Abstract
Zinc oxide (ZnO) thin films were deposited by sol–gel spin coating method on the glass substrate and then the film was annealed at 350, 450, 550 °C for 1 h. Effect of annealing temperature on the structural and optical properties of the film was investigated. Annealed ZnO thin films are polycrystalline with (002) preferential orientation. The information on Crystalline size is obtained from the full width-at half- maximum (FWHM) of the diffraction peaks. The surface morphology of the films was investigated by atomic force microscopy (AFM). Surface roughness was found minimum (8.4 nm) for ZnO sample annealed at 450 °C. The maximum transmittance of 87 % is observed for the film annealed at 450 °C. The optical band gap value decreased and crystalline size increased with increasing the annealing temperatures.
Access provided by Autonomous University of Puebla. Download to read the full chapter text
Chapter PDF
Similar content being viewed by others
References
D. C. Look, D. C. Reynolds, J. R. Sizelove, R L Jpnes, C. W Litton, G. Cantwell, W.C. Harch, Solid state comm., 105, 399 (1998).
Sun H, Zhang Q F and Wu J L Acta Phys. Sin. 56 3479 (2007)
Kulkarni A. J. and Zhou M Appl. Phys. Lett. 88 141921 (2006)
Liu D F,Tang D S,Ci L J,Yan X Q,Liang Y X,Zhou Z P, Yuan H J, Zhou W Y and Wang G Chin. Phys.Lett. 20 928 (2003).
Wen Q,Li Q H,Chen Y J,Wang T H,He X L,Li J P and Lin C L Appl. Phys. Lett. 84 3654 (2004)
A. J. Ronovich, D. Golmoya, H. R. Bube, J. Appl. Phys., 51, 4260 (1980).
V. Srikant, D. R. Clarke, J. Appl. Phys., 81, 6357 (1997).
T. Minami, H. Nato, S. A. Takata, Thin Solid Films, 124, 43 (1985).
M. D. McCluskey and S. J. Jokela, J. Appl. Phy, 106, 071101 (2009).
O,vigil, F. Cruz, G.santana et al material chemistry and physics 68 249-252 (2001).
S. Muthukumar, C.R. Gorla, N.W. Emanetoglu, S. Liang, Y. Lu, J. Cryst. Growth 225 197–201 (2001).
B.J. Jin, S.H. Bae, S.Y. Lee, S. Im, Mater. Sci. Eng. B 71 301–305 (2000).
B.J. Jin, S. Im, S.Y. Lee, Thin Solid Films 366 107–110 (2000).
F.singh, Sanjeev kumar A.Kapoor et al. J.Appl.phys 112, 73101 (2012).
D. C. Look, D. C. Reynolds, J. W. Hemsky, R. L. Jones and J. R. Sizelove, Appl. Phys. Lett. 75, 811 (1999).
V. L. Azaroff, Elements of X-ray Crystallography, McGraw Hill, New York (1968).
X. Jiang, F. L. Wong, M. K. Fung, S. T. Lee, Appl. Phys. Lett. 83 1875 (2003).
A. E. Jimenez-Gonzalez, J. A. S. Urueta, R. J. Suarez-Parra, Cryst. Growth 192 430 (1998).
K. F. Lin, H. M. Cheng, H. C. Hsu, W. F. Hsieh, Chem. Phys. Let 409, 208 (2005).
M. Ohring: Material Science of Thin Films: Deposition and Structure, 2nd edn, Academic, San Diego, 386 - 400 (2001).
R. Sharma, K. Sehrawat, A. Wakahara and R.M. Mehra: Appl. Surf. Sci., 255, 5781(2009).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2014 Springer International Publishing Switzerland
About this paper
Cite this paper
Kumar, S., Singh, F., Kapoor, A. (2014). Structural and Optical Studies of Sol-Gel Deposited Nanostructured ZnO Thin Films: Annealing Effect. In: Jain, V., Verma, A. (eds) Physics of Semiconductor Devices. Environmental Science and Engineering(). Springer, Cham. https://doi.org/10.1007/978-3-319-03002-9_183
Download citation
DOI: https://doi.org/10.1007/978-3-319-03002-9_183
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-03001-2
Online ISBN: 978-3-319-03002-9
eBook Packages: Earth and Environmental ScienceEarth and Environmental Science (R0)