinement of Al–Si–Mg cast alloys under Al3Ti3B. Furthermore, seldom did research focus on Si poisoning and promotion on the mechanical properties of Al–Si–Mg cast alloys.
The objective of this paper is to study the multiple effects of Si on the microstructure and mechanical properties of hypoeutectic Al–Si–Mg cast alloys under different grain refiners, especially Si poisoning under Al5Ti1B and Si promotion under Al3Ti3B, to provide high-performance cast Al–Si–Mg alloys with high strength and high ductility and meet the increasing requirements in automotive industry.
Experimental
Materials and melt preparation
A serial of hypoeutectic Al–Si–Mg cast alloys with 0.45 wt% Mg and different Si contents (6.5, 7.5, 8.5 and 9.5 wt%) were prepared and melted in 12-kg capacity clay–graphite crucibles separately using the electric resistance furnace, and the detail compositions of the investigated alloys were measured by inductively coupled plasma atomic emission spectroscopy (ICP-AES) and are listed in Table 1. During melting, the temperature of the furnace was controlled at 750 °C. After 1 h of homogenisation, Al–10 wt% Sr master alloy was added into the melt to make the desired Sr content of 140 ppm for modification. The melt was subsequently degassed through injecting pure argon into the melt by using a rotary degassing impeller at a speed of 350 rpm for 4 min. After degassing, the melt was hold for 10 min for temperature recovery, followed by adding 0.2 wt% Al5Ti1B or 0.2 wt% Al3Ti3B for grain refinement.
Casting process and heat treatment
With the intention of casting tensile test bars, the prepared melt was poured at 720 °C into an ASTM B-108 permanent mould preheated at 460 °C, as shown in Fig. 1a. Figure 1b shows the gravity casting made by the permanent mould, and two round tensile test bars were made from each casting, as indicated by the dashed rectangle box in Fig. 1a. With the intention of testing the fluidity of the investigated alloys, the prepared melt was poured at 720 °C into an ASTM standard spiral flow fluidity test mould preheated at 460 °C. Three fluidity tests and three density tests were made for each alloy to give the average spiral flow length and average porosity percentage with error bar, respectively. The cast tensile test bars were subjected to T6 heat treatment, including solution treatment and artificial ageing. Solution treatment was carried out at 540 °C for 8 h, followed by immediate water quenching to room temperature. Ageing treatment was performed at 170 °C for 8 h, followed by air cooling to room temperature.
Microstructure characterisation and tensile tests
The microstructure was examined using the Zeiss optical microscopy (OM), the Zeiss scanning electron microscope (SEM), the JEOL-2100 transmission electron microscopy (TEM) and the D8 X-ray diffraction (XRD) instrument. The specimens for OM and SEM analysis were prepared by the standard technique of grinding. Polarised OM observation of grain size was performed after anodised with Barker solution (97 vol% H2O and 3 vol% HBF4). SEM analysis was conducted after etching with the Keller solution (1 vol% HF, 1.5 vol% HCl, 2.5 vol% HNO3 and 95 vol% H2O). Five polarised OM images with a magnification of 25 were counted to give each of the statistical average grain sizes with error bar. Thin specimens for TEM observation were prepared by standard electropolishing. The electrolytic solution was a mixture of nitric acid and methyl alcohol (2:8), used at − 20 to – 30 °C and 20 V. TEM operating at 200 kV was used for bright-field imaging and high-resolution TEM (HRTEM) imaging. XRD analysis was conducted from 2θ degrees 25°–90°. Tensile tests were conducted at room temperature following the ASTM B557 standard using an Instron 5500 Testing System. Each tensile test data reported with error bar were based on the mechanical properties obtained from 6 to 8 samples.
Results
As-cast microstructure
Figure 2a–d presents the polarised optical micrographs showing the grain size of primary α-Al in the as-cast Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, respectively, under the refinement of Al5Ti1B. When the Si content is increased to 7.5 wt%, with the increase in Si, the grain size of primary α-Al phase is coarsened significantly, which indicates that the poisoning of Si on grain refinement is significant when the Si content is up to 7.5 wt%, under the refinement of Al5Ti1B.
Figure 3a–d presents the polarised optical micrographs showing the grain size of primary α-Al phase in the as-cast Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, separately, under the refinement of Al3Ti3B. The grain size of primary α-Al phase in the Al–xSi–0.45Mg alloys refined by Al3Ti3B is obviously smaller than that of the alloys refined by Al5Ti1B. With the increase in Si, the coarsening of the primary α-Al in the Al–xSi–0.45Mg alloys refined by Al3Ti3B is not obvious, which indicates that the poisoning of Si on the grain refinement of Al–xSi–0.45Mg alloys is weak with the Si content up to 9.5 wt%, under the refinement of Al3Ti3B.
Figure 4 shows the statistical average grain size of the primary α-Al phase in the as-cast Al–xSi–0.45Mg (x = 6.5, 7.5, 8.5, 9.5) alloys refined by Al5Ti1B and Al3Ti3B. Under the refinement of Al5Ti1B, the grain size of the primary α-Al phase is 350 ± 40 μm with a Si content of 6.5 wt%; with the increase in Si content to 7.5, 8.5 and 9.5 wt%, the primary α-Al phase is coarsened obviously to 400 ± 50, 475 ± 50 and 560 ± 80 μm. The grain size of the primary α-Al phase increases with the increase in Si content when refined by Al5Ti1B; the grain size of the primary α-Al phase is coarsened obviously when the Si content is up to 7.5 wt% and coarsened nearly linear after. Under the refinement of Al3Ti3B, the grain size of the primary α-Al phase is fine as 215 ± 30 μm at 6.5 wt% Si, and the grain size is increased to 265 ± 35 μm at 7.5 wt% Si, then the grain size is maintained at 265 ± 30 μm at 8.5 wt% Si, after the grain size is increased to 315 ± 25 μm at 9.5 wt% Si. The grain size of the primary α-Al phase in the Al3Ti3B-refined alloy is significantly smaller than that of the Al5Ti1B-refined alloy. With the increase in Si, the coarsening of the primary α-Al phase in the Al3Ti3B-refined alloy is obviously slighter than that of the Al5Ti1B-refined alloy.
Figure 5a–d shows the SEM morphology of the as-cast hypoeutectic Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, respectively, under the refinement of Al5Ti1B master alloy. Figure 5e–h shows the SEM morphology of the as-cast Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, separately, under the refinement of Al3Ti3B master alloy. The insert in each figure shows the SEM morphology with high magnification. Primary α-Al phase, eutectic Si phase and β-Mg2Si intermetallic phase coexist in the as-cast alloys refined by both Al5Ti1B and Al3Ti3B. β-Mg2Si phase is located in the Al–Si eutectic region. With the increase in Si, the fraction of eutectic Si phase in the as-cast Al–xSi–0.45Mg alloys increases, for the condition both refined by Al5Ti1B and Al3Ti3B.
Microstructure after heat treatment
Solution treatment can spheroidise the eutectic Si phase and dissolve intermetallic phases to form saturated solid solution [25]. Figure 6a–d shows the SEM morphology of the T6 heat-treated Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, respectively, under the refinement of Al5Ti1B. Figure 6e–h shows the SEM morphology of the T6 heat-treated Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, separately, under the refinement of Al3Ti3B. The insert in each figure shows the SEM morphology with high magnification. Eutectic Si phase is spheroidal morphology, which indicates that the eutectic Si phase is spheroidised after T6 heat treatment. The spheroidised Si particles are fine, which are beneficial to ductility [26]. The morphology of the spheroidised Si particles in the Al5Ti1B- and Al3Ti3B-refined alloys is much similar. No β-Mg2Si intermetallic phase was observed, which indicated that the β-Mg2Si phase was well dissolved into the α-Al matrix after the solution treatment. The well solid solution of β-Mg2Si phase could ensure the precipitation of nanoscale strengthening precipitates in the α-Al matrix after ageing treatment, which contributes to the strengthening of the alloys after T6 heat treatment. With the increase in Si, the volume fraction of spheroidised Si phase increases, for the condition refined by both Al5Ti1B and Al3Ti3B.
Figure 7a–d presents the bright-field TEM micrographs showing the β″ strengthening precipitate in the Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, respectively, after T6 heat treatment. Embedded and lying β″ precipitates were found in the α-Al matrix, which are the same precipitate since the β″ precipitate is needle-like. In Fig. 7, the number density of the β″ precipitate increases slightly with the increase in Si content. Figure 8a shows the HRTEM image of the β″ precipitate embedded in the (001)Al plane, and it clearly presents the unit cell of C-centred monoclinic structure with a = 1.52 nm and c = 0.67 nm, which verifies that the embedded precipitate is β″ [27, 28]. Figure 8b shows the corresponding FFT patterns of the rectangle area in Fig. 8a, and it also confirms that the embedded precipitate is β″. Figure 8c shows the HRTEM image of the β″ precipitate lying on the (001)Al plane, and Fig. 8d shows the corresponding FFT patterns of the rectangle area in Fig. 8c, which verifies that the lying precipitate is β″, and the β″ precipitate is coherent with the α-Al matrix along the b-axis. The needle-like β″ precipitate provides peak strengthening effect [29, 30], which indicates that the T6 heat-treated Al–xSi–0.45Mg alloys are in the peak strengthening state.
Mechanical properties after heat treatment
Figure 9a, b shows the tensile stress–strain curves and tensile properties of the Al5Ti1B-refined Al–xSi–0.45Mg alloys, after T6 heat treatment. Under the refinement of Al5Ti1B, with the increase in Si content from 6.5 to 7.5, 8.5 and 9.5 wt%, the yield strength (YS) increases nearly linear from 294 ± 2 to 299 ± 2, 304 ± 1 and 309 ± 2 MPa, and the tensile strength (UTS) increases from 336 ± 7 to 351 ± 4, 358 ± 3 and 363 ± 4 MPa, while the elongation (El) first increases slightly from 3.5 ± 0.8 to 4.5 ± 1.0%, then increases significantly to 7.8 ± 1.4%, after decreases to 5.5 ± 1.2%. Figure 9c, d shows the tensile stress–strain curves and tensile properties of the Al3Ti3B-refined Al–xSi–0.45Mg alloys, after T6 heat treatment. Under the refinement of Al3Ti3B, with the increase in Si content from 6.5 to 7.5, 8.5 and 9.5 wt%, the YS also increases nearly linear from 300 ± 1 to 305 ± 2, 312 ± 1 and 317 ± 2 MPa, and the UTS increases from 352 ± 3 to 360 ± 3, 367 ± 3 and 372 ± 3 MPa, while the elongation increases from 6.1 ± 1.1 to 8.5 ± 1.2, 11.8 ± 1.5 and 12.1 ± 1.6%. The Al3Ti3B-refined alloys have both higher strength and ductility than the Al5Ti1B-refined alloys. The YS and UTS of the alloys increase with increasing Si content. The ductility shows inverted ‘V’-shaped evolution with Si content and reaches the peak at 8.5 wt% Si when refined by Al5Ti1B, while the ductility increases with Si content when refined by Al3Ti3B.
Discussion
Si poisoning on microstructure under Al5Ti1B
Figure 10a shows the XRD pattern of the Al5Ti1B master alloy used for refinement; TiAl3 and TiB2 particles were found coexisting in the master alloy, which is consistent with the report that the particles introduced into the melt through the addition of Al5Ti1B are the soluble TiAl3 and the insoluble TiB2 particles [12]. Si in the melt reacted with Ti to form Ti–Si compounds, and the TiB2 particles that act as heterogeneous nucleation sites for primary α-Al phase could be poisoned by Si by coating the surfaces with Ti–Si compounds [16, 17]. The detail poisoning mechanism of Si on TiB2 particles has been verified by experiment recently with Al–Si–Ti particles observed on the prism face of TiB2 [18]. The formation of Ti–Si compounds also consumes the Ti dissolved in the melt for grain growth restriction, and the solute Ti was reported hardly offering any grain growth restriction effect in Al–Si alloys with a Si content up to 7 wt% [15]. With the increase in Si content from 6.5 to 9.5 wt%, the poisoning effect of Si on the TiB2 particles increases, and the heterogeneous nucleation of primary α-Al phase on TiB2 particles becomes more difficult, which results in the continuous significant coarsening of the primary α-Al phase in the Al–xSi–0.45Mg alloys refined by Al5Ti1B. The increase in grain size coarsening rate in Al5Ti1B-refined Al–xSi–0.45Mg alloys from 7.5 wt% Si might be attributed to the loss of grain growth restriction.
Si poisoning and promotion on microstructure under Al3Ti3B
Figure 10b shows the XRD pattern of the Al3Ti3B master alloy used for refinement; TiB2 and AlB2 particles were found coexisting in the Al3Ti3B master alloy. It was reported that AlB2 alone without Si cannot effectively refine α-Al, while AlB2 with the presence of Si could refine α-Al efficiently, indicating that the solute Si may interfere with AlB2 to enhance its heterogeneous nucleating potential [20, 21]. It was speculated that the formation of unstable SiB6 layer reduced the crystallographic mismatch between AlB2 and Al, which enhanced the heterogeneous nucleating potency of AlB2 for primary α-Al phase [22]. The formation of SiB6 layer is still not verified by experiments, but the promotion of heterogeneous nucleation potency of AlB2 by Si is the fact. There are two opposite effects of Si on the heterogeneous nucleation potency of TiB2 and AlB2 particles. With the increase in Si, the Si poisoning of the heterogeneous nucleation on TiB2 particles increases, while the Si promotion of the heterogeneous nucleation on AlB2 particles increases. For the Al3Ti3B-refined Al–xSi–0.45Mg alloys, the poisoning of Si on TiB2 is not significant at 6.5 wt% Si, resulting in the fine primary α-Al grain size of 215 ± 30 μm; with the increase in Si content to 7.5 wt%, the poisoning of Si on TiB2 is a little more significant than the promotion of Si on AlB2, which leads to the slight increase in primary α-Al grain size to 265 ± 35 μm; with the further increase in Si content to 8.5 wt%, there is a balance between the poisoning of Si on TiB2 and the promotion of Si on AlB2, which maintains the primary α-Al grain size; with the increase in Si content to 9.5 wt%, the poisoning of Si on TiB2 is again a little more superior than the promotion of Si on AlB2, which causes the slight increase in primary α-Al grain size to 315 ± 25 μm. The sole nucleation site of TiB2 suffers from enhancing Si poisoning with increasing Si under the refinement of Al5Ti1B, while the AlB2 nucleation site benefits from continuous Si promotion with increasing Si besides the Si poisoning of TiB2 nucleation site under the refinement of Al3Ti3B, which results in the significant finer grain size of primary α-Al and the slight coarsening of the primary α-Al with increasing Si in the Al3Ti3B-refined alloys, comparing with the Al5Ti1B-refined alloys.
Multiple effects of Si on mechanical properties
Effects on yield strength
The strengthening mechanisms in aluminium alloys generally include secondary phase strengthening, solution strengthening, precipitate strengthening, grain size strengthening and strain strengthening. For the T6 heat-treated Al–xSi–0.45Mg alloys, the yield strength is mainly controlled by the secondary phase strengthening of Si phase, the precipitate strengthening of β″ precipitation phase and the grain size strengthening of primary α-Al phase. In Figs. 5 and 6, the secondary eutectic Si phase in the as-cast Al–xSi–0.45Mg alloys was fully spheroidised after T6 heat treatment. So the volume fraction of the secondary Si phase in the as-cast alloys is the same as the volume fraction of the spheroidised Si phase in the T6 heat-treated alloys, which can be used for the evaluation of the secondary phase strengthening in the T6 heat-treated alloys. In Fig. 6, the β-Mg2Si intermetallic phase was fully dissolved into the α-Al matrix after the solution treatment. In Figs. 7 and 8, the dissolved β-Mg2Si phase precipitates in the form of β″ precipitate in the α-Al matrix for the precipitation strengthening of the alloys after the ageing treatment. Thus, the ratio between the volume fraction of Mg2Si phase and α-Al phase in the as-cast alloys is the same as the ratio between the volume fraction of β″ precipitate and primary α-Al phase in the T6 heat-treated alloys, which can be used for the evaluation of the precipitate strengthening in the T6 heat-treated alloys. Figure 11 shows the evolution of the volume fraction of secondary Si phase and the ratio between volume fraction of β-Mg2Si phase and α-Al phase with Si in the as-cast Al–xSi–0.45Mg alloys, which were calculated by the multicomponent phase diagram calculation software Pandat. With the increase in Si content, the volume fraction of secondary Si phase increases linearly, and the ratio between the volume fraction of β-Mg2Si phase and α-Al phase increases nearly linearly. Thus, the secondary phase strengthening of spheroidised Si phase and the precipitate strengthening of β″ precipitation phase increase with increasing Si content in the T6 heat-treated alloys.
In Figs. 2, 3 and 4, it can be expected that the grain size of primary α-Al in the Al5Ti1B-refined alloys increases significantly with increasing Si, and the grain size of primary α-Al in the Al3Ti3B-refined alloys increases slightly with increasing Si, after T6 heat treatment, since T6 heat treatment hardly has any effect on the grain size. According to the Hall–Petch relation, the grain size strengthening decreases with increasing grain size. The decrease in the grain size strengthening with increasing Si in the T6 heat-treated alloys refined by Al3Ti3B is slighter than the alloys refined by Al5Ti1B. Under the refinement of both Al5Ti1B and Al3Ti3B, with the increase in Si, the increase in the secondary phase strengthening of spheroidised Si phase and the precipitate strengthening of β″ precipitation phase is superior to the decrease in grain size strengthening, which results in the increase in the yield strength with increasing Si, as shown in Fig. 9.
Effects on tensile strength and ductility
The tensile strength and ductility of the T6 heat-treated cast Al–Si–Mg alloys without porosity or other casting defects depend on the scale of the dendritic structure and the size and shape of the Si particles [31, 32]. The tensile strength and ductility of the T6 heat-treated cast Al–Si–Mg alloys with defects present are determined by the size and area fraction of defects on the fracture surface, rather than the bulk volume percentage of defects, and the tensile strength and ductility decrease monotonically with an increase in the area fraction of defects on the fracture surface [33, 34].
Figure 12a shows the evolution of the spiral flow length of the Al–xSi–0.45Mg alloys versus Si content under the standard fluidity tests. The spiral flow length increases with the increase in Si content, which indicates that the fluidity of the Al–xSi–0.45Mg alloys increases with increasing Si. Figure 12b shows the volume percentage of porosity in the alloys refined by Al5Ti1B and Al3Ti3B. Under the refinement of Al5Ti1B, with the increase in Si content from 6.5 to 7.5, 8.5 and 9.5 wt%, the porosity percentage first decreases slightly from 0.22 ± 0.02 to 0.18 ± 0.02%, then decreases significantly to 0.11 ± 0.01%, after increases to 0.15 ± 0.01%. Under the refinement of Al3Ti3B, with the increase in Si content from 6.5 to 7.5, 8.5 and 9.5 wt%, the volume percentage of porosity first decreases slightly from 0.13 ± 0.01 to 0.1 ± 0.01%, then decreases significantly to 0.024 ± 0.008%, after decreases slightly to 0.017 ± 0.006%.
Figure 13a–d presents the SEM images showing the fracture morphology in the Al5Ti1B-refined Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, respectively, after T6 heat treatment. Porosity defect was found on the fracture surface of the Al5Ti1B-refined alloys, and the insert in each figure shows the porosity morphology with higher magnification. With the increase in Si content from 6.5 to 7.5, 8.5 and 9.5 wt%, the size and area fraction of porosity on the fracture surface first decrease, then reach the minimum at 8.5 wt% Si, after increase, which is consistent with the evolution of the porosity percentage with Si content shown in Fig. 12b. From the insert in each figure, the grain size in the Al5Ti1B-refined alloys increases with increasing Si, which is consistent with the microstructure and statistical results of grain size shown in Figs. 2 and 4.
Figure 14a–d presents the SEM images showing the fracture morphology in the Al3Ti3B-refined Al–xSi–0.45Mg alloys with 6.5 wt% Si, 7.5 wt% Si, 8.5 wt% Si and 9.5 wt% Si, separately, after T6 heat treatment. Porosity defect was found on the fracture surface of Al–6.5Si–0.45Mg and Al–7.5Si–0.45Mg alloys, and the inserts in Fig. 14a, b show the porosity morphology with higher magnification. With the increase in Si content from 6.5 to 7.5 wt%, the size and area fraction of porosity on the fracture surface decrease. With the further increase in Si content to 8.5 and 9.5 wt%, the porosity defect disappears from the fracture surface. The inserts in Fig. 14c, d show the enlarged fracture morphology, and the fracture comprises uniform distributed Al dimples and cracked Si, which is very similar to the reported Al3Ti3B-refined Al9SiMg alloy [10]. The evolution of porosity on the fracture surface of the Al3Ti3B-refined alloys with Si is consistent with the evolution of the porosity percentage shown in Fig. 12b.
For the hypoeutectic Al–Si cast alloys, the porosity defect is mainly dependent on the solidification interval of the alloy, the fluidity of the liquid alloy and the grain size. Smaller solidification interval will result in lower tendency of porosity formation. Higher fluidity and smaller grain size will make the compensation of shrinkage easier and decrease the tendency of porosity formation. The solidification interval of the hypoeutectic Al–xSi–0.45Mg alloys decreases with increasing Si, which indicates that the tendency of porosity formation decreases with increasing Si from the viewpoint of solidification interval. In Fig. 12a, the fluidity of the liquid Al–xSi–0.45Mg alloys increases with increasing Si, indicating that the tendency of porosity formation also decreases with increasing Si from the viewpoint of fluidity. According to Figs. 2 and 4, the grain size in the Al5Ti1B-refined alloys increases significantly with increasing Si due to the enhancing Si poisoning of TiB2 nucleation site, which indicates that the tendency of porosity formation in the Al5Ti1B-refined alloys increases with increasing Si from the viewpoint of grain size. In Figs. 3 and 4, the grain size in the Al3Ti3B-refined alloys increases slightly with increasing Si due to the enhancing Si promotion of AlB2 nucleation site besides Si poisoning, which indicates that the tendency of porosity formation in the Al3Ti3B-refined alloys increases slightly with increasing Si from the viewpoint of grain size.
For the Al5Ti1B-refined Al–xSi–0.45Mg alloys, with the increase in Si content from 6.5 to 8.5 wt%, the decrease in porosity formation by decreasing solidification interval and increasing fluidity is superior to the increase in porosity formation by increasing grain size, resulting in the decrease in size and area fraction of porosity on the fracture surface and the consequent increase in tensile strength and ductility till 8.5 wt% Si; after the decrease in porosity formation by decreasing solidification interval and increasing fluidity is inferior to the increase in porosity formation by increasing grain size, resulting in the increase in size and area fraction of porosity on the fracture surface and the consequent decrease in ductility at 9.5 wt% Si. For the Al3Ti3B-refined Al–xSi–0.45Mg alloys, with the increase in Si content from 6.5 to 9.5 wt%, the decrease in porosity formation by decreasing solidification interval and increasing fluidity is superior to the increase in porosity formation by slightly increasing grain size, which leads to the consecutive decrease in size and area fraction of porosity on the fracture surface and the consequent continuous increase in tensile strength and ductility.
Conclusions
The effects of Si poisoning and promotion on the microstructure and mechanical properties of hypoeutectic Al–xSi–0.45Mg (x = 6.5, 7.5, 8.5, 9.5) cast alloys were investigated. The main conclusions are summarised as follows:
-
1.
Al3Ti3B is superior to Al5Ti1B for the grain refinement of the Al–xSi–0.45Mg (x = 6.5, 7.5, 8.5, 9.5) alloys. With the increase in Si, Si poisoning on TiB2 results in the obvious coarsening of primary α-Al in Al5Ti1B-refined alloys from 350 ± 40 to 400 ± 50, 475 ± 50 and 560 ± 80 μm, and the competition between Si promotion on AlB2 and Si poisoning on TiB2 leads to the slight coarsening of primary α-Al in Al3Ti3B-refined alloys from 215 ± 30 to 265 ± 35, 265 ± 30 and 315 ± 25 μm.
-
2.
The strength and ductility of Al3Ti3B-refined alloys are superior to that of the Al5Ti1B-refined alloys, after T6 heat treatment. With increasing Si, the yield strength (YS) of Al5Ti1B-refined alloys increases from 294 ± 2 to 299 ± 2, 304 ± 1 and 309 ± 2 MPa, and the elongation first increases from 3.5 ± 0.8 to 4.5 ± 1.0 and 7.8 ± 1.4%, after decreases to 5.5 ± 1.2%, while the YS of the Al3Ti3B-refined alloys increases from 300 ± 1 to 305 ± 2, 312 ± 1 and 317 ± 2 MPa, and the elongation increases from 6.1 ± 1.1 to 8.5 ± 1.2, 11.8 ± 1.5 and 12.1 ± 1.6%.
-
3.
The increase in the secondary phase and precipitation strengthening is superior to the decrease in grain size strengthening, which results in the increase in strength with increasing Si. With the increase in Si, the decrease in porosity formation by decreasing solidification interval and increasing fluidity is superior to the increase in porosity formation by slightly coarsening grain size, which leads to the continuous increase in ductility in the Al3Ti3B-refined alloys, while the competition between porosity decreasing and increasing factors leads to the inverted ‘V’-shaped evolution of ductility in the Al5Ti1B-refined alloys.
References
Li PT, Liu SD, Zhang LL, Liu XF (2013) Grain refinement of A356 alloy by Al–Ti–B–C master alloy and its effect on mechanical properties. Mater Des 47:522–528
Samuel E, Golbahar B, Samuel AM, Doty HW, Valtierra S, Samuel FH (2014) Effect of grain refiner on the tensile and impact properties of Al–Si–Mg cast alloys. Mater Des 56:468–479
Birol Y (2017) Melt treatment of Al–Si foundry alloys with B and Sr additions. J Mater Sci 52:6856–6865. https://doi.org/10.1007/s10853-017-0923-y
Dong XX, Mi GB, He LJ, Li PJ (2013) 3D simulation of plane induction electromagnetic pump for the supply of liquid Al–Si alloys during casting. J Mater Process Technol 213:1426–1432
Dong XX, He LJ, Mi GB, Li PJ (2015) Two directional microstructure and effects of nanoscale dispersed Si particles on microhardness and tensile properties of AlSi7Mg melt-spun alloy. J Alloy Compd 618:609–614
Dong XX, He LJ, Huang XS, Li PJ (2015) Effect of electromagnetic transport process on the improvement of hydrogen porosity defect in A380 aluminum alloy. Int J Hydrog Energy 40:9287–9297
Dong XX, He LJ, Huang XS, Li PJ (2015) Coupling analysis of the electromagnetic transport of liquid aluminum alloy during casting. J Mater Process Technol 222:197–205
Dong XX, Huang XS, Liu LH, He LJ, Li PJ (2016) A liquid aluminum alloy electromagnetic transport process for high pressure die casting. J Mater Process Technol 234:217–227
Wang YX, Guan RG, Hou DW et al (2017) The effects of eutectic silicon on grain refinement in an Al–Si alloy processed by accumulative continuous extrusion forming. J Mater Sci 52:1137–1148. https://doi.org/10.1007/s10853-016-0409-3
Dong XX, Zhang YJ, Ji SX (2017) Enhancement of mechanical properties in high silicon gravity cast AlSi9Mg alloy refined by Al3Ti3B master alloy. Mater Sci Eng A 700:291–300
Dong XX, Zhang YJ, Amirkhanlou S, Ji SX (2018) High performance gravity cast Al9Si0.45Mg0.4Cu alloy inoculated with AlB2 and TiB2. J Mater Process Technol 252:604–611
Fan Z, Wang Y, Zhang Y, Qin T, Zhou XR, Thompson GE, Pennycook T, Hashimoto T (2015) Grain refining mechanism in the Al/Al–Ti–B system. Acta Mater 84:292–304
Spittle JA, Sadli SB (1995) Effect of alloy variable on grain refinement of binary aluminium alloys with Al–Ti–B. Mater Sci Technol 11:533–537
Lee YC, Dahle AK, Stjohn DH, Hutt JEC (1999) The effect of grain refinement and silicon content on grain formation in hypoeutectic Al–Si alloys. Mater Sci Eng A 259:43–52
Birol Y (2012) Effect of silicon content in grain refining hypoeutectic Al–Si foundry alloys with boron and titanium additions. Mater Sci Technol 28:385–389
Mohanty PS, Gruzleski JE (1996) Grain refinement mechanisms of hypoeutectic Al–Si alloys. Acta Metall Mater 44:3749–3760
Qiu D, Taylor JA, Zhang MX, Kelly PM (2007) A mechanism for the poisoning effect of silicon on the grain refinement of Al–Si alloys. Acta Mater 55:1447–1456
Schumacher P (2017) Probing the heterogeneous nucleation interface of TiB2 in alloys by advanced electron microscopy. In: 6th Decennial international conference on solidification processing, Old Windsor, UK
Wang T, Chen Z, Fu H, Xu J, Fu Y, Li T (2011) Grain refining potency of Al–B master alloy on pure aluminum. Scr Mater 64:1121–1124
Kori SA, Murty BS, Chakraborty M (2000) Development of an efficient grain refiner for Al–7Si alloy and its modification with strontium. Mater Sci Eng A 283:94–104
Birol Y (2012) Grain refinement of pure aluminium and Al–7Si with Al-3B master alloy. Mater Sci Technol 28:363–367
Chen ZN, Kang HJ, Fan GH et al (2016) Grain refinement of hypoeutectic Al–Si alloys with B. Acta Mater 120:168–178
Birol Y (2012) Performance of AlTi5B1, AlTi3B3 and AlB3 master alloys in refining grain structure of aluminium foundry alloys. Mater Sci Technol 28:481–486
Birol Y (2009) A novel Al–Ti–B alloy for grain refining Al–Si foundry alloys. J Alloy Compd 486:219–222
Tiryakioğlu M (2008) Si particle size and aspect ratio distributions in an Al–7%Si–0.6%Mg alloy during solution treatment. Mater Sci Eng A 473:1–6
Xu C, Xiao WL, Zheng RX, Hanada S, Yamagata H, Ma CL (2015) The synergic effects of Sc and Zr on the microstructure and mechanical properties of Al–Si–Mg alloy. Mater Des 88:485–492
Andersen SJ, Zandbergen HW, Jansen J, Traeholt C, Tundal U, Reiso O (1998) The crystal structure of the β″ phase in Al–Mg–Si alloys. Acta Mater 46:3283–3298
Yang WC, Wang MP, Zhang RR, Zhang Q, Sheng XF (2010) The diffraction patterns from β″ precipitates in 12 orientations in Al–Mg–Si alloy. Scr Mater 62:705–708
Yang WC, Huang LP, Zhang RR, Wang MP, Li Z, Jia YL, Lei RS, Sheng XF (2012) Electron microscopy studies of the age-hardening behaviors in 6005A alloy and microstructural characterizations of precipitates. J Alloy Compd 514:220–233
Yang WC, Ji SX, Huang LP, Sheng XF, Zhou L, Wang MP (2014) Initial precipitation and hardening mechanism during non-isothermal aging in an Al–Mg–Si–Cu 6005A alloy. Mater Charact 94:170–177
Cáceres CH, Davidson CJ, Griffiths JR (1995) The deformation and fracture behaviour of an Al–Si–Mg casting alloy. Mater Sci Eng A 197:171–179
Cáceres CH, Griffiths JR (1996) Damage by the cracking of silicon particles in an Al–7Si–0.4Mg casting alloy. Acta Mater 44:25–33
Surappa MK, Blank EW, Jaquet JC (1986) Effect of macro-porosity on the strength and ductility of cast Al–7Si–0.3Mg alloy. Scr Metall 20:1281–1286
Cáceres CH, Selling BI (1996) Casting defects and the tensile properties of an Al–Si–Mg alloy. Mater Sci Eng A 220:109–116
Acknowledgements
Financial support from Innovate UK under project 131817 is gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Dong, X., Ji, S. Si poisoning and promotion on the microstructure and mechanical properties of Al–Si–Mg cast alloys. J Mater Sci 53, 7778–7792 (2018). https://doi.org/10.1007/s10853-018-2022-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-018-2022-0