Abstract
Our recent works on resistive RAMs (ReRAMs) are reviewed, where in-situ transmission electron microscopy (TEM) realizing simultaneous electric measurements and TEM observations was applied to investigate resistive switching operation of some conductive bridging RAMs (CBRAMs). In multiple switching cycles, the Cu conductive filament was experimentally confirmed to appear in the Set process giving the low resistance state (LRS, on-state) and to disappear in the Reset process giving the high resistance state (HRS, off-state). No drastic change in the geometry of the conductive filament was seen when the switching current was small. With increasing the current, the filament became thick, but its position was unstable, and too much Cu moved into the switching layer in a wide area. This may induce the device degradation and failure.
Access provided by CONRICYT-eBooks. Download conference paper PDF
Similar content being viewed by others
Keywords
1 Introduction
Large resistance change with voltage application was widely known in Perovskite type complex oxides , binary oxides such as NiO, TiO2, HfO2 and Ta2O5, and solid electrolyte (e.g. Ge-S) with Cu or Ag. In recent years, many works have been reported to apply this phenomenon on non-volatile resistive RAM s (ReRAMs) and on neuromorphic devices [1–4]. To guarantee the operation of these devices, clarification of the switching mechanism is strongly required. Based on the electrochemical discussion of their electric properties, it is a common knowledge that the resistance switching in binary oxides and solid electrolytes is caused by formation and rupture of the conductive filament [1, 2]. However, details of its operation mechanism are still ambiguous and difficult to be clarified only using electric properties. Dynamical observations in real space using in-situ transmission electron microscopy (TEM) are a method to overcome this difficulty, where the electric measurements and TEM observations can be performed synchronously [5–10]. Several types of in-situ TEM holders became commercially available in recent years, and the number of reports in this category has increased. However, works on realistic switching operations such as the current-voltage (I-V) switching cycle, the switching repetition and the pulse endurance are rare [11, 12].
In this report, our recent works on ReRAMs using the in-situ TEM are reviewed, which are categorized as the conductive bridging RAM (CBRAM) such as GeS-Cu [13, 14], Cu/MoOx [11, 15, 16] and Cu/WOx [17, 18]. In all of these CBRAM systems, the Cu conductive filament was experimentally confirmed to appear in the Set process giving the low resistance state (LRS, on-state) and to disappear in the Reset process giving the high resistance state (HRS, off-state). No drastic change in the geometry of the conductive filament was seen at the Set/Reset switching moment, and the filament growth/erasure was seen during continuation of the current flow.
2 Experimental Procedure
Three types of ReRAM s were used for investigation, which were composite GeS-Cu(8–60 nm) deposited on a wedge-shaped PtIr, Pt(100 nm)/Cu(30 nm)/MoOx(50nm) or Pt(100nm)/Cu(30nm)/WOx(20nm) trilayer films on a TiN/Si wafer chip. For all samples, the film deposition was done using conventional RF sputtering (Ar) or reactive sputtering (Ar-20 %O2) of metal targets at room temperature (RT). In the latter two samples, the Cu and the TiN layers worked as the top electrode (TE) and the bottom electrode (BE), respectively. The GeS-Cu sample was used for in-situ TEM without any further processing, because the tip of the PtIr wedge was thin enough for TEM observations. On the other hand, the ReRAM samples of MoOx and WOx were processed using the ion-shadow method [19] which is a kind of the ion-milling method.
In-situ TEM experiments were carried out using the system shown in Fig. 1 composed of a hand-made piezo-driven TEM holder and a JEM-2010 microscope (C s = 0.5 mm). A movable Pt-Ir probe was contacted to one of the ReRAM devices formed on the TEM sample, and the I-V switching cycles were measured using a commercially available source-measure-unit (SMU, Yokogawa GS610). To prevent eternal device destruction caused by the strong overshoot current in the Set process, current limitation (compliance current; I comp) was introduced using this SMU. In the GeS-Cu sample, the wedge-shaped PtIr substrate was biased while the probe was grounded. On the other hand, in MoOx and WOx samples, the TiN/Si substrate was grounded while the probe was biased. Geometrical change of the filament was dynamically recorded using a CCD camera (30 ms/frame).
3 Results and Discussion
3.1 Filament Formation in Cu-GeS
The I-V curve measured in TEM is shown in Fig. 2, where the horizontal axis corresponds to the potential of the substrate relative to the probe [13, 14]. The voltage was varied in a sequence of 0 V, +7 V, −2 V and 0 V, and a clear hysteresis curve was obtained. Though the retention time (memory holding time) of the LRS was not long enough for the practical memory application, formation and erasure of the conductive filament was clearly confirmed.
The TEM images extracted from the video are shown in Fig. 3. There are a Cu-GeS amorphous film containing Ge nanocrystals on the Pt-Ir substrate (Fig. 3a). In the first quadrant of the I-V graph, where the substrate was positively biased relative to the probe, the current increased gradually. There was drastic increase at the voltage of +2.6 V, and its resistance was converted to the LRS (Set operation). Correspondingly to this change, a filamentary dark contrast appeared (Fig. 3b). In the selected area diffraction (SAD) pattern during the Set process, Debye rings of Cu appeared. In addition, the energy dispersive X-ray spectroscopy (EDX) measurements were done during the Set process with positive bias voltage to the substrate (but on another filament than that in Fig. 3). In Fig. 4, the EDX spectra before (Fig. 4a) and during (Fig. 4b) the Set operation are compared. It was clearly identified that the deposit contained much Cu. Considering these two results, the deposit appeared in the Set process was concluded to be made of Cu nanocrystals. Afterwards, a negative voltage sweep was done, and the deposit gradually disappeared and completely erased at about −2.8 V (Fig. 3c, d). The resistance showed a sudden increase at this moment. This is the Reset process which converts the LRS to the HRS. The deposit observed here worked as a conductive filament for the CBRAM switching.
Repeating switching cycles, the Set voltage (V set) gradually decreased. This indicates that the Cu-GeS layer in the HRS after the Reset operation changed from the initial state as confirmed in Fig. 5. First, a filament was formed (Fig. 5a) and erased. Afterwards, the Pt-Ir probe was shifted by 100 nm (Fig. 5b left panel), and a positive voltage was applied to generate a filament again (Fig. 5b right panel). The filament appeared from the probe toward the position of the first filament. It did not reach the nearest position on the substrate. The region in which the filament was formed once must be a priority position for the formation and the growth of a filament. It is expected that there are some residuals such as Cu nanocrystals even after filament erasure, which can behave as filament nuclei. This is thought to make the filament formation easy and to induce reduction of V Set.
The results mentioned above suggest that the Cu filament is formed/erased by application of positive/negative voltage, and the CBRAM operation is achieved. Checking the TEM video, the filament grew from the probe (negative voltage side) with positive voltage, and it was ruptured and erased from the substrate (negative voltage side) with negative voltage. This dynamics fits to the electrochemical model (ECM) reported so far, where the Cu ions drifted along the electric field are reduced to be the metal by receiving electrons on the cathode surface, and the Cu filament is formed towards the anode [1]. However, the current was small (<1 μA), and the retention property of the LRS was not good enough. The probe used as the BE was mechanically contacted to the solid electrolyte switching layer (Cu-GeS), and this is different from the realistic CBRAM device. To investigate more realistic switching operation, a Cu/MoOx/TiN trilayer CBRAM will be discussed in the next subsection.
3.2 Set/Reset Switching of Cu/MoOx/TiN
The sample was Pt/Cu/MoOx/TiN/Si where Cu and TiN were the TE and BE, respectively [11, 15, 16]. The device size was 350 nm in diameter. The electric properties were measured between the Pt cap layer (biased) and the Si substrate (grounded). An example of the I-V curve is shown in Fig. 6a, which was the second switching cycle after the initialization process called as Forming. A shaper Set than in Cu-GeS is seen in the first quadrant. The corresponding TEM images extracted from a video are presented in Fig. 6b. The resistance state was the HRS between the states A and B, and there was no clear change in the image. Just after the Set switching (state C), a small dark region (nucleus of the filament) appeared near the TiN BE. Though the current was almost the compliance value (I comp), there was no dark region binding the TE and BE. The ionic current of the Cu anion is thought to contribute to electric conduction. Afterwards, the filament grew from the TiN BE towards the Cu TE. The bridging of the filament between the TE and the BE was completed within 200 ms.
The Reset operation was started at 5 min. after the Set process was completed. The LRS was kept after this interval, because I comp was large (400 μA). Two small current jumps between −1 and −2 V in Fig. 6a correspond to the Reset switching. The Reset curve was uneven as frequently observed in conventional CBRAM devices. This may suggest that Reset is more complicated process than Set. In the corresponding TEM image (Fig. 6b), there is no clear structure change just after Reset switching (state F). This switching is thought to occur very locally, and it was not identified in the TEM image. Increasing negative current to about −300 μA (at −2.6 V), the filament was ruptured near the interface between MoOx and TiN and shrank toward the Cu TE (states G). This process with additional negative current is called the over-Reset process in this report. The filament erasure here cannot be explained by the ECM model where the filament shrinks from the Cu TE to the BE. In the present work, the surface of the TiN BE was oxidized. The resistance at this oxidized region is high, and the local temperature must increase by Joule heating. Thus, it is thought that the electrochemical reaction of Cu in this region preferentially occurred, and the Cu filament shrank toward the TE. The current of 100 μA (or more) was used for switching operation in many CBRAM devices reported earlier. While the details are still obscure, it must be sure that the Joule heat influences the Reset operation.
In this paragraph, the filament position and size will be discussed. Images after Set of five switching cycles are compared in Fig. 7, where I comp was increased stepwise. Here, the filament was almost completely erased by performing over-Reset. The initial state was the HRS, and the contrast in Fig. 7a is due to the matters such as the outer shape of the specimen. In the first switch with I comp = 200 μA, a filament having a width of 7 nm was formed (Fig. 7b). By increasing I comp, the filament width increased to 35, 45 and 100 nm in Figs. 7c–e respectively. This increase can be used for the multi-bit memory operation. However, the filament position changed as seen in these figures. This position instability is thought to be caused by almost complete filament erasure during over-Reset.
3.3 Device Degradation of Cu/WOx/TiN
The investigated sample was Pt/Cu/WOx/TiN/Si [17, 18]. Examples of I-V graphs measured during in-situ TEM are shown in Fig. 8a–c where the horizontal axis denotes the potential of the Cu electrode relative to TiN/Si. Figure 8a is the Forming curve. There was a current jump at 2.4 V. This resistance change to the LRS was much quicker than in MoOx. Correspondingly, a filament was formed between the Cu and TiN electrodes within one video frame (30 ms). The LRS was kept just before the Reset operation which was performed at 9.5 min after Set, and the retention time was long enough for in-situ TEM experiments. By carefully checking the video during the Reset operations, clear filament erasure was not identified though sharp switching to the HRS was realized. No strong over-Reset was adopted in this switching series as seen in Fig. 8b, c, and thus the filament was not erased (but with switching to the HRS). This result suggests that ReRAM switching occurs in local area of the filament. The resistance change in switching repetition (endurance graph) is shown in Fig. 8d. The resistance ratio of HRS/LRS was kept about 100, and a reasonable CBRAM endurance property is seen. However, as seen in this graph, the resistance in the HRS gradually decreased with the switching cycle. This degradation is known also in realistic ReRAM devices, and it has been reported to induce the endurance failure where the ReRAM switching cannot be achieved [20, 21]. This is believed to be caused by imbalance between Set and Reset. In Fig. 9, TEM images after Set/Reset switching cycles are compared. During switching repetition with increasing I comp, Cu moved into the WOx layer in a wide area, and the effective thickness of the WOx layer became thin. This is thought to be the origin of the endurance failure.
4 Conclusion
In this work, in-situ TEM was applied on three CBRAMs to investigate the microstructure during the switching operation. It was experimentally confirmed that the Cu filament is formed in Set, ruptured in Reset and erased in over-Reset. The filament becomes thick with increasing the operation current, but its position becomes instable. It was also confirmed that Cu moved into the solid electrolyte and thinned the switching layer. This reduces the resistance of the HRS and finally induces the endurance failure. The retention property must improve by increasing the Set current, and large resistance ratio of HRS/LRS is expected by over-Reset. However, these treatments induce instability of the filament position and movement of excess Cu in wide area. These can be origins of device failure. Selection of materials and the device structure for easy Set/Reset balancing must be important for further development of ReRAM devices.
References
Waser, R., Aono, M.: Nanoionics-based resistive switching memories. Nat. Mater 6, 833–840 (2007). doi:10.1038/nmat2023
Akinaga, H., Shima, H.: Resistive random access memory (ReRAM) based on metal oxides. Proc. IEEE 98, 2237–2251 (2010). doi:10.1109/JPROC.2010.2070830
Prezioso, M., Merrikh-Bayer, F., Hoskins, B.D., Adam, G.C., Likharev, K.K., Strukov, D.B.: Training and operation of an integrated neuromorphic network based on metal-oxide memristors. Nature 521, 61–64 (2015). doi:10.1038/nature14441
DeSalvo, B., Vianello, E., Garbin, D., Bichler, O., Perniola, L.: From memory in our brain to emerging resistive memories in neuromorphic systems. In: Proceedings of 7th International Memory Workshop (IMW), pp. 9–12. IEEE, Piscataway (2015). doi:10.1109/IMW.2015.7150286
Fujii, T., Kaji, H., Kondo, H., Hamada, K., Arita, M., Takahashi, Y.: I-V hysteresis of Pr0.7Ca0.3MnO3 during TEM observation. IOP Conf. Ser. Mater. Sci. Eng. 8, 012033 (2010). doi:10.1088/1757-899X/8/1/012033
Kwon, D.-H., et al.: Atomic structure of conducting nanofilaments in TiO2 resistive switching memory. Nat. Nanotechnol. 5, 148–153 (2010). doi:10.1038/NNANO.2009.456
Fujii, T., et al.: I-V measurement of NiO nanoregion during observation by transmissionelectron microscopy. J. Appl. Phys. 109, 053702 (2011). doi:10.1063/1.3553868
Choi, S.-J., et al.: In situ observation of voltage-induced multilevel resistive switching in solid electrolyte memory. Adv. Mater. 23(3272–3277), 2011 (2011). doi:10.1002/adma.00507
Yang, Y., Gao, P., Gaba, S., Chang, T., Pan, X., Lu, W.: Observation of conducting filament growth in nanoscale resistive memories. Nat. Commun. 3, 732 (2012). doi:10.1038/ncomms1737
Liu, Q., et al.: Real-time observation on dynamic growth/dissolution of conductive filaments in oxide-electrolyte-based ReRAM. Adv. Mater. 24, 1844–1849 (2012). doi:10.1002/adma.201104104
Kudo, M., Arita, M., Ohno, Y., Takahashi, Y.: Filament formation and erasure in molybdenum oxide during resistive switching cycles. Appl. Phys. Lett. 105, 173504 (2014). doi:10.1063/1.4898773
Kudo, M., Arita, M., Takahashi, Y., Ohba, K., Shimuta, M., Fujiwara, I.: Visualization of conductive filament during write and erase cycles on nanometer-scale ReRAM achieved by in-situ TEM. In: Proceedings of 7th International Memory Workshop (IMW), pp. 85–88. IEEE, Piscataway (2015). doi:10.1109/IMW.2015.7150312
Fujii, T., Arita, M., Takahashi, Y., Fujiwara, I.: In situ transmission electron microscopy analysis of conductive filament during solid electrolyte resistance switching. Appl. Phys. Lett. 98, 212104 (2011). doi:10.1063/1.3593494
Fujii, T., Arita, M., Takahashi, Y., Fujiwara, I.: Analysis of resistance switching and conductive filaments inside Cu-Ge-S using in situ transmission electron microscopy. J. Mater. Res. 27, 886–896 (2012). doi:10.1557/jmr.2011.437
Kudo, M., Ohno, Y., Hamada, K., Arita, M., Takahashi, Y.: In-situ TEM observation of Cu/MoOx ReRAM switching. ECS Trans. 58, 19–25 (2013). doi:10.1149/05805.0019ecst
Arita, M., Ohno, Y., Takahashi, Y.: Switching of Cu/MoOx/TiN CBRAM at MoOx/TiN interface. Phys. Status Solidi A 213, 306–310 (2016). doi:10.1002/pssa.201532414
Takahashi, A., Ohno, Y., Kudo, M., Nakane, A., Arita, M., Takahashi, Y.: Study on in-situ TEM observation of WOx ReRAMs with Cu top electrodes. Paper presented at European Material Research Society (EMRS) 2015, Spring Meeting, Congress Center, Lille, 11–15 May 2015
Arita, M., Takahashi, A., Ohno, Y., Nakane, A., Tsurumaki-Fukuchi, A., Takahashi, Y.: Switching operation and degradation of resistive random access memory composed of tungsten oxide and copper investigated using in-situ TEM. Sci. Rep. 5, 17103 (2015). doi:10.1038/srep17103
Kudo, M., et al.: Preparation of resistance random access memory samples for in situ transmission electron microscopy experiments. Thin Solid Films 533, 48–53 (2013). doi:10.1016/j.tsf.2012.10.102
Rahama, S.Z., et al.: Excellent resistive memory characteristics and switching mechanism using a Ti nanolayer at the Cu/TaOx interface. Nano. Res. Lett. 7, 345 (2012). doi:10.1186/1556-276X-7-345
Chen, Y.Y., et al.: Balancing SET/RESET pulse for >1010 endurance in HfO2/Hf 1T1R bipolar RRAM. IEEE Trans. Electr. Dev. 59, 3243–3249 (2012). doi:10.1109/TED.2012.2218607
Acknowledgments
This work was supported by KAKENHI by JSPS (Nos. 25420279, 26630141, 15H01706) and the Mitsubishi Foundation. Part of this work was collaborated with STARC and Cooperative Research Program of “Network Joint Research Center for Materials and Devices”. Support by the Nanotechnology Platform Program is also acknowledged. We are also grateful to our laboratory members for collaboration.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2017 Springer International Publishing AG
About this paper
Cite this paper
Arita, M., Takahashi, Y. (2017). Investigation on Switching Operation in Resistive RAM Using In-Situ TEM. In: Oral, A., Bahsi Oral, Z. (eds) 3rd International Multidisciplinary Microscopy and Microanalysis Congress (InterM). Springer Proceedings in Physics, vol 186. Springer, Cham. https://doi.org/10.1007/978-3-319-46601-9_24
Download citation
DOI: https://doi.org/10.1007/978-3-319-46601-9_24
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-46600-2
Online ISBN: 978-3-319-46601-9
eBook Packages: Physics and AstronomyPhysics and Astronomy (R0)