Abstract
Reinforced concrete (RC) deep beams with small shear span-to-depth ratio (a/d) are common elements in structures. They are usually designed using the Strut-and-Tie Model (STM). To mitigate the corrosion-induced damage, fibre-reinforced polymer (FRP) bars have been used as an alternative to steel bars. Among FRP types, glass FRP (GFRP) reinforcement is of particular interest to the construction industry because of its lower cost and large deformation at failure However, due to its linear-elastic behaviour and relatively low modulus of elasticity compared to steel, GFRP-RC deep beams would be susceptible to deeper and wider cracks, which will adversely affect the capacity of such beams. In addition, GFRP has a different bar surface and bond characteristics compared to steel, which require a longer development length. This paper reports on an experimental study designed to investigate the shear behaviour of GFRP-RC deep beams. In this study, three large-scale, simply supported concrete deep beams reinforced with headed-end GFRP bars were constructed and tested up to failure. The specimens had a rectangular-section of 590-mm high by 250 mm wide, while the length of the specimens were 2,100 mm. The main variable was the longitudinal reinforcement ratio, which varied between 0.6, 1.0 and 1.4%. The specimens were tested in a three-point bending setup over a clear span of 1.38 m with a/d ratio of 1.0. The test results indicated that increasing the longitudinal reinforcement ratio led to increasing the load capacity of such beams.
Access provided by Autonomous University of Puebla. Download conference paper PDF
Similar content being viewed by others
1 Introduction
In the last century, numerous research have been conducted to understand the behaviour of steel-reinforced concrete (RC) structures. In general, concrete members can be classified into two categories based on shear behavior: slender and deep. Of particular interest, in this paper, is the shear behaviour of deep members containing no distributed web reinforcement. They are well-known with their relatively higher load capacity compared to slender beams. RC structures are exposed to harsh environment especially in North America, which, over time, can cause severe deterioration due to the corrosion problems. Thus, the use of fibre-reinforced polymers (FRP) bars became more common in the last two decades as they are noncorrosive materials [1].
It is well established that in deep beams, which have a shear span-to-depth ratio (a/d) less than 2.5 [2, 7], after the formation of the diagonal crack, a significant amount of load is transferred to the supports by a compression thrust linking the load and forming the arch action. In the meantime, the longitudinal reinforcement works as a tie. Such load transfer mechanism is named arch action or strut-and-tie model (STM) [6]. Generally, the glass FRP (GFRP)-RC beams behaves in a similar manner to their steel-RC counterparts [4, 5]. However, with respect to steel bars, the GFRP bars had different characteristics such as relatively low modules of elasticity, which results in wider and deeper cracks that adversely affect the shear capacity of beams internally reinforced with GFRP. This paper aims to investigate the shear behaviour of simply supported deep beams reinforced with GFRP bars that do not contain any web reinforcement.
2 Experimental Program
2.1 Test Specimens
Three large scale concrete deep beams reinforced with GFRP bars were constructed and tested to failure. All specimens had a rectangular cross section of 250 × 590 mm, a/d of 1.0, and an overall length of 3,500 mm. The longitudinal reinforcement ratio, ρ, varied between 1.4, 1.0 and 0.6%. The test specimens were labelled based on the longitudinal reinforcement ratio. For example, Specimen B1.4 is the beam specimen that has ρ = 1.4%. Table 1 lists the details of the specimens.
2.2 Materials Properties
Table 2 shows the properties of the used GFRP reinforcing bars. The headed ends are made of thermoplastic matrix reinforced with short glass fibre, cast at the end of bars at high temperature. The head is approximately 100 mm in length with a maximum outer diameter of 50 mm at the end as shown in Fig. 1. The concrete compressive strength was determined on the day of testing according to ASTM C39 [3]. The obtained concrete strengths are listed in Table 1.
2.3 Test Setup and Instrumentation
The beams were tested under a single monotonic load acting at the mid-span. All specimens were loaded using an MTS loading machine with a capacity of 5,000 kN. Bearing plates were 150 × 250 × 50 mm and 200 × 250 × 50 mm at supports and loading point, respectively.
To capture the strain profile in the reinforcement, seven strain gauges were attached to the reinforcement at critical locations. In addition, five linear variable displacement transducers (LVDTs) were installed, three to measure the deflection, the other two were installed to report any slippage between the FRP bars and the heads. In addition, three PI-gauges were installed to capture the propagation and widening of cracks. All instrumentation was connected to a data acquisition system (DAQ) to record the readings during the test. Figure 2 shows a schematic drawing of the test setup.
3 Test Results and Discussion
3.1 Mode of Failure
At initial stages of loading, 14–16% of ultimate load, flexural cracks were noticed near the mid-span section for all tested beams. As the load increased, such cracks propagated vertically upward to the proximity of mid-height of beam. As loading continued, flexural shear cracks developed in the shear spans. With further loading, cracks became diagonal and parallel to the compression strut connecting the loading point and the support. At high level of loads, the width of the diagonal crack kept increasing until failure, except for B1.4. Failure of diagonal compression strut in the region between the loading and supporting plates occurred in B0.6 and B1.0. The failure for both beams was very brittle and the concrete was broken away or snapped off, as shown in Fig. 3a and b. On the other hand, the beam with high reinforcement ratio, B1.4, experienced premature failure around the loading point as shown in Fig. 3c.
3.2 Load–Deflection
Figure 4 shows the effect of the reinforcement ratio on the load–deflection response of the tested beams. All three specimens exhibited similar overall behavior before the formation of the flexural cracks where the deflection was of very small values. This behaviour was characterized by a nearly bilinear response. After cracking, a reduction in the flexural stiffness of the specimens was observed but with different tendencies, which is attributed to the different reinforcement ratio of each specimen. The figure indicates that as the amount of reinforcement was increased, the post-cracking flexural stiffness increased. Thus, the flexural behaviour of the tested beams, in terms of load–deflection response, seems to be a function of the axial stiffness of the reinforcing bars. Supposedly, an increase in ρ is known to produce a higher shear capacity in deep beams when other design parameters are kept constant. This trend was observed between B1.0 and B0.6. For example, specimen B1.0, which had a reinforcement ratio 67% larger than B0.6 had a stiffer loading response and a higher capacity of about 20%. On the other hand, this trend was not observed, when the load carrying capacity of the two tested beams B1.0 and B1.4 were compared. The failure load for both beams was similar and measured about 900 kN. This was attributed to that a local failure at the loading point due to high compressive stress occurring around the loading point was taken place in B1.4. This failure is recognised as a premature failure, which is not desirable.
4 Conclusions
Based on the presented discussions, the following can be concluded:
-
1.
The mode of failure for B0.6 and B1.0 was brittle reflected by several diagonal cracks in the region between the loading and supporting plates.
-
2.
A premature failure around the loading point was observed for B1.4.
-
3.
During the pre-cracking stage, the load deflection response for all tested beams was similar.
-
4.
The load capacity of the specimens increased as the reinforcement ratio increased, except for B1.4.
References
ACI Committee 440 (2015) Guide for the design and construction of structural concrete reinforced with FRP bars. ACI 440.1R-15, American Concrete Institute, Detroit, MI, USA, pp 1–88
ASCE-ACI Committee 426 (1973) Shear and diagonal tension. ASCE, J Struct Div 6:1091–1187
ASTM (2012) Standard test method for compressive strength of cylindrical concrete specimens. ASTM C39–12, West Conshohocken, PA
Manuel R, Slight B, Suter G (1971) Deep beam behavior affected by length and shear span variations. ACI J Proc 68(12):954–958
Rogowsky DM, MacGregor JG, Ong SY (1986) Design of reinforced concrete deep beams. ACI J Proc 83(4):614–623
Tuchscherer R, Birrcher D, Huizinga M, Bayrak O (2011) Distribution of stirrups across web of deep beams. ACI Struct J 108(6):108–115
Wight JK, MacGregor JG (2009) Reinforced concrete: mechanics and design, 6th edn. Pearson Prentice Hall, Upper Saddle River, New Jersey, USA, pp 1–1157
Acknowledgements
The authors wish to express their gratitude for the financial support received from the Natural Sciences and Engineering Council of Canada (NSERC). The assistance received from the technical staff of the W.R. McQuade Structures Laboratory at the University of Manitoba is acknowledged.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2023 Canadian Society for Civil Engineering
About this paper
Cite this paper
Bediwy, A., Mahmoud, K., El-Salakawy, E. (2023). Effect of Longitudinal Reinforcement Ratio on the Behaviour of Deep Beams Reinforced with GFRP Headed-End Bars. In: Walbridge, S., et al. Proceedings of the Canadian Society of Civil Engineering Annual Conference 2021 . CSCE 2021. Lecture Notes in Civil Engineering, vol 241. Springer, Singapore. https://doi.org/10.1007/978-981-19-0511-7_6
Download citation
DOI: https://doi.org/10.1007/978-981-19-0511-7_6
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-19-0510-0
Online ISBN: 978-981-19-0511-7
eBook Packages: EngineeringEngineering (R0)