Abstract
The paper describes an experimental study to evaluate the need of nickel electroplating on stainless steel part in vacuum brazed oxygen-free electronic (OFE) copper-type 316L stainless steel transition joints with silver copper eutectic braze filler metal (BVAg-8 of AWS A5.8). The results of the study demonstrated that nickel electroplating is not required to obtain hermetically sealed sound and strong OFE copper-316L stainless steel transition vacuum brazed joints. The only pre-treatment requirement for stainless steel part is simple ultrasonic cleaning, although pickling treatment has been found to have a favorable effect in improving its wettability for the braze filler metal. Brazed joints made with unplated stainless steel (SS) not only displayed (i) required level of hermeticity (helium leak rate ≤2 × 10−10 mbar·l/s) and bakeablility at 523 K for ultra-high vacuum application and (ii) reasonably good tensile strength comparable to those made with Ni-plated SS, but also exhibited significantly suppressed extent of intergranular penetration of braze filler metal into copper. Important factors responsible for the development of sound OFE copper-316L stainless steel brazed joints with ultrasonically cleaned stainless steel part are excellent wettability of OFE copper which compensated for poor wettability of stainless steel surface and presence of hydrocarbon-free high vacuum environment during brazing.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Gold SH, Ting A, Jabotinski V, Zhou B, Sprangle P (2013) Development of a high average current rf linac thermionic injector. Phys Rev ST Accel Beams 16:083401 (1–12)
Kondo Y, Morishita T, Hasegawa K, Chishiro E, Hirano K, Hori T, Oguri H, Sato F, Shinozaki S, Sugimura T, Kawamata H, Naito F, Fukui Y, Futatsukawa K, Nanmo K (2013) High-power test and thermal characteristics of a new radio-frequency quadrupole cavity for the Japan Proton Accelerator Research, Complex Linac. Phys Rev ST Accel Beams 16:040102 (1–8)
Tamura K, Oishi M, Ohkuma H, Okayasu Y, Shoji M, Takano S, Taniuchi Y, Masaki M, Mochihashi A (2013) Development of a high-heat-load compact photon absorber for SPring-8 diagnostics beamline II. J Phys Conf Ser 425(2013):212005. doi:10.1088/1742-6596/425/21/212005, 1-4
Cverna F (ed) (2012) Thermal properties of metals, ASM Ready Reference. ASM International, Materials Park, Ohio, p 410, 363
Li Y, Lin X, Vacuum Science and Technology for Accelerator Vacuum System. https//uspas.fnal.gov/materials/13Duke/USPASVacuumSession4_1VacMaterials.pdf. Accessed on 18 April 2015
Savage WF, Nippes EP, Mushala MC (1978) Copper-contamination cracking in the weld heat-affected zone. Weld J 57:145s–152s
Kore SD, Date PP, Kulkarni SV, Kumar S, Rani D, Kulkarni MR, Desai SV, Rajawat RK, Nagesh KV, Chakravarty DP (2011) Application of electromagnetic impact technique for welding copper-to-stainless steel sheets. Int J Adv Manuf Technol 54:949–955
Al-Roubaiy AO, Nabat SM, Batako ADL (2014) Experimental and theoretical analysis of friction stir welding of Al-Cu joints. Int J Adv Manuf Technol 71:1631–1642
Teker T (2013) Joining of stainless-steel and aluminum materials by friction welding. Int J Adv Manuf Technol 66:303–310
Zhu Z, Lee KY, Wang X (2012) Ultrasonic welding of dissimilar metals AA6061 and Ti6Al4V. Int J Adv Manuf Technol 59:569–574
Mathot S (2008) RFQ Vacuum Brazing at CERN, Proc. 11th European Particle Accelerator Conf. 2008. European Physical Society Accelerator Group (EPS-AG), Genoa, Italy, 1494–96
ASTM E2734/E2734M-10 (2010) Standard Specification for Dimensions of Knife-Edge Flanges. ASTM International, West Conshohocken
Kozlova O, Voytovych R, Devismes MF, Eustathopoulos N (2008) Wetting and brazing of stainless steels by copper-sliver eutectic. Mater Sci Eng A 495:96–101
Shaprio AE (2013) Brazing Q & A. Weld J 92:26
Singh R, Pant KK, Lal S, Yadav DP, Garg SR, Raghuvanshi VK, Mundra G (2012) Vacuum brazing of accelerator components. J Phys Conf Ser 390:012025
Fukikoshi T, Watanabe Y, Miyazawa Y, Kanasaki F (2014) Brazing of copper to stainless steel with a low-silver-content brazing filler metal, IOP Conference Series. Mater Sci Eng 61:012016
Liaw DW, Shiue RK (2005) Brazing of Ti-6Al-4V and niobium using three silver-base braze alloys. Metall Mater Trans 36A:2415–2427
Kumar A, Ganesh P, Kaul R, Bhatnagar VK, Yedle K, Ram Sankar P, Sindal BK, Kumar KVANPS, Singh MK, Rai SK, Bose A, Veerbhadraiah T, Ramteke S, Sridhar R, Mundra G, Joshi SC, Kukreja LM (2015) A new vacuum brazing route for niobium-316L stainless steel transition joints for superconducting RF cavities. J Mater Eng Perform 24:952–963
Kumar A, Ganesh P, Kaul R, Sindal BK, Yedle K, Bhatnagar VK, Ram Sankar P, Singh MK, Rai SK, Bose A, Sridhar R, Joshi SC, Kukreja LM (2015) New brazing recipe for ductile niobium-316L stainless steel joints. Weld J. 94:241s–249s
Keller DL, McDonald MM, Heiple CR, Johns WL, Hofmann WE (1990) Wettability of brazing filler metals. Weld J 69:31–34
http://www.industrialheating.com/articles/89702-the-ellingham-diagram-how-to-use-it-in-heat-treat-process-atmosphere-troubleshooting, Accessed on 9 Oct. 2015
Zhuang WD, Eagar TW (1997) Diffusional breakdown of nickel protective coatings on copper substrate in silver-copper eutectic melts. Metall Mater Trans A 28A:969–977
Xin L, Wenqing Q, Haitao L, Guojian W (2014) Grain boundary penetration behavior analysis of OFC brazed with AgCu28 brazing filler. J Beijing University Aeronaut Astronaut 40:717–720
Sekulić DP (ed) (2013) Advances in Brazing - Science, Technology and Applications. Woodhead Publishing Ltd., Philadelphia, pp 3–28
Sharps PR, Tomsia AP, Pask JA (1980) Wetting and spreading in the Cu-Ag system., Lawrence Berkeley Laboratory, University of California. LBL-11119c.2. http://escholarship.org/uc/item/46c2n06b#page-1. Accessed on 20 April 2015
Holm VCF (1941) Observations on the tarnishing of stainless steels on heating in vacuum, Surface Treatment of Metals. American Society for Metals, Ohio, p 379
Holm VCF (1942) Elimination of oxide films on ferrous materials by heating in vacuum. J Res Natl Bur Stand 28:569–579
Yoshiaki A, Akira O, Fu CH (1983) Studies on vacuum brazing (Report II): removal of oxide film from stainless steel surface and brazing alloy spreading mechanism. Trans JWRI 12:27–34
Tweeddale JG (2013) The fabrication of materials: materials technology. Elsevier, London, p 129
Kirchner HP (1964) The thermal expansion of ceramic crystals. Prog Solid State Chem 1:1–36. doi:10.1016/0079-6786(64)90002-0-17
http://www.brazingandsoldering.org/faqs/faq7.pdf. Accessed on 20 March 2015
Philip R (2013) Industrial brazing practice, CRC Press, 2nd edn. Taylor and Francis Group, BocaRaton, p 221
Battenbough AJ, Osmanda Dipl.-Ing AM, Staines AM (2011) Surface preparation for high vacuum brazing., NICROBRAZ NEWS. www.wallcolmonoy.com/wp-content/uploads/ 2012/12/NicrobrazNews_Nov2011.pdf. Accessed 20 March 2015
Dorn L, Iversen K, Stroiczek M, Tillmann W, Weise W (2007) Hartloeten und Hochtemperaturloeten - Grundlagen und Anwendung. Expert Verlag, Renningen, Kontakt and Studium Band 677
Dan Kay. The famous joint-strength vs. joint clearance chart. http://vacaero.com/information-resources/vacuum-brazing-with-dan-kay/1300-the-famous-joint-strength-vs-joint-clearance-chart.html, Accessed on 9 Oct., 2015
M. H. Sloboda. Design and strength of brazed joints. http://www.jm-metaljoining.com/french/pdfs-uploaded/Design%20and%20Strength.pdf, Accessed on 9 Oct., 2015
ASM Specialty Handbook: Copper and Copper Alloys. Ed. J. R. Davis. ASM International, Materials Park, OH, 65.
Elements of Metallurgy and Engineering Alloys, Ed. F. C. Campbell, 2008, ASM International, Materials Park, OH, 482.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kumar, A., Ganesh, P., Kaul, R. et al. Study on requirement of nickel electroplating in OFE copper-316L stainless steel brazed joints. Int J Adv Manuf Technol 87, 2639–2651 (2016). https://doi.org/10.1007/s00170-016-8664-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-016-8664-7