Abstract
WC-based coatings deposited by high velocity oxy-fuel (HVOF) spraying have been widely used in many industrial fields, where mechanical components are subjected to severe abrasive wear. Much attention has been especially paid to nanostructured and multimodal WC-based coatings due to their excellent abrasive wear resistance. In this study, a new kind of multi-dimensional WC-10Co4Cr coating, composed of nano, submicron, micron WC particles and CoCr alloy, was developed by HVOF. The microstructure, porosity, microhardness, fracture toughness, and electrochemical properties of the coating were investigated in comparison with nanostructured WC-10Co4Cr coating deposited by HVOF. Abrasive wear resistance of both WC-10Co4Cr coatings was evaluated on wet sand rubber wheel abrasion tester. The results show that the multi-dimensional coating possesses low porosity (0.31 ± 0.09%), excellent microhardness (1126 ± 115 HV0.3), fracture toughness (4.66 ± 0.51 MPa m1/2), and outstanding electrochemical properties. Moreover, the multi-dimensional coating demonstrates approximately 36% wet abrasive resistance enhancement than the nanostructured coating. The superior abrasive wear resistance originates from the coating’s multi-dimensional structure and excellent mechanical and electrochemical properties.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Kamdi Z, Shipwaya PH, Voiseya KT, Sturgeon AJ (2011) Abrasive wear behavior of conventional and large-particle tungsten carbide-based cermet coatings as a function of abrasive size and type. Wear 271:1264–1272
Wang Q, Chen ZH, Ding ZX (2009) Performance of abrasive wear of WC-12Co coatings sprayed by HVOF. Tribol Int 42:1046–1051
Stewart DA, Shipway PH, and McCartney DG (1999) Abrasive wear behaviour of conventional and nanocomposite HVOF sprayed WC-Co coatings. Wear 225–229:789–798
Singh R, Tiwari SK, Mishra SK (2012) Cavitation erosion in hydraulic turbine components and mitigation by coatings: current status and future needs. J Mater Eng Perform 21(7):1539–1551
Shipway PH, McCartney DG, Sudaprasert T (2005) Sliding wear behavior of conventional and nanostructured HVOF sprayed WC/Co coatings. Wear 259:820–827
Jafarzadeh K, Valefi Z, Ghavidel B (2010) The effect of plasma spray parameters on the cavitation erosion of Al2O3-TiO2 coatings. Surf Coat Technol 205(7):1850–1855
Hong S, Wu YP, Zhang JF, Zheng YG, Zheng Y, Lin JR (2016) Synergistic effect of ultrasonic cavitation erosion and corrosion of WC-CoCr and FeCrSiBMn coatings prepared by HVOF spraying. Ultrason Sonochem 31:563–569
Wang Q, Tang ZX, Cha LM (2015) Cavitation and sand slurry erosion resistances of WC-10Co-4Cr coatings. J Mater Eng Perform 24(6):2435–2443
Kim HJ, Yang HS, Baik KH (2006) Development and properties of nanostructured thermal spray coatings. Curr Appl Phys 6(6):1002–1006
Tillmann W, Baumann I, Hollingsworth PS et al (2014) Sliding and rolling wear behavior of HVOF-sprayed coatings derived from conventional, fine and nanostructured WC-12Co powders. J Therm Spray Technol 23(1/2):262–280
Zhou KS, Deng CM, Liu M (2009) Characterizations of fatigue and salt spray corrosion resistance of HVAF sprayed WC-17Co and WC-10Co4Cr coatings on the substrate of 300M steel. Rare Metal Mat Eng 38(4):671–676
Hong S, Wu YP, Zhang JF (2015) Cavitation erosion behavior and mechanism of HVOF sprayed WC-10Co-4Cr coating in 3.5 wt% NaCl solution. Trans Indian Inst Metals 68(1):151–159
Hong S, Wu YP, Zhang JF (2015) Ultrasonic cavitation erosion of high-velocity oxygen-fuel (HVOF) sprayed near-nanostructured WC-10Co-4Cr coating in NaCl solution. Ultrason Sonochem 26:87–92
Ghabchi A, Varis T, Turunen E, Suhonen T, Liu XW, Hannula SP (2010) Behavior of HVOF WC-10Co4Cr coatings with different carbide size in fine and coarse particle abrasion. J Therm Spray Technol 19(1–2):368–377
Armstrong RW (2011) The hardness and strength properties of WC-Co composites. Materials 4(7):1287–1308
Ma N, Guo L, Cheng ZX, Wu HT, Ye FX, Zhang KK (2014) Improvement on mechanical properties and wear resistance of HVOF sprayed WC-12Co coatings by optimizing feedstock structure. Appl Surf Sci 320:364–371
Jia K, Fischer TE (1996) Abrasion resistance of nanostructured and conventional cemented carbides. Wear 200:206–214
Li CJ, Ohmori A, Tani K (1999) Effect of WC particle on the abrasive wear of thermally sprayed WC-Co coatings. Mater Manuf Process 14:175–184
Scieska SF, Filipowicz K (1998) An integrated testing method for cermet abrasion resistance and fracture toughness evaluation. Wear 216:202–212
Gee MG, Gant A, Roebuck B (2007) Wear mechanism in abrasion and erosion of WC/Co and related materials. Wear 263:137–148
Guilemany JM, Dosta S, Miguel JR (2006) The enhancement of the properties of WC–Co HVOF coatings through the use of nanostructured and microstructured feedstock powders. Surf Coat Technol 201:1180–1190
Zhao XQ, Zhou HD, Chen JM (2006) Comparative study of the friction and wear behavior of plasma sprayed conventional and nanostructured WC-12%Co coatings on stainless steel. Mater Sci Eng 431(1–2):290–297
Chen H, Gou GQ, Tu MJ (2009) Characteristics of nano particles and their effect on the formation of nanostructures in air plasma spraying WC-17Co coating. Surf Coat Technol 203(13):1785–1789
Shipway PH, Hogg JJ (2005) Dependence of microscale abrasion mechanisms of WC-Co hard metals on abrasive type. Wear 259(1–6):44–51
He J, Liu Y, Qiao Y, Fischer TE, Lavernia EJ (2002) Near-nanostructured WC-18 pct Co coatings with low amounts of non-WC carbide phase: part I. Synthesis and characterization. Metall Mater Trans A 33(1):145–157
Stewart DA, Shipway PH, McCartney DG (2000) Microstructural evolution in thermally sprayed WC-Co coatings: compassion between nanocomposite and conventional starting powders. Acta Mater 48:1593–1604
Babua PS, Basub B, Sundararajan G (2010) Abrasive wear behavior of detonation sprayed WC-12Co coatings: influence of decarburization and abrasive characteristics. Wear 268:1387–1399
Dent AH, DePaloand S, Sampath S, Therm J (2002) Examination of the wear properties of HVOF sprayed nanostructured and conventional WC-Co cermets with different binder phase contents. Spray Technol 11:551–558
Yang QQ, Senda T, Ohmori A (2003) Effect of carbide grain size on microstructure and sliding wear behavior of HVOF-sprayed WC-12%Co coatings. Wear 254:23–34
Skandan G, Yao R, Sadangi R (2000) Multimodal coatings: a new concept in thermal spraying. J Therm Spray Technol 9(3):329–331
Gang CJ, Hong TW, Xiao C et al (2013) Characterization of cold-sprayed multimodal WC-12Co coating. Surf Coat Technol 235:536–543
Wang Q, Chen ZH, Lia LX, Yang GB (2012) The parameters optimization and abrasion wear mechanism of liquid fuel HVOF sprayed bimodal WC-12Co coating. Surf Coat Technol 206:2233–2241
Ding ZX, Chen W, Wang Q (2011) Resistance of cavitation erosion of multimodal WC-12Co coatings sprayed by HVOF. Trans Nonferrous Met Soc China 21:2231–2236
Skandan G, Yao R, Kear BH, Qiao Y, Liu L, Fischer TE (2001) Multimodal powders: a new class of feedstock material for thermal spraying of hard coatings. Scripta Mater 44:1699–1702
Ma N, Guo L, Chen ZX, Wu H, Ye F, Zhang K (2014) Improvement on mechanical properties and wear resistance of HVOF sprayed WC-12Co coatings by optimizing feedstock structure. Appl Surf Sci 320:364–371
Wang HT, Chen X, Bai XB, Ji GC, Dong ZX, Yi DL (2014) Microstructure and properties of cold sprayed multimodal WC-17Co deposits. Int J Refract Met Hard Mater 45:196–203
Toma D, Brandl W, Marginean G (2001) Wear and corrosion behaviour of thermally sprayed cermet coatings. Surf Coat Technol 138:149–158
Thakur L, Arora N (2013) A study on erosive wear behavior of HVOF sprayed nanostructured WC-CoCr coatings. J Mar Sci Technol 27(5):1461–1467
Sahraoui T, Guessasma S, Jeridane ML et al (2010) HVOF sprayed WC-Co coatings: microstructure, mechanical properties and friction moment prediction. Mater Des 31:1431–1437
Lekatou A, Sioulas D, Karantzalis AE, Grimanelis D (2015) A comparative study on the microstructure and surface property evaluation of coatings produced from nanostructured and conventional WC-Co powders HVOF-sprayed on Al7075. Surf Coat Technol 276:539–556
Sugiyama K, Nakahama S, Hattori S, Nakano K (2005) Slurry wear and cavitation erosion of thermal-sprayed cermets. Wear 258(5–6):768–775
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ding, X., Cheng, XD., Li, C. et al. Microstructure and performance of multi-dimensional WC-CoCr coating sprayed by HVOF. Int J Adv Manuf Technol 96, 1625–1633 (2018). https://doi.org/10.1007/s00170-017-0837-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-017-0837-5